Size Effect of Ordered Mesoporous Carbon Nanospheres for Anodes in Li-Ion Battery
Previous Article in Journal
Nanocarriers for DNA Vaccines: Co-Delivery of TLR-9 and NLR-2 Ligands Leads to Synergistic Enhancement of Proinflammatory Cytokine Release
Previous Article in Special Issue
Nanoscience Supporting the Research on the Negative Electrodes of Li-Ion Batteries
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 5
Issue 4
10.3390/nano5042335
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Facile and Eco-Friendly Synthesis of Finger-Like Co3O4 Nanorods for Electrochemical Energy Storage

by
Shijiao Sun
,
Xiangyu Zhao
*,
Meng Yang
,
Liqun Ma
and
Xiaodong Shen
College of Materials Science and Engineering, Nanjing Tech University, Nanjing 210009, China
*
Author to whom correspondence should be addressed.
Nanomaterials 2015, 5(4), 2335-2347; https://0-doi-org.brum.beds.ac.uk/10.3390/nano5042335
Submission received: 15 October 2015 / Revised: 2 December 2015 / Accepted: 14 December 2015 / Published: 17 December 2015
(This article belongs to the Special Issue Nanostructured Materials for Li-Ion Batteries and Beyond)
Browse Figures
Versions Notes

Abstract

:
Co3O4 nanorods were prepared by a facile hydrothermal method. Eco-friendly deionized water rather than organic solvent was used as the hydrothermal media. The as-prepared Co3O4 nanorods are composed of many nanoparticles of 30–50 nm in diameter, forming a finger-like morphology. The Co3O4 electrode shows a specific capacitance of 265 F g−1 at 2 mV s−1 in a supercapacitor and delivers an initial specific discharge capacity as high as 1171 mAh g−1 at a current density of 50 mA g−1 in a lithium ion battery. Excellent cycling stability and electrochemical reversibility of the Co3O4 electrode were also obtained.

1. Introduction

One-dimensional nanomaterials have been attracting much attention for electrochemical energy storage, especially in a supercapacitor and a lithium ion battery [1,2,3]. Their high surface to volume ratio permits a high contact area with the electrolyte and hence more electroactive sites [4]. Moreover, the low dimension can enhance electron transport and ion diffusion. The time constant for diffusion is given by τ = L2/2D, where L is the diffusion length and D is the diffusion coefficient. L of the one-dimensional nanomaterials is decreased as compared with that of the bulk materials and accordingly a lower time constant is obtained [5,6]. In addition, nanomaterials can better accommodate the volume change during lithiation and delithiation [5].
Transition metal oxides which possess variable valence states have received considerable interest as electrodes in electrochemical energy storage systems, such as supercapacitors and the lithium ion battery. Cobalt oxides including binary oxides (CoO, Co2O3, and Co3O4) and ternary oxides (MCo2O4, M = transition metal) have been extensively studied. Compared with CoO or Co2O3, Co3O4 can be more easily prepared because many cobalt salts give Co3O4 upon heating in air at 300–400 °C [7]. For example, Co3O4 nanoparticles could be prepared by a molten salt method [8,9] or a urea combustion method [10]. For the application of Co3O4 in the lithium ion battery, the main problems include the large voltage hysteresis and amorphization upon discharge. Furthermore, cobalt is expensive and toxic. Partial substitution of Co with other abundant and/or eco-friendly elements to form ternary oxides MCo2O4 (M = Cu [11], Zn [12] or Mg [13]) has been performed in order to reduce the cost and toxicity of Co3O4. However, the reversible capacity of the ternary oxides usually degrades upon long-term cycling [7].
Up to now, one-dimensional Co3O4 nanomaterials with different architectures, such as nanotubes [4,14,15,16,17,18,19], nanorods [14,19,20,21,22,23,24], nanowires [25,26,27,28,29,30], nanobelts [20,31], nanofibers [32] and nanoneedles [33], have been prepared for electrochemical energy storage via various strategies. Nanorod is one of the most studied nanostructures. Several methods have been employed to synthesize Co3O4 nanorods. For example, Co3O4 nanorods with an average diameter of 20–50 nm and a length up to several micrometers were prepared via a complicated microwave-assisted hydrothermal method [24], in which a specially designed autoclave for the microwave heating is needed. Porous Co3O4 nanorods were prepared by a co-precipitation method, where argon protection is necessary, which also complicates the synthesis [23]. A microemulsion route was employed to prepare finger-like Co3O4 nanorods but unfortunately toxic cyclohexane and n-pentanol organic solvents were used [22].
Different from the above methods which are either complicate or toxic for the preparation of Co3O4 nanorods, herein, a facile hydrothermal strategy using H2O as solvent for the large-scale preparation of finger-like Co3O4 nanorods has been performed. These Co3O4 nanorods possess a length of several hundreds of nanometers. The electrochemical properties of the as-prepared Co3O4 nanorods as electrode material in the lithium ion battery or supercapacitor were investigated.

2. Results and Discussion

Figure 1 shows the X-ray diffraction (XRD) pattern of the as-prepared Co3O4 material. All the diffraction peaks can be indexed to the pure cubic Co3O4 phase (JCPDS 65-3103). No impurity phase was detected. The average crystallite size of the as-prepared Co3O4 material calculated according to Scherrer’s formula is around 23 nm, which is smaller than that of the nanorods (48.2 nm) prepared via a gas bubble-assisted assembly method [19]. This small crystallite size can shorten the Li+ diffusion distance in the lithium ion battery.
Nanomaterials 05 02335 g001 1024
Figure 1. X-ray diffraction (XRD) pattern of the as-prepared Co3O4 nanorods.
Figure 1. X-ray diffraction (XRD) pattern of the as-prepared Co3O4 nanorods.
Nanomaterials 05 02335 g001
Figure 2 shows the scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images of the as-prepared Co3O4 material. The low-magnification SEM image (Figure 2a) shows that the as-prepared Co3O4 material is composed of many nanorods of several hundreds of nanometers in length. Upon further magnification, we found these nanorods were formed by stacking many nanoparticles of 30–50 nm in diameter (Figure 2b), showing a finger-like morphology. TEM images (Figure 2c,d) confirm that each nanorod is composed of many aggregated nanoparticles. Mesopores are generated between adjacent nanoparticles, as shown in Figure 2d.
Nanomaterials 05 02335 g002 1024
Figure 2. (a,b) Scanning electron microscopy (SEM) and (c,d) transmission electron microscopy (TEM) images of the as-prepared Co3O4 nanorods.
Figure 2. (a,b) Scanning electron microscopy (SEM) and (c,d) transmission electron microscopy (TEM) images of the as-prepared Co3O4 nanorods.
Nanomaterials 05 02335 g002
The N2 adsorption-desorption technique was used to characterize the porous structure of the as-prepared Co3O4 material. Figure 3 shows the isotherm and the corresponding Barrett-Joyner-Halenda (BJH) pore size distribution curve. The isotherm can be classified as mixed type II and type IV according to the unsaturated character at a partial pressure close to unity and the presence of a hysteresis loop, which are characteristics of the meso-macroporous materials [34]. The BJH pore size distribution curve exhibits a maximum value at around 18 nm. There, pores could be related to the interstices between the nanoparticles as shown in the TEM image in Figure 2d. The calculated average pore size, Brunauer-Emmett-Teller (BET) surface area, and pore volume are 15 nm, 33 m2 g−1 and 0.11 cm3 g−1, respectively. The surface area of the as-prepared Co3O4 material is smaller than the reported values of 95.2 m2 g−1 and 115.27 m2 g−1 for the Co3O4 nanorods prepared by the co-precipitation [23] and microemulsion [22] methods, respectively. While it is much larger than 0.31–19.4 m2 g−1 for the Co3O4 nanoparticles prepared by the molten salt method [8,9]. The porous structure of our finger-like Co3O4 nanorods may facilitate electrolyte penetration and provide spaces for the strain release in both the supercapacitor and lithium ion battery systems.
Nanomaterials 05 02335 g003 1024
Figure 3. N2 adsorption-desorption isotherm and Barrett-Joyner-Halenda (BJH) pore size distribution (inset) curve of the as-prepared Co3O4 nanorods.
Figure 3. N2 adsorption-desorption isotherm and Barrett-Joyner-Halenda (BJH) pore size distribution (inset) curve of the as-prepared Co3O4 nanorods.
Nanomaterials 05 02335 g003
The capacitive performance of the as-prepared Co3O4 electrode was evaluated by cyclic voltammetry (CV). Figure 4a shows the CV curve at a scan rate of 5 mV s−1 in a potential range of 0–0.45 V. Two pairs of redox peaks (0.29/0.18 V and 0.34/0.31 V) were observed. The redox couple located at 0.29/0.18 V corresponds to the conversion reaction between CoOOH and Co3O4. The other couple located at 0.34/0.31 V is related to the conversion reaction between CoOOH and CoO2 [30]. The CV curves at different scan rates are shown in Figure 4b. With the increase of the scan rate, the current response increases. A quasi-linear relationship is observed between the redox peak current and the scan rate (Figure 4c), indicating a diffusion-controlled process and dominant surface redox reactions [35,36]. These characteristics are typical for a pseudocapacitor. The calculated specific capacitances at scan rates of 2, 5, 10, 20, and 25 mV s−1 are 265, 197, 186, 170, and 162 F g−1, respectively. The specific capacitance of the as-prepared finger-like Co3O4 nanorods is higher than the reported value of the needle-like Co3O4 nanorods (111 F g−1) [37], although our sample has a lower surface area. The unique finger-like morphology of our Co3O4 material is responsible for its better performance.
Nanomaterials 05 02335 g004 1024
Figure 4. Capacitive performance of the as-prepared Co3O4 nanorods in a potential range of 0–0.45 V. (a) Cyclic voltammetric (CV) curve at a scan rate of 5 mV s−1; (b) CV curves at different scan rates; (c) peak current as a function of scan rate from (b); (d) rate dependent specific capacitance.
Figure 4. Capacitive performance of the as-prepared Co3O4 nanorods in a potential range of 0–0.45 V. (a) Cyclic voltammetric (CV) curve at a scan rate of 5 mV s−1; (b) CV curves at different scan rates; (c) peak current as a function of scan rate from (b); (d) rate dependent specific capacitance.
Nanomaterials 05 02335 g004
The as-prepared Co3O4 nanorods were further tested as the anode in a lithium ion battery. Figure 5a shows the first three charge (delithiation) and discharge (lithiation) curves at a current density of 50 mA g−1 between 0.01 and 3.0 V. The first discharge profile displays a small plateau at around 1.25 V and a distinct plateau at around 1.0 V. The small plateau at 1.25 V corresponds to the intercalation reaction by the formation of LixCo3O4 when nanosized Co3O4 anode material was used [7,9]. The subsequent discharge results in the destruction of the LixCo3O4 structure and the formation of Co metal nanoparticles and Li2O. This is responsible for the distinct plateau at 1.0 V. The as-prepared Co3O4 nanorods deliver an initial discharge capacity as high as 1171 mAh g−1. In the first charge process, a voltage plateau at around 2.1 V is observed, which could be attributed to the reversible oxidation of Co to cobalt oxide. Besides, the discharge profiles in the subsequent cycles are different in shape from that in the first cycle. This is similar to previous reports [4,38,39,40,41,42]. The discharge capacity and coulombic efficiency as a function of the cycle number are shown in Figure 5b. The as-prepared Co3O4 nanorod electrode demonstrates excellent cycling capability. The increase of the discharge capacity in the initial cycles may be due to the gradual establishment of the Co/Li2O interface for extra Li storage, i.e., an activation process [38]. After 50 cycles, the discharge capacity still maintains 1006 mAh g−1, which is comparable with or even higher than the reported values for other forms of Co3O4 nanostructures [19,43,44,45,46,47,48]. Moreover, the coulombic efficiency maintains around 95% since the second cycle, indicates the excellent electrochemical reversibility of the as-prepared Co3O4 nanorod electrode. This superior electrochemical performance can be ascribed to its unique nanostructure. As the as-prepared Co3O4 nanorods are composed of many nanoparticles, the number of boundaries between adjacent nanoparticles is large. Correspondingly, compared with a perfect nanorod, the as-prepared Co3O4 nanorod is more thermodynamically unstable and many more electroactive sites are generated. Note that the specific discharge capacities of the finger-like Co3O4 nanorods are much higher than the theoretical capacity of Co3O4 (890 mAh g−1). The extra capacity may be ascribed to the lithium storage at the Co/Li2O interface [48]. Furthermore, the rate capability of the as-prepared Co3O4 nanorods was studied, as shown in Figure 5c. When the current density increases from 100 to 1000 mA g−1, the specific discharge capacity decreases from 872 to 518 mAh g−1.
Nanomaterials 05 02335 g005 1024
Figure 5. The lithium storage performance of the as-prepared Co3O4 nanorods at a current density of 50 mA g−1. (a) The first three charge-discharge curves; (b) cycling performance; (c) rate performance.
Figure 5. The lithium storage performance of the as-prepared Co3O4 nanorods at a current density of 50 mA g−1. (a) The first three charge-discharge curves; (b) cycling performance; (c) rate performance.
Nanomaterials 05 02335 g005
The electrochemical impedance spectroscopy (EIS) technique was used to investigate the charge transfer in the electrode material. Figure 6a shows the Nyquist plots of the fresh and cycled Co3O4 electrodes measured at open circuit voltage over a frequency range from 105 Hz to 0.01 Hz with an amplitude of 5 mV. For both electrodes, a depressed semicircle in the high-frequency region, a broad arc in the medium-frequency region and an inclined line in the low-frequency region were observed. The broad arc for the fresh electrode is visible only when the plot is presented in the whole frequency range (inset in Figure 6a) and more obvious from the corresponding bode plot (Figure S1). The equivalent circuit model shown in Figure 6b was used to fit the Nyquist plots of both electrodes. The semicircles at the high frequency region for the fresh and cycled electrodes represent the contact resistance (Rc) or the resistance caused by the SEI layer (RSEI). The arc at the medium frequency region and the inclined line at the low frequency correspond to the Li+ charge-transfer resistance (Rct) on the electrode/electrolyte interface and the Warburg resistance (W), respectively. The diameter of the arc represents the value of Rct. The Warburg resistance reflects the solid-state diffusion of Li ions in the bulk electrode [43]. Constant phase elements (CPE1 and CPE2) rather than the pure capacitance (C) reflect the non-homogeneous nature of the electrode, which leads to the formation of a depressed semicircular shape [49]. The fitting results are shown in Table 1. Consistent with previous reports [46,50], the charge-transfer resistance of the cycled electrode (215 Ω) is much smaller than that of the fresh electrode (695 Ω). The conversion reaction at the Co3O4 anode leads to the generation of many new grain boundaries and interfaces, which would facilitate the charge transfer reaction upon cycling. Moreover, the charge-transfer resistance of the cycled electrode herein is comparable with those of Co3O4 nanoparticles with opened-book morphology [44] and mesoporous Co3O4 nanoflakes [51].
Nanomaterials 05 02335 g006 1024
Figure 6. (a) Enlarged Nyquist plot of the fresh Co3O4 nanorod electrode at high frequency and Nyquist plot of the cycled electrode in the whole frequency region; the dot and the line are related to the experimental and fitting results, respectively; the inset is the Nyquist plot of the fresh electrode in the whole frequency region. (b) Equivalent circuit for the fresh and cycled electrodes; R1 represents the solution resistance (Rs) for both electrodes; R2 is the contact resistance (Rc) for the fresh electrode or the resistance caused by the SEI layer (RSEI) for the cycled electrode; R3 corresponds to the Li+ charge-transfer resistance (Rct); CPE1 and CPE2 are constant phase elements; W represents the Warburg resistance.
Figure 6. (a) Enlarged Nyquist plot of the fresh Co3O4 nanorod electrode at high frequency and Nyquist plot of the cycled electrode in the whole frequency region; the dot and the line are related to the experimental and fitting results, respectively; the inset is the Nyquist plot of the fresh electrode in the whole frequency region. (b) Equivalent circuit for the fresh and cycled electrodes; R1 represents the solution resistance (Rs) for both electrodes; R2 is the contact resistance (Rc) for the fresh electrode or the resistance caused by the SEI layer (RSEI) for the cycled electrode; R3 corresponds to the Li+ charge-transfer resistance (Rct); CPE1 and CPE2 are constant phase elements; W represents the Warburg resistance.
Nanomaterials 05 02335 g006
Table
Table 1. Impedance parameters based on the equivalent circuit above for both the fresh and cycled Co3O4 electrodes.
Table 1. Impedance parameters based on the equivalent circuit above for both the fresh and cycled Co3O4 electrodes.
Resistance (Ω)Fresh ElectrodeCycled Electrode
Rs3.749.02
Rc or RSEI11142
Rct695215

3. Experimental Section

3.1. Sample Preparation and Characterization

All chemicals were purchased from Shanghai Chemical Regent Co. (Shanghai, China) with analytical grade and used without further purification. Co3O4 nanorods were prepared via a facile and eco-friendly hydrothermal route. Typically, 1.99 g of cobalt acetate tetrahydrate (C4H6CoO4·4H2O), 1.92 g of urea and 1.00 g of surfactant cetyltrimethylammonium bromide (CTAB) were dissolved in 100 mL deionized water to give a transparent solution. The obtained solution was loaded into a Teflon-lined stainless steel autoclave, which was sealed and heated at 100 °C for 24 h in an oven. The system was then naturally cooled to room temperature, and a pink precipitation was collected. The product was washed with distilled water and anhydrous alcohol, and dried at 60 °C. Finally, the product was calcined at 400 °C for 2 h in a muffle furnace in air.
The crystal structure of the as-prepared Co3O4 material was examined by powder X-ray diffraction (XRD) (Rigaku D/MAX 2200, using Ni-filtered Cu Ka radiation, Rigaku Corporation, Tokyo, Japan). The morphology of the as-prepared Co3O4 material was investigated by field emission scanning electron microscopy (FESEM) (JEOL JSM-6700F, operating at 20 kV, JEOL Ltd., Tokyo, Japan) and transmission electron microscopy (TEM) (JEOL JEM-2010, operating at 200 kV, JEOL Ltd., Tokyo, Japan). Nitrogen adsorption-desorption isotherm was performed at 77 K using a Micromeritics ASAP 2020M analyzer (Micromeritics Corporate, Norcross, GA, USA). Prior to determination of the isotherm, the sample was degassed at 150 °C for 5 h under vacuum. The Brunauer-Emmett-Teller (BET) specific surface area was calculated using the adsorption data in the relative pressure (P/P0) range of 0.05 to 0.3, and the total pore-volume was determined from the amount adsorbed at P/P0 = 0.98. The pore-size distribution curve was calculated based on the desorption branch of the isotherm using the Barrett-Joyner-Halenda (BJH) method.

3.2. Electrochemical Characterization

For capacitive measurement, the working electrode containing 7 mg of the active material was prepared according to the following steps. 70 wt % as-prepared Co3O4, 25 wt % acetylene black as a conducting agent and 5 wt % polytetrafluoroethylene (PTFE) as a binder were homogeneously mixed and pressed onto a nickel foam (1.5 cm × 1.5 cm) current collector under a pressure of 12 MPa. The capacitive performance was evaluated in 6 M KOH electrolyte using a three electrode experimental setup. The as-prepared electrode, platinum sheet and Ag/AgCl electrode were used as working, counter, and reference electrodes, respectively. Cyclic voltammetric (CV) measurement was conducted using a CHI440 Electrochemical Workstation (CH Instruments Inc., Austin, TX, USA).
For lithium storage measurement, a working electrode containing 1–2 mg of the active material was constructed according to the following steps. 75 wt % as-prepared Co3O4, 15 wt % acetylene black as a conductive agent and 10 wt % polyvinylidene fluoride (PVDF) as a binder were homogeneously mixed in N-methyl-2-pyrrolidone (NMP) solvent. The obtained paste was cast onto Cu foil. After evaporation of the solvent at 80 °C for 2h, the electrode was punched into disks of 14 mm in diameter. The electrode was further dried at 100 °C under vacuum for 12 h. The lithium storage performance was evaluated using a two-electrode CR2032-type coin cell. The electrolyte was 1 M LiPF6 in ethylene carbonate (EC) and dimethyl carbonate (DMC) (1:1 w/w). Metallic lithium was used as both counter and reference electrodes. Cell assembly was operated in an argon-filled glove box. Galvanostatic and electrochemical impedance measurements were conducted on a LAND CT2001A battery test system (Landt Instrument, Wuhan, China) and an Autolab electrochemical workstation (Metrohm Autolab, Utrecht, The Netherlands), respectively.
All the electrochemical measurements were conducted at ambient temperature.

4. Conclusions

Finger-like Co3O4 nanorods were prepared by a facile and eco-friendly hydrothermal method. The as-prepared Co3O4 nanorods consist of many nanoparticles of 30–50 nm in diameter, forming a unique finger-like architecture. Moreover, these unique Co3O4 nanorods exhibited excellent electrochemical performance for the supercapacitor and lithium ion battery. The initial discharge capacity at the current density of 50 mA g−1 is as high as 1171 mAh g−1. After 50 cycles, the discharge capacity still maintains 1006 mAh g−1, which is comparable with or even higher than the reported values on other Co3O4 nanomaterials. The as-prepared finger-like Co3O4 nanorods show great potential for application in the lithium ion battery.

Supplementary Materials

Supplementary materials can be accessed at: https://0-www-mdpi-com.brum.beds.ac.uk/2079-4991/5/4/2335/s1.

Acknowledgments

The support from the National Natural Science Foundation of China (Grant No. 51201089) and the Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD) is gratefully acknowledged.

Author contributions

The manuscript was written through contribution of all authors. All authors have given approval to the final version of the manuscript.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Wang, Y.; Zeng, J.; Li, J.; Cui, X.; Al-Enizi, A.M.; Zhang, L.; Zheng, G. One-dimensional nanostructures for flexible supercapacitors. J. Mater. Chem. A 2015, 3, 16382–16392. [Google Scholar] [CrossRef]
  2. Li, L.; Zhang, Y.; Liu, X.; Shi, S.; Zhao, X.; Zhang, H.; Ge, X.; Cai, G.; Gu, C.; Wang, X.; et al. One-dimension MnCo2O4 nanowire arrays for electrochemical energy storage. Electrochim. Acta 2014, 116, 467–474. [Google Scholar] [CrossRef]
  3. Jiang, J.; Li, Y.; Liu, J.; Huang, X. Building one-dimensional oxide nanostructure arrays on conductive metal substrates for lithium-ion battery anodes. Nanoscale 2011, 3, 45–58. [Google Scholar] [CrossRef] [PubMed]
  4. Chen, M.; Xia, X.; Yin, J.; Chen, Q. Construction of Co3O4 nanotubes as high-performance anode material for lithium ion batteries. Electrochim. Acta 2015, 160, 15–21. [Google Scholar] [CrossRef]
  5. Bruce, P.G.; Scrosati, B.; Tarascon, J.-M. Nanomaterials for rechargeable lithium batteries. Angew. Chem. Int. Edit. 2008, 47, 2930–2946. [Google Scholar] [CrossRef] [PubMed]
  6. Ren, Y.; Armstrong, A.R.; Jiao, F.; Bruce, P.G. Influence of size on the rate of mesoporous electrodes for lithium batteries. J. Am. Chem. Soc. 2010, 132, 996–1004. [Google Scholar] [CrossRef] [PubMed]
  7. Reddy, M.V.; Subba Rao, G.V.; Chowdari, B.V.R. Metal oxides and oxysalts as anode materials for Li ion batteries. Chem. Rev. 2013, 113, 5364–5457. [Google Scholar] [CrossRef] [PubMed]
  8. Reddy, M.V.; Zhang, B.; Loh, K.P.; Chowdari, B.V.R. Facile synthesis of Co3O4 by molten salt method and its Li-storage performance. CrystEngComm 2013, 15, 3568–3574. [Google Scholar] [CrossRef]
  9. Reddy, M.V.; Zhang, B.; Nicholette, L.J.; Zhang, K.; Chowdari, B.V.R. Molten salt synthesis and its electrochemical characterization of Co3O4 for lithium batteries. Electrochem. Solid State Lett. 2011, 14, A79–A82. [Google Scholar] [CrossRef]
  10. Reddy, M.V.; Prithvi, G.; Loh, K.P.; Chowdari, B.V.R. Li storage and impedance spectroscopy studies on Co3O4, CoO, and CoN for Li-ion batteries. ACS Appl. Mater. Interfaces 2014, 6, 680–690. [Google Scholar] [CrossRef] [PubMed]
  11. Reddy, M.V.; Cai, Y.; Fan, J.; Loh, K.P.; Chowdari, B.V.R. Molten salt synthesis and energy storage studies on CuCo2O4 and CuO·Co3O4. RSC Adv. 2012, 2, 9619–9625. [Google Scholar] [CrossRef]
  12. Reddy, M.V.; Kenrich, K.Y.H.; Wei, T.Y.; Chong, G.Y.; Leong, G.H.; Chowdari, B.V.R. Nano-ZnCo2O4 material preparation by molten salt method and its electrochemical properties for lithium batteries. J. Electrochem. Soc. 2011, 158, A1423–A1430. [Google Scholar] [CrossRef]
  13. Krishnan, S.G.; Reddy, M.V.; Harilal, M.; Vidyadharan, B.; Misnon, I.I.; Rahim, M.H.A.; Ismail, J.; Jose, R. Characterization of MgCo2O4 as an electrode for high performance supercapacitors. Electrochim. Acta 2015, 161, 312–321. [Google Scholar] [CrossRef]
  14. Li, W.; Xu, L.; Chen, J. Co3O4 nanomaterials in lithium-ion batteries and gas sensors. Adv. Funct. Mater. 2005, 15, 851–857. [Google Scholar] [CrossRef]
  15. Du, N.; Zhang, H.; Chen, B.; Wu, J.; Ma, X.; Liu, Z.; Zhang, Y.; Yang, D.; Huang, X.; Tu, J. Porous Co3O4 nanotubes derived from Co4(CO)12 clusters on carbon nanotube templates: A highly efficient material for li-battery applications. Adv. Mater. 2007, 19, 4505–4509. [Google Scholar] [CrossRef]
  16. Lou, X.W.; Deng, D.; Lee, J.Y.; Feng, J.; Archer, L.A. Self-supported formation of needlelike Co3O4 nanotubes and their application as lithium-ion battery electrodes. Adv. Mater. 2008, 20, 258–262. [Google Scholar] [CrossRef]
  17. Yao, M.; Hu, Z.; Xu, Z.; Liu, Y. Template synthesis of 1D hierarchical hollow Co3O4 nanotubes as high performance supercapacitor materials. J. Alloy. Compd. 2015, 644, 721–728. [Google Scholar] [CrossRef]
  18. Xu, J.; Gao, L.; Cao, J.; Wang, W.; Chen, Z. Preparation and electrochemical capacitance of cobalt oxide (Co3O4) nanotubes as supercapacitor material. Electrochim. Acta 2010, 56, 732–736. [Google Scholar] [CrossRef]
  19. Tong, G.; Liu, Y.; Guan, J. In situ gas bubble-assisted one-step synthesis of polymorphic Co3O4 nanostructures with improved electrochemical performance for lithium ion batteries. J. Alloy. Compd. 2014, 601, 167–174. [Google Scholar] [CrossRef]
  20. Xing, L.; Chen, Z.; Xue, X. Controllable synthesis Co3O4 nanorods and nanobelts and their excellent lithium storage performance. Solid State Sci. 2014, 32, 88–93. [Google Scholar] [CrossRef]
  21. Zhang, H.; Wu, J.; Zhai, C.; Ma, X.; Du, N.; Tu, J.; Yang, D. From cobalt nitrate carbonate hydroxide hydrate nanowires to porous Co3O4 nanorods for high performance lithium-ion battery electrodes. Nanotechnology 2008, 19. [Google Scholar] [CrossRef] [PubMed]
  22. Xu, R.; Wang, J.; Li, Q.; Sun, G.; Wang, E.; Li, S.; Gu, J.; Ju, M. Porous cobalt oxide (Co3O4) nanorods: Facile syntheses, optical property and application in lithium-ion batteries. J. Solid State Chem. 2009, 182, 3177–3182. [Google Scholar] [CrossRef]
  23. Vijayanand, S.; Kannan, R.; Potdar, H.S.; Pillai, V.K.; Joy, P.A. Porous Co3O4 nanorods as superior electrode material for supercapacitors and rechargeable Li-ion batteries. J. Appl. Electrochem. 2013, 43, 995–1003. [Google Scholar] [CrossRef]
  24. Cui, L.; Li, J.; Zhang, X.-G. Preparation and properties of Co3O4 nanorods as supercapacitor material. J. Appl. Electrochem. 2009, 39, 1871–1876. [Google Scholar] [CrossRef]
  25. Wang, Y.; Zhou, T.; Jiang, K.; Da, P.; Peng, Z.; Tang, J.; Kong, B.; Cai, W.-B.; Yang, Z.; Zheng, G. Reduced mesoporous Co3O4 nanowires as efficient water oxidation electrocatalysts and supercapacitor electrodes. Adv. Energy Mater. 2014, 4. [Google Scholar] [CrossRef]
  26. Meher, S.K.; Rao, G.R. Effect of microwave on the nanowire morphology, optical, magnetic, and pseudocapacitance behavior of Co3O4. J. Phys. Chem. C 2011, 115, 25543–25556. [Google Scholar] [CrossRef]
  27. Li, Y.; Tan, B.; Wu, Y. Mesoporous Co3O4 nanowire arrays for lithium ion batteries with high capacity and rate capability. Nano Lett. 2007, 8, 265–270. [Google Scholar] [CrossRef] [PubMed]
  28. Xia, X.; Tu, J.; Mai, Y.; Wang, X.; Gu, C.; Zhao, X. Self-supported hydrothermal synthesized hollow Co3O4 nanowire arrays with high supercapacitor capacitance. J. Mater. Chem. 2011, 21, 9319–9325. [Google Scholar] [CrossRef]
  29. Rakhi, R.B.; Chen, W.; Cha, D.; Alshareef, H.N. Substrate dependent self-organization of mesoporous cobalt oxide nanowires with remarkable pseudocapacitance. Nano Lett. 2012, 12, 2559–2567. [Google Scholar] [CrossRef] [PubMed]
  30. Xia, X.; Tu, J.; Zhang, Y.; Mai, Y.; Wang, X.; Gu, C.; Zhao, X. Freestanding Co3O4 nanowire array for high performance supercapacitors. RSC Adv. 2012, 2, 1835–1841. [Google Scholar] [CrossRef]
  31. Wang, Y.; Xia, H.; Lu, L.; Lin, J. Excellent performance in lithium-ion battery anodes: rational synthesis of Co(CO3)0.5(OH)0.11H2O nanobelt array and its conversion into mesoporous and single-crystal Co3O4. ACS Nano 2010, 4, 1425–1432. [Google Scholar] [CrossRef] [PubMed]
  32. Ding, Y.; Zhang, P.; Long, Z.; Jiang, Y.; Huang, J.; Yan, W.; Liu, G. Synthesis and electrochemical properties of Co3O4 nanofibers as anode materials for lithium-ion batteries. Mater. Lett. 2008, 62, 3410–3412. [Google Scholar] [CrossRef]
  33. Xue, X.; Yuan, S.; Xing, L.; Chen, Z.; He, B.; Chen, Y. Porous Co3O4 nanoneedle arrays growing directly on copper foils and their ultrafast charging/discharging as lithium-ion battery anodes. Chem. Commun. 2011, 47, 4718–4720. [Google Scholar] [CrossRef] [PubMed]
  34. Sing, K.S.W.; Everett, D.H.; Haul, R.A.W.; Moscou, L.; Pierotti, R.A.; Rouquerol, J.; Siemieniewska, T. Reporting physisorption data for gas/solid systems with sepcial reference to the determination of surface area and porosity. Pure Appl. Chem. 1984, 57, 603–619. [Google Scholar]
  35. Meher, S.K.; Justin, P.; Rao, G.R. Pine-cone morphology and pseudocapacitive behavior of nanoporous nickel oxide. Electrochim. Acta 2010, 55, 8388–8396. [Google Scholar] [CrossRef]
  36. Meher, S.K.; Justin, P.; Rao, G.R. Microwave-mediated synthesis for improved morphology and pseudocapacitance performance of nickel oxide. ACS Appl. Mater. Interfaces 2011, 3, 2063–2073. [Google Scholar] [CrossRef] [PubMed]
  37. Zhu, T.; Chen, J.; Lou, X.W. Shape-controlled synthesis of porous Co3O4 nanostructures for application in supercapacitors. J. Mater. Chem. 2010, 20, 7015–7020. [Google Scholar] [CrossRef]
  38. Wang, B.; Lu, X.; Tang, Y. Synthesis of snowflake-shaped Co3O4 with a high aspect ratio as a high capacity anode material for lithium ion batteries. J. Mater. Chem. A 2015, 3, 9689–9699. [Google Scholar] [CrossRef]
  39. Zheng, Y.; Qiao, L.; Tang, J.; Yang, Z.; Yue, H.; He, D. Electrochemically deposited interconnected porous Co3O4 nanoflakes as anodes with excellent rate capability for lithium ion batteries. RSC Adv. 2015, 5, 36117–36121. [Google Scholar] [CrossRef]
  40. Li, C.; Chen, T.; Xu, W.; Lou, X.; Pan, L.; Chen, Q.; Hu, B. Mesoporous nanostructured Co3O4 derived from MOF template: a high-performance anode material for lithium-ion batteries. J. Mater. Chem. A 2015, 3, 5585–5591. [Google Scholar] [CrossRef]
  41. Jin, Y.; Wang, L.; Shang, Y.; Gao, J.; Li, J.; He, X. Facile synthesis of monodisperse Co3O4 mesoporous microdisks as an anode material for lithium ion batteries. Electrochim. Acta 2015, 151, 109–117. [Google Scholar] [CrossRef]
  42. Su, P.; Liao, S.; Rong, F.; Wang, F.; Chen, J.; Li, C.; Yang, Q. Enhanced lithium storage capacity of Co3O4 hexagonal nanorings derived from Co-based metal organic frameworks. J. Mater. Chem. A 2014, 2, 17408–17414. [Google Scholar] [CrossRef]
  43. Wang, D.; Yu, Y.; He, H.; Wang, J.; Zhou, W.; Abruña, H.D. Template-free synthesis of hollow-structured Co3O4 nanoparticles as high-performance anodes for lithium-ion batteries. ACS Nano 2015, 9, 1775–1781. [Google Scholar] [CrossRef] [PubMed]
  44. Yan, B.; Chen, L.; Liu, Y.; Zhu, G.; Wang, C.; Zhang, H.; Yang, G.; Ye, H.; Yuan, A. Co3O4 nanostructures with a high rate performance as anode materials for lithium-ion batteries, prepared via book-like cobalt-organic frameworks. CrystEngComm 2014, 16, 10227–10234. [Google Scholar] [CrossRef]
  45. Sun, H.Y.; Ahmad, M.; Zhu, J. Morphology-controlled synthesis of Co3O4 porous nanostructures for the application as lithium-ion battery electrode. Electrochim. Acta 2013, 89, 199–205. [Google Scholar] [CrossRef]
  46. Fang, D.; Li, L.; Xu, W.; Li, G.; Li, G.; Wang, N.; Luo, Z.; Xu, J.; Liu, L.; Huang, C.; et al. Self-assembled hairy ball-like Co3O4 nanostructures for lithium ion batteries. J. Mater. Chem. A 2013, 1, 13203–13208. [Google Scholar] [CrossRef]
  47. Zhao, X.; Pang, Z.; Wu, M.; Liu, X.; Zhang, H.; Ma, Y.; Sun, Z.; Zhang, L.; Chen, X. Magnetic field-assisted synthesis of wire-like Co3O4 nanostructures: Electrochemical and photocatalytic studies. Mater. Res. Bull. 2013, 48, 92–95. [Google Scholar] [CrossRef]
  48. Su, D.; Xie, X.; Munroe, P.; Dou, S.; Wang, G. Mesoporous hexagonal Co3O4 for high performance lithium ion batteries. Sci. Rep. 2014, 4. [Google Scholar] [CrossRef] [PubMed]
  49. Kang, J.; Ko, Y.; Park, J.; Kim, D. Origin of capacity fading in nano-sized Co3O4 electrdes: Electrochemical impedance spectroscopy study. Nanoscale Res. Lett. 2008, 3, 390–394. [Google Scholar] [CrossRef]
  50. Liu, Y.; Mi, C.; Su, L.; Zhang, X. Hydrothermal synthesis of Co3O4 microspheres as anode material for lithium-ion batteries. Electrochim. Acta 2008, 53, 2507–2513. [Google Scholar] [CrossRef]
  51. Chen, S.; Zhao, Y.; Sun, B.; Ao, Z.; Xie, X.; Wei, Y.; Wang, G. Microwave-assisted synthesis of mesoporous Co3O4 nanoflakes for application in lithium ion batteries and oxygen evolution reactions. ACS Appl. Mater. Interfaces 2015, 7, 3306–3313. [Google Scholar] [CrossRef] [PubMed]

Share and Cite

MDPI and ACS Style

Sun, S.; Zhao, X.; Yang, M.; Ma, L.; Shen, X. Facile and Eco-Friendly Synthesis of Finger-Like Co3O4 Nanorods for Electrochemical Energy Storage. Nanomaterials 2015, 5, 2335-2347. https://0-doi-org.brum.beds.ac.uk/10.3390/nano5042335

AMA Style

Sun S, Zhao X, Yang M, Ma L, Shen X. Facile and Eco-Friendly Synthesis of Finger-Like Co3O4 Nanorods for Electrochemical Energy Storage. Nanomaterials. 2015; 5(4):2335-2347. https://0-doi-org.brum.beds.ac.uk/10.3390/nano5042335

Chicago/Turabian Style

Sun, Shijiao, Xiangyu Zhao, Meng Yang, Liqun Ma, and Xiaodong Shen. 2015. "Facile and Eco-Friendly Synthesis of Finger-Like Co3O4 Nanorods for Electrochemical Energy Storage" Nanomaterials 5, no. 4: 2335-2347. https://0-doi-org.brum.beds.ac.uk/10.3390/nano5042335