Abstract

Crumb rubber modification has been proven to enhance the properties of pure bitumen. This paper looks at some of the international standards for producing crumb rubber modified bitumen (CRMB) and reviews the effect of crumb rubber to the rheology of crumb rubber modified bitumen. The review shows that the rheology of CRMB depends on internal factors such as crumb rubber quantity, particle size, and pure bitumen composition, and external factors such as the mixing time, temperature, and also the modification technique. These factors govern the swelling process of crumb rubber particles that lead to the increase of viscosity of the modified bitumen. However, the mixing temperature and duration can cause rubber particles to depolymerize and subsequently cause loss of viscosity. Crumb rubber modification also improves the properties of bitumen by increasing the storage and loss modulus and enhancing the high and low temperature susceptibility. The effect of crumb rubber to aging properties of CRMB is also discussed. Finally several techniques of chemical modification to terminal blends of CRMB and the subsequent improvement to the settling property of CRMB are explained.

1. Introduction

Crumb rubber from waste tyres has been used in pavement construction since the 1930s. The usage has currently increased due the potential it offers in improving the performance of the asphaltic mixes and the potential solution in reducing waste tyres in landfills. Rubber crumbs can be mixed with aggregates within the asphaltic mix (dry process) or blended in bitumen at a specific temperature where rubber crumbs serves as a binder modifier (wet process). Crumb rubber modification by the wet process has been shown to have the ability to help improve the rutting resistance, resilience modulus, and fatigue cracking resistance of asphaltic mixes. This is due to the alteration to the property of the bituminous binder in terms of the viscosity, softening point, [1] loss modulus, and storage modulus [2]. The improvement is governed by the swelling process of rubber particles that interacted with bitumen. Rubber crumbs can swell up to 3 to 5 times its original size due to the absorption of maltenes component of the bitumen [3, 4]. This left a higher proportion of asphaltenes in the binder, therefore increasing its viscosity. The properties of crumb rubber modified bitumen (CRMB) is very sensitive and are highly governed by the mixing process which is dependent on external factors such as the mixing temperature, mixing duration, and type and internal factors such as type of bitumen, crumb rubber quantity, particle size, and type. Accurate selection of the processing variables is the key to successful CRMB production. Table 1 lists the key parameters in for preparing CRMB that are suggested by American Society of Testing Material (ASTM), California Department of Transportation (Caltrans), South African Bitumen Association (Sabita), and Association of Australian and New Zealand Road Transport and Traffic Authorities (Austroads) [5].

In recent developments, terminal blend CRMB has gained popularity due to a higher quality product [6, 7]. Unlike conventional wet mix that creates gel-like rubber particles through swelling, terminal blend process uses high shear mechanism to completely depolmerize rubber particles, therefore achieving total digestion of crumb rubber into bitumen. Although the viscosity of such mix is reduced, total digestion of crumb rubber resolves the problem of crumb rubber settlement in CRMB. However, some researches argue that too much digestion can cause CRMB to lose its stiffening and elastic effect on the mix [8], thus eliminating the benefit of rubber modification.

This paper reviews the effect of crumb rubber to the rheology of crumb rubber modified bitumen. The interaction between bitumen and crumb rubber and the factors governing the interaction process such the modification technique, mixing time, temperature, and crumb rubber characteristics are also being discussed along with the properties of the resulting CRMB. This is to give a comprehensive review on the effect of each factor to the property of the resulting crumb rubber modified bitumen.

2. External Factors

The mixing temperature and duration of crumb rubber modified bitumen are very crucial and will affect the performance of the binder. Due to the unique and delicate interaction process and the number of parameters involved, it is important that the mixing process of bitumen with rubber is handled with extra precautions and care. For instance, coarser rubber particles and higher rubber concentrations would require a higher mixing temperature where a more stable binder against rubber segregation and settling can be achieved [6, 11]. However, rubber will be depolymerized and dispersed into the mix if the temperature is too high and the duration is too long [12]. Crumb rubber mesh size, curing time, temperature, and mixing rate are the factors that affect the rubber depolymerisation rate [13]. Table 2 summarises the mixing parameters by some of Transportation Agencies in the United States and Canada.

The rate of swelling and the extent of swelling are highly dependent on the temperature of the interaction process. The rate of swelling increases when the temperature is increased; however, with the increase in temperature, the extent of swelling on the other hand decreases [14]. Lalwani et al. [15] reported that, at lower temperatures, the rubber-asphalt mix is nonhomogenous and has a higher viscosity; however, when the temperature is increased beyond 200°C, depolymerisation occurs causing undesirable hardening of the binder. Depolymerisation process occurs slowly when the temperature is between 150°C and 200°C and proceeds rapidly (within several hours) when the temperature is above 200°C [16]. Viscosity increases continually at 150°C and at 175°C or 200°C, and the viscosity initially increases rapidly, then reduces its pace, and subsequently decreases. At higher temperatures, (225°C) the viscosity reaches a maximum value within 5 min and decreases rapidly thereafter [17].

Shen and Amirkhanian [18] concluded that a mixing process for 15 minutes at 177°C is adequate for 15% of rubber crumb addition sizing between 30 and 40 mesh size to fully interact with the binder. Jeong et al. [19] on the other hand concluded that, for a 10% crumb rubber mixture, a longer blending time up to 60 minutes and mixing temperature up to 177°C can contribute to a higher failure temperature and viscosity of binder at 135°C. However, while releasing harmful gases into the environment, longer mixing duration and higher mixing and storage temperature have been shown to cause a higher rubber particles size reduction which leads to depolymerisation and subsequently leads to loss in viscosity. In an attempt to balance performance and storage compatibility of crumb rubber modified bitumen, Attia and Abdelrahman [6] suggested the use of fine rubber crumb to produce terminal blends of CRM. This approach saves energy as only 8% of the total interaction time requires high temperature of 200°C and lower temperature can be used for the storage period. Billiter et al. [7] also suggested that by increasing the mixing temperature, mixing time and shear rate can be reduced and this can in fact produce a homogenous and truly elastic terminal blend that have an enhanced performance.

At higher temperatures, the viscosity of CRMB was found to increase quite dramatically. According to Jeong et al. [19] compared to binder that was mixed at 177°C, at 200°C the viscosity is 5% higher, and at 223°C the viscosity increased 41%. With regards of the blending time, it was found that the viscosity of binder that was mixed for 5 minutes increases 11%, while at 480 minutes the viscosity increased to 46%. On the other hand, the failure temperature between binder mixed at 177°C and 200°C was found to be negligible. However, the failure temperature increased with blending time up to 60 minutes. Beyond the 60 minute period, the fail temperature was found not to be affected by blending time.

Mixing type too can affect the properties of crumb rubber modified bitumen. Low temperature properties, for instance, were improved with high shear mixing, while low shear mixing improves medium and high temperature properties and its resistance to fatigue cracking [20]. Dynamic viscosity, however, is not affected by blending type [21]. For high shear mixing technique, to produce optimal results for softening point and penetration values for modified binder with less than 25% crumb rubber, Li et al. had suggested a shearing time of 40 min and a shearing temperature of 180°C with a shearing rotational speed of 7000 rpm. High shear mixing will reduce the size of coarser rubber, thus speeding the interaction process. Storage stability and rubber particle dispersal can also be improved with high speed shear mixing. Attia and Abdelrahman [6] had proven that 88% (0.6% remaining from 5% rubber by the weight of bitumen) of the rubber particle can be digested by the end of the interaction process. The shape of the impeller, on the other hand, does not contribute to any changes to the rheology of binders [11]. Celauro et al. [22], however, mentioned that a low shear mixing can also produce the best performing CRMB provided that the base bitumen and crumb rubber are appropriately selected.

3. Internal Factor: Crumb Rubber Quantity and Type of Bitumen

The addition of crumb rubber has been shown to increase the properties of the bitumen such as the softening point, penetration, and the viscosity in proportion of the amount of the rubber [10, 19, 23, 24]. Table 3 shows the properties of AC-20 asphalt blended with up to 21% of 1.18 mm whole tire crumb rubber size with mixing time of 90 minutes at 176°C. Bitumen with higher viscosity will generally have a higher failure temperature and therefore have a longer service life due to higher temperature stability. Comparing crumb rubber addition of 10% and 20%, Jeong et al. [19] show that the 20% crumb rubber addition increased the viscosity by 550% and (stiffness) value by 225%. However, when subjected to Rolling Thin Film Oven test (RTFOT) which simulated short-term aging, it is found that the viscosity decreases with increasing rubber concentration [23]. This is probably due to higher rubber dissolution as demonstrated by Billiter et al. [7].

Apart from increasing the viscosity at high temperature, crumb rubber also contributes to a lower creep stiffness of the asphaltic mix which increases the low temperature cracking resistance of asphaltic pavement and lowering the aging index [2326]. Wang et al. [23] recommended 15% to 20% crumb rubber addition for a significant improvement in aging effects, creep stiffness, and economic factors. Shen and Amirkhanian [18] on the other hand showed that 10% of CRM addition increased the performance grade of bitumen from 64°C to 70°C and 15% CRM addition increased at least two high temperature performance grades from 64°C to 76°C. However, Khalid and Artamendi [27] highlight that an addition of crumb rubber of more than 10% would produce a binder that is too viscous for field mixing operations.

Crumb rubber modified bitumen, however, can have storage problems due the settling of the rubber crumbs. Shearing the mix in high temperature until the rubber particles depolymerize is one of the options that can eliminate sedimentation problems and subsequently improve the properties of the bitumen if properly manufactured [6]. Very fine rubber particles (100 to 500 mesh) on the other hand have nonsettling properties when processed with high shear mixing. This can reduce the mixing time and temperature and therefore reduce depolymerisation and enhance aging resistance [25]. Cong et al. [28] showed that a high amount of rubber (e.g., 25%), with a high swelling rate and a high lightweight fraction bitumen can improve the storage stability of CRMB. This is due to the reduction of the nondissolved rubber particle, thus reducing the sedimentation trend of the rubber particles. Navarro et al. [29] on the other hand reported that crumb rubber modified bitumen is stable for particles that are sized 0.29 mm or less.

Crumb rubber from waste tyres typically contains several types of compounds such as synthetic rubber content, natural rubber content, total rubber hydrocarbon content, and acetone extractables [10]. This is due to the different proportion of natural rubber, synthetic rubber, and other components between truck tyres and passenger car tyres. For instance, truck tyres contain more natural rubber when compared to passenger cars (which is higher in synthetic rubber) and this can affect the interaction between bitumen and rubber particles. Higher dissolution of crumb rubber that contains a mixture of truck and passenger car tyres can improve the viscoelastic properties of bitumen, while higher dissolution of crumb rubber solely sourced from truck tyres does not enhance the properties of the modified binder [30]. Table 4 shows the chemical composition of passenger car tire and truck tires [10]. Thodesen et al. [31], however, showed that CRMB produced using truck tire crumb poses the highest viscosity, and Cao and Bai [32] reported that crumb rubber that comes from truck tires gives a better performance in terms of a better fatigue resistance and high temperature performance.

The properties of pure bitumen used to produce CRMB also are very important to the quality of the modified binder. Softer bitumen with higher lightweight fraction gives a higher swelling rate to the rubber particles and thus displays a better high and low temperature properties compared to harder bitumen with the same amount of rubber modification [12, 28]. Stiffer bitumen will typically show better high temperature stiffness compared to CRMB produced with softer bitumen that have improved low temperature stiffness. Bitumen with a lower lightweight fraction will also produce CRMB that has lower viscosities and lesser degree of modification properties [10].

Ould Henia and Dumont [33] studied the effect of pure bitumen with different composition of saturates, aromatics, resin, and asphaltenes to the viscoelastic properties and the extent of crumb rubber swelling in CRMB. The study shows that aromatic oils perform as lubricant for asphaltenes, hence bitumen with higher aromatic content has a higher viscosity and displays a higher sensitivity to temperature than harder bitumen. The quantity of aromatics in the bitumen is also important to be determined prior to the mixing process in order to obtain the optimum amount of swelling in the rubber particles and subsequently ensuring the consistency of the physical properties of the mix.

4. Internal Factor: Crumb Rubber Type and Particle Size

Crumb rubber sizes can be classified into four groups, which are coarse (9.5 mm and 6.3 mm); medium size (10–30 mesh or 2 mm to 600 μm); fine (40–80 mesh or 425 μm to 180 μm); and superfine (100–200 mesh or 150 μm to 75 μm) [34]. Similar to mixing time and temperature, crumb rubber mesh size is one of the important factors that govern the rubber depolymerization rate [35]. Finer crumb rubber will swell faster due to a larger specific area and therefore gives higher viscosities compared to coarser size. CRMB produced from fine rubber particles will also have a faster viscosity reduction in the heating process due to its faster swelling rate and thus a faster depolymerisation process. Sun and Li mentioned that the factors that influence the viscosity of CRMA according to their order of significance are crumb rubber content, mixing temperature, rubber particle size, and mixing time [17, 36].

Apart from its sizing, crumb rubber properties can also differ in terms of its microstructure. Several methods have been used to improve the microstructure of crumb rubber surface. Microwave irradiation of crumb rubber surface method cleft the surface of the vulcanization network, giving crumb rubber higher surface activity, and therefore improves its viscoelastic nature and storage stability [37]. Shatanawi et al. [38] explore the possibility of using hot water to activate the surfaces of crumb rubber. This process removes light oil fractions in the crumb rubber particles, where it reduces segregation between rubber particles and binder, thus improving its compatibility. Although the process does improve the settling properties of CRMB, it does not improve the rheology of the binder.

The difference in the crumb rubber surface microstructure can also differ due to the method the crumb rubber is manufactured. Rubber crumbs that are produced using the cryogenic method have angular, smooth, and cracked appearance, while crumbs that were produced using ambient grinding have a rather porous surface [18]. This gives the crumb rubber that was produced using the ambient grinding twice the amount of surface area when compared with its cryogenic counterpart [39].

Due to its larger surface area and subsequent swelling rate, ambient processed crumb rubber will generally give a better performance than its cryogenic counterpart [28]. CRMB produced from ambient crumb rubber gives a higher viscosity, complex modulus, and phase angle and thus gives better rutting resistance and higher elasticity [3942]. Porous surface of ambient crumb rubber assisted the absorption of higher light constituents from the asphalt, thus increasing its failure temperature regardless of the mixing time. Lee et al. [41] showed that CRM binders produced with ambient CRM also showed a better resistance on low temperature cracking than those with cryogenic CRM.

Crumb rubber particle size also plays an important role in determining the outcome performance of CRMB. Smaller particle size produces modified bitumen that has higher viscosity, softening point, and resilience due to a higher surface area [17, 25, 43, 44] and aspect ratio [45]. Wang et al. [23] reported that finer crumb rubber attains higher viscosity at high temperature and lower creep stiffness at low temperature. Higher viscosity also leads to a better rutting resistance as shown by C. C. Wong and W.-g. Wong [46]. Cao and Bai [32] on the other hand showed that larger crumb rubber gives a better high temperature performance and similar low temperature cracking resistance between CRMB manufactured with smaller crumb rubber particle size.

Similar results are demonstrated by Sebaaly et al. [26] where the authors mentioned that while crumb rubber size does not have a significant effect on the low temperature properties of bitumen, different combinations of crumb rubber size and content can either improve or jeopardize the low temperature performance grade of the CRMB. A separate design of optimum rubber content is therefore required for each crumb rubber size and bitumen grade to ensure a properly designed CRMB.

Attia and Abdelrahman [6] and Navarro et al. [45] focused on a wide variety of crumb rubber sizes in their attempt to study the effect of crumb rubber particle size to the rheology of bitumen. Their study concluded that the incorporation of coarser rubber into bitumen increases the value [6] and subsequently increases the value of storage ( ) and loss moduli ( ) especially at low frequencies. However, according to Tayebali et al. [47], the coefficient of variance for the values obtained from samples modified with 40 mesh crumb rubber size is statistically in close approximate with the one modified with an 80 mesh crumb rubber. Liu et al. [36] also mentioned that there is no significant difference between basic performances of bitumen modified with different crumb rubber size. However, it is important to note that in this particular research, the crumb rubber sizes used are 60 mesh and 80 mesh size which is rather closely spaced.

5. Aging Properties of CRMB

Binder aging is a process of oxidation and loss of lightweight constituents in bitumen that leads to hardening of the material. There are two types of aging, namely, short-term aging and long-term aging. Short-term aging occurs during the mixing period of aggregate and bitumen, while long-term aging occurs in a longer time period after the construction process. In the oxidation process, polar aromatics component of the bitumen is converted into asphaltenes, and this can be indicated by carbonyl formation [48] and resulted in a binder that has a higher viscosity. For this reason, it is important that the selection of pure bitumen to produce CRMB is done correctly since the short-term aging of CRMB manufactured using harder bitumen can create a binder that is too hard and cannot be used for paving applications [49].

Rubber addition can help to reduce the hardening rate and susceptibility of bitumen [4951]. Rubber also helps in lowering viscosity buildup with aging at low temperatures [52]. Gel permeation chromatography analysis shows that a higher proportion of crumb rubber (15% to 20%) in the bitumen contributes to the reduction of large molecular size value of the binder. This is due to the ejection of lighter constituents that were earlier absorbed by the rubber from the bitumen [53]. This helps in reducing the rate of asphaltenes formation, therefore slowing the aging process [51]. In order to further improve the aging characteristics of CRMB, Chipps et al. recommend the use of low-asphaltene bitumen processed with high-cure (terminal blend) CRMB with minimum rubber content of 10% [48]. Although hardening of asphalt cannot be avoided, there are ways that aged bitumen can be rejuvenated to its original properties with the help of rejuvenating agent [54] or other substance such as recycled waste cooking oil [55]. This technology has the potential to be an excellent solution in using recycled asphaltic pavement.

6. Chemical Modification of CRMB

Chemical modification of CRMB aims to alter the typical chemical bonding between bitumen and rubber particles. This is typically achieved with terminal blending process enhanced with certain chemicals or activators. Kocevski et al. [56] use grafting process to improve the properties of CRMB. In this process, the surface of crumb rubber is modified by bulk polymerization of acrylic acid. This process also can increase the viscosity and failure temperature of the CRMB. Chemical modifications that generate free radicals on the surface of crumb rubber are used by the US Federal Highway Administration where better interactions with bitumen are achieved resulting in a homogenous CRMB mix, therefore improving storage stability of the mix [57].

Yadollahi and Sabbagh Mollahosseini [58] on the other hand uses polyphosphoric acid and an additive known as Vestenamer to achieve crosslinking between the sulphur elements in the asphaltenes and maltenes in the bitumen to produce macropolymer network. This produces a CRMB that has better elastic properties at high temperatures and lower creep stiffness at low temperatures. Shatanawi et al. [59] showed that storage stability of CRMB can be highly improved with the addition of furfural as an activation agent in the mix. Better storage stability is also achieved by Cheng et al. [60] that uses polymeric compatibilizer containing conjugated diene that reacts as a crosslinking agent. In addition to that, the CRMB produced also has an improved permanent deformation and thermal cracking resistance.

7. Conclusion

Crumb rubber modifications of bitumen have been proven to improve characteristics of bituminous binder such as the viscosity, softening point, loss modulus, and storage modulus. This subsequently improves the rutting resistance, resilience, and improving fatigue cracking resistance of asphaltic mixes. In order to achieve a superior and balanced CRMB in term of high and low temperature properties, factors such as the mixing time, temperature, characteristics, and source of the crumb rubber and bitumen type must be considered since these are the factors that govern the resulting performance of asphaltic mixes. Aging mechanism of CRMB is also important to be considered in order that the resulting CRMB has a workable viscosity to be applied in the construction process. Finally, chemical modification of CRMB is a new area that has promising possibilities in the future to further enhance the properties of CRMB and at the same time eliminate rubber particle settling problem that is one of the limiting factor in the current application of crumb rubber modified bitumen.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.