Next Article in Journal
Lavandula Luisieri and Lavandula Viridis Essential Oils as Upcoming Anti-Protozoal Agents: A Key Focus on Leishmaniasis
Next Article in Special Issue
Mechanical Properties of Sandstone Cement-Stabilized Macadam
Previous Article in Journal
Design and Optimization on a Novel High-Performance Ultra-Thin Barrier AlGaN/GaN Power HEMT With Local Charge Compensation Trench
Previous Article in Special Issue
Crossover Effect in Cement-Based Materials: A Review
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Advances in the Study of the Behavior of Full-Depth Reclamation (FDR) with Cement

1
Department of Civil Engineering, University of Burgos, c/Villadiego, s/n, 09001 Burgos, Spain
2
Mechanical Engineering Department, University of the Basque Country UPV/EHU, Pº Rafael Moreno Pitxitxi, 2, 48013 Bilbao, Spain
3
Spanish Institute of Cement and Its Applications (IECA), c/José Abascal, 53, 1º, 28003 Madrid, Spain
*
Author to whom correspondence should be addressed.
Submission received: 28 June 2019 / Revised: 18 July 2019 / Accepted: 24 July 2019 / Published: 29 July 2019
(This article belongs to the Special Issue Low Binder Concrete and Mortars)

Abstract

:
Road maintenance and rehabilitation are expected to meet modern society’s demands for sustainable development. Full-depth reclamation with cement as a binder is closely linked to the concept of sustainability. In addition to the environmental benefits of reusing the existing pavement as aggregate, this practice entails significant technical and economic advantages. In Spain, in the absence of tests specifically designed to determine the behavior of recycled pavements stabilized with cement, these materials are treated as soil-cement or cement-bound granular material. This assumption is not entirely accurate, because this recycled pavement contains some bituminous elements that reduce its stiffness. This study aimed to obtain the relationships between flexural strength (FS) and the parameters that describe the pavement behavior (long-term unconfined compressive strength (UCS) and indirect tensile strength (ITS)) and compare the findings with the relationships between these parameters in soil-cement and cement-bound granular materials. The results showed that the similar behavior hypothesis is not entirely accurate for recycled pavements stabilized with cement, because they have lower strength values—although, this is not necessarily an indication of poorer performance.

1. Introduction

Pavement recycling is a road-rehabilitation technique in which a deteriorated pavement is transformed into a new course. Depending on the recycling processes and mixing temperature, pavement recycling technique can be classified as hot recycling (HR) and cold recycling (CR). HR methodology involves two techniques: Hot in-place recycling and hot central-plant recycling. On the other hand, there are three techniques for CR according to the processing place, the construction technology, and the reclamation depth: Cold in-place recycling, cold central-plant recycling, and full-depth reclamation [1,2].
Full depth reclamation (FDR) is a recycling technique in which all the asphalt pavement section and a previously quantified amount of underlying base material are treated. This mixture is pulverized, either mixed with a stabilizing agent or not, and compacted to produce a stabilized base course [3]. The usual depth that is reclaimed varies from 100 to 300 mm [4,5,6]. Sometimes, due to the structural capabilities of the mixture, it is not necessary to add any stabilizing additive, and therefore, the compacted material can be the base for a new surface layer. Nevertheless, if the obtained material does not provide enough structural strength, possible stabilizers are classified as chemical additives (Portland cement, hydrated lime, calcium chloride, and fly ash) and bitumen additives (bitumen emulsions). The most employed stabilizers worldwide are bituminous emulsions and Portland cement [3,6,7,8,9].
In this case, full depth reclamation with Portland cement (FDR-PC) yields a base course with significant structural capacity, for which the existing road is used as a “quarry” or source of aggregate. With this technique, the materials in the road are reused by pulverizing them, and adding cement, water, and sometimes a small percentage of aggregate or even an additive, in the proportions established through preliminary testing. This mixture is compacted and cured to form the course with the greatest structural strength in the new pavement [6,10,11,12,13,14].
This procedure is, without a doubt, more effective for ensuring user comfort and safety than reinforcing or rebuilding heavily cracked or deteriorated pavements.
FDR with cement has a number of technical, economic, and environmental advantages [15]. It results in a longer-lasting, less erosive, and water-resistant pavements, able to withstand the stress from traffic loads that reach the subgrade more efficiently. This high-performance technique requires no manufacturing plant or transportation of materials. It is also environmentally friendly; since the materials are reused in their present location, new aggregate deposits need not be found, nor existing quarries over-mined. The elimination of transport reduces CO2 emissions and the associated impact on the road and the traffic [3,16]. Furthermore, the reclaimed pavement can be regarded as solid waste generated from deteriorated roadways [5]. Finally, a life cycle cost analysis of construction and maintenance practices indicates that the maintenance and rehabilitation strategy based on pavement in situ recycling is the least costly, providing savings to the overall economic performance of the road pavement over the life cycle [17].
In recent years, around one million square metres of pavement were recycled in Spain annually, covering a total surface area of nearly 30 million square metres between 1998 and 2018 [18]. This is a proven method that has been widely used and has shown exceptional results to date. Based on the many advantages described, it has a promising future.
Pavement recycling as a rehabilitation method is a technique that was first used in the United Kingdom in the 1940s to repair secondary roads damaged during World War II [19]. However, FDR did not make a comeback until the mid 1980s, when a better understanding of the characteristics of semi-rigid pavements and the development of advanced machinery led to the inclusion of cement in the mix [1,20].
In Spain, cold-recycling techniques first came into use in 1991 after several unsuccessful hot-recycling experiments in the early 1990s [19,21]. The first cold-recycling trial was in Huelva, where the Ministry of Public Works recycled a 12 km stretch of road, N-431, to a depth of 30 cm [22]. Other regions subsequently undertook experiments of their own, and in some cases, such as in the region of Castilla y León, standardized the technique through widespread use. The number of recycled roads quickly grew, ultimately reaching the aforementioned 30 million square metres.
Although FDR with cement is, in principle, more widely used on roads with traffic of low intensity [3,16,23], good results have also been obtained in some of the trials conducted on roads with high-intensity flows of heavy vehicles [8,19].
However, it must be taken into account that these pavements are being designed based on the assumption that FDR with cement and soil-cement exhibit similar behavior, but it differs due to the inclusion of reclaimed asphalt pavement aggregates in their blend, which reduces the stiffness and strength of the mixture [8,14,24]. Therefore, to verify this hypothesis, the long-term characteristics of the recycled material must be determined, as they have only been estimated to date [4].
In 2001, Kolias et al. [25] reported the results of an analysis of the mechanical properties of recycled pavements with different granular and bituminous mix percentages and 3% and 5% cement. The aim was to determine the effect of the bituminous mix percentage and temperature on the strength of the recycled pavement with cement. Compressive, tensile, flexural, and fatigue strength values were found for a small number of one and 60 day specimens. The authors determined that both compressive strength and the modulus of elasticity declined with rising bituminous content. At the same time, they concluded that flexural and tensile strength did not fall at low proportions of bituminous mix, but did so very quickly at higher contents.
In 2008, Díaz et al. [26] published a preview of the unconfined compressive strength (UCS), indirect tensile strength (ITS), and flexural strength (FS) results that form part of the first phase of this study. Since then, the number of trials conducted has grown significantly.
In FDR, the most used test to verify that material was manufactured correctly is the unconfined compressive strength (UCS) test at short-term [10,27,28,29,30]. But, in order for a better long-term characterization, it is necessary to perform flexural strength tests, and, more specifically, the four-point flexural beam test [8,31,32,33,34,35,36,37,38].
This FS test is carried out using prismatic specimens and manufacturing them requires a high level of qualification and experience within the testing team [10,39]. This is the main reason for usually estimating their behavior from standardized tests, such as the unconfined compressive strength and the indirect tensile strength (ITS) tests [31,40,41,42]. For this reason, the method used in this research is the one proposed by the University of Burgos [33].
This research aimed to fill the void in the understanding of the relationships among flexural strength, unconfined compressive strength, and indirect tensile strength based on the results of the tests conducted. To this end, the methods used for other materials mixed with hydraulic binders [33,34,40,43] and the tests described by Kolias et al. [25] were taken as a starting point. Here, however, the applicable European (EN) or Spanish (UNE or NLT, as appropriate) standards were used to characterize the behavior of an FDR with cement. The accuracy of the initial hypothesis of similarity with soil-cement and cement-bound granular material was also evaluated.

2. Materials and Methods

2.1. Material

While the number of possible granular material/bituminous material combinations is virtually countless, the proportion consisting of one-third mix asphalt and two-thirds granular material is the one most commonly used in roads [16], and was consequently chosen for this study (10 cm of mix asphalt and 20 cm of granular material), as can be seen in Figure 1. The bituminous layer has approximately 4.5% of bitumen.
The granular material used in the laboratory trials was recycled pavement taken from road SA-801 (Peñaranda de Bracamonte to Campo de Peñaranda) from the west of Spain, with a maximum aggregate size of 40 mm. Figure 2 shows the granulometry of the material, which is inside the range of the SC40 (soil–cement with a maximum aggregate size of 40 mm) according to the Spanish standards [28]. It not was necessary to add any aggregate to improve the grading. The recycled material exhibited no plasticity and was free of organic matter and other substances that might prevent the cement setting.
The cement used was ESP VI-1 32.5 N [44]. This is a widely used cement type for recycled pavements stabilized with cement in roads, because of its low thermal shrinkage and long period workability due to the low quantity of clinker (<50%), high quantity of additives, and moderate strength, mainly short-term [45].
The characteristics of this type of cement are showed in Table 1.

2.2. Mix Design

The determination of maximum dry density and optimum moisture content was conducted following the UNE 103-501-94 [46] for cylindrical samples, whose prescriptions are analogous to the ASTM D1557-12 [47]. The density to be achieved in the test specimens was 2.10 g/cm3 with an optimum modified Proctor moisture content of 7.61% [46] (Figure 3).
Further to the results of the proportioning study, 3.5% ESP VI-1 32.5 N cement [44] was used to ensure a 7-day compressive strength [48,49] of at least 2.5 MPa, the minimum value required by the Spanish Ministry of Public Works [29] and the Council of Castilla y León [50] (Table 2).

2.3. Testing Program

Twenty-four prismatic specimens were prepared for flexural strength testing to characterize the recycled pavement in accordance with standard UNE-EN 12390-5, “Testing hardened concrete. Flexural strength of test specimens” [51], which is analogous to the ASTM D1635/D1635M-12 [52]. The mould dimensions where 15 cm × 15 cm × 60 cm. Samples were stored in a curing room at 20 ± 2 °C and 95% relative humidity [53]. At a curing age of at least 90 days, the four-point flexural beam test was conducted. This method ensures that the specimens break at the weakest section (uniformity of the bending moment between the two points where the load is applied).
The rollers over the specimen were placed at a distance of 15 cm (the height of the specimen), and the rollers bellow the specimen at a distance of 45 cm (three times the height of the specimen).
The applied load was transmitted by means of a plate between the specimen and the rollers over it. An increasing tension of 0.04 MPa was selected in the slowest way of the standard range of 0.04–0.06 MPa/s [51].
After each specimen of 15 × 15 × 60 cm was tested for flexural strength, specimens are broken approximately in the middle. The two resulting halves were also tested without being trimmed, one for the unconfined compressive strength (UCS) test and the other for the indirect tensile strength (ITS) test, to find the relationship between these values and the FS of the initial test specimen.
For simulating the behavior of a cubic sample in the UCS test, an auxiliary metal sheet (15 cm × 15 cm) was introduced between the lower plate and the lower side of the sample (a half from the prismatic sample), and between the top plate and the top side of the sample. This way, a uniform tensile distribution in a 15 cm cube is obtained (Figure 4a). In the case of the ITS test, the load was applied perpendicularly to the axle of the specimen with a modified metal sheet. Hence, the load was applied with a width of 15 cm (Figure 4b).
UCS tests were conducted following the standard UNE-EN 13286-41 [49], with a load speed in the range interval of 0.1 ± 0.1 MPa/s [54]. ITS strength tests were performed in accordance with UNE-EN 12390-6, “Testing hardened concrete. Tensile splitting strength of test specimens” [55].

3. Results and Discussion

Obtained results from the 72 tests conducted on the 24 prismatic specimens are shown in Table 3.

3.1. Relationship Between Flexural and Unconfined Compressive Strength

The correlation between the values of the UCS at long-term and FS at long-term is shown in Figure 5.
After examining various possible functions for correlating these two variables, the best correlation was obtained with an S shape function, with natural logarithm of the FS as dependent variable and 1/UCS as the independent variable. The developed relationship is shown in Equation (1).
Ln(FSLT-UCS)= 0.33 − 0.3225/UCSLT
where FSLT-UCS is the estimated value of the flexural strength at long-term by means of UCSLT, and UCSLT is the unconfined compressive strength at long-term, both expressed in MPa.
The coefficient of determination (R2) has a value of 0.629, which indicates that the model can explain more than the 62% of the variability of the model.
The average values obtained in the tests for these two parameters for the recycled material were compared to the usual values for soil-cement and cement-bound granular material [26,42,45,56,57,58] in Table 4.
As seen in Table 4, while the values obtained in the analysis were lower than soil-cement strength due to the bituminous matrix, the relationship between the two parameters was closer to the cement-bound granular material.

3.2. Relationship Between Flexural Strength at Long-Term and Indirect Tensile Strength at Long-Term

The correlation between FS and ITS values at long-term is shown in Figure 6, indicating a linear relationship between these parameters.
A statistical analysis was performed and it was observed that the best relationship was obtained by means of a simple linear regression, expressed in Equation (2).
FSLT-ITS = 0.187 + 1.063 ITSLT
where FSLT-ITS is the estimated value of the flexural strength at long-term obtained by means of ITSLT, and ITSLT is the indirect tensile strength at long-term, both in MPa.
The regression has a R2 value of 0.65 and the F of Fisher-Snedecor test indicated that the relationship was true with a significance level over 99%. The Student’s t-tests for the coefficients indicated that they were true, different from 0 with a significance level over 99%.
Once again, the average values obtained in the tests for these two parameters for the recycled material were compared to the usual values for soil-cement and cement-bound granular material [45] in Table 5. Although a direct relationship between ITS and FS is not established for cement-bound granular materials, it is indicated that the UCS value is approximately 10 times the ITS value [26,42,45,56,57,58]. This assumption is adopted for the analysis in Table 5.
It is observed that the ITS of the recycled material was similar to the value specified for soil-cement, while the relationship between ITS and FS was closer to a cement-bound granular material.

3.3. Relationship Between Indirect Tensile Strength and Unconfined Compressive Strength at Long-Term

The values of these two parameters (UCS and ITS) are compared in Figure 7.
The correlation between both parameters was statistically analyzed and a linear correlation was proposed, as shown in Equation (3).
ITSLT = 0.098 UCSLT
where ITSLT and UCSLT are as defined in Equations (1) and (2), respectively, both in MPa.
Equation (3) omitted the intercept because the p-value of the Student’s t-test was over 0.99, indicating that it was not significant. The relationship has an R2 value of 0.49. The F test indicated that the relationship was true with a significance level over 99%.
The relationship between these two parameters at long-term obtained for the recycled material and the usual values for cement-treated base courses [45] were found to be similar (Table 6).

3.4. Estimation of Flexural Strength at Long-Term Using the UCS and ITS Values

An additional equation for estimating the flexural strength at long-term of the FDR with cement was developed as a function of the unconfined compressive strength and the indirect tensile strength by means of a multiple linear regression, as shown in Equation (4).
FSLT-2 = 0.074 UCSLT + 0.826 ITSLT
where FSLT-2 is the flexural strength at long-term by means of UCSLT and ITSLT simultaneously, and UCSLT and STSLT are as defined in Equations (1) and (2), respectively.
Equation (4) has a coefficient of determination (R2) of 0.684. Including an intercept in Equation (4) made the coefficients of the intercept and UCS not significant. Without the intercept, both coefficients are different from 0, with a significance level over 99% (p-value of the Student’s t-test >0.99).
Figure 8 shows the obtained values of FS and the values estimated by Equations (1), (2), and (4).
As seen in Figure 8, Equation (4) is suitable for calculating FS at long-term, especially with regard to the average values of the material, despite the disperse values obtained for some specimens of the recycled material. For the extreme values, the proposed model does not fit so accurately. For specimens with the lowest values in FS, higher values are predicted with all the developed equations. On the other hand, for the highest values of FS, lower values are predicted. This fact can be attributed to the heterogeneity of the material or flawed specimen preparation or testing.
From the point of view of sustainability, the advantages of FDR when compared with soil-cement and cement-bound granular mixture are considerable. When manufacturing FDR, it is avoided to transport -emove material to landfills; there is no need to use quarries and the quantity of material that must be transported is lower and, hence, CO2 emissions are reduced. Moreover, the roads that are used for transporting the material are not so damaged.
With regard to the (expected) behavior, it can be said that the average UCS and ITS value at long-term are similar to soil-cement. In the case of the FS at long-term, the value is lower than usual for soil-cement. The fact that the FS values are lower could be regarded as a disadvantage, and perhaps the expected life of the pavement structure would not be as long as with soil-cement. However, if we compare the expected life of the new higher quality base that we are designing with the previous pavement structure, which was composed of unbound aggregates, an improvement is observed. The quality is not as high as with soil-cement, but it must be taken into account that there is a big increase in the quality of the new base compared to the previous one. With this technique, a material that is near to a standardized material is designed, which is cheaper and more sustainable. Consequently, the advantages overcome the disadvantages.

4. Conclusions

The study aimed to establish the long-term relationships among flexural, unconfined compressive, and indirect tensile strength in FDR with cement, and compared them to the strength relationships between soil-cement and cement-bound granular materials to verify the hypothesis that their behavior was similar.
The statistical analysis proved the existence of fairly close relationships among these three strength tests in the FDR, but with different behaviors to what it was expected. Flexural strength exhibited lower values in the recycled pavements than in soil-cements, whereas the indirect tensile strength and unconfined compressive strength values were similar. The relationships between unconfined compressive strength and flexural strength, and between indirect tensile strength and flexural strength, were even closer than in cement-bound granular material. In the analyzed recycled material, only the relationship between unconfined compressive strength and indirect tensile strength was similar to the relationship in cement-bound granular material and soil-cement.
With the research, in the case that only the unconfined compressive strength value is available, Equation (1) is recommended to calculate the flexural strength at long-term of the FDR. If only the indirect tensile strength is known, Equation (2) is then recommended to calculate the flexural strength of the FDR. If we have both the unconfined compressive strength and indirect tensile strength at long-term, Equation (4) is proposed to estimate the flexural strength of the FDR.
It is important to know the flexural strength, because the fatigue strength of the FDR material is calculated using this value. The hypothesis that the FDR with cement, soil-cement, and cement-bound granular material exhibit similar behaviors is not accurate and, therefore, there is a need to undertake a fatigue behavior study on this type of recycled base course to ensure the optimum design of this type of pavements.

Author Contributions

All the authors have contributed to this work in similar capacities.

Funding

The authors are grateful to the Education Council of Castilla y León for the funds received for project number BU009A06 and UB 07/03.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Xiao, F.; Yao, S.; Wang, J.; Li, X.; Amirkhanian, S. A literature review on cold recycling technology of asphalt pavement. Constr. Build. Mater. 2018, 180, 579–604. [Google Scholar] [CrossRef]
  2. Yu, B.; Liu, Q.; Tian, X.; Zhou, L.; Lin, M. Empirical performance models of hot in-place recycling of asphalt pavements. Int. J. Pavement Eng. 2017, 18, 1081–1088. [Google Scholar] [CrossRef]
  3. Jones, D.; Louw, S.; Wu, R. Full-Depth Reclamation: Cost-Effective Rehabilitation Strategy for Low-Volume Roads. Transp. Res. Rec. 2016, 2591, 1–10. [Google Scholar] [CrossRef]
  4. Smith, S.; Braham, A. Comparing layer types for the use of PavementME for asphalt emulsion Full Depth Reclamation design. Constr. Build. Mater. 2018, 158, 481–489. [Google Scholar] [CrossRef]
  5. Suebsuk, J.; Horpibulsuk, S.; Suksan, A.; Suksiripattanapong, C.; Phoo-ngernkham, T.; Arulrajah, A. Strength prediction of cement-stabilised reclaimed asphalt pavement and lateritic soil blends. Int. J. Pavement Eng. 2019, 20, 332–338. [Google Scholar] [CrossRef]
  6. Ghanizadeh, A.R.; Rahrovan, M.; Bafghi, K.B. The effect of cement and reclaimed asphalt pavement on the mechanical properties of stabilized base via full-depth reclamation. Constr. Build. Mater. 2018, 161, 165–174. [Google Scholar] [CrossRef]
  7. Hill, R.; Braham, A. Investigating the raveling test for full-depth reclamation. Front. Struct. Civ. Eng. 2018, 12, 222–226. [Google Scholar] [CrossRef]
  8. Fedrigo, W.; Núñez, W.P.; Castañeda López, M.A.; Kleinert, T.R.; Ceratti, J.A.P. A study on the resilient modulus of cement-treated mixtures of RAP and aggregates using indirect tensile, triaxial and flexural tests. Constr. Build. Mater. 2018, 171, 161–169. [Google Scholar] [CrossRef]
  9. Alizadeh, A.; Modarres, A. Mechanical and Microstructural Study of RAP–Clay Composites Containing Bitumen Emulsion and Lime. J. Mater. Civ. Eng. 2019, 31, 04018383. [Google Scholar] [CrossRef]
  10. Reeder, G.D.; Harrington, D.; Ayers, M.E.; Adaska, W.S. Guide to Full-Depth Reclamation (FDR) with Cement; National Concrete Pavement Technology Center, Institute for Transportation of Iowa State University, Portland Cement Association: Ames, IA, USA, 2017. [Google Scholar]
  11. Wirtgen. Cold Recycling Manual, 3rd ed.; Wirtgen GmbH: Windhagen, Germany, 2010. [Google Scholar]
  12. Babashamsi, P.; Yusoff, N.I.M.; Ceylan, H.; Nor, N.G.M. Recycling toward sustainable pavement development: End-of-life considerations in asphalt pavement. J. Teknol. 2016, 78, 25–32. [Google Scholar]
  13. Ghasemi, P.; Christopher Williams, R.; Jahren, C.; Ledtji, P.; Yu, J. Field Investigation of Stabilized Full-Depth Reclamation (SFDR); Minnesota Department of Transportation Research Service & Library: St. Paul, MN, USA, 2018; No. MN/RC 2018-33. [Google Scholar]
  14. Castañeda López, M.A.; Fedrigo, W.; Kleinert, T.R.; Matuella, M.F.; Núñez, W.P.; Ceratti, J.A.P. Flexural fatigue evaluation of cement-treated mixtures of reclaimed asphalt pavement and crushed aggregates. Constr. Build. Mater. 2018, 158, 320–325. [Google Scholar] [CrossRef]
  15. Portland Cement Association. Full Depth Reclamation: Recycling Roads Saves Money and Natural Resource; PCA: Skokie, IL, USA, 2005; p. 6. [Google Scholar]
  16. Godenzoni, C.; Graziani, A.; Bocci, E.; Bocci, M. The evolution of the mechanical behaviour of cold recycled mixtures stabilised with cement and bitumen: Field and laboratory study. Road Mater. Pavement Des. 2018, 19, 856–877. [Google Scholar] [CrossRef]
  17. Santos, J.; Bryce, J.; Flintsch, G.; Ferreira, A. A comprehensive life cycle costs analysis of in-place recycling and conventional pavement construction and maintenance practices. Int. J. Pavement Eng. 2017, 18, 727–743. [Google Scholar] [CrossRef]
  18. Díaz Minguela, J.; López Bachiller, M. Reciclado de Firmes In Situ con Cemento (Full Depth Reclamation with Cement); Instituto Español del Cemento y sus Aplicaciones (IECA) & Asociación Nacional Técnica de Estabilizados de Suelos y Reciclado de Firmes (ANTER): Madrid, Spain, 2018; p. 270. [Google Scholar]
  19. Jofré, C.; Kraemer, C.; Díaz, J. Manual de Firmes Reciclados In Situ con Cemento (Guide of Full Depth Reclamation with Cement); Instituto Español del Cemento y sus Aplicaciones (IECA): Madrid, Spain, 1999. [Google Scholar]
  20. Boz, I.; Solaimanian, M. Investigating the effect of rejuvenators on low-temperature properties of recycled asphalt using impact resonance test. Int. J. Pavement Eng. 2018, 19, 1007–1016. [Google Scholar] [CrossRef]
  21. Miró, R.; Edmundo Pérez Jiménez, F.; Castillo Aguilar, S. Mixed recycling with emulsion and cement of asphalt pavements. Design procedure and improvements achieved. Mater. Struct. 2000, 33, 324–330. [Google Scholar] [CrossRef] [Green Version]
  22. Díaz, J. State of the Art of In Situ Subgrade Stabilisation and Pavement Recycling with Cement in Spain; Asociación Española de la Carretera (AEC) e Instituto Español del Cemento y sus Aplicaciones (IECA): Madrid, Spain, 2001; pp. 133–161. [Google Scholar]
  23. Ozarín, T.; Gonzalo-Orden, H. Reciclado “In Situ” de firmes con cemento en carreteras autonómicas de la provincia de Palencia (On-site pavement recycling with Portlant cement on regional roads in Palencia). Carreteras 2006, 144, 34–44. [Google Scholar]
  24. Grilli, A.; Bocci, E.; Graziani, A. Influence of reclaimed asphalt content on the mechanical behaviour of cement-treated mixtures. Road Mater. Pavement Des. 2013, 14, 666–678. [Google Scholar] [CrossRef]
  25. Kolias, S.; Katsakou, M.; Kaloidas, V. Mechanical properties of flexible pavement materials recycled with cement. In Proceedings of the First International Symposium on Subgrade Stabilisation and In Situ Pavement Recycling Using Cement, Salamanca, Spain, 1–4 October 2001; Asociación Española de la Carretera (AEC) e Instituto Español del Cemento y sus Aplicaciones (IECA): Madrid, Spain, 2001; pp. 659–674. [Google Scholar]
  26. Díaz, J.; Murga, P.; Gonzalo-Orden, H.; González, D. Estudio del Comportamiento de Firmes Reciclados In Situ con Cemento (Study of the Behaviour of Full Depth Reclamation with Cement); Asociación Española de la Carretera (AEC): Madrid, Spain, 2008; pp. 519–527. [Google Scholar]
  27. BS. BS-1924-1: Stabilized Materials for Civil Engineering Purposes. General Requirements, Sampling, Sample Preparation and Tests on Materials before Stabilization; British Standards Institution: London, UK, 1990. [Google Scholar]
  28. Ministerio De Fomento. Pliego de Prescripciones Técnicas Generales para Obras de Carretera y Puentes (PG-3) (Statement of General Requirements for Construction of Roads and Bridges (PG-3)); MFOM: Madrid, Spain, 2015.
  29. Ministerio de Fomento. Pliego de Prescripciones Técnicas Generales PG-4 (Statement of General Requirements for Road Maintenance Works (PG-4)); MFOM: Madrid, Spain, 2001.
  30. Mi, S. Material and mechanics performance of full depth asphalt pavement. Fresenius Environ. Bull. 2019, 28, 2063–2066. [Google Scholar]
  31. Ismail, A.; Baghini, M.S.; Karim, M.R.; Shokri, F.; Al-Mansob, R.A.; Firoozi, A.A.; Firoozi, A.A. Laboratory Investigation on the Strength Characteristics of Cement-Treated Base. Appl. Mech. Mater. 2014, 507, 353–360. [Google Scholar] [CrossRef]
  32. Otte, E. A Structural Design Procedure for Cement-Treated Layers in. Pavements.Sc.D. Thesis, University of Pretoria, Pretoria, South Africa, 1978. [Google Scholar]
  33. Linares-Unamunzaga, A.; Gonzalo-Orden, H.; Minguela, J.; Pérez-Acebo, H. New Procedure for Compacting Prismatic Specimens of Cement-Treated Base Materials. Appl. Sci. 2018, 8, 970. [Google Scholar] [CrossRef]
  34. Linares-Unamunzaga, A.; Pérez-Acebo, H.; Rojo, M.; Gonzalo-Orden, H. Flexural Strength Prediction Models for Soil–Cement from Unconfined Compressive Strength at Seven Days. Materials 2019, 12, 387. [Google Scholar] [CrossRef]
  35. Kolias, S.; Williams, R.I.T. Cement-Bound Road Materials: Strength and Elastic Properties Measured in the Laboratory; Report SR 344; Transport and Road Research Laboratory: Crowthorne, UK, 1978. [Google Scholar]
  36. Austroads. Publication No. AP–T101/08. The Development and Evaluation of Protocols for the Laboratory Characterisation of Cemented Materials.; Austroads: Sydney, Australia, 2008. [Google Scholar]
  37. Mansoor, J.; Shah, S.; Khan, M.; Sadiq, A.; Anwar, M.; Siddiq, M.; Ahmad, H. Analysis of Mechanical Properties of Self Compacted Concrete by Partial Replacement of Cement with Industrial Wastes under Elevated Temperature. Appl. Sci. 2018, 8, 364. [Google Scholar] [CrossRef]
  38. Díaz, J. El Estudio de Comportamiento de los Firmes Reciclados In Situ con Cemento (Study of the Behaviour of Pavements Recycled In Situ with Cement). Ph.D. Thesis, Universidad de Burgos, Burgos, Spain, 2011. [Google Scholar]
  39. American Society for Testing and Materials International (ASTM). D1632-17: Standard Practice for Making and Curing Soil-Cement Compression and Flexure Test Specimens in the Laboratory; ASTM: West Conshohocken, PA, USA, 2017. [Google Scholar]
  40. Xuan, D.X.; Houben, L.J.M.; Molenaar, A.A.A.; Shui, Z.H. Mechanical properties of cement-treated aggregate material—A review. Mater. Des. 2012, 33, 496–502. [Google Scholar] [CrossRef]
  41. Lim, S.; Zollinger, D.G. Estimation of the compressive strength and modulus of elasticity of cement-treated aggregate base materials. Transp. Res. Rec. 2003, 1837, 30–38. [Google Scholar] [CrossRef]
  42. Kersten, M.S. Soil Stabilization with Portland Cement; National Academy of Sciences-National Research Council: Washington, DC, USA, 1961. [Google Scholar]
  43. Portland Cement Association (PCA). Soil-Cement Laboratory Handbook; PCA: Skokie, IL, USA, 1992. [Google Scholar]
  44. Asociación Española de Normalización y Certificación (AENOR). UNE-EN 197-1. Part 1: Composition, Specifications and Conformity Criteria for Common Cements; AENOR: Madrid, Spain, 2011. [Google Scholar]
  45. IECA-CEDEX. Manual de Firmes con Capas Tratadas con Cemento (Guideline for Pavements with Cement Bound Materials), 2nd ed.; Centro de Estudios y Experimentación de Obras Públicas (CEDEX): Madrid, Spain, 2003; p. 265. [Google Scholar]
  46. Asociación Española de Normalización y Certificación (AENOR). UNE 103-501-94: Geotechnic Compactation Test. Modified Proctor; AENOR: Madrid, Spain, 1994. [Google Scholar]
  47. American Society for Testing and Materials International (ASTM). D1557-12e1: Standard Test Methods for Laboratory Compaction Characteristics of Soil Using Modified Effort (56,000 ftlbf/ft3 (2,700 kN-m/m3)); ASTM: West Conshohocken, PA, USA, 2012. [Google Scholar]
  48. American Society for Testing and Materials International (ASTM). D1634-00: Standard Test Method for Compressive Strength of Soil-Cement Using Portions of Beams Broken in Flexure (Modified Cube Method) (Withdrawn 2015); ASTM: West Conshohocken, PA, USA, 2006. [Google Scholar]
  49. Asociación Española de Normalización y Certificación (AENOR). Norma UNE-EN 13286-41. Unbound and Hydraulically Bound Mixtures—Part 41: Test Method for the Determination of the Compressive Strength of Hydraulically Bound Mixtures; AENOR: Madrid, Spain, 2003. [Google Scholar]
  50. JCyL. Recomendaciones de Proyecto y Construcción de Firmes y Pavimentos (Recommendations for the Design and Construction of Road Pavements); Dirección General de Carreteras e Infraestructuras, Consejería de Fomento, Junta de Castilla y León: Valladolid, Spain, 2004. [Google Scholar]
  51. Asociación Española de Normalización y Certificación (AENOR). UNE-EN 12390-5. Testing Hardened Concrete—Part 5: Flexural Strength of Test Specimens; AENOR: Madrid, Spain, 2009. [Google Scholar]
  52. American Society for Testing and Materials International (ASTM). D1635/D1635M-12: Standard Test Method for Flexural Strength of Soil-Cement Using Simple Beam with Third-Point Loading; ASTM: West Conshohocken, PA, USA, 2012. [Google Scholar]
  53. Asociación Española de Normalización y Certificación (AENOR). UNE-EN 12390-2. Part 2: Making and Curing Specimens for Strength Tests; AENOR: Madrid, Spain, 2009. [Google Scholar]
  54. CEDEX. Norma NLT-305/90. Resistencia a Compresión Simple de Materiales Tratados con Conglomerantes Hidráulicos (Unconfined Compressive Strength for Bound Materials); CEDEX, Dirección General de Carreteras, Ministerio de Fomento: Madrid, Spain, 1990. [Google Scholar]
  55. Asociación Española de Normalización y Certificación (AENOR). UNE-EN 12390-6. Testing Hardened Concrete—Part 6: Tensile Splitting Strength of Test Specimens; AENOR: Madrid, Spain, 2010. [Google Scholar]
  56. Thompson, M.R. Mechanistic Design Concepts for Stabilized Base Pavements; University of Illinois: Urbana, IL, USA, 1986; p. 52. [Google Scholar]
  57. Solís Villa, L.A.; Díaz Minguela, J. Los firmes con suelocemento en la Red Autonómica de Castilla y León (Pavements with soil-cement in the regional road network of Castilla y León). Cem. Hormig. 2002, 835, 74–89. [Google Scholar]
  58. Marshall, B.P.; Kennedy, T.W. Tensile and Elastic Characteristics of Pavement Materials; Research Report 183-1; Center for Highway Research, The University of Texas at Austin: Austin, TX, USA, 1974. [Google Scholar]
Figure 1. Full-depth reclamation section.
Figure 1. Full-depth reclamation section.
Applsci 09 03055 g001
Figure 2. Used material granulometry and granulometry range for SC40.
Figure 2. Used material granulometry and granulometry range for SC40.
Applsci 09 03055 g002
Figure 3. Modified Proctor density of the material.
Figure 3. Modified Proctor density of the material.
Applsci 09 03055 g003
Figure 4. (a) UCS test; (b) indirect tensile strength (ITS) test.
Figure 4. (a) UCS test; (b) indirect tensile strength (ITS) test.
Applsci 09 03055 g004
Figure 5. Relationship between unconfined compressive strength at long-term (UCSLT) and flexural strength at long-term (FSLT).
Figure 5. Relationship between unconfined compressive strength at long-term (UCSLT) and flexural strength at long-term (FSLT).
Applsci 09 03055 g005
Figure 6. Relationship between indirect tensile strength and flexural strength.
Figure 6. Relationship between indirect tensile strength and flexural strength.
Applsci 09 03055 g006
Figure 7. Relationship between ITS and UCS at long-term.
Figure 7. Relationship between ITS and UCS at long-term.
Applsci 09 03055 g007
Figure 8. Relationship between observed flexural strength and predicted values by means of the proposed equations.
Figure 8. Relationship between observed flexural strength and predicted values by means of the proposed equations.
Applsci 09 03055 g008
Table 1. Cement ESP VI-1 32.5 N properties [44].
Table 1. Cement ESP VI-1 32.5 N properties [44].
Main Standardized ComponentValueCement Standardized SpecificationsValue
Clinker (K)25–55%Sulfate≤3.5%
Silica fumes (D) 145–75%Initial setting time≥60 min
Natural pozzolans (P) 1Final setting time≤720 min
Calcined natural pozzolans (Q) 1Expansion≤10 mm
Siliceous fly ash (V) 1UCS at 28 days22.5 ≤ R ≤ 42.5 MPa
Calcareous fly ash (W) 1UCS at 90 days 2≥32.5 MPa
Minority components0–5%Puzzolanicity8 to 15 days
Chlorides≤0.10%--
1 The natural pozzolans (P) content for Cements ESP VI-1 must be lower than 40%. 2 The code for special cements it is given by its UCS at 90 days.
Table 2. Unconfined compressive strength (UCS) at seven days for different cement content.
Table 2. Unconfined compressive strength (UCS) at seven days for different cement content.
Sample% CementDry Density (g/cm3)UCS at 7 Days (MPa)Average UCS (MPa)
P1.13.02.1511.7572.071
P1.23.02.1081.465
P1.33.02.1222.991
P2.13.52.0702.2592.637
P2.23.52.1432.560
P2.33.52.1513.092
Table 3. Long-term results obtained for flexural strength, unconfined compression strength, and indirect tensile strength tests.
Table 3. Long-term results obtained for flexural strength, unconfined compression strength, and indirect tensile strength tests.
SampleFS (MPa)UCS (MPa)ITS (MPa)
S10.8063.7660.520
S20.5983.3440.313
S30.5803.2030.402
S40.7753.9470.447
S50.7873.5800.423
S60.6103.3170.398
S70.3612.2730.198
S80.3502.8960.273
S90.5993.6490.393
S100.3662.1690.209
S110.5384.1990.488
S120.6674.3400.483
S130.5563.9180.457
S140.2212.3130.155
S150.6383.8270.394
S160.4272.9190.174
S170.4202.4650.128
S180.5855.1030.314
S190.6734.6510.345
S200.6094.5590.427
S210.5613.6630.380
S220.5163.6600.379
S230.6674.4230.386
S240.5013.6000.310
Table 4. Comparison between average UCS values at long-term and flexural strength (FS) values at long-term for soil-cement, cement-bound granular material, and obtained values for the full-depth reclamation (FDR) with cement of the study.
Table 4. Comparison between average UCS values at long-term and flexural strength (FS) values at long-term for soil-cement, cement-bound granular material, and obtained values for the full-depth reclamation (FDR) with cement of the study.
MaterialsUCSLT (MPa)FSLT (MPa)UCSLT/FSLT
Soil-cement40.94–5
Cement-bound granular material and compacted concrete81.65–6
FDR with cement3.73
(2.9 to 4.9)
0.60
(0.53 to 0.69)
6.21
Table 5. Comparison between averages of ITS values at long-term and FS values at long-term for soil-cement, cement-bound granular material, and obtained values for the FDR with cement of the study.
Table 5. Comparison between averages of ITS values at long-term and FS values at long-term for soil-cement, cement-bound granular material, and obtained values for the FDR with cement of the study.
MaterialsITSLT (MPa)FSLT (MPa)ITSLT/FSLT
Soil-cement0.40.90.4–0.5
Cement-bound granular material and compacted concrete0.81.60.5–0.6
FDR with cement0.40
(0.33 to 0.48)
0.60
(0.53 to 0.69)
0.67
Table 6. Comparison of the relationship between unconfined compressive strength and indirect tensile strength at long-term for soil-cement, cement-bound granular material, and obtained values for the FDR with cement of the study.
Table 6. Comparison of the relationship between unconfined compressive strength and indirect tensile strength at long-term for soil-cement, cement-bound granular material, and obtained values for the FDR with cement of the study.
MaterialsUCSLT/ITSLT
Soil-cement, cement-bound granular material, compacted concrete8–10
FDR pavement with cement10.20

Share and Cite

MDPI and ACS Style

Gonzalo-Orden, H.; Linares-Unamunzaga, A.; Pérez-Acebo, H.; Díaz-Minguela, J. Advances in the Study of the Behavior of Full-Depth Reclamation (FDR) with Cement. Appl. Sci. 2019, 9, 3055. https://0-doi-org.brum.beds.ac.uk/10.3390/app9153055

AMA Style

Gonzalo-Orden H, Linares-Unamunzaga A, Pérez-Acebo H, Díaz-Minguela J. Advances in the Study of the Behavior of Full-Depth Reclamation (FDR) with Cement. Applied Sciences. 2019; 9(15):3055. https://0-doi-org.brum.beds.ac.uk/10.3390/app9153055

Chicago/Turabian Style

Gonzalo-Orden, Hernán, Alaitz Linares-Unamunzaga, Heriberto Pérez-Acebo, and Jesús Díaz-Minguela. 2019. "Advances in the Study of the Behavior of Full-Depth Reclamation (FDR) with Cement" Applied Sciences 9, no. 15: 3055. https://0-doi-org.brum.beds.ac.uk/10.3390/app9153055

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop