Modification of Type B Inclusions by Calcium Treatment in High-Carbon Hard-Wire Steel

Abstract

To investigate the modification of type B inclusions in high-carbon hard-wire steel with Ca treatment, Si-Ca alloy was added to high-carbon hard-steel, and the composition, morphology, size, quantity, and distribution of inclusions were observed. The samples were investigated by scanning electron microscopy-energy dispersive spectroscopy (SEM-EDS). The experimental thermal results showed that the modification effect of inclusion was better in high-carbon hard-wire steel with Al of 0.0053% and Ca of 0.0029% than that in steel with Al of 0.011% and Ca of 0.0052%, in which the inclusions were mainly spherical semi-liquid and liquid CA₂, CA, and C₁₂A₇. The inclusion size decreased from 3.2 μm to 2.1 μm. The degree of inclusions segregation was reduced in high-carbon hard-wire steels after calcium treatment. The results indicate that the modification of inclusions is conducive to obtaining dispersed inclusions with fine size. The ratio of length to width decreased and tended to be 1 with the increase in CaO content in the inclusion. When the content of CaO was higher than 30%, the aspect ratio was in the range of 1 to 1.2. The relationship between the activity of aluminum and calcium and the inclusions type at equilibrium in high-carbon hard-wire steel was estimated using classical thermodynamics. The calculated results were consistent with the experimental results. The thermodynamic software Factsage was used to analyze the effect of aluminum and calcium additions on the type and quality of inclusions in high-carbon hard-wire steels. The modification law and mechanism of type B inclusions in high-carbon hard-wire steels are discussed.

1. Introduction

The wire rod rolled by structural steel with carbon content not less than 0.6% is called high-carbon hard-wire steel, which is widely used in construction, transportation, and other industries [1,2,3]. Nonmetallic inclusions affect the mechanical properties and corrosion performance of steel [4]. Compared with low-carbon steel, high-carbon steel has high hardness and low ductility and is more sensitive to nonmetallic inclusions [5,6]. In recent years, the output and quality of high-carbon hard-wire steel produced in China have been greatly improved. However, the breaking rate of the wire is relatively high during the drawing and twisting processes [7]. Controlling the number, size, distribution, and morphology of brittle inclusions is very important in the smelting process of high-carbon hard-wire steel [1].

B-type inclusions (Al₂O₃ inclusions) are brittle inclusions and tend to accumulate at the nozzle, which affects the stable operation of the production process [8]. The modification of inclusions is a good way to reduce the adverse effect of B-type inclusions on the production and performance of steel [9,10,11]. Calcium treatment [12,13,14,15,16,17] can effectively modify Al₂O₃ inclusions into calcium aluminate inclusions with a low melting point, which can effectively prevent nozzle clogging [18,19,20,21]. Calcium alloy was added into liquid steel by powder spraying or wire feeding to promote the transformation of high melting point Al₂O₃ inclusions into plastic or semi-plastic low melting point calcium aluminate inclusions [22,23]. The inclusion after calcium treatment is composed of a certain proportion of liquid phase and solid phase, and the composition of the inclusion has a very important effect on the castability and deformation of the inclusion during rolling. Therefore, it is very important to study the phase composition of inclusions during calcium treatment. [24]

Numata et al. [25] studied the effect of calcium content on the modification of inclusions by laboratory experiments. Verma et al. [26] demonstrated that the inclusion size decreased significantly after Ca treatment, mainly from 10–20 μm to 1–2.5 μm. The inclusion size was the smallest after 2 min of Ca treatment and then gradually increased. Yuan et al. [27] treated medium and high carbon with Al content of 0.025–0.044% with calcium. When the Ca content was less than 10 ppm, the solid rate of inclusion reached more than 60%, and they believed that the suitable Ca content was 17–23 ppm. Yoshihiko et al. [28] modified the inclusions in mild steel by adding Ca-Si alloy. They found that the modification effect was better in the steel with a Ca content of 20 ppm, in which the content of CaO in the oxide inclusion was close to 50%. Simpson et al. [29] showed that calcium aluminate inclusions with lower melting points formed when the mass ratio of w[Ca]/w[Al] is larger than 0.11 in molten steel.

Many studies have been carried out on the treatment of Al₂O₃ inclusions with calcium, but most of them were focused on low carbon steel. Limited research was conducted on the modification of B-type inclusions in steel with high carbon. In order to expand the application of calcium in the production of high-carbon hard-wire steel, the effect of calcium treatment on the quantity, morphology, distribution, and composition of B-type inclusions in the molten steel by adding alloy was studied.

2. Experimental Method

A vacuum induction furnace was applied in the production of base metal of high-carbon hard-wire steel.

Table 1. Compositions of raw materials (mass%).

Raw Material	Fe	Si	Mn	S	C	Ca	Al	Others
Industrial pure iron	99.7	0.02	0.03	0.0002	0.0018	-	0.001	0.0024
electrolytic manganese	-	-	99.999	-	-	-	-	0.001
Si-Fe alloy	21	78	0.4	0.02	0.1	-	-	0.48
Al alloy	0.7	0.8	0.15	-	-	-	96.94	1.41
Si-Ca alloy	-	57.13	20.44	-	0.83	19.56	2.02	0.02
QT400	95.8	0.17	0.5	0.01	3.45	-	-	0.07

lists the compositions of raw materials used in the study. The base metal was put into a tubular resistance furnace and heated to 1600 °C. After melting for 30 min, aluminum powder was added, and timing started. The time of adding aluminum powder was recorded as 0 min. After 5 min, calcium alloy was added. After 65 min, the sample was taken out and placed in water for cooling. During the whole smelting process, high purity argon gas was fed into the tubular resistance furnace. The samples can be divided into three groups according to the amount of aluminum alloy and calcium alloy added to the steel. The composition of the three groups of samples is shown in

Table 2. Chemical Composition (Mass Percent).

No	C	Si	Mn	S	Al	Ca	O	N	Fe
Sample1	0.640	0.189	0.313	0.0010	0.013	-	0.0082	0.0024	Others
Sample2	0.636	0.202	0.311	0.0012	0.011	0.0052	0.0065	0.0029	Others
Sample3	0.638	0.196	0.320	0.0011	0.0053	0.0029	0.0053	0.0027	Others

. In sample 1, only aluminum alloy was added for deoxygenation, and calcium alloy was not added. A large amount of aluminum and calcium was added in sample 2, and a small amount of aluminum and calcium was added in sample 3.

The three groups of samples were processed into metallographic samples of 10 mm × 10 mm × 10 mm, rod samples of Φ5 × 100 mm, and metal chips, respectively. The metallographic samples were ground to a mirror finish with different mesh sandpaper and emery polishing paste. The composition and characteristics of inclusions were analyzed by scanning electron microscope and energy dispersive spectrometer (SEM-EDS). Twenty inclusions were randomly selected from each sample to detect the content of corresponding chemical elements. The composition and type of inclusions were analyzed according to the stoichiometric relationship. One hundred fields of view were selected for each sample. Sample surface pictures were taken under the scanning electron microscope (SEM) 1000× field. Image-ProPlus image processing software was used to analyze the size, quantity, coordinate parameters, and other characteristic values of inclusions.

3. Experimental Results

3.1. Composition and Morphology of Inclusions

Inclusions with a low deformation rate induce cracks in high-carbon hard-wire steel during drawing, mainly due to the different thermal expansion coefficients between inclusions and steel matrix where a radial tensile force is generated in the matrix around inclusions, which leads to a stress concentration around inclusions. When inclusions change to a spherical shape, the stress concentration around inclusions weakens, which improves the drawing performance of high-carbon hard-wire steel [22].

The composition and morphology of inclusions in three groups of samples are shown in Figure 1. Figure 1a–c shows the composition and morphology of typical inclusions in sample 1 without calcium treatment. It can be seen that all inclusions were alumina inclusions with irregular morphology. Figure 1d–f shows the composition and morphology of typical inclusions in the calcium-treated sample 2. Almost all inclusions in sample 2 were transformed into calcium-aluminate inclusions after 60 min of calcium treatment, but the morphology of inclusions was still irregular. The inclusions in sample 3 treated with calcium were mainly calcium aluminate, and the content of CaO in the inclusions was higher than that in sample 2, and the morphology of the inclusions was almost spherical. The surface scanning results of inclusions in Figure 2 also showed that the inclusions in samples 2 and 3 were calcium aluminate, and the elements of Ca and Al distributed in inclusions homogeneously.

Figure 3 shows the inclusion composition distribution of samples 2 and 3. It can be seen that CaO content in the inclusion of sample 2 was in the range of 5 to 25%, and most of the calcium aluminates were CA₂ and CA₆. The CaO content in sample 3 inclusions ranged from 20 to 50%, and most of the calcium aluminates were CA₂ and CA. A small amount of C₁₂A₇ was found in sample 3. According to the phase diagram of CaO-Al₂O₃ calculated by Factsage as shown in Figure 4, the melting point of CaO-6Al₂O₃ (CA₆) was 1833 °C, CaO-2Al₂O₃ (CA₂) was 1765 °C, CaO-Al₂O₃ (CA) was 1604 °C, 12CaO-7Al₂O₃ (C₁₂A₇) was 1455 °C, 3CaO-Al₂O₃(C₃A) melting point was 1539 °C. The liquid calcium aluminate at 1600 °C is marked by shadow area in Figure 3, where the CaO content was in the range of 37 to 57%. When the composition of calcium aluminate inclusions was between CA and CA₂, the inclusions were semi-liquid at 1600 °C. The calcium aluminate inclusions ranging from CA₂ to CA₆ were solid-state at 1600 °C. Figure 3 indicates that most of the inclusions in sample 2 were solid and those in sample 3 were semi-liquid or liquid. The inclusion in sample 1 was a solid alumina inclusion. The research [9,30,31] showed that the deformability of inclusion is directly related to its melting point, and the lower the melting point, the better the deformability. The modification of B-type brittle inclusions into low melting point plastic inclusions will reduce their harmful effects on the production and performance of steel. At the same time, it also showed that the inclusion in sample 3 had a good deformation effect.

In order to explore the relationship between inclusion morphology and inclusion composition, the relationship between CaO content in inclusion and inclusion aspect ratio was statistically analyzed in this study, as shown in Figure 5. With the increase in calcium oxide content in the calcium aluminate inclusions, the ratio of length to width was closer to 1. When the content of CaO was higher than 30%, the aspect ratio was in the range of 1 to 1.2, indicating that the inclusion was approximately spherical. The main reason is that when the content of calcium oxide in the calcium aluminate inclusions was higher than 30%, the inclusions were located in the solid–liquid two-phase region or the liquid phase region.

3.2. Size and Number of Inclusions

Figure 6 shows the inclusion size distribution in high-carbon hard-wire steels. Among the three groups of samples, the inclusion size of sample 1 was the most widely distributed, and the diameter of the largest inclusion was more than 10 μm. The size of the largest inclusion was less than 8 μm in the samples treated with calcium, i.e., samples 2 and 3. The number of inclusions with 1–3 μm was the largest in these three groups of samples.

According to the analysis of the average size and number of inclusions in Figure 7, it can be seen that the average size of inclusions in calcium-treated steel was significantly smaller than that of high-carbon hard-wire steel without calcium treatment. The size of inclusion in sample 3 was obviously smaller than that in sample 2, indicating that the better modification of inclusion is beneficial to the refinement of inclusions. In addition, the number of inclusions in sample 2 was the largest, while the number of inclusions in sample 3 was the least.

3.3. Surface Density Distribution of Inclusions

To describe the distribution of inclusions directly, the area percentage of inclusions at different locations on the surface of the steel sample was statistically obtained according to the two-dimensional coordinates of the inclusions and the area of each inclusion, as shown in Figure 8. Area density represents the percentage of inclusion area to sample area, and it was obtained by Equation (1).

$$A=\frac{A_{\mathit{inclusion}}}{A_{\mathit{steel}}}\times 100\%$$

(1)

where A represents the area density of inclusions on the surface of the steel sample. Ainclusion represents the total area of all inclusions in the observed region. Asteel is the area of steel in the observed region, and it was 0.0286 mm² in this study.

It can be observed that the distribution of inclusions was not uniform in the high-carbon hard-wire steel without calcium treatment. The density of inclusions per unit area on the steel surface was high in sample 1. The inclusions aggregate in the red region in Figure 8a and the maximum density of inclusions reached 1.4% in sample 1. The density of inclusions in calcium-treated steels was less than 0.2%, and the distribution of calcium-aluminate inclusions was more uniform than that of alumina inclusions. In addition, the segregation area of inclusion in sample 3 was smaller than that in sample 2, indicating that the inclusions tend to distribute more homogeneously in steel with a better modification effect.

In conclusion, the inclusions were modified after calcium treatment of high-carbon hard-wire steel. The modification of inclusions in sample 3 was better, where the CaO content of inclusions was higher, and there were more liquid and semi-liquid inclusions. Furthermore, the dispersed inclusions with fine size were obtained in sample 3 because the liquid calcium aluminate inclusions have good wettability.

4. Discussion

According to the detected results of inclusion composition, it is concluded that the chemical reactions that occur in the formation process of a calcium aluminate inclusion in hard-wire steel are (2)–(7) [32,33]

$$2\left[\mathrm{Al}\right]+3\left[\mathrm{O}\right]={\mathrm{Al}}_2{\mathrm{O}}_3;\Delta {\mathrm{G}}_1^{\mathsf{\theta }}=-1,202,000+386.3\mathrm{T},\mathrm{J}·{\mathrm{mol}}^{-1}$$

(2)

$$3\left[\mathrm{Ca}\right]+19{\mathrm{Al}}_2{\mathrm{O}}_3=3\left(\mathrm{CaO}·6{\mathrm{Al}}_2{\mathrm{O}}_3\right)+2\left[\mathrm{Al}\right];\Delta {\mathrm{G}}_2^{\mathsf{\theta }}=-786,553-59.9\mathrm{T},\mathrm{J}·{\mathrm{mol}}^{-1}$$

(3)

$$12\left[\mathrm{Ca}\right]+7\left(\mathrm{CaO}·6{\mathrm{Al}}_2{\mathrm{O}}_3\right)=19\left(\mathrm{CaO}·2{\mathrm{Al}}_2{\mathrm{O}}_3\right)+8\left[\mathrm{Al}\right];\Delta {\mathrm{G}}_3^{\mathsf{\theta }}=-3,134,242-19.58\mathrm{T},\mathrm{J}·{\mathrm{mol}}^{-1}$$

(4)

$$3\left[\mathrm{Ca}\right]+4\left(\mathrm{CaO}·2{\mathrm{Al}}_2{\mathrm{O}}_3\right)=7\left(\mathrm{CaO}·{\mathrm{Al}}_2{\mathrm{O}}_3\right)+2\left[\mathrm{Al}\right];\Delta {\mathrm{G}}_4^{\mathsf{\theta }}=-802,303+30.7,\mathrm{J}·{\mathrm{mol}}^{-1}$$

(5)

$$15\left[\mathrm{Ca}\right]+33\left(\mathrm{CaO}·{\mathrm{Al}}_2{\mathrm{O}}_3\right)=4\left(12\mathrm{CaO}·7{\mathrm{Al}}_2{\mathrm{O}}_3\right)+10\left[\mathrm{Al}\right];\Delta {\mathrm{G}}_5^{\mathsf{\theta }}=-3,134,242-19.58\mathrm{T}, \mathrm{J}·{\mathrm{mol}}^{-1}$$

(6)

$$9\left[\mathrm{Ca}\right]+2\left(12\mathrm{CaO}·7{\mathrm{Al}}_2{\mathrm{O}}_3\right)=11\left(3\mathrm{CaO}·{\mathrm{Al}}_2{\mathrm{O}}_3\right)+14\left[\mathrm{Al}\right];\Delta {\mathrm{G}}_6^{\mathsf{\theta }}=-2,868,511+1108.65\mathrm{T}, \mathrm{J}·{\mathrm{mol}}^{-1}$$

(7)

The activity of solute in molten steel can be calculated according to Equation (8)

$$a_i=f_i\left[\%i\right]$$

(8)

$a_i$, $f_i$ and [%i] are the activity, activity coefficient, and mass fraction of solute i in steel, respectively. The activity coefficient of solute in molten steel was calculated by the Wagner model [34,35]:

$$\lg f_i={\displaystyle \sum }(e_i^j·\left[\%j\right]+{\gamma }_i^j·{\left[\%j\right]}^2)$$

(9)

where i and j represent different solutes, $e_i^j$ is the first-order interaction coefficients, and ${\gamma }_i^j$ is second-order interaction coefficient.

Table 3. First-order interaction coefficients of elements with Al and Ca in molten steel (1873 K).

${\mathit{e}}_{\mathit{i}}^{\mathit{j}}$	C	Si	Mn	S	Al	O	Ca
Ca	−0.34	−0.095	−0.007	−28	−0.072	−780	−0.002
Al	0.091	0.056	−0.004	0.035	−0.043	−1.98	−0.047

[36] and

Table 4. Second-order interaction coefficients of elements with Al and Ca in molten steel (1873 K).

${\mathit{\gamma }}_{\mathit{i}}^{\mathit{j}}$	Ca	Al	O
Ca	-	-	−36,000
Al	-	−0.0284	-

[37] list the value of $e_i^j$ and ${\gamma }_i^j$, respectively.

Combined with the data in Table 2, Table 3 and Table 4, Formulas (7) and (8) were used to calculate the activity coefficient and activity of Ca and Al in sample 2 and sample 3 and listed in

Table 5. Activity coefficient and activity of Ca and Al in test steel.

No.	fAl	aAl	fCa	aCa
2	1.138	0.0125	1.37 × 10−7	7.13 × 10−10
3	1.143	0.006	3.85 × 10−6	1.08 × 10−8

.

According to the thermodynamic data of chemical reactions (3)–(7) in molten steel, the classical thermodynamic calculated method was adopted to obtain the equilibrium relations of various calcium aluminate salts, as shown in Figure 9. According to Figure 9, when a_Al was more than 0.0030, the type of calcium-aluminate inclusions mainly depended on the calcium activity in steel. With the increase in calcium activity, the inclusions gradually underwent the following transformation: Al₂O₃→CA₆→CA₂→CA→C₁₂A₇→C₃A. According to the activity of calcium and aluminum in samples 2 and 3, as shown in Table 5, two points in Figure 8 were obtained. The thermodynamic calculated results showed that the types of inclusions at equilibrium in sample 2 were CA₆ and CA₂, and the types of inclusions in sample 3 were CA and C₁₂A₇, which was consistent with the experimental test results.

To study the modification of type B inclusion in high-carbon hard-wire steel, Factsage 7.2 software was used and combined with the high-carbon hard-wire steel composition in Table 2. The effect of the amount of Ca and Al addition on the composition and quality of inclusions in the high-carbon hard-wire steel was calculated and illustrated in Figure 10. It indicates that the inclusions were alumina, solid calcium aluminate, liquid oxide, and calcium silicate in high-carbon hard-wire steel when adding Ca ranging from 0 to 0.0080% and adding Al ranging from 0.0050% to 0.0150%. When the amount of added aluminum was 0.0050%, the alumina inclusion gradually turned into liquid calcium aluminate with an increase in Al content. There was a small amount of solid calcium aluminate with the addition of calcium in steel ranging from 0.0020% to 0.0021%. As the amount of calcium was less than 0.0070%, the amount of liquid oxide increased with the increase in calcium addition. When the amount of calcium addition was greater than 0.0070%, the amount of liquid oxide was reduced with an increase in calcium addition, which was transfer into calcium silicate. As the addition amount of aluminum was 0.01% and 0.015%, the content of CaO in liquid calcium aluminate increased with the increase in calcium content, and the inclusions gradually underwent the following transformation: Al₂O₃→CA₆→CA₂→liquid calcium aluminate. The appropriate amount of Ca addition to modify B-type inclusions into calcium aluminates was less in high-carbon hard-wire steel with lower aluminum content.

5. Conclusions

The mechanism and law on the modification of type B inclusions in high-carbon hard-wire steel with Ca treatment were studied by thermal experiment and thermodynamic calculation. The main conclusions are as follows:

(1) Ca treatment has a great effect on the composition and morphology of type B inclusions in high-carbon hard-wire steels. The modification effect of inclusion was better in high-carbon hard-wire steel with Al of 0.0053% and Ca of 0.0029% than that in steel with Al of 0.011% and Ca of 0.0052%, in which the inclusions were mainly spherical semi-liquid and liquid CA₂, CA, and C₁₂A₇. The experimental results have a good agreement with the classical thermodynamic calculation results.

(2) CaO content in calcium aluminate inclusions directly affects the morphology of inclusions. The ratio of length to width decreases and tend to be 1 with the increase in CaO content in the inclusion. When the content of CaO was higher than 30%, the aspect ratio was in the range of 1 to 1.2, indicating that the inclusion is approximately spherical. The main reason is that when the content of calcium oxide in the calcium aluminate inclusions is higher than 30%, the inclusions are located in the solid–liquid two-phase region or the liquid phase region.

(3) The size distribution of inclusion in high-carbon hard-wire steel became narrower, and inclusion size was smaller, and inclusions were distributed more uniformly in high-carbon hard-wire steels after calcium treatment. It indicates that the modification of inclusions is conducive to obtaining dispersed inclusions with fine size. Compared with the high-carbon hard-wire steel without calcium treatment, when the calcium content was 0.0029%, the average size of inclusion decreased from 3.2 to 2.1, and the inclusions were difficult to segregate.

(4) The thermodynamic calculated results based on Factsage indicate that when the added amount of aluminum was 0.0050%, the alumina inclusions gradually changed into liquid calcium aluminate inclusions with the increase in the addition amount of calcium in the high-carbon hard-wire steel. When the addition amount of aluminum was 0.01% and 0.015%, the content of CaO in liquid calcium aluminate increased with the increase in calcium addition in high-carbon hard-wire steels, and the inclusions gradually underwent the following transformation: Al₂O₃→CA₆→CA₂→liquid calcium aluminate. The appropriate amount of Ca addition to modify B-type inclusions into calcium aluminates is less in high-carbon hard-wire steel with a lower aluminum content.