Application Potential of Cyanide Hydratase from Exidia glandulosa: Free Cyanide Removal from Simulated Industrial Effluents
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Catalysts
Volume 11
Issue 11
10.3390/catal11111411
catalysts-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Ethanol Dehydrogenation to Acetaldehyde over Co@N-Doped Carbon

by
Aleksey N. Chernov
1,
Tatiana V. Astrakova
2,
Konstantin Yu. Koltunov
1 and
Vladimir I. Sobolev
1,*
1
Boreskov Institute of Catalysis, Russian Academy of Sciences, Pr. Akademika Lavrentieva, 5, 630090 Novosibirsk, Russia
2
Department of Natural Sciences, Novosibirsk State University, Pirogova, 2, 630090 Novosibirsk, Russia
*
Author to whom correspondence should be addressed.
Catalysts 2021, 11(11), 1411; https://0-doi-org.brum.beds.ac.uk/10.3390/catal11111411
Submission received: 29 October 2021 / Revised: 12 November 2021 / Accepted: 19 November 2021 / Published: 21 November 2021
Browse Figures
Versions Notes

Abstract

:
Cobalt and nitrogen co-doped carbon materials (Co@CN) have recently attracted significant attention as highly efficient noble-metal-free catalysts exhibiting a large application range. In a similar research interest, and taking into account the ever-increasing importance of bioethanol as a renewable raw material, here, we report the results on ethanol dehydrogenation to acetaldehyde over Co@NC catalysts. The catalyst samples were synthesized by a variety of affordable techniques, ensuring generation of various types of Co species incorporated in carbon, such as subnanosized cobalt sites and nano-sized particles of metallic cobalt and cobalt oxides. The catalytic activity was tested under both oxidative and non-oxidative gas-phase conditions at 200–450 °C using a fixed-bed flow reactor. The non-oxidative conditions proved to be much more preferable for the target reaction, competing, however, with ethanol dehydration to ethylene. Under specified reaction conditions, ethanol conversion achieved a level of 66% with 84% selectivity to acetaldehyde at 400 °C. The presence of molecular oxygen in the feed led mainly to deep oxidation of ethanol to COx, giving acetaldehyde in a comparatively low yield. The potential contribution of carbon itself and supported cobalt forms to the observed reaction pathways is discussed.

1. Introduction

Ethanol is one of the most important biomass-derived platform molecules [1,2]. Given the ongoing trend towards using bioethanol as a renewable feedstock for the production of commodity chemicals, the development of heterogeneous catalysts for the selective conversion of ethanol into acetaldehyde, ethylene, acetic acid, ethyl acetate, propylene, 1-butanol, 1,3-butadiene and other key chemical intermediates continues to be a challenge [3,4,5].
In particular, both oxidative and non-oxidative dehydrogenations of ethanol to obtain acetaldehyde have been extensively studied, and many catalysts have been already tested in these reactions [3,4,5]. It should be noted, however, that ethanol dehydrogenation is often inclined to compete with dehydration, giving ethylene. For that reason, the most efficient heterogeneously catalyzed conversion of ethanol into acetaldehyde (irrespective of oxidative or non-oxidative conditions) has been performed with supported noble-metal catalysts, exhibiting, in addition, the lowest surface acidity [3].
As an alternative route, gaining significant interest, a number of studies have used catalysts based on readily available, inexpensive transition metals deposited on a low-acidity carrier. In line with that approach, activated carbon as itself [6,7,8,9,10,11], and much more successfully, carbon doped with MoO3 or Cu, have shown high catalytic performances in the selective non-oxidative dehydrogenation of ethanol to acetaldehyde [12,13,14,15,16,17]. For example, conversion of ethanol over Cu deposited on activated carbon has attained a level of 65% with 96% selectivity to acetaldehyde at 350 °C under gas flow reaction conditions [15], while the use of Cu deposited on mesoporous carbon appeared even more effective, affording acetaldehyde in a 79% yield at 280 °C [13]. On the other hand, the use of carbon doped with such additives as Ce, Co or Ni has shown poor results [15].
However, it is noteworthy in this regard that carbon materials doped by a combination of a transition metal (Fe, Ni, Cu, and especially Co) and nitrogen have recently attracted significant interest as highly efficient noble-metal-free catalysts in a variety of applications [18,19,20,21,22,23,24,25,26]. Above all, liquid phase oxidative esterification of alcohols [19,27,28,29,30,31,32,33], oxidative dehydrogenation of 1,2,3,4-tetrahydroquinolines into quinolines [20,21], non-oxidative dehydrogenation of propane to propylene [19] and selective dehydrogenation of formic acid [34,35,36] catalyzed by Co@NC materials should be highlighted as quite encouraging for the use of the analogous catalysts in a gas phase ethanol-to-acetaldehyde conversion.
Notably, the Co@NC catalysts have been prepared by a variety of techniques. They were often obtained by the incipient wetness impregnation of carbon black or carbon nanotubes with cobalt(II) salts and N-ligands, followed by pyrolysis [21,22]. In addition, Co@NC can be synthesized through carbonization of cobalt–nitrogen containing metal-organic frameworks (MOFs), such as zeolitic-imidazole frameworks (ZIFs) [23,30,35]. Even more practical seems to be a synthetic approach based on a solid-state mixing of carbon black with cobalt(II) salts and N-ligands, followed by heat treatment, which can result in Co@NC catalysts of comparable activity with regard to particular reactions [36,37]. In any case, all the synthetic techniques finally require a high-temperature (700–1000 °C) pyrolysis of the catalyst precursor, yielding thereby quite similar materials consisting of nano-sized particles of metallic cobalt, cobalt oxides and subnanosized cobalt species. The latter proved to be atomically-dispersed Co(II)-Nx sites incorporated in graphene/graphitic carbon [35]. It is remarkable, however, that the relative content of the structural elements listed may be regulated by using special synthetic or post-synthetic approaches [19,23,34,35,36]. This, in principle, allows the establishment of which of the active sites determines the catalytic performance in any given reaction.
Herein, in continuation of our long-standing interest in the selective conversion of ethanol into value added chemicals under both oxidative and non-oxidative reaction conditions [38,39,40], and in order to explore further the potential applicability limits of Co@NC type catalysts, we report the findings on the catalytic activity of Co@NC materials in the ethanol dehydrogenation reaction.

2. Results and Discussion

2.1. Catalysts Characterization

Figure 1 shows the XRD patterns of as-synthesized catalysts. In the case of Co@NC-Gr, Co@NC-ZIF and Co@C-Gr samples, the clearly visible peaks at 44.0, 51.7 and 75.9° correspond to (111), (200) and (220) crystallographic planes of cubic Co. These peaks reflect the presence of metallic cobalt in the samples. In contrast, such peaks look very faint for the acid treated samples, Co@NC-GrSA and Co@NC-ZIFSA. Moreover, they are completely absent in the pattern of the cobalt-free NC-Gr material. The XRD pattern of Co@NC-ZIF contains also a well distinguishable set of peaks related to crystallographic planes of CoO and Co3O4 particles. The residual presence of cobalt oxides in Co@NC-ZIF is obviously related to some carbon deficiency when this material is formed during carbonization of ZIF-67. As could be expected, metallic Co is mainly formed upon the pyrolysis process, provided the amount of carbon is sufficient for the reduction of Co+2. However, with the relative lack of carbon, as in the case of ZIF-67, cobalt oxides cannot be reduced completely to Co0. Lastly, for all the catalysts two broad diffraction peaks are observed at ~25 and 44°, which can be assigned to a turbostratic (amorphous-graphitic) carbon [41].
Though Co@NC-Gr and Co@NC-ZIF catalysts are obtained by different synthetic approaches, their TEM images look very similar except a higher proportion of cobalt nanoparticles in the latter sample (Figure S1 and Figure S2, Supplementary Materials). The nanoparticles observed are mainly 10 ÷ 30 nm size for both the catalysts, in accordance with our previous results [36,37]). Despite being enveloped by graphitic carbon, the metallic cobalt particles practically disappeared after treatment of Co@NC-Gr with sulfuric acid (Figure S3). In contrast, Co@NC-ZIFSA retained some parts of cobalt nanoparticles if they were in dense graphite packaging (Figure 2a,c). In addition, well-resolved fragments of CoOx are present in the catalyst (Figure 2d). That is also confirmed by EDX-STEM mapping images of Co@NC-ZIFSA, where location of cobalt and oxygen conglomerates definitely coincides in some cases (Figure 3a–c).
Figure 3d–f demonstrates STEM images of another fragment of the same sample, illustrating a uniform distribution of subnanosized Co species and nitrogen in carbon. According to EDX analysis, the atomic fraction of Co in this area is only 0.27% (1.33 wt.%), while the atomic and mass fractions of nitrogen are 2.32 and 2.66%, respectively (Figure S4). The subnanosized cobalt can be assumed to exist mainly in the form of a single-atom sites coordinated to nitrogen atoms (cf. [34,35,36]). The estimated Co fraction is certainly less than that in an area of Co@NC-ZIFSA, containing Co/CoOx nanoparticles (~6 wt.%, Figure S5), and well below of the average Co content determined by XRF technique (Table 1).
The wide-range XPS spectra confirm the major presence of Co, C, N and O elements on the surface of Co@NC-ZIF, Co@NC-Gr, Co@NC-ZIFSA and Co@NC-GrSA catalysts (Figure S6). Predictably, no cobalt or nitrogen is present in the samples of Co@C-Gr and NC-Gr, respectively. In the high-resolution Co 2p spectrum, the peaks at 780.6 and ~797 eV can be assigned to Co2+, while the peak at 778.8 eV is related to metallic cobalt (Figure 4a). As expected, the most significant Co0 inclusion is detected in the Co@NC-ZIF and Co@NC-ZIFSA samples (Table S1 and Table S2). For all the catalysts, the C 1s region is mainly represented by the peak of graphitic carbon at the binding energy of 284.5 eV, while the contribution of C=N (285.8 eV) and C=O (288.1 eV) bonds, and also carbonates (290.2 eV) is not as considerable (Figure 4b, Table S3). The N 1s XPS spectrum is resolved into four peaks corresponding to pyridinic (398.8 eV), pyrrolic/graphitic (400.8 eV) and NOx (402.8, 405.6 eV) functions (Figure 4c). Their relative contributions are given in Table S4. As it can be seen, the pyridinic- and pyrrolic-graphitic forms of nitrogen are predominant in all the Co@NC catalysts and in the NC-Gr sample. However, their input obviously correlates with the N-ligand taken, and the catalysts based on 1,10-phenanthroline, Co@NC-Gr and Co@NC-GrSA, have a higher percentage of pyridinic nitrogen. The XPS characteristics are fully in line with those of Co@NC materials known in the literature [19,20,21,22,23,24,27,28,29,30,34,35,36,37].
Summarizing the above characterizations and taking into account the relevant literary data [34,35,36], it can be concluded that the parent samples Co@NC-Gr and Co@NC-ZIF contain significant, though rather different amounts of nano-sized particles of metallic cobalt, and comprise also a uniformly distributed atomically-dispersed cobalt species Co-Nx in pyridinic/pyrrolic environment. In addition, the Co@NC-ZIF sample contains a considerable amount of cobalt oxides, detectable by XRD, while Co@NC-Gr may include such oxides in a less amount, as revealed by TEM [36]. After leaching these samples with sulfuric acid, the resulting Co@NC-GrSA and Co@NC-ZIFSA materials consist mainly of graphitic carbon with the inclusion of cobalt single-atomic centers (Co-Nx) which stood intact upon the acid treatment conditions. In addition, Co@NC-ZIFSA contains residual amounts of Co nanoparticles, enveloped by carbon, and nanoparticles of CoOx.

2.2. Gas-Phase Catalytic Reactions of Ethanol in a Flow Reactor

Initially, we examined the catalytic performance of the selected samples, Co@NC-Gr, Co@NC-ZIF and Co@NC-ZIFSA, in a single pass flow oxidation of ethanol (Figure 5). As it can be seen, formation of acetaldehyde was highly unselective even at a low conversion of ethanol, competing strongly with the deep oxidation pathway already at 200 °C. In contrast to Co@NC-ZIF, Co@NC-ZIFSA appeared notably more active at the initial range of temperatures, from 200 to 230 °C, but this activity led only to deeper oxidation of ethanol, yielding mainly COx.
It should be noticed that these findings are quite different from the results on liquid phase aerobic oxidation of alcohols over Co@NC catalysts leading normally to highly efficient oxidative (cross)esterification reactions under comparatively mild conditions (25–60 °C) [19,27,28,29,30,31,32,33]. However, such difference can be easily understood given the considerably greater concentration of ethanol in the liquid phase, prompting the formation of an intermediate hemiacetal with its further oxidation to an ester. This avoids the alternative reaction pathways occurring in the gas phase.
Figure 6 demonstrates the catalytic performance of Co@NC-Gr, Co@NC-ZIF, Co@NC-GrSA, Co@NC-ZIFSA, Co@C-Gr, and NC-Gr samples in ethanol dehydrogenation under non-oxidative conditions. With the exception of Co@NC-ZIF, these catalysts provide significant selectivity to acetaldehyde at the temperature range of 250–400 °C. However, the catalytic activity of the samples is very different, which is quite evident when considering the corresponding conversions of ethanol on the same graph (Figure S7). It is especially noticeable here that the cobalt-free catalyst, NC-Gr, is the least active compared to others. This indicates the predominant contribution of cobalt species to the target reaction. It should also be noted that the nitrogen-free catalyst, Co@C-Gr, is less active than Co@NC catalysts, confirming a certain role of nitrogen in the catalytic activity.
Furthermore, Figure 7 illustrates explicitly that Co@NC-Gr and moreover Co@NC-ZIF samples are more inclined to catalyze ethanol dehydration to ethylene compared to Co@NC-GrSA and Co@NC-ZIFSA samples. This is probably due to a higher presence of CoOx species in the parent catalysts. Indeed, cobalt oxides are known to reveal significant Lewis acidity [42] and therefore can initiate an acid-catalyzed conversion of ethanol to ethylene. After sulfuric acid leaching, the obtained Co@NC-GrSA and Co@NC-ZIFSA samples become less active toward ethanol dehydration (Figure 7b). Obviously, this is due to at least partial removal of CoOx (though along with Co nanoparticles). At the same time, it is clearly seen that the removing of Co nanoparticles and CoOx strongly influences the catalytic activity towards ethanol dehydrogenation as well (Figure 7a). For Co@NC-ZIF catalyst, the maximum yield of acetaldehyde, around 50%, is observed at 300 °C, while for Co@NC-ZIFSA that occurs at 400 °C. A similar tendency also occurs for Co@NC-Gr and Co@NC-GrSA samples, which provide the maximum yield of acetaldehyde (~60%) at 350 and 450 °C, respectively. These observations may indicate that at a lower temperature, ethanol is dehydrogenated by metal cobalt and cobalt oxide nanoparticles, whereas subnanosized cobalt species are active at higher temperatures and provide better selectively.
Figure 8 allows a straight comparison of the catalytic activity of Co@NC-Gr, Co@NC-ZIF and Co@NC-ZIFSA catalysts in the ethanol to acetaldehyde conversion under oxidative versus non-oxidative reaction conditions. It is clear that in the presence of oxygen, catalytic activity, but not selectivity, is much higher. Notably, such catalytic behaviour is very consistent with that for supported gold and other noble metal catalysts [39,43,44,45], which was mainly due to the direct involvement of atomic or molecular oxygen species in reaction with ethanol [43] or due to shifting the equilibrium in the dehydrogenation of ethanol through the hydrogen oxidation [39]. Likewise, Co@NC materials, largely known as active catalysts in the oxygen reduction reaction (ORR) [23,24,25], induce an efficient generation of reactive oxygen species due to the surface mono-atomic Co active sites in pyridinic and pyrrolic environment [25,46]. These oxygen forms can oxidize ethanol directly or subsequently react with atomic or molecular hydrogen.
A long-term experiment on ethanol dehydrogenation was carried out by the example of Co@NC-GrSA sample, which demonstrated significant catalytic stability (Figure 9). No drop of selectivity to acetaldehyde (~90%) at practically constant conversion of ethanol (~40%) was observed during 6 h. It indicates that the Co@NC-GrSA composite combines the favorable characteristics in terms of its potential use in practice.
Finally, a comparative catalytic performance of a set of carbon and selected carbon-supported catalysts in the gas phase dehydrogenation of ethanol is shown in Table 1. Although Co@NC-GrSA demonstrates an activity and selectivity somewhat inferior to those of the presented Cu-based catalysts, it turns out to be notably more efficient catalyst than the metal-free carbon materials. It is noteworthy also that Co/ACC exhibited a comparatively poor catalytic performance, close to that of purely carbon catalysts. In contrast, 4%Co/C catalyst, derived from coffee residue, showed a much higher catalytic activity [47]. This, however, could be related to the carbon support’s own considerable activity, as the parent cobalt-free catalyst AC-D showed a very close activity.

3. Experimental

3.1. Materials

Cobalt(II) nitrate hexahydrate (Fisher Scientific UK, Loughborough, UK), cobalt(II) acetate tetrahydrate (99.5%, Vekton, St. Petersburg, Russia), 2-methylimidazole (97%, Alfa Aesar, Thermo Fisher, Kandel, Germany), 1,10-phenanthroline monohydrate (99%, Sigma-Aldrich, Saint Louis, MO, USA) and VulcanXC72R carbon powder (Cabot Carbon Limited, Ellesmere Port, UK) were used as received from the chemical suppliers.

3.2. Catalysts Preparation

3.2.1. Preparation of Co@NC-ZIF and Co@NC-Gr

The samples denoted as Co@NC-ZIF and Co@NC-Gr were synthesized according to the literature, via a separate ZIF-67 synthesis [30,33] and through the use of solid-state grinding technique [36,37], respectively (Table 2).

3.2.2. Preparation of Co@NC-ZIFSA and Co@NC-GrSA

Co@NC-ZIF (1.16 g) was suspended in a 1 M sulfuric acid water solution (90 mL) at room temperature and after an intensive gas discharge of 5 min, the suspension obtained was stirred at 90 °C for 5 h. The catalyst was filtered off, washed consecutively with deionized water, followed by 0.3 M K2CO3 aqueous solution and deionized water until neutral. The solid obtained was dried under vacuum at 80 °C for 5 h, yielding 0.78 g of Co@NC-ZIFSA. The sample denoted as Co@NC-GrSA was prepared analogously from Co@NC-Gr.

3.2.3. Preparation of CoC-Gr

VulcanXC72R carbon (0.8 g), cobalt(II) nitrate hexahydrate (0.2 g) and a few drops of water were hand-ground with a pestle in an open mortar for 10 min. The resultant mixture was then heat treated in a ceramic crucible under conditions indicated in Table 2.

3.2.4. Preparation of NC-Gr

VulcanXC72R carbon (1.0 g), 1,10-phenanthroline monohydrate (0.3 g) and a few drops of water were hand-ground with a pestle in an open mortar for 10 min. The resultant mixture then underwent thermal processing in a ceramic crucible at conditions shown in Table 2.

3.3. Catalysts Characterization Techniques

Catalysts characterization techniques are described in the Supplementary Materials (SI).

3.4. Catalytic Performance Tests

The temperature-programmed gas-phase reactions were performed in a quartz tube flow reactor with an internal diameter of 6 mm. Reactions were conducted at atmospheric pressure using a catalyst sample (200 mg, ~0.2 mL) mixed with quartz sand (0.5 mL, d = 0.25 mm). The gas mixture of EtOH/He = 5/95 or EtOH/O2/He = 1/9/40; was fed to the reactor (GHSV ≈ 18,000 h−1, based on the active phase of the catalyst only). The heating rate was 2 °C min−1. The temperature of reaction (±1 °C) was controlled inside the reactor with a thermocouple placed in the catalyst bed. During the catalyst testing, gas samples were analyzed periodically by integrated online gas chromatography (GC, Tsvet-500; 30 m × 0.32 mm monolithic poly(divinylbenzene) capillary column; 170 °C) with a flame-ionization detector for determination of organics (ethanol, acetaldehyde, acetic acid, ethyl acetate, diethyl ether, ethylene and methane). For determination of carbon oxides, they were preliminarily separated on a 1.5 m × 3 mm steel column filled with Porapak Q at 20 °C followed by methanation. Prior to the catalytic runs, the catalysts were activated at 300 °C in a flow of helium for 1 h. The reactor was then cooled to 200 °C and the feed was switched to a mixture of gaseous reagents by 20 min to reach the steady state initial conditions.

4. Conclusions

The catalytic activity of Co@N-doped carbon materials has been studied with regard to the selective dehydrogenation of ethanol to acetaldehyde under both oxidative and non-oxidative gas phase conditions.
It turned out that the presence of oxygen in the reaction feed resulted in a significant contribution of deep oxidation to the reaction, yielding COx.
In contrast, non-oxidative conditions appeared more applicable to the target reaction, which is quite selective in the temperature range of 200 to 400 °C, especially at a low content of CoOx in the catalyst, which catalyze largely the concurrent dehydration of ethanol to ethylene. Removal of Co and CoOx nanoparticles by treating of the parent Co@NC catalysts with sulfuric acid led to increased selectivity of reaction to acetaldehyde. Nevertheless, this has led to a simultaneous decrease in catalytic activity in general, indicating partial contribution of Co and CoOx nanoparticles to the ethanol non-oxidative dehydrogenation. However, as opposed to the participation of Co/CoOx nanoparticles, subnanosized cobalt species (which are single atomic cobalt sites in pyridinic/pyrrolic environment, uniformly distributed in Co@NC catalysts) provide more selective conversion of ethanol to acetaldehyde, though with a higher temperature.

Supplementary Materials

The following are available online at https://0-www-mdpi-com.brum.beds.ac.uk/article/10.3390/catal11111411/s1, Catalysts characterization techniques, Figure S1: TEM images of Co@NC-Gr, Figure S2: TEM images and EDX analysis of Co@NC-ZIF, Figure S3: EDX-STEM mixed Co/C mapping image and TEM images of Co@NC-GrSA, Figure S4: HAADF and EDX-STEM mixed C/N/Co mapping images of Co@NC-ZIFSA, Figure S5: HAADF and EDX-STEM mixed C/N/Co and O mapping images of Co@NC-ZIFSA for the area containing Co/CoOx nanoparticles, Figure S6: Survey XPS of the samples, Figure S7: Conversions of ethanol under non-oxidative conditions as a function of temperature, Table S1: The XPS-derived chemical composition of the samples, Table S2: The XPS-derived atomic fractions of elements in the samples, Table S3: The relative contribution of carbon species in the N 1s spectra, Table S4: The relative contribution of nitrogen species in the C 1s spectra, Table S5: Textural parameters of the samples.

Author Contributions

A.N.C.: Investigation. T.V.A.: Investigation. K.Y.K.: Data curation, Writing—original draft. V.I.S.: Investigation, Data curation, Supervision. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the Ministry of Science and Higher Education of the Russian Federation within the governmental order for Boreskov Institute of Catalysis (project AAAA-A21-121011390008-4).

Data Availability Statement

The results presented in this work were not previously published anywhere.

Acknowledgments

The studies were carried out using facilities of the shared research center “National center of investigation of catalysts” at Boreskov Institute of Catalysis.

Conflicts of Interest

The authors declare that they have no known competing financial interest or personal relationships that could have appeared to influence the work reported in this paper.

References

  1. Serrano-Ruiz, J.C.; Luque, R.A. Sepulveda-Escribano, Transformations of biomass-derived platform molecules: From high added-value chemicals to fuels via aqueous-phase processing. Chem. Soc. Rev. 2011, 40, 5266–5281. [Google Scholar] [CrossRef] [PubMed]
  2. Farmer, T.J.; Mascal, M. Platform Molecules. In Introduction to Chemicals from Biomass; Clark, J., Deswarte, F., Eds.; John Wiley & Sons Ltd.: Hoboken, NJ, USA, 2015; pp. 89–155. [Google Scholar] [CrossRef]
  3. Angelici, C.; Weckhuysen, B.M.; Bruijnincx, P.C.A. Chemocatalytic Conversion of Ethanol into Butadiene and Other Bulk Chemicals. ChemSusChem 2013, 6, 1595–1614. [Google Scholar] [CrossRef]
  4. Abdulrazzaq, H.T.; Schwartz, T.J. Catalytic Conversion of Ethanol to Commodity and Specialty Chemicals. In Ethanol: Science and Engineering; Basile, A., Adolfo, I., Francesco, D., Nejat, V.T., Eds.; Elsevier: Amsterdam, The Netherlands, 2019; pp. 3–24. [Google Scholar] [CrossRef]
  5. Grim, R.G.; To, A.T.; Farberow, C.A.; Hensley, J.E.; Ruddy, D.A.; Schaidle, J.A. Growing the Bioeconomy through Catalysis: A Review of Recent Advancements in the Production of Fuels and Chemicals from Syngas-Derived Oxygenates. ACS Catal. 2019, 9, 4145–4172. [Google Scholar] [CrossRef]
  6. Szymanski, G.S.; Rychlicki, G.; Terzyk, A.P. Catalytic conversion of ethanol on carbon catalysts. Carbon 1994, 32, 265–271. [Google Scholar] [CrossRef]
  7. Klinthongchai, Y.; Prichanont, S.; Praserthdam, P.; Jongsomjit, B. Synthesis, characteristics and application of mesocellular foam carbon (MCF-C) as catalyst for dehydrogenation of ethanol to acetaldehyde. J. Environ. Chem. Eng. 2020, 8, 103752. [Google Scholar] [CrossRef]
  8. Ob-eye, J.; Praserthdam, P.; Jongsomjit, B. Ethanol Dehydrogenation to Acetaldehyde over Activated Carbons-Derived from Coffee Residue. Bull. Chem. React. Eng. Catal. 2019, 14, 268–282. [Google Scholar] [CrossRef] [Green Version]
  9. Tveritinova, E.A.; Zhitnev, Y.N.; Chernyak, S.A.; Arkhipova, E.A.; Savilov, S.V.; Lunin, V.V. Catalytic Conversion of Aliphatic Alcohols on Carbon Nanomaterials: The Roles of Structure and Surface Functional Groups. Russ. J. Phys. Chem. A 2017, 91, 448–454. [Google Scholar] [CrossRef]
  10. Jasińska, J.; Krzyżyńska, B.; Kozłowski, M. Influence of activated carbon modifications on their catalytic activity in methanol and ethanol conversion reactions. Cent. Eur. J. Chem. 2011, 9, 925–931. [Google Scholar] [CrossRef]
  11. Li, S.; Wang, W.; Liu, X.; Zeng, X.; Li, W.; Tsubaki, N.; Yu, S. Nitrogen-doped graphene nanosheets as metal-free catalysts for dehydrogenation reaction of ethanol. RSC Adv. 2016, 6, 13450–13455. [Google Scholar] [CrossRef]
  12. Grunewald, G.C.; Drago, R.S. Carbon Molecular Sieves as Catalysts and Catalyst Supports. J. Am. Chem. Soc. 1991, 113, 1636–1639. [Google Scholar] [CrossRef]
  13. Wang, Q.-N.; Shi, L.; Lu, A.-H. Highly Selective Copper Catalyst Supported on Mesoporous Carbon for the Dehydrogenation of Ethanol to Acetaldehyde. ChemCatChem 2015, 7, 2846–2852. [Google Scholar] [CrossRef]
  14. Lu, W.-D.; Wang, Q.-N.; He, L.; Li, W.-C.; Schuth, F.; Lu, A.-H. Copper Supported on Hybrid C@SiO2 Hollow Submicron Spheres as Active Ethanol Dehydrogenation Catalyst. ChemNanoMat 2018, 4, 505–509. [Google Scholar] [CrossRef]
  15. Ob-eye, J.; Praserthdam, P.; Jongsomjit, B. Dehydrogenation of Ethanol to Acetaldehyde over Different Metals Supported on Carbon Catalysts. Catalysts 2019, 9, 66. [Google Scholar] [CrossRef] [Green Version]
  16. Li, M.-Y.; Lu, W.-D.; He, L.; Schüth, F.; Lu, A.-H. Tailoring the Surface Structure of Silicon Carbide Support for Copper Catalyzed Ethanol Dehydrogenation. ChemCatChem 2019, 11, 481–487. [Google Scholar] [CrossRef]
  17. Thumbayil, R.P.; Christensen, D.B.; Mielby, J.; Kegnæs, S. Dehydrogenation of bioethanol using Cu nanoparticles supported on N-doped ordered mesoporous carbon. ChemCatChem 2020, 12, 5644–5655. [Google Scholar] [CrossRef]
  18. Liu, L.; Corma, A. Metal Catalysts for Heterogeneous Catalysis: From Single Atoms to Nanoclusters and Nanoparticles. Chem. Rev. 2018, 118, 4981–5079. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  19. Xie, J.; Kammert, J.D.; Kaylor, N.; Zheng, J.W.; Choi, E.; Pham, H.N.; Sang, X.; Stavitski, E.; Attenkofer, K.; Unocic, R.R.; et al. Atomically Dispersed Co and Cu on N-Doped Carbon for Reactions Involving C–H Activation. ACS Catal. 2018, 8, 3875–3884. [Google Scholar] [CrossRef]
  20. Cui, X.; Li, Y.; Bachmann, S.; Scalone, M.; Surkus, A.-E.; Junge, K.; Topf, C.; Beller, M. Synthesis and Characterization of Iron–Nitrogen-Doped Graphene/Core–Shell Catalysts: Efficient Oxidative Dehydrogenation of N-Heterocycles. J. Am. Chem. Soc. 2015, 137, 10652–10658. [Google Scholar] [CrossRef]
  21. Iosub, A.V.; Stahl, S.S. Catalytic Aerobic Dehydrogenation of Nitrogen Heterocycles Using Heterogeneous Cobalt Oxide Supported on Nitrogen-Doped Carbon. Org. Lett. 2015, 17, 4404–4407. [Google Scholar] [CrossRef]
  22. Banerjee, D.; Jagadeesh, R.V.; Junge, K.; Pohl, M.-M.; Radnik, J.; Bruckner, A.; Beller, M. Convenient and Mild Epoxidation of Alkenes Using Heterogeneous Cobalt Oxide Catalysts. Angew. Chem. Int. Ed. 2014, 53, 4359–4363. [Google Scholar] [CrossRef]
  23. Zhang, M.; Zhang, E.; Hu, C.; Zhao, Y.; Zhang, H.; Zhang, Y.; Ji, M.; Yu, J.; Cong, G.; Liu, H.; et al. Controlled Synthesis of Co@N-Doped Carbon by Pyrolysis of ZIF with 2-Aminobenzimidazole Ligand for Enhancing Oxygen Reduction Reaction and the Application in Zn−Air Battery. ACS Appl. Mater. Interfaces 2020, 12, 11693–11701. [Google Scholar] [CrossRef] [PubMed]
  24. Wang, X.; Fu, H.; Li, W.; Zheng, J.; Li, X. Metal (metal = Fe, Co), N codoped nanoporous carbon for efficient electrochemical oxygen reduction. RSC Adv. 2014, 4, 37779–37785. [Google Scholar] [CrossRef]
  25. Sahraie, N.R.; Kramm, U.I.; Steinberg, J.; Zhang, Y.; Thomas, A.; Reier, T.; Paraknowitsch, J.-P.; Strasser, P. Quantifying the density and utilization of active sites in non-precious metal oxygen electroreduction catalysts. Nat. Commun. 2015, 6, 8618. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  26. Morozan, A.; Goellner, V.; Nedellec, Y.; Hannauer, J.; Jaouen, F. Effect of the Transition Metal on Metal–Nitrogen–Carbon Catalysts for the Hydrogen Evolution Reaction. J. Electrochem. Soc. 2015, 162, H719–H726. [Google Scholar] [CrossRef]
  27. Jagadeesh, R.V.; Junge, H.; Pohl, M.-M.; Radnik, J.; Brückner, A.; Beller, M. Selective oxidation of alcohols to esters using heterogeneous Co3O4–N@C catalysts under mild conditions. J. Am. Chem. Soc. 2013, 135, 10776–10782. [Google Scholar] [CrossRef]
  28. Su, H.; Zhang, K.-X.; Zhang, B.; Wang, H.-H.; Yu, Q.-Y.; Li, X.-H.; Antonietti, M.; Chen, J.-S. Activating cobalt nanoparticles via the Mott–Schottky effect in nitrogen rich carbon shells for base-free aerobic oxidation of alcohols to esters. J. Am. Chem. Soc. 2017, 139, 811–818. [Google Scholar] [CrossRef] [Green Version]
  29. Zhong, W.; Liu, H.; Bai, C.; Liao, S.; Li, Y. Base-free oxidation of alcohols to esters at room temperature and atmospheric conditions using nanoscale co-based catalysts. ACS Catal. 2015, 5, 1850–1863. [Google Scholar] [CrossRef]
  30. Zhou, Y.-X.; Chen, Y.-Z.; Cao, L.; Lu, J.; Giang, H.-L. Conversion of a metal–organic framework to N-doped porous carbon incorporating Co and CoO nanoparticles: Direct oxidation of alcohols to esters. Chem. Commun. 2015, 51, 8292–8295. [Google Scholar] [CrossRef]
  31. Eisenberg, D.; Slot, T.K.; Rothenberg, G. Understanding oxygen activation on metal- and nitrogen-codoped carbon catalysts. ACS Catal. 2018, 8, 8618–8629. [Google Scholar] [CrossRef]
  32. Yasukawa, T.; Yang, X.; Kobayashi, S. Development of N-doped carbon-supported cobalt/copper bimetallic nanoparticle catalysts for aerobic oxidative esterifications based on polymer incarceration methods. Org. Lett. 2018, 20, 5172–5176. [Google Scholar] [CrossRef]
  33. Astrakova, T.V.; Chernov, A.N.; Sobolev, V.I.; Koltunov, K.Y. Effect of bases on catalytic properties of cobalt-nitrogen-carbon composites in oxidative esterification of benzyl alcohol with methanol. Russ. J. Appl. Chem. 2019, 92, 295–299. [Google Scholar] [CrossRef]
  34. Tang, C.; Surkus, A.-E.; Chen, F.; Pohl, M.-M.; Agostini, G.; Schneider, M.; Junge, H.; Beller, M. A stable nanocobalt catalyst with highly dispersed CoNx active sites for the selective dehydrogenation of formic acid. Angew. Chem. Int. Ed. 2017, 56, 16616–16620. [Google Scholar] [CrossRef] [PubMed]
  35. Li, X.; Surkus, A.-E.; Rabeah, J.; Anwar, M.; Dastigir, S.; Junge, H.; Bruckner, A.; Beller, M. Cobalt Single-Atom Catalysts with High Stability for Selective Dehydrogenation of Formic Acid. Angew. Chem. Int. Ed. 2020, 59, 15849–15854. [Google Scholar] [CrossRef] [PubMed]
  36. Chernov, A.N.; Astrakova, T.V.; Sobolev, V.I.; Koltunov, K.Y. Liquid versus gas phase dehydrogenation of formic acid over Co@N-doped carbon materials. The role of single atomic sites. Mol. Catal. 2021, 504, 111457. [Google Scholar] [CrossRef]
  37. Astrakova, T.V.; Sobolev, V.I.; Koltunov, K.Y. Facile mechanochemical synthesis of Co@NC catalysts for oxidative esterification of benzyl alcohol with methanol. Catal. Commun. 2020, 137, 105952. [Google Scholar] [CrossRef]
  38. Sobolev, V.I.; Koltunov, K.Y. MoVNbTe Mixed Oxides as Efficient Catalyst for Selective Oxidation of Ethanol to Acetic Acid. ChemCatChem 2011, 3, 1143–1145. [Google Scholar] [CrossRef]
  39. Sobolev, V.I.; Koltunov, K.Y.; Simakova, O.A.; Leino, A.-R.; Murzin, D.Y. Low temperature gas-phase oxidation of ethanol over Au/TiO2. Appl. Catal. A 2012, 433–434, 88–95. [Google Scholar] [CrossRef]
  40. Vodyankina, O.V.; Blokhina, A.S.; Kurzina, I.A.; Sobolev, V.I.; Koltunov, K.Y.; Chukhlomina, L.N.; Dvilis, E.S. Selective oxidation of alcohols over Ag-containing Si3N4 catalysts. Catal. Today 2013, 203, 127–132. [Google Scholar] [CrossRef]
  41. Li, Z.Q.; Lu, C.J.; Xia, Z.P.; Zhou, Y.; Luo, Z. X-ray diffraction patterns of graphite and turbostratic carbon. Carbon 2007, 45, 1686–1695. [Google Scholar] [CrossRef]
  42. Mekhemer, G.A.H.; Abd-Allah, H.M.M.; Mansour, S.A.A. Surface characterization of silica-supported cobalt oxide catalysts. Coll. Surf. A 1999, 160, 251–259. [Google Scholar] [CrossRef]
  43. Guan, Y.; Hensen, E.J.M. Ethanol dehydrogenation by gold catalysts: The effect of the gold particle size and the presence of oxygen. Appl. Catal. A 2009, 361, 49–56. [Google Scholar] [CrossRef]
  44. Blokhinaa, A.S.; Kurzina, I.A.; Sobolev, V.I.; Koltunov, K.Y.; Mamontov, G.V.; Vodyankina, O.V. Selective Oxidation of Alcohols over Si3N4 Supported Silver Catalysts. Kinet. Catal. 2012, 53, 477–481. [Google Scholar] [CrossRef]
  45. Torbina, V.V.; Vodyankin, A.A.; Ten, S.; Mamontov, G.V.; Salaev, M.A.; Sobolev, V.I.; Vodyankina, O.V. Ag-Based Catalysts in Heterogeneous Selective Oxidation of Alcohols: A Review. Catalysts 2018, 8, 447. [Google Scholar] [CrossRef] [Green Version]
  46. Cheng, Q.; Han, S.; Mao, K.; Chen, C.; Yang, L.; Zou, Z.; Guc, M.; Hu, Z.; Yang, H. Co nanoparticle embedded in atomically-dispersed Co-N-C nanofibers for oxygen reduction with high activity and remarkable durability. Nano Energy 2018, 52, 485–493. [Google Scholar] [CrossRef]
  47. Ob-Eye, J.; Jongsomjit, B. Dehydrogenation of ethanol to acetaldehyde over Co/C catalysts. Eng. J. 2019, 23, 1–13. [Google Scholar] [CrossRef]
Catalysts 11 01411 g001 550
Figure 1. Powder XRD patterns of the prepared catalysts.
Figure 1. Powder XRD patterns of the prepared catalysts.
Catalysts 11 01411 g001
Catalysts 11 01411 g002a 550Catalysts 11 01411 g002b 550
Figure 2. TEM images of Co@NC-ZIFSA: (a) general view; (b) a typical structural motif representing graphitic carbon; (c) cobalt residual nanoparticle densely coated with graphite carbon; (d) the fragment containing cobalt oxides.
Figure 2. TEM images of Co@NC-ZIFSA: (a) general view; (b) a typical structural motif representing graphitic carbon; (c) cobalt residual nanoparticle densely coated with graphite carbon; (d) the fragment containing cobalt oxides.
Catalysts 11 01411 g002aCatalysts 11 01411 g002b
Catalysts 11 01411 g003 550
Figure 3. Selected EDX-STEM mapping images of Co@NC-ZIFSA: (a–c) mixed C/Co, Co and O elements of a fragment containing CoOx; (d–f) Co/C, Co and N elemental mapping of the catalyst area free from Co and CoOx nanoparticles.
Figure 3. Selected EDX-STEM mapping images of Co@NC-ZIFSA: (a–c) mixed C/Co, Co and O elements of a fragment containing CoOx; (d–f) Co/C, Co and N elemental mapping of the catalyst area free from Co and CoOx nanoparticles.
Catalysts 11 01411 g003
Catalysts 11 01411 g004 550
Figure 4. High resolution XPS spectra of (a) Co 2p, (b) C 1s and (c) N 1s of the samples.
Figure 4. High resolution XPS spectra of (a) Co 2p, (b) C 1s and (c) N 1s of the samples.
Catalysts 11 01411 g004
Catalysts 11 01411 g005 550
Figure 5. Catalytic performance of (a) Co@NC-Gr, (b) Co@NC-ZIF and (c) Co@NC-ZIFSA catalysts as a function of temperature: conversion of ethanol (■) and selectivities toward acetaldehyde (●) and CO + CO2 (▲). Gas mixture: 2 vol.% EtOH, 18 vol.% O2, He balance; GHSV ≈ 18,000 h−1.
Figure 5. Catalytic performance of (a) Co@NC-Gr, (b) Co@NC-ZIF and (c) Co@NC-ZIFSA catalysts as a function of temperature: conversion of ethanol (■) and selectivities toward acetaldehyde (●) and CO + CO2 (▲). Gas mixture: 2 vol.% EtOH, 18 vol.% O2, He balance; GHSV ≈ 18,000 h−1.
Catalysts 11 01411 g005
Catalysts 11 01411 g006 550
Figure 6. Catalytic performance of (a) Co@NC-Gr, (b) Co@NC-ZIF, (c) Co@NC-GrSA, (d) Co@NC-ZIFSA, (e) Co@C-Gr and (f) NC-Gr catalysts as a function of temperature: conversion of ethanol (■) and selectivities toward acetaldehyde (●) and ethylene (►). Gas mixture: 5 vol.% EtOH, He balance; GHSV ≈ 18,000 h−1.
Figure 6. Catalytic performance of (a) Co@NC-Gr, (b) Co@NC-ZIF, (c) Co@NC-GrSA, (d) Co@NC-ZIFSA, (e) Co@C-Gr and (f) NC-Gr catalysts as a function of temperature: conversion of ethanol (■) and selectivities toward acetaldehyde (●) and ethylene (►). Gas mixture: 5 vol.% EtOH, He balance; GHSV ≈ 18,000 h−1.
Catalysts 11 01411 g006
Catalysts 11 01411 g007 550
Figure 7. Yields of (a) acetaldehyde and (b) ethylene over Co@NC-Gr (○), Co@NC-ZIF (▽), Co@NC-GrSA (●) and Co@NC-ZIFSA (▼) catalysts as a function of temperature. Gas mixture: 5 vol.% EtOH, He balance; GHSV ≈ 18,000 h−1.
Figure 7. Yields of (a) acetaldehyde and (b) ethylene over Co@NC-Gr (○), Co@NC-ZIF (▽), Co@NC-GrSA (●) and Co@NC-ZIFSA (▼) catalysts as a function of temperature. Gas mixture: 5 vol.% EtOH, He balance; GHSV ≈ 18,000 h−1.
Catalysts 11 01411 g007
Catalysts 11 01411 g008 550
Figure 8. Yields of acetaldehyde over (a) Co@NC-Gr, (b) Co@NC-ZIF and (c) Co@NC-ZIFSA catalysts as a function of temperature. For feed compositions: 2 vol.% EtOH, 18 vol.% O2, He balance (▲); 5 vol.% EtOH, He balance (▼); GHSV ≈ 18,000 h−1.
Figure 8. Yields of acetaldehyde over (a) Co@NC-Gr, (b) Co@NC-ZIF and (c) Co@NC-ZIFSA catalysts as a function of temperature. For feed compositions: 2 vol.% EtOH, 18 vol.% O2, He balance (▲); 5 vol.% EtOH, He balance (▼); GHSV ≈ 18,000 h−1.
Catalysts 11 01411 g008
Catalysts 11 01411 g009 550
Figure 9. Catalytic performance of Co@NC-GrSA catalyst versus reaction time at 365 °C: conversion of ethanol (■) and selectivity to acetaldehyde (●). Feed composition: 5 vol.% EtOH, He balance; GHSV ≈ 18,000 h−1.
Figure 9. Catalytic performance of Co@NC-GrSA catalyst versus reaction time at 365 °C: conversion of ethanol (■) and selectivity to acetaldehyde (●). Feed composition: 5 vol.% EtOH, He balance; GHSV ≈ 18,000 h−1.
Catalysts 11 01411 g009
Table
Table 1. Catalytic activity of selected carbon based catalysts in ethanol dehydrogenation to acetaldehyde a.
Table 1. Catalytic activity of selected carbon based catalysts in ethanol dehydrogenation to acetaldehyde a.
Catalysts 11 01411 i001
CatalystReaction Temperature
(°C)		Ethanol Conversion
(%)		Selectivity to Acetaldehyde
(%)		Ref.
NC-Gr4002591This work
Co@C-Gr4005282This work
Co@NC-GrSA4006684This work
3001597
MCF-C b4001780[7]
NG c350~10~100[11]
AC-D d4004898[8,47]
CNT-AO e3005997[9]
Co/ACC f400793[15]
4%Co/C g4005492[47]
Cu/ACC h3506596[15]
1Cu/NMC-7 i3505799[17]
Cu/MC j2808395[13]
Cu/C/SiC k2806699[16]
a The data refer to non-oxidative gas phase reactions under comparable flow conditions. b Mesocellular foam carbon. c Nitrogen-doped graphene nanosheets. d Activated carbon derived from coffee residue. e Carbon nanotubes treated with HNO3. The data obtained by the pulsed microcatalytic technique. f Co on activated carbon. g Co on activated carbon derived from coffee residue. h Cu on activated carbon. i Cu on N-doped ordered mesoporous carbon. j Cu on mesoporous carbon. k Cu on carbon/silicon carbide.
Table
Table 2. Characterization data for Co@NC materials.
Table 2. Characterization data for Co@NC materials.
Entry CatalystCobalt Salt/L aCarbon Support b
(wt.%)		Pyrolysis
(°C, h, Gas)		Co c (wt.%)SBET
(m2 g−1)
1 Co@NC-ZIF dCo2/L2 = 1:40-850, 2, Ar32.8174
2Co@NC-ZIFSA e---10.9507
3Co@NC-Gr fCo1/L1 = 1:2 65800, 2, Ar5.093
4Co@NC-GrSA e---1.845
5Co@C-Gr fCo1 80800, 2, Ar5.3234
6NC-Gr fL1 77800, 2, Ar0.0202
a Molar ratio. Salts: Co1 = Co(OAc)2 × 4H2O; Co2 = Co(NO3)2 × 6H2O. Ligands: L1 = 1,10-phenanthroline × 1H2O; L2 = 2-methylimidazole. b VulcanXC72R, weight content before heat treatment. c Overall Co loading based on XRF analysis. d A MOF (ZIF-67)-derived sample. e The sample after treatment with a 1 M solution of sulfuric acid at 90 °C for 5 h. f Sample obtained by the solid-state grinding approach.
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Chernov, A.N.; Astrakova, T.V.; Koltunov, K.Y.; Sobolev, V.I. Ethanol Dehydrogenation to Acetaldehyde over Co@N-Doped Carbon. Catalysts 2021, 11, 1411. https://0-doi-org.brum.beds.ac.uk/10.3390/catal11111411

AMA Style

Chernov AN, Astrakova TV, Koltunov KY, Sobolev VI. Ethanol Dehydrogenation to Acetaldehyde over Co@N-Doped Carbon. Catalysts. 2021; 11(11):1411. https://0-doi-org.brum.beds.ac.uk/10.3390/catal11111411

Chicago/Turabian Style

Chernov, Aleksey N., Tatiana V. Astrakova, Konstantin Yu. Koltunov, and Vladimir I. Sobolev. 2021. "Ethanol Dehydrogenation to Acetaldehyde over Co@N-Doped Carbon" Catalysts 11, no. 11: 1411. https://0-doi-org.brum.beds.ac.uk/10.3390/catal11111411

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.