Next Article in Journal
Application of Reactive Oxygen Species-Based Nanomaterials in Dentistry: A Review
Next Article in Special Issue
Effect of Argon Flow on Oxygen and Carbon Coupled Transport in an Industrial Directional Solidification Furnace for Crystalline Silicon Ingots
Previous Article in Journal
Three-Dimensional Electron Diffraction for Structural Analysis of Beam-Sensitive Metal-Organic Frameworks
Previous Article in Special Issue
Hydrodynamics and Mass Transfer during the Solution Growth of the K2(Co,Ni)(SO4)2•6H2O Mixed Crystals in the Shapers
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Control of Oxygen Impurities in a Continuous-Feeding Czochralski-Silicon Crystal Growth by the Double-Crucible Method

Key Laboratory of Thermo-Fluid Science and Engineering, Ministry of Education, School of Energy and Power Engineering, Xi’an Jiaotong University, Xi’an 710049, China
*
Author to whom correspondence should be addressed.
Submission received: 29 January 2021 / Revised: 22 February 2021 / Accepted: 24 February 2021 / Published: 8 March 2021
(This article belongs to the Special Issue Modeling of Crystal Growth)

Abstract

:
The continuous-feeding Czochralski method is a cost-effective method to grow single silicon crystals. An inner crucible is used to prevent the un-melted silicon feedstock from transferring to the melt-crystal interface in this method. A series of global simulations were carried out to investigate the impact of the inner crucible on the oxygen impurity distributions at the melt-crystal interface. The results indicate that, the inner crucible plays a more important role in affecting the O concentration at the melt-crystal interface than the outer crucible. It can prevent the oxygen impurities from being transported from the outer crucible wall effectively. Meanwhile, it also introduces as a new source of oxygen impurity in the melt, likely resulting in a high oxygen concentration zone under the melt-crystal interface. We proposed to enlarge the inner crucible diameter so that the oxygen concentration at the melt-crystal interface can be controlled at low levels.

1. Introduction

The continuous-feeding Czochralski method (CCZ) is an effective method to produce single crystals, especially for crystalline silicon (Si) [1,2]. Compared with the standard Czochralski (CZ) method, it has many advantages. For example, since silicon melt can be replenished continuously during a CCZ crystal growth process, the melt volume can remain limited and unchanged in the crucible so that the melt flow becomes stable and the unsteady kinetics of the melt will be suppressed. In addition, continuous recharging of the melt allows for stable control of dopant [3], impurities, and resistivity distribution in a growing crystal, which helps to improve the crystal quality [4,5]. Therefore, it is a very promising technology to produce high-quality crystals at a low cost. However, the CCZ grown crystal exhibits special defects, which are considered to be related to the relatively high hydrogen content of the recharged Si granules [6]. These defects lead to serious challenges in the application of CCZ single crystals of silicon in electronic devices. Fortunately, with respect to the solar application, they are considered unlikely to have an adverse effect on solar cell performance [7]. In recent years, with a strong demand for producing n-type crystals for high-efficiency solar cells, the CCZ method has become very promising [8,9,10]. It is predicted that the CCZ method will make significant gains in the market share over conventional CZ in the next 3–5 years [11].
The growth of crystalline silicon is invariably accompanied by impurities transport, such as oxygen (O), carbon (C), and other related products, from reactions [12]. Special attention has been paid to, and, therefore, many researches [13,14,15,16,17,18,19,20,21,22] have been contributed, the control O concentration in the melt and growing crystals. In the growth process of some conventional methods, it affects the formation of micro-defects in the growing crystal in a complex manner [13]. In the CCZ process, to prevent the unmelted silicon feedstock from transferring to the melt-crystal (m-c) interface, an inner quartz crucible is usually placed on the bottom of the outer quartz crucible [23]. Since O impurities are dissolved from the quartz crucible wall, a new source of O impurity is thus introduced. Therefore, it is important to investigate the impact of the inner crucible on the O distributions in the melt, especially at the m-c interface, because O impurities will enter the crystal through the m-c interface. If the initial O concentration of n-type CCZ wafers is too high, the solar cell efficiency will be reduced [24]. Previous research indicates that the inner crucible is the main reason for this phenomenon, and the O concentration at the m-c interface will increase in the double-crucible CCZ method [25]. Providing an electromagnetic stirring of the melt is an effective way to decrease the O concentration at the m-c interface [26]. However, the complexity of the crystal growth systems and the cost will be increased by this method.
This study aims to find an effective way to reduce the O concentration by the double-crucible CCZ method. The impact of the inner crucible was investigated by global simulations, including coupled O and C transport, which have been widely used to study the O distributions in a crystal growth process [16,20,27,28,29,30,31,32,33]. The influence mechanism of the inner crucible on the O concentration in the melt was analyzed. Based on this research, an effective method to decrease the O distribution in the double-crucible CCZ method was proposed.

2. Problem Description and Mathematical Models

2.1. Furnace Configuration

A schematic diagram of the CCZ furnace for industrial manufacture is given in Figure 1. The diameter of the crystal was 200 mm. The crystal length was 600 mm. The inner and outer crucible diameters were 300 mm and 540 mm, respectively. To prevent the un-melted silicon feedstock from transferring to the m-c interface, an inner quartz crucible was placed on the bottom of the outer quartz crucible. The main dimensions of the CCZ furnace are listed in Table 1.
In our investigation, we compared the case of the conventional CZ method with a single crucible (the single-crucible case) and the proposed CCZ method with two crucibles (the double-crucible case). For the single-crucible case, the crystal and crucible rotation rates were set as 12 rpm and −6 rpm, respectively. For the double-crucible case, the rotation rates of crystal and crucible were set as 12 rpm and −4 rpm, respectively.

2.2. Numerical Modeling

A series of global simulations were carried out in this study. An in-house software (CGeMoS) which has been developed and used in our researches [16,27,28,34,35,36] for more than 18 years (see http://cgsolar.xjtu.edu.cn/, accessed on 29 January 2021), was applied in our investigation. A grid independence test was carried out for our simulations, and the total grid number was about 60,000. The latent heat released at the m-c interface was taken into account. A dynamic meshing technique was employed to get the m-c interface position that coincides with the isotherm of 1685 K.
For O calculation, a well-developed global model of coupled O and C transport in the whole furnace was employed to study the impurities transportation in the furnace [29,30]. For the governing equations and boundary conditions of the O and C transport model, please refer to [30]. The global model has been validated in previous researches [16,18].

3. The Effect of Inner Crucible on the O Distributions in Melt

3.1. Comparison of O Distributions in the Melt between Single-Crucible and Double-Crucible Cases

Since the O is dissolved from the quartz crucible wall, an extra O source is introduced when an inner crucible is placed in the outer crucible. This may lead to the increase in O concentration in the melt. However, it is the O concentration at the m-c interface that affects the O concentration in the growing crystal. Therefore, we needed to investigate the impact of the inner crucible on the O concentration at the m-c interface. For this purpose, we first carried out a series of simulations to compare the O concentration at the m-c interface between the case with a single-crucible and the case with a double-crucible.
Temperature distributions in the silicon melt using the single-crucible and double-crucible methods are shown in Figure 2. It was found that the highest melt temperature increased by about 14 K in the double-crucible case. This is because that the thermal conductivity of the inner quartz crucible is much smaller than that of the silicon melt. The introduction of the inner crucible in the melt makes the heat transferred more difficult from the outer crucible to the m-c interface, and more oxygen is released from the crucible wall with a higher temperature.
The stream function and O concentration in the melt in the single-crucible and double-crucible cases are shown in Figure 3. The O distribution patterns in the melt were similar to the melt flow patterns, which indicates that the O transportation is affected by the melt flow remarkably. For the single-crucible case, there were two vortexes in the melt, which were driven by thermal buoyancy, as shown in the left part of Figure 3a. Oxygen impurities dissolved from the crucible bottom wall were transported to the crucible sidewall by the melt flow, resulting in a high O concentration near the crucible sidewall. Then, with the interaction between the outer and inner vortexes, oxygen impurities were transported to the m-c interface by the inner vortex. A low O concentration zone was, therefore, located right under the m-c interface. Compared with the high O concentration near the crucible wall, O concentration under the m-c interface decreased by about 60%. Obviously, the flow patterns in the single-crucible case are beneficial to reduce the O concentration at the m-c interface. While for the double-crucible case, as shown in Figure 3b, high O concentration zones were observed near both the inner and outer crucible walls. Just like the single-crucible case, O impurities dissolved from the outer crucible wall were transported by the melt flow from the crucible bottom to the crucible sidewall. Melt with a high O concentration near the outer crucible wall was blocked by the inner crucible, which is helpful to decrease the O concentration at the m-c interface. However, melt with a high O concentration near the inner wall of the inner crucible can be transported to the m-c interface directly by the vortex inside the inner crucible, which may lead to the increase in O concentration at the m-c interface. Compared with the single-crucible case, O concentration under the m-c interface increased from 15 ppma to 19 ppma, which indicates that the O concentration at the m-c interface will increase in the CCZ crystal growth process with double crucibles. This result agrees well with the research reported in [25].
To clarify if this is a general conclusion for the CCZ method with double-crucible, we compared the O distributions at the crucible walls, as shown in Figure 4, for both cases with a single crucible and with double crucibles, which act as the origins of oxygen impurities. From the results shown in Figure 4, we can see that the oxygen concentration at the outer crucible walls was higher and the oxygen concentration at the inner crucible walls was lower in the double-crucible case than that in the single crucible case. Since O impurities dissolve from both the inner and outer crucible walls, it is essential to make clear which crucible is the dominant source of oxygen impurities transported to the m-c interface.

3.2. Study of the O Source at the Melt-Crystal Interface with Double-Crucible Method

To make clear which crucible is the dominant source of oxygen impurities transported to the m-c interface in the double-crucible CCZ method, we investigated the impact of the inner crucible and the outer crucible, respectively, on the O concentration at the m-c interface. For the sake of convenience in our numerical investigation, we introduced a concept of a virtual coating layer that is of no thickness and no oxygen dissolution. For example, when the inner crucible walls are covered with the virtual coating layer, there is no oxygen dissolved into the melt from the inner crucible. Therefore, the outer crucible becomes the unique source of oxygen impurities.
In Figure 5a, we show the O distribution in the melt for the case in which the outer crucible was covered by this virtual coating layer, which means that the inner crucible was the unique source of oxygen impurities in the melt. Compared with the results in Figure 3b, we found that the O concentration under the m-c interface only slightly decreased. Correspondingly, in Figure 5b, we show the O distribution in the melt for the case in which the inner crucible was covered by this virtual coating layer, which means that the outer crucible was the unique source of oxygen impurities in the melt. It is obviously found in this case that the O concentration under the m-c interface was remarkably reduced as compared to the results shown in Figure 3b and Figure 5a. In Figure 6, we compared the impact of the inner crucible and outer crucible on the oxygen distribution at the m-c interface. The results verified that the inner crucible can effectively prevent the O impurities dissolved from the outer crucible walls from being transported to the m-c interface, but the inner crucible itself acts as the dominant source of O impurities transported to the m-c interface. Therefore, the design of the inner crucible and control of the melt flow in the inner crucible are the key factors to reduce the O concentration at the m-c interface in the CCZ double-crucible method.

3.3. Approach to Decrease O Distributions at the m-c Interface by Double-Crucible Method

Based on our research, the inner crucible was the dominant source of oxygen impurities transported to the m-c interface, and the melt flow inside the inner crucible plays a key role in transporting the oxygen dissolved from the crucible walls to the m-c interface. Therefore, we proposed an approach with a larger inner crucible in the CCZ method to reduce the oxygen content in the growing crystals. We carried out numerical simulations to verify our proposed approach.
Except for the case with an inner crucible diameter of 300 mm, as we have investigated in detail, global simulations of the thermal field and oxygen transport in the whole furnace were carried out for two cases with larger inner crucible diameters of 360 mm and 420 mm, respectively. The melt flow pattern and oxygen distributions in the melt for the two cases are shown in Figure 7. Comparing the results shown in Figure 7 and Figure 3b, we can see that when the diameter of the inner crucible was enlarged, the melt flow patterns in the crucibles were similar. However, the O concentration in the melt between the two crucibles increased while it decreased inside the inner crucible. As a result, the O concentration at the m-c interface decreased accordingly, as shown in Figure 8, where a comparison is shown for O distributions at the m-c interface for cases with different inner crucible diameters and the case with a single crucible. The oxygen concentration at the m-c interface in the case with the inner crucible diameter of 420 mm was reduced by nearly 40% from about 20 ppma to about 12 ppma when compared to the case with the inner crucible diameter of 300 mm, and reduced by 25% from 16 ppma to about 12 ppma when compared to the case of conventional method with a single crucible. This finding is exciting to us because it is very useful to reduce the oxygen impurities in the silicon crystals grown by a CCZ method. Our proposed approach is, therefore, verified as effective.

4. Conclusions

In this research, a series of global simulations were carried out for a double-crucible CCZ furnace. The impact of the inner crucible on the O distribution at the m-c interface was investigated. On the one hand, the inner crucible can prevent the O impurities dissolved from the outer crucible from transporting to the m-c interface effectively. On the other hand, the inner crucible itself is the main source of O impurities transported to the m-c interface in the melt. We proposed an improved approach with a larger inner crucible diameter to reduce the O concentration at the m-c interface in a double-crucible CCZ method. The numerical investigation results verified the proposed approach as effective. The O concentration at the m-c interface can be reduced by 25% compared to the conventional CZ method with a single crucible.

Author Contributions

Conceptualization, L.L.; methodology, W.Z. and L.L.; validation, W.Z. and J.L.; formal analysis, W.Z. and L.L.; investigation, W.Z. and L.L.; writing—original draft preparation, W.Z.; writing—review and editing, W.Z., J.L., and L.L. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the National Natural Science Foundation of China (Grant No. 51676154).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Acknowledgments

The authors gratefully thank the support of National Natural Science Foundation of China (Grant No. 51676154).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Kitashima, T.; Liu, L.; Kitamura, K.; Kakimoto, K. Numerical analysis of continuous charge of lithium niobate in a double-crucible Czochralski system using the accelerated crucible rotation technique. J. Cryst. Growth 2004, 266, 109–116. [Google Scholar] [CrossRef]
  2. Kitashima, T.; Liu, L.; Kitamura, K.; Kakimoto, K. Effects of shape of an inner crucible on convection of lithium niobate melt in a double-crucible Czochralski process using the accelerated crucible rotation technique. J. Cryst. Growth 2004, 267, 574–582. [Google Scholar] [CrossRef]
  3. Yoon, Y.; Yan, Y.; Ostrom, N.P.; Kim, J.; Rozgonyi, G. Deep level transient spectroscopy and minority carrier lifetime study on Ga-doped continuous Czochralski silicon. Appl. Phys. Lett. 2012, 101, 222107. [Google Scholar] [CrossRef]
  4. Anselmo, A.; Koziol, J.; Prasad, V. Full-scale experiments on solid-pellets feed continuous Czochralski growth of silicon crystals. J. Cryst. Growth 1996, 163, 359–368. [Google Scholar] [CrossRef]
  5. Ono, N.; Arai, Y.; Abe, K.; Sahira, K. A new technique for controlling the dopant concentration in the double-crucible method. J. Cryst. Growth 1994, 135, 359–364. [Google Scholar] [CrossRef]
  6. Iino, E.; Takano, K.; Kimura, M.; Yamagisi, H. Cavities owing to hydrogen in Si single crystals grown by continuously charging CZ method. Mater. Sci. Eng. B 1996, 36, 146–149. [Google Scholar] [CrossRef]
  7. Giannattasio, A. A simplified model to predict resistivity profiles in continuous-feeding Cz-silicon crystals. J. Cryst. Growth 2020, 542, 125686. [Google Scholar] [CrossRef]
  8. Von Ammon, W. FZ and CZ crystal growth: Cost driving factors and new perspectives. Phys. Status Solidi A 2014, 211, 2461–2470. [Google Scholar] [CrossRef]
  9. Xu, H. Characterization of n-type mono-crystalline silicon ingots produced by continuous Czochralski (Cz) Technology. Energy Procedia 2015, 77, 658–664. [Google Scholar] [CrossRef] [Green Version]
  10. Xu, H.; Tian, X. Minority carrier lifetime of n-type mono-crystalline silicon produced by continuous Czochralski technology and its effect on hetero-junction solar cells. In Proceedings of the 6th International Conference on Crystalline Silicon Photovoltaics (SiliconPV), Chambéry, France, 7–10 March 2016; Ribeyron, P.J., Cuevas, A., Weeber, A., Ballif, C., Glunz, S., Poortmans, J., Brendel, R., Aberle, A., Sinton, R., Verlinden, P., et al., Eds.; Elsevir: Amsterdam, The Netherlands, 2016; Volume 92, pp. 708–714. [Google Scholar]
  11. International Technology Roadmap for Photovoltaic (ITRPV). Results 2015, 7th ed.; ITRPV: Frankfurt, Germany, 2015. [Google Scholar]
  12. Liaw, H.M. Oxygen and carbon in Czochralski-grown silicon. Microelectron. J. 1981, 12, 33–36. [Google Scholar] [CrossRef]
  13. Kulkarni, M.S. Defect dynamics, in the presence of oxygen in growing Czochralski silicon crystals. J. Cryst. Growth 2007, 303, 438–448. [Google Scholar] [CrossRef]
  14. Kesavan, V.; Srinivasan, M.; Ramasamy, P. Optimizing oxygen impurities using different heater design in the directional solidification of multi-crystalline silicon. Mater. Res. Express 2019, 6, 106323. [Google Scholar] [CrossRef]
  15. Shao, Y.; Li, Z.; Yu, Q.; Liu, L. Control of melt flow and oxygen distribution using traveling magnetic field during directional solidification of silicon ingots. Silicon 2020, 12, 2395–2404. [Google Scholar] [CrossRef]
  16. Li, Z.; Liu, L.; Ma, W.; Kakimoto, K. Effects of argon flow on impurities transport in a directional solidification furnace for silicon solar cells. J. Cryst. Growth 2011, 318, 304–312. [Google Scholar] [CrossRef]
  17. Teng, Y.-Y.; Chen, J.-C.; Huang, B.-S.; Chang, C.-H. Numerical simulation of impurity transport under the effect of a gas flow guidance device during the growth of multicrystalline silicon ingots by the directional solidification process. J. Cryst. Growth 2014, 385, 1–8. [Google Scholar] [CrossRef]
  18. Gao, B.; Nakano, S.; Kakimoto, K. Global Simulation of Coupled Carbon and Oxygen Transport in a Unidirectional Solidification Furnace for Solar Cells. J. Electrochem. Soc. 2010, 157, H153–H159. [Google Scholar] [CrossRef]
  19. Wang, H.; Liu, L.; Liu, X.; Li, Z. Control of Oxygen Transport in the Melt of a Czochralski-Silicon Crystal Growth. J. Enhanc. Heat Transf. 2012, 19, 505–514. [Google Scholar] [CrossRef]
  20. Smirnov, A.D.; Kalaev, V.V. Development of oxygen transport model in Czochralski growth of silicon crystals. J. Cryst. Growth 2008, 310, 2970–2976. [Google Scholar] [CrossRef]
  21. Liu, X.; Harada, H.; Miyamura, Y.; Han, X.-F.; Nakano, S.; Nishizawa, S.-I.; Kakimoto, K. Transient global modeling for the pulling process of Czochralski silicon crystal growth. II. Investigation on segregation of oxygen and carbon. J. Cryst. Growth 2020, 532, 125404. [Google Scholar] [CrossRef]
  22. Teng, Y.-Y.; Chen, J.-C.; Lu, C.-W.; Huang, C.-C.; Wun, W.-T.; Chen, H.-I.; Chen, C.-Y.; Lan, W.-C. Numerical simulation of the effect of heater position on the oxygen concentration in the CZ silicon crystal growth process. Int. J. Photoenergy 2012, 2012, 395235. [Google Scholar] [CrossRef]
  23. Jomaa, M.; M’Hamdi, M. Effect of crucible diameter on heat transfer and melt flow in continuous czochralski process for silicon crystal growth. In Proceedings of the 27th European Photovoltaic Solar Energy Conference and Exhibition, Frankfurt, Germany, 24–28 September 2012; pp. 1072–1075. [Google Scholar]
  24. Binns, M.J.; Kearns, J.; Good, E.A. (Invited) Impact of oxygen-related defects on lifetime degradation in n-type CCZ/CZ mono-crystalline silicon during cell processing. ECS Trans. 2014, 60, 1233–1238. [Google Scholar] [CrossRef]
  25. Ono, N.; Kida, M.; Arai, Y.; Sahira, K. A numerical study on oxygen transport in silicon melt in a double-crucible method. J. Cryst. Growth 1994, 137, 427–434. [Google Scholar] [CrossRef]
  26. Ono, N.; Trapaga, G. A numerical study of the effects of electromagnetic stirring on the distributions of temperature and oxygen concentration in silicon double-crucible Czochralski processing. J. Electrochem. Soc. 1997, 144, 764–772. [Google Scholar] [CrossRef]
  27. Liu, X.; Gao, B.; Kakimoto, K. Numerical investigation of carbon contamination during the melting process of Czochralski silicon crystal growth. J. Cryst. Growth 2015, 417, 58–64. [Google Scholar] [CrossRef]
  28. Liu, X.; Gao, B.; Nakano, S.; Kakimoto, K. Numerical investigation of carbon and silicon carbide contamination during the melting process of the Czochralski silicon crystal growth. Cryst. Res. Technol. 2015, 50, 458–463. [Google Scholar] [CrossRef]
  29. Matsuo, H.; Ganesh, R.B.; Nakano, S.; Liu, L.; Kangawa, Y.; Arafune, K.; Ohshita, Y.; Yamaguchi, M.; Kakimoto, K. Thermodynamical analysis of oxygen incorporation from a quartz crucible during solidification of multicrystalline silicon for solar cell. J. Cryst. Growth 2008, 310, 4666–4671. [Google Scholar] [CrossRef]
  30. Vorob’ev, A.N.; Sid’ko, A.P.; Kalaev, V.V. Advanced chemical model for analysis of Cz and DS Si-crystal growth. J. Cryst. Growth 2014, 386, 226–234. [Google Scholar] [CrossRef]
  31. Bornside, D.E.; Brown, R.A.; Fujiwara, T.; Fujiwara, H.; Kubo, T. The Effects of Gas-Phase Convection on Carbon Contamination of Czochralski-Grown Silicon. J. Electrochem. Soc. 1995, 142, 2790–2804. [Google Scholar] [CrossRef]
  32. Chen, J.-C.; Chiang, P.-Y.; Chang, C.-H.; Teng, Y.-Y.; Huang, C.-C.; Chen, C.-H.; Liu, C.-C. Three-dimensional numerical simulation of flow, thermal and oxygen distributions for a Czochralski silicon growth with in a transverse magnetic field. J. Cryst. Growth 2014, 401, 813–819. [Google Scholar] [CrossRef]
  33. Lan, C. Recent progress of crystal growth modeling and growth control. Chem. Eng. Sci. 2004, 59, 1437–1457. [Google Scholar] [CrossRef]
  34. Liu, L.; Nakano, S.; Kakimoto, K. Investigation of oxygen distribution in electromagnetic CZ-Si melts with a transverse magnetic field using 3D global modeling. J. Cryst. Growth 2007, 299, 48–58. [Google Scholar] [CrossRef]
  35. Liu, L.J.; Kakimoto, K.; Taishi, T.; Hoshikawa, K. Computational study of formation mechanism of impurity distribution in a silicon crystal during solidification. J. Cryst. Growth 2004, 265, 399–409. [Google Scholar] [CrossRef]
  36. Zhao, W.; Liu, L. Control of heat transfer in continuous-feeding Czochralski-silicon crystal growth with a water-cooled jacket. J. Cryst. Growth 2017, 458, 31–36. [Google Scholar] [CrossRef]
Figure 1. Schematic diagram of the continuous-feeding Czochralski method (CCZ) furnace with double crucibles.
Figure 1. Schematic diagram of the continuous-feeding Czochralski method (CCZ) furnace with double crucibles.
Crystals 11 00264 g001
Figure 2. Temperature distributions (K) in the melt: (a) the case with the conventional single-crucible method, (b) the case with the double-crucible method.
Figure 2. Temperature distributions (K) in the melt: (a) the case with the conventional single-crucible method, (b) the case with the double-crucible method.
Crystals 11 00264 g002
Figure 3. The stream function (left) and oxygen concentration (right, ppma) in the melt: (a) the case with the conventional single-crucible method, (b) the case with the double-crucible method.
Figure 3. The stream function (left) and oxygen concentration (right, ppma) in the melt: (a) the case with the conventional single-crucible method, (b) the case with the double-crucible method.
Crystals 11 00264 g003aCrystals 11 00264 g003b
Figure 4. The oxygen distribution (ppma) at crucible walls.
Figure 4. The oxygen distribution (ppma) at crucible walls.
Crystals 11 00264 g004
Figure 5. The O distribution (ppma) in the melt: (a) there is no oxygen dissolved into the melt from the outer crucible and the inner crucible is the unique source of oxygen impurities, (b) there is no oxygen dissolved into the melt from the inner crucible and the outer crucible is the unique source of oxygen impurities.
Figure 5. The O distribution (ppma) in the melt: (a) there is no oxygen dissolved into the melt from the outer crucible and the inner crucible is the unique source of oxygen impurities, (b) there is no oxygen dissolved into the melt from the inner crucible and the outer crucible is the unique source of oxygen impurities.
Crystals 11 00264 g005
Figure 6. Impacts of the inner crucible and outer crucible on the oxygen distribution (ppma) at the m-c interface.
Figure 6. Impacts of the inner crucible and outer crucible on the oxygen distribution (ppma) at the m-c interface.
Crystals 11 00264 g006
Figure 7. The melt flow patterns (left) and O distributions (right, ppma) in the melt: (a) the inner crucible radius is 180 mm, (b) the inner crucible radius is 210 mm.
Figure 7. The melt flow patterns (left) and O distributions (right, ppma) in the melt: (a) the inner crucible radius is 180 mm, (b) the inner crucible radius is 210 mm.
Crystals 11 00264 g007
Figure 8. Comparison of O distributions (ppma) at the m-c interface.
Figure 8. Comparison of O distributions (ppma) at the m-c interface.
Crystals 11 00264 g008
Table 1. The dimensions of the continuous-feeding Czochralski method (CCZ) furnace.
Table 1. The dimensions of the continuous-feeding Czochralski method (CCZ) furnace.
Crystal Diameter (mm)Crystal Length (mm)Diameter of Inner Crucible (mm)Diameter of Outer Crucible (mm)
200600300540
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Zhao, W.; Li, J.; Liu, L. Control of Oxygen Impurities in a Continuous-Feeding Czochralski-Silicon Crystal Growth by the Double-Crucible Method. Crystals 2021, 11, 264. https://0-doi-org.brum.beds.ac.uk/10.3390/cryst11030264

AMA Style

Zhao W, Li J, Liu L. Control of Oxygen Impurities in a Continuous-Feeding Czochralski-Silicon Crystal Growth by the Double-Crucible Method. Crystals. 2021; 11(3):264. https://0-doi-org.brum.beds.ac.uk/10.3390/cryst11030264

Chicago/Turabian Style

Zhao, Wenhan, Jiancheng Li, and Lijun Liu. 2021. "Control of Oxygen Impurities in a Continuous-Feeding Czochralski-Silicon Crystal Growth by the Double-Crucible Method" Crystals 11, no. 3: 264. https://0-doi-org.brum.beds.ac.uk/10.3390/cryst11030264

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop