ABSTRACT

Introduction:

Plaque accumulation and bond failure are drawbacks of orthodontic treatment, which requires composite for bonding of brackets. As the antimicrobial properties of TiO₂ nanoparticles (NPs) have been proven, the aim of this study was to evaluate the antimicrobial and mechanical properties of composite resins modified by the addition of TiO₂ NPs.

Methods:

Orthodontics composite containing 0%, 1%, 5% and 10% NPs were prepared. 180 composite disks were prepared for elution test, disk agar diffusion test and biofilm inhibition test to collect the counts of microorganisms on three days, measure the inhibition diameter and quantify the viable counts of colonies consequently. For shear bond strength (SBS) test, 48 intact bovine incisors were divided into four groups. Composites containing 0%, 1%, 5% and 10% NPs were used for bonding of bracket. The bracket/tooth SBS was measured by using an universal testing machine.

Results:

All concentration of TiO₂ NPs had a significant effect on creation and extension of inhibition zone. For S. mutans and S. sanguinis, all concentration of TiO₂ NPs caused reduction of the colony counts. Composite containing 10% TiO₂ NPs had significant effect on reduction of colony counts for S. mutans and S. sanguinis in all three days. The highest mean shear bond strength belonged to the control group, while the lowest value was seen in 10% NPs composite.

Conclusions:

Incorporating TiO₂ nanoparticles into composite resins confer antibacterial properties to adhesives, while the mean shear bond of composite containing 1% and 5% NPs still in an acceptable range.

Keywords:
Titanium dioxide, nanoparticles; Dental bonding; Antimicrobial orthodontic adhesive; Shear strength

RESUMO

Introdução:

o acúmulo de placa e as descolagens de braquetes são algumas desvantagens presentes no tratamento ortodôntico, no qual se requer o uso de materiais compósitos para a colagem dos braquetes.

Objetivo:

tendo em vista que as propriedades antimicrobianas das nanopartículas (NPs) de TiO₂ já foram confirmadas, o objetivo do presente estudo foi avaliar as propriedades antimicrobianas e mecânicas de resinas compostas modificadas pela adição de NPs de TiO₂.

Métodos:

compósitos ortodônticos contendo 0%, 1%, 5% e 10% de NPs foram preparados. Cento e oitenta discos de compósito foram preparados para o teste de eluição, o ensaio de difusão em ágar por disco, e o ensaio de inibição da formação de biofilme, para se calcular as contagens de microrganismos ao longo de três dias, medir o diâmetro da inibição e, consequentemente, quantificar as contagens de colônias viáveis. Para o teste de resistência da colagem ao cisalhamento (SBS), 48 incisivos bovinos intactos foram divididos em quatro grupos, nos quais os compósitos contendo 0%, 1%, 5% e 10% de NPs foram utilizados para colagem dos braquetes. A SBS da interface braquete/dente foi medida em uma máquina universal de ensaios.

Resultados:

todas as concentrações de NPs de TiO₂ apresentaram efeito significativo na formação e na extensão da zona de inibição. Para o S. mutans e o S. sanguinis, todas as concentrações de NPs de TiO₂ causaram redução na contagem das colônias. O compósito contendo 10% de NPs de TiO₂ apresentou uma diminuição significativa na contagem de colônias de S. mutans e S. sanguinis durante os três dias. A média mais alta da SBS foi observada no grupo controle, enquanto o valor mais baixo foi observado para o compósito com 10% de NPs.

Conclusões:

a incorporação de nanopartículas de TiO₂ nas resinas compostas lhes conferiu propriedades antibacterianas, e o valor médio da SBS das resinas contendo 1% e 5% de NPs apresentou-se dentro de uma faixa aceitável.

Palavras-chave:
Nanopartículas de dióxido de titânio; Colagem ortodôntica; Adesivo ortodôntico antibacteriano; Resistência ao cisalhamento

INTRODUCTION

Bonding technique with resin-based composite as an adhesive agent has been primarily used in Orthodontics for securing orthodontic brackets to the surface of the teeth. Unfortunately, in spite of the fact that bonding technique have many advantages - such as high esthetic and simple procedure -, still have some drawbacks such as plaque accumulation, development of white spot lesions and bond failure, which cause prolonging the treatment course, imposing high cost, consuming more chair time and a less than optimal esthetic result occurs after treatment, due to demineralization of enamel adjacent to the brackets, specially around the bracket margin, due to the surface exposed to composite.¹1 William A Brantley; Theodore Eliades. Orthodontic Material: Sienttific and clinical aspect. New York: Thieme Medical Publishers. 2002

2 Allaker RP. The use of nanoparticles to control oral biofilm formation. J Dent Res. 2010 Nov;89(11):1175-86.

3 Bernd W. Zimmer YR. Assessing patient-specific decalcification risk in fixed orthodontic treatment and its impact on prophylactic procedures. Am J Orthod Dentofacial Orthop. 2004 Sep;126(3):318-24.

4 Demling A, Heuer W, Elter C, Heidenblut T, Bach FW, Schwestka-Polly R, et al. Analysis of supra- and subgingival long-term biofilm formation on orthodontic bands. Eur J Orthod. 2009 Apr;31(2):202-6.

5 Schmit JL, Staley RN, Wefel JS, Kanellis M, Jakobsen JR, Keenan PJ. Effect of fluoride varnish on demineralization adjacent to brackets bonded with RMGI cement. Am J Orthod Dentofacial Orthop 2002 Aug;122:125-34.^-66 Arhun N, Arman A, Cehreli SB, Arikan S, Karabulut E, Gulsahi K. Microleakage beneath ceramic and metal brackets bonded with a conventional and an antibacterial adhesive system. Angle Orthod 2006 Nov;76:1028-34.

Several methods have been used to inhibit biofilm growth, which contributes to dental caries. For instance, one group of such efforts has been evaluation of effectiveness of incorporating different antimicrobial agents in the adhesives; two of the most common examples are fluoride and chlorhexidine.⁷7 Imazato S, Ebi N, Takahashi Y, et al. Antibacterial activity of bactericide- immobilized filler for resin-based restoratives. Biomaterials 2003 Seo;24(20):3605-9.

8 Yamamoto K, Ohashi S, Aono M, et al. Antibacterial activity of silver ions implanted in SiO2 filler on oral streptococci. Dent Mater 1996 Jul;12(4):227-9.

9 Syafiuddin T, Hisamitsu H, Toko T, et al. In vitro inhibition of caries around a resin composite restoration containing antibacterial filler. Biomaterials 1997 Aug;18(15):1051-7.

10 Sodagar A, Bahador A, Khalil S, et al. The effect of TiO2 and SiO2 nanoparticles on flexural strength of poly (methyl methacrylate) acrylic resins. J prosthodont Res 2013 Jan;57(1): 15-9.

11 Leung D, Spratt DA, Pratten J, et al. Chlorhexidine-releasing methacrylate dental composite materials. Biomaterials 2005 Dec;26(34): 7145-53.^-1212 Jedrychowski JR, Caputo AA, Kerper S. Antibacterial and mechanical properties of restorative materials combined with chlorhexidines. J Oral Rehabil 1983 Sep;10(5):373-81.

Today one of the most important advances in dental material field is the application of nanotechnology to resin composites. Many studies investigated the effect of antimicrobial nanoparticles incorporated into composite resins to prevent plaque accumulation and bacterial adhesion. Nanoparticles are believed to penetrate into the cell wall of bacteria efficiently due to their smaller size, effectively exerting their antibacterial properties.¹³13 Uysal T, Yagci A, Uysal B, Akdogan G. Are nano-composites and nano-ionomers suitable for orthodontic bracket bonding? Eur J Orthod. 2010 Feb;32(1):78-82.^,1414 Yacoby I, Benhar I. Antibacterial nanomedicine. Nanomedicine (Lond). 2008; 3(3): 329-41. A study evaluated the antibacterial effect of composite with different concentration of incorporated nanosilver, which has been used in Medicine as an antimicrobial agent. The result of this study showed that nanosilver containing composite could confer surface antibacterial activity without significant difference on shear bond strength.¹⁵15 AMiresmaeili, M. Atai, K.Mansouri , N.Farhadian, Effect of nanosilver incorporation on antibacterial properties and bracket bond strength of composite resin, Iranian Journal of Orthodontics. 2012;7:14-19 Another study demonstrated that addition of nanosilver significantly decreased the shear bond strength of orthodontic brackets; however, the obtained mean value was still higher than the estimated force required for orthodontic treatment.¹⁶16 Rodriguez-Arguelles MC, Sieiro C, Cao R, Nasi L. Chitosan and silver nanoparticles as pudding with raisins with antimicrobial properties. J Colloid Interface Sci. 2011 Dec 1;364(1):80-4. Silver/hydroxyapatite nanoparticles were shown to decrease the shear bond strength as their concentration increased.¹⁷17 Akhavan A, Sodagar A, Mojtahedzadeh F, Sodagar K. Investigating the effect of incorporating nanosilver/nanohydroxyapatite particles on the shear bond strength of orthodontic adhesives. Acta Odontol Scand. 2013 Sep;71(5):1038-42. Evidence shows that addition of ZnO nanoparticles to composite resin increases the mechanical properties such as compressive strength and flexural modulus.¹⁸18 Tavassoli Hojati S, Alaghemand H, Hamze F, Ahmadian Babaki F, Rajab-Nia R, Rezvani MB, et al. Antibacterial, physical and mechanical properties of flowable resin composites containing zinc oxide nanoparticles. Dent Mater. 2013 May;29(5):495-505. ZnO nanoparticles also possess antimicrobial properties and inhibit the formation of biofilm.¹⁹19 Aydin Sevinc B, Hanley L. Antibacterial activity of dental composites containing zinc oxide nanoparticles. J Biomed Mater Res B Appl Biomater. 2010 Jul;94(1):22-31. Chitosan is also used in many industries and is available in nano and microforms.²⁰20 Pinto RJ, Fernandes SC, Freire CS, Sadocco P, Causio J, Neto CP, et al. Antibacterial activity of optically transparent nanocomposite films based on chitosan or its derivatives and silver nanoparticles. Carbohydr Res. 2012 Feb 1;348:77-83.^,2121 Fujimoto T, Tsuchiya Y, Terao M, Nakamura K, Yamamoto M. Antibacterial effects of chitosan solution against Legionella pneumophila, Escherichia coli, and Staphylococcus aureus. Int J Food Microbiol. 2006 Nov 1;112(2):96-101. Recently, it has been shown that chitosan has antibacterial activity against a wide range of bacteria. Chitosan nanoparticles also enhance the antibacterial properties of composite resins without compromising their shear bond strength.²²22 Sodagar A, Bahador A. Evaluating the effect of Nano-Chitosan particle incorporation with dental Composite used in Orthodontics on shear bond strength and antimicrobial properties 1392. It has also been demonstrated that chitosan nanoparticles in conjunction with ZnO nanoparticles could improve the antimicrobial effect of composite resins, while the obtained shear bond strength values were approximately similar to conventional orthodontic composites.²³23 Mirhashemin AH, Bahador A, Kassaee MZ, Daryakenari G, Antimicrobial Effect of Nano-Zinc Oxide and Nano-Chitosan Particles in Dental Composite Used in Orthodontics, J Med Bacteriol 2013;2:1-10

Antimicrobial properties of TiO₂ nanoparticles and their application in Medicine, Dentistry and other science have been widely known. Haghi et al²⁴24 Haghi M, Hekmatafshar M, Janipour MB, Gholizadeh SS, Faraz MK, Sayyadifar F, Ghaedi M. Antibacterial effect of TiO2 nanoparticles on pathogenic strain of E. coli. International Journal of Advanced Biotechnology and Research. 2012;3(3):621-4. evaluated the antimicrobial effect of TiO₂ NPs on pathogenic strain of E. coli and they showed that the TiO₂ NPs cause little pores in bacterial cell walls, leading to increased permeability and cell death. Based on this study, nano-TiO₂ has efficient antibacterial effect and can be used as an antibacterial agent for different purposes.

We decided to assess the effect of incorporating different percentages (wt %) of TiO₂ nanoparticles into composite resin to obtain a composite with excellent antimicrobial properties and sufficient bond strength to enamel surface for use in Orthodontics.

MATERIAL AND METHODS

Nanocomposite preparation

For the fabrication of composite containing different concentration of TiO₂ NPs, 400 mg of TiO₂ NP powder was manually mixed with 3600 mg of Transbond XT composite (3M Unitek, Monrovia, CA, USA), in order to obtain 4000 mg of composite containing TiO₂NPs with 10% concentration. To fabricate composite containing 5% TiO₂ NPs, 1200 mg of composite containing 10% TiO₂ NPs was mixed with 1200 mg of plain composite. To fabricate composite containing 1% TiO₂NPs, 240 mg of 10% TiO₂ NPs was mixed with 2160 mg of plain composite. Thus, 2560 mg of composite containing 10% TiO₂NPs, 2400 mg of composite containing 5% TiO₂ NPs and 2400 mg of composite containing 1% TiO₂ NPs were thus obtained.

Shear bond strength test

Forty-eight bovine central incisors with no visible cracks or caries were disinfected in 0.5% chloramine-T solution (4°C) for one week. Specimens were randomly divided into four groups (n = 12) of composites with 0%, 1%, 5% and 10% NP content. Buccal surfaces were cleaned with a prophylaxis brush without powder, rinsed and dried; 35% phosphoric acid (Ultra-Etch, Ultradent, USA) was then applied to the buccal surfaces for 30 seconds, followed by 30 seconds of rinsing and gentle air drying. A uniform, thin layer of adhesive (3M Unitek, USA) was applied to the buccal surfaces and light cured (Woodpecker, UK) for 10 seconds after placing the stainless steel orthodontic brackets (Standard edgewise, 0.018-in slot, 12.62 mm² base area).

All specimens were thermocycled (Vafaei Industrial, Iran) for 1000 rounds in 24 hours to simulate oral environment. Each cycle consisted of 15 seconds of immersion in 5°C water bath, 10 seconds of dwell time and 15 seconds of immersion in 55°C water bath. The thermocycled teeth were then fixed to the corners of 2.5-cm diameter metal molds using rectangular wire and then the molds were filled with self-curing acrylic resin (Acropars, Iran) up to the level of the cementoenamel junction.

The shear bond strength (SBS) was measured using Roell-7060 universal testing machine (Zwick/Roell, Germany). Specimens were positioned in such way that the bracket base was parallel to the direction of the applied force. A 0.6-mm metal blade was used in an inciso-gingival direction at a crosshead speed of 0.5 mm/min to apply shear force to the composite interface (Fig 1). The obtained value (N) was divided by the bracket surface area (mm²) to calculate the SBS in megapascals. Each tooth and bracket complex was then checked under a stereomicroscope (Nikon, SMZ800, Japan) at 10 X magnification, to score the amount of remaining adhesive, by using the adhesive remnant index (ARI) as follows: 0 = no adhesive on bracket, 1 = < 25% adhesive on bracket, 2 = 25-50% adhesive on bracket, 3 = 50-75% adhesive on bracket and 4 = 75-100% adhesive on bracket.

Antimicrobial test

Preparation of bacterial suspensions: Streptococcus mutans ATCC25175, Streptococcus sanguinis ATCC10556 and Lactobacillus acidophilus ATCC4356 were supplied in liophilised form and incubated in broth, in anaerobic and 37°C conditions for 48 hours. 10⁸8 Yamamoto K, Ohashi S, Aono M, et al. Antibacterial activity of silver ions implanted in SiO2 filler on oral streptococci. Dent Mater 1996 Jul;12(4):227-9. CFU/ml microorganism suspensions were prepared by spectrophotometer for determining the antimicrobial effect of TiO₂ NPs.

Optical density for L. acidophilus in 600 nm is 1 (OD = 1); which is 10⁸8 Yamamoto K, Ohashi S, Aono M, et al. Antibacterial activity of silver ions implanted in SiO2 filler on oral streptococci. Dent Mater 1996 Jul;12(4):227-9. cells per ml. This density was then diluted ten times and inoculated on BHI (brain-heart infusion) agar. Optical density for S. mutans and S. sanguinis was OD = 0.2.

Composite disc preparation

Metal washers were placed on a glass slab and inside the washers, composite was applied with 5-mm diameter and 0.64-mm thickness. Next, a thin layer of bonding agent was applied on the samples. The reason behind selection of this particular diameter of metal washers was their equal size to bracket base. A smooth thin glass slob was placed on top of the samples and mildly compressed, to obtain a smooth composite surface with no porosity, and also to obtain equal thickness in all samples. Each sample was light-cured for 30 seconds. Then, the samples were separated from the washers and sterilized in Iran’s Nuclear Science and Technology gamma radiation center with 25 KGy dosages (Fig 2).

Biofilm inhibition

Three-day biofilms were generated on composite discs (n = 36) using 24-well plates. Each well was inoculated with adjusted bacterial inoculum. Biofilms were grown at 37°C. At the end of the third day, each disc was rinsed with sterile saline solution to remove loosely adsorbed proteins and biofilm matrix residues. To count the colony forming units (CFUs) responsible for biofilm formation, specimens were sonicated in sterile saline solution and then vortexed. CFU/ml of the microorganism present in the suspension was counted with drop-plate method using rapid dilution in microtiter plates.

Disc Agar Diffusion test (DAD)

Antibacterial activity of discs via solubility and diffusion of TiO₂ NPs was examined by DAD. Composite discs (n = 36) were placed, 2 cm apart, on BHI agar plates, which were inoculated with a 200 µL bacterial solution (≈10⁸8 Yamamoto K, Ohashi S, Aono M, et al. Antibacterial activity of silver ions implanted in SiO2 filler on oral streptococci. Dent Mater 1996 Jul;12(4):227-9.CFU/mL) by a sterile swab. After 48-hour incubation, the bacterial growth inhibition diameter was optically measured.

Antibacterial properties of eluted components

This test was used to assess the antimicrobial activity of TiO₂ NPs released from composite discs. Composite discs were placed in tubes containing 0.5 ml of BHI broth. After 3, 15 and 30 days, the discs were transferred to 15-ml plastic tubes and 50 µL of the bacterial culture was added to each tube containing 5 ml of TSA (final concentration of 10⁵5 Schmit JL, Staley RN, Wefel JS, Kanellis M, Jakobsen JR, Keenan PJ. Effect of fluoride varnish on demineralization adjacent to brackets bonded with RMGI cement. Am J Orthod Dentofacial Orthop 2002 Aug;122:125-34. CFUs/ml in 1 ml of medium). The tubes were shaken at 300 rpm at 37^oC for 24 hours. The obtained suspension was serially diluted in microtiter plates and spread cultured in TSA. The bacterial colonies (CFUs/ml) were counted using drop-plate method (Fig 3).

Statistical analysis

Shear bond strength test results were analyzed using one-way ANOVA followed by post-hoc Tukey’s HSD test. The Kruskal-Wallis test was also applied to analyze the ARI results. Antimicrobial test results were analyzed with multiple statistical tests. One-way ANOVA was first used for biofilm inhibition test, followed by Tukey HSD test. Kruskal-Wallis test was used to analyze data attained from DAD test. Two-way ANOVA was first used to analyze day × concentration relation in eluted components test. For those groups with significant difference, one-way ANOVA was used.

RESULTS

Biofilm inhibition test

Mature biofilm on four different composite groups were recorded after 3 days. Descriptive results are shown in Table 1. All tests were carried out three times for each group. Kruskal-Wallis test showed that S. mutans and S. sanguinis colonies were meaningfully lowered in all three groups of composites containing NPs (p< 0.05). However, L. acidophilus colonies were meaningfully lowered only in 10% NP containing composite (p< 0.002).

DAD test

In all three repeated tests, all three groups of composites containing NPs had a significant diameter of bacterial growth inhibition for all three microorganisms. Kruskal-Wallis test did not show any significant difference between 1%, 5% and 10% NPs groups. The results are illustrated in Table 2.

Eluted components test

For S. mutans no significant difference was found for any of the groups in any day (p= 0.144). Groups of composites containing more than 5% NPs on all days significantly reduced colony counts of S. mutans (p< 0.001). Statistically differences in all three days were found for S. sanguinis (p= 0.004) and L. acidophilus (p= 0.020) so each of the categories were analyzed by One-way ANOVA, which showed no significant difference for L. acidophilus on different days, and was only statistically significant in groups of composites containing more than 5% NPs for S. sanguinis on day 30 (p< 0.005).

Shear bond strength

Descriptive results showed that the highest mean SBS belonged to the control group, while the lowest value was seen in 10% NP composite group.

One-way ANOVA revealed a statistically significant difference in SBS among the groups (p= 0.000).

Pairwise comparison of groups revealed that the tooth/bracket SBS was significantly higher in the control group and the 1% NP group than the group containing 10% NP (p< 0.005).

The Kruskal-Wallis test did not show any significant difference among groups in terms of the ARI (p= 0.823).

DISCUSSION

The application of nanotechnology in dental composite resins has been introduced to enhance the long-term antimicrobial properties and provide superior mechanical strength simultaneously.¹³13 Uysal T, Yagci A, Uysal B, Akdogan G. Are nano-composites and nano-ionomers suitable for orthodontic bracket bonding? Eur J Orthod. 2010 Feb;32(1):78-82.^,2525 Initiative Nn. nanotechnology, big things from a tiny world. 2012.

This research assessed the antibacterial effect and shear bond strength of composite resins containing different percentage of TiO₂ nanoparticles. The result demonstrated that bacterial biofilm inhibition in composite containing NPs is significantly greater than conventional composite resins. This effect increased as the percentage of NPs in the composites increased in such a way that the composite containing more than 5% NPs significantly reduced S. mutans and S. sanguinis. However this had no effect on biofilm inhibition of L. acidophilus, which help the development of caries and are found in more advanced lesions. Therefore, the biofilm containing these microorganisms is very resistant and is not affected by adding NPs to the composite resins. This finding is in agreement with Poosti et al,²⁶26 poosti M. shear bond strenght and antibacterial effect of orthodontic composite containing TiO2 nanoparticles. Eur J Orthod. 2013 Oct;35(5)676-9. which investigated the inhibition of bacterial biofilm only on S. mutans and showed that the inhibition is more prominent with composite containing 1% TiO₂ (standard P₂₅) NPs.

For other nanoparticles such as Ag, higher antibacterial effect than conventional composite has been shown only in direct contact with S. mutans. However, bacterial growth was not significantly different in composites with or without NPs when BHI containing S. mutans was used¹⁵15 AMiresmaeili, M. Atai, K.Mansouri , N.Farhadian, Effect of nanosilver incorporation on antibacterial properties and bracket bond strength of composite resin, Iranian Journal of Orthodontics. 2012;7:14-19. On the other hand, some other studies proved that nanosilver and nanosilica filler-containing composites prevent enamel demineralization around orthodontic bracket, and showed silver NPs have antimicrobial effect against refractory bacteria.²⁷27 Alt V, Bechert T,Steinrucke P, An in vitro assessment of the antibacterial properties and cytotoxicity of nanoparticulate silver bone cement. Biomaterials 2004 Aug 25(18):4383-91^,2828 Ahn SJ, Lee SJ, Kook JK, Lim BS, Experimental antimicrobial orthodontic adhesives using nanofillers and silver nanoparticles. Dent Mater. 2009 Feb;25(2):206-13^,2929 Sodagar A, Bahador A, Azizi B. Evaluation and comparison of antibacterial effect of nano Ag in Polymethyl methacrylate Acrylic in Orthodontics., Tehran University of Medical Sciences, School of Dentistry. 2009 ;Num 4643. Silver NPs create a dark grey color change in composites, which defies the esthetic purposes.

Other nanoparticles - such as chitosan, ZnO and combination of chitosan and ZnO - in dental composites cause inhibition of bacterial biofilm, and this effect is increased as the percentage of NPs increases in composite. Although the greatest effect was seen in composite containing 10% NPs on the first day of testing,¹⁹19 Aydin Sevinc B, Hanley L. Antibacterial activity of dental composites containing zinc oxide nanoparticles. J Biomed Mater Res B Appl Biomater. 2010 Jul;94(1):22-31.^,2323 Mirhashemin AH, Bahador A, Kassaee MZ, Daryakenari G, Antimicrobial Effect of Nano-Zinc Oxide and Nano-Chitosan Particles in Dental Composite Used in Orthodontics, J Med Bacteriol 2013;2:1-10 the shear bond strength of composite was reduced as the percentage of NPs increased. The obtained shear bond strength in <5% NPs groups were in an acceptable range.²²22 Sodagar A, Bahador A. Evaluating the effect of Nano-Chitosan particle incorporation with dental Composite used in Orthodontics on shear bond strength and antimicrobial properties 1392.

The results of eluted component test showing continuity of antibacterial effect indicated significant reduction of the colony count of S. mutans and S. sanguinis, only for 10%NPs group. Similar results were showed in other NPs such as ZnO, chitosan and the combination of ZnO and chitosan, compared to TiO₂. They showed that NPs maintain their properties for a long time, up to three weeks, since just a slight increase in the number of colonies was observed, unlike L. acidophilus that by increasing time the number of colonies remains constant.¹⁹19 Aydin Sevinc B, Hanley L. Antibacterial activity of dental composites containing zinc oxide nanoparticles. J Biomed Mater Res B Appl Biomater. 2010 Jul;94(1):22-31.^,2222 Sodagar A, Bahador A. Evaluating the effect of Nano-Chitosan particle incorporation with dental Composite used in Orthodontics on shear bond strength and antimicrobial properties 1392.^,2323 Mirhashemin AH, Bahador A, Kassaee MZ, Daryakenari G, Antimicrobial Effect of Nano-Zinc Oxide and Nano-Chitosan Particles in Dental Composite Used in Orthodontics, J Med Bacteriol 2013;2:1-10

Composites containing TiO₂ nanoparticles have a significantly different shear bond strength from that of the original Transbond XT composites - used as gold standard. The bond strength decreased as the percentage of nanoparticles increased in the composite. The highest mean SBS belonged to the control group, while the lowest value was seen in 10% NP composite group. However, there was no significant difference between the obtained shear bond strength values in composite containing less than 5% nanoparticles and they were within the acceptable range of 6-8Mpa. However this may not be true for 10% NP group.

These results are in contrast to the results of other²⁶26 poosti M. shear bond strenght and antibacterial effect of orthodontic composite containing TiO2 nanoparticles. Eur J Orthod. 2013 Oct;35(5)676-9. study that showed equal bond strengths in the composites containing TiO₂ (standard P₂₅) and the control group. They just evaluated 1% nanoparticles incorporated into the composite. They concluded that adding TiO₂ nanoparticles to orthodontic composite couldn’t compromise the shear bond strength and debonding pattern of composite resins.²⁶26 poosti M. shear bond strenght and antibacterial effect of orthodontic composite containing TiO2 nanoparticles. Eur J Orthod. 2013 Oct;35(5)676-9. Similar results were obtained by Elsaka et al.³⁰30 Elasak SE, Hamaouda IM,Swain MV, Taitanium dioxide nanoparticles addition to a conventional glass-inomer restorative: influence on physical and antibacterial properties. J Dent. 2011 Sep;39(9): 589-89 after incorporating TiO₂ nanoparticles to glass-ionomer powder. They showed 3% concentration of TiO₂ improved mechanical properties of composite resins.

CONCLUSION

Incorporating TiO₂ nanoparticles into composite resins confer antibacterial properties to adhesives, while the mean shear bond of composite containing 1% and 5% nanoparticles still in an acceptable range.