Next Article in Journal
The Use of Click-Type Reactions in the Preparation of Thermosets
Next Article in Special Issue
Experimental and Theoretical Study of Zirconocene-Catalyzed Oligomerization of 1-Octene
Previous Article in Journal
Influence of Cross-Linking Degree on Hydrodynamic Behavior and Stimulus-Sensitivity of Derivatives of Branched Polyethyleneimine
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 12
Issue 5
10.3390/polym12051082
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

Fair Look at Coordination Oligomerization of Higher α-Olefins

by
Ilya Nifant’ev
* and
Pavel Ivchenko
*
A.V. Topchiev Institute of Petrochemical Synthesis RAS, 29 Leninsky Pr., 119991 Moscow, Russia
*
Authors to whom correspondence should be addressed.
Polymers 2020, 12(5), 1082; https://0-doi-org.brum.beds.ac.uk/10.3390/polym12051082
Submission received: 20 April 2020 / Revised: 29 April 2020 / Accepted: 30 April 2020 / Published: 9 May 2020
(This article belongs to the Special Issue Coordination Catalysis in Additive Polymerization)
Browse Figures
Versions Notes

Abstract

:
Coordination catalysis is a highly efficient alternative to more traditional acid catalysis in the oligomerization of α-olefins. The distinct advantage of transition metal-based catalysts is the structural homogeneity of the oligomers. Given the great diversity of the catalysts and option of varying the reaction conditions, a wide spectrum of processes can be implemented. In recent years, both methylenealkanes (vinylidene dimers of α-olefins) and structurally uniform oligomers with the desired degrees of polymerization have become available for later use in the synthesis of amphiphilic organic compounds and polymers, high-quality oils or lubricants, and other prospective materials. In the present review, we discussed the selective dimerization and oligomerization of α-olefins, catalyzed by metallocene and post-metallocene complexes, and explored the prospects for the further applications of the coordination α-olefin dimers and oligomers.

Graphical Abstract

1. Introduction

The achievement of the best characteristics of chemical product by the use of efficient knowledge-intensive technologies is the most productive avenue for achieving real development goals in the modern chemical industry. The Ziegler–Natta polymerization of α-olefins [1,2,3,4,5] is an excellent example of such technologies that provides humanity with ~2 × 108 tons of plastics per year. Ethylene and propylene are raw materials for the modern polyolefin industry; thousands of articles and hundreds of reviews are devoted to the coordination homopolymerization and copolymerization of these monomers. The polymerization and oligomerization of higher α-olefins have been studied less intensively. The oligomerization of C8+ α-olefins followed by hydrogenation to form engine Group 4 poly-α-olefin oil (PAO) base stocks and lubricants (Scheme 1a) [6,7], and the synthesis of ultra-high MW polyolefins (Scheme 1b) as drag reducing agents [8,9], were actual topics of the applied research.
It was the Group 4 oil industry that led to the growing interest in the oligomerization of higher α-olefins in the mid-20th century [10,11]. The conventional technologies of acid-catalyzed oligomerization with the use of BF3/ROH or Al chloride catalysts remains relevant for the production of the lower oligomers of α-olefins [12,13]. The cationic oligomerization is accompanied by huge numbers of rearrangements [14,15]. However, lower α-olefin oligomers obtained by cationic oligomerization were exceedingly defined as structurally uniform reaction products [16,17]. Moreover, most of the recent publications devoted to the oligomerization of higher α-olefins have discussed acid-catalyzed processes [18,19,20,21,22,23,24,25,26,27,28,29,30,31,32].
The review of Nicholas [7] was also focused on cationic polymerization; the mini-review of Ray et al., devoted to the synthesis of PAOs [12], addresses only part of the problem of coordination polymerization. The reviews of Janiak [33,34] and Belov [35] were focused on the coordination oligomerization of α-olefins, but these works, published more than 10 years ago, are now objectively outdated.
Taking into account the fact that the selective coordination oligomerization of α-olefins is a growth point of the actual petrochemical industry [7], in the present review, we tried to organize the current scientific information on that topic. In our review, we discussed the plausible mechanisms of the coordination dimerization and oligomerization of α-olefins, collated the data on the catalytic properties of different single-site catalysts, and discussed the problem of the catalyst design. Additionally, we were to focus on looking at the relationship between molecular structure and the characteristics of the oligomers of α-olefins, and on the prospects of the application of these dimers and oligomers in the synthesis of amphiphilic organic compounds and polymers, in the production of fuels, oils, lubricants, and other actual products.

2. Coordination Dimerization of α-Olefins

2.1. Group 4 Metallocene-Catalyzed Synthesis of Methylenealkanes

The zirconocene-catalyzed dimerization of α-olefins (Scheme 2) has been known since the late 1980s [36]. The reaction proceeds in the presence of zirconocene dichloride (η5-C5H5)2ZrCl2 (1, Scheme 2a), activated by minimal amounts of methylalumoxane (MAO) and results in the selective formation of methylenealkanes, olefins containing the vinylidene fragment >C=CH2. The prospects of the synthetic use of this reaction in the synthesis of methylenealkanes were studied by Christoffers and Bergman for linear α-olefins, allylbenzene, and 1,2-diallylbenzene [37,38], and by Erker et al. for 1,5-hexadiene and 1,6-heptadiene [39] (Scheme 2a). The reaction was complicated by the isomerization of the starting α-olefins, by the formation of higher oligomers, and by the deactivation of the catalyst.
Nifant’ev et al. optimized this approach significantly. Based on the results of X-ray diffraction studies of bis(cyclopentadienyl) zirconium complexes 1–6 (Scheme 3), they proposed the structure of highly active and selective pre-catalyst 6. The use of 6 activated by ~20 equivalents (eq.) of triisobutylalumnium (TIBA) and 10 eq. of methylalumoxane (MAO) provided 92%–94% yields of vinylidene dimers of linear α-olefins [40,41,42,43]. As compared with zirconocene 1, in the presence of the 6 dimer of sterically hindered olefin, 3-methylbut-1-ene was obtained with an average yield; substituted silanes and allylthiophenes also formed vinylidene dimers [41] (Scheme 2b). Note that the zirconium pre-catalysts 7 [44,45,46], 8 [47], 3 [48], 9 [49,50], and 10 [51] and the hafnium complex 11 [48], studied previously in α-olefin dimerization, were less active and selective in comparison with 6.
The replacement of the activator of the zirconocene pre-catalyst by perfluoroaryl borate resulted in the migration of the C=C bond: thus, in the presence of dimethyl zirconocene 12 (Scheme 3), activated by [PhNMe2H][B(C6F5)4], 1-decene formed trisubstituted C20 olefins, and the yield of 9-methylenenonadecane was only 30% [52,53]. Tens of Group 4 metallocenes were studied in the coordination oligomerization of α-olefins (Scheme 3, Section 3); however, dimer fractions were the main reaction products only for the first dozen, 1–12.
The mechanism of the zirconocene-catalyzed dimerization of α-olefins remains unclear in terms of detail. On the surface, this mechanism is not very different from the conventional cationic mechanism, and the high selectivity of dimerization can be explained by the low value of the activation barrier of β-hydride transfer (or β-hydride elimination) after the insertion of the second molecule of monomer in comparison with the activation energy of the chain propagation. However, this interpretation does not match the results of the catalytic experiments. As far back as the 1990s [37,38], Christoffers and Bergman demonstrated that chloride is an indispensable component of the catalyst system that provides the high selectivity of dimerization; the special role of Zr–Cl bonding was also proposed by Hessen et al. [54]. Such an effect was confirmed experimentally by an increase in the selectivity of zirconocene/MAO-catalyzed dimerization in the presence of R2AlCl [40,55,56], and by the formation of oligomers when Cp2ZrMe2/B(C6F5)3 was used [57]. To explain the experimental facts, Nifant’ev et al. proposed a binuclear Zr–Al mechanistic concept [40,41] involving the Zr-(μ-Cl)(μ-H)AlR2 catalytic species (Scheme 2c). The early studies of the interaction of 1 with TIBA and HAl(iBu)2 [58,59,60,61] were the experimental basis of this concept.
Recently, this Zr–Al binuclear mechanism was studied theoretically for propylene oligomerization [62]. Using the quantum chemical modeling at the M-06x/DGDZVP level of the density functional theory (DFT), the qualitative difference between mononuclear and binuclear mechanisms (for [(η5-C5H5)2Zr–Alkyl]+ and [(η5-C5H5)2Zr–Alkyl(R2AlX)]+ species, respectively), was demonstrated. Without R2AlX coordination (mononuclear mechanism), oligomerization was found to be a preferable reaction pathway. In binuclear complexes (X = H, Cl), the formation of vinylidene dimers had been greatly facilitated by an explicit Zr–Al cooperative effect (Figure 1).

2.2. Dimerization of α-Olefins Catalyzed by Other Complexes of Transition and Rare-Earth Metals

A number of complexes—namely, WCl6/Et2AlCl [63], zirconium and hafnium adducts with tetradentate ligand 64 [64], half-sandwich complexes of Ta 65 [65,66] and Co 66 [67], a bis-indenyl complex of Y 67 [68], a zwitter-ionic zirconium complex 69 [54], and a sandwich hydride complex of Sc 68 [69]—were studied in the coordination dimerization of α-olefins (Scheme 4a). In the presence of a WCl6-based catalyst, a mixture of vinylidene olefins was formed (Scheme 4b); similar mixtures were obtained in the presence of 65. The half-sandwich complex 66 catalyzed the formation of dimers containing significant amounts of linear olefins. The sandwich complexes of rare-earth metals 67 and 68, as well as the zwitter-ionic complex 69 demonstrated moderate catalytic activity and high selectivity in the formation of the single reaction product; however, the catalytic performance of these complexes dramatically decreased over time (TON ~ 100). Among the complexes mentioned above, only 64Hf (R = nBu) was capable of beating zirconocenes on the criteria of selectivity and catalytic productivity; however, its stability was much lower.

3. Coordination Oligomerization of α-Olefins

3.1. Common Aspects of the Coordination Oligomerization of α-Olefins

Different types of transition metal complex were studied in the coordination oligomerization of α-olefins. Traditional Ziegler–Natta catalysts demonstrated low activity [70,71] and will not be discussed in our review. Group 4 metal sandwich complexes, metallocenes, are the most efficient and most extensively researched catalysts for this process. Scheme 5 illustrates the main and side reactions observed during metallocene-catalyzed oligomerization. The degree of polymerization, DPn, is related to a variety of factors, such as the molecular structure of metallocene, type and quantity of the activator, reaction temperature, and presence of the molecular hydrogen. In the heyday of metallocene catalysis (1990s–early 2000s), the zirconocene-catalyzed polymerization of higher α-olefins was largely viewed as a model process for the study of the mechanism of chain propagation and chain release [72,73,74,75,76,77,78,79].
Usually, the zirconocene-catalyzed oligomerization and polymerization of higher α-olefins was studied in the laboratory using the activation of LZrCl2 pre-catalysts by MAO with extremely high Al/Zr ratios (103–104), or the activation of LZrMe2 pre-catalysts by perfluoroaryl borates. Many of the zirconocenes under these conditions catalyzed the formation of high MW polyolefins (Mn ~104–105 Da); however, several complexes were efficient in the synthesis of oligomers (see below, Section 3.2). High AlMAO/Zr ratios facilitate the formation of Zr–Al alkyl complexes [81,82,83,84,85] that are unable to perform monomer coordination. Such complexes are intermediates of the chain release via Zr–Al transfer [86,87,88]. At the same time, the practice of using high AlMAO/Zr ratios in the laboratory was due to lthe ow effectiveness of MAO as an alkylation agent; the AlMAO/Zr ratios of 102 MAO were found to be insufficient for the activation of bis-indenyl and bis-fluorenyl complexes [89]. In 2017, Nifant’ev et al. proposed a two-stage activation method for a wide array of LZrCl2 complexes. This method was based on the reaction of LZrCl2 with TIBA (formation of Zr–Al alkyl-hydrides) followed by the reaction with ~10 eq. of aMAO; dozens of zirconocene dichlorides were studied in such industrially important conditions [40,80,90,91,92] (see Section 3.3). In contrast to dimerization, the activation of zirconocenes by perfluoroaryl borates was successfully used in the oligomerization of higher α-olefins (see Section 3.4). The formulas of the metallocenes studied in the oligomerization of α-olefins are presented in Scheme 3.

3.2. Metallocene-Catalyzed Oligomerization of α-Olefins and Activation by 102–103 eq. MAO

Dozens of scientific articles and patents have been devoted to the oligomerization of higher α-olefins, catalyzed by Zr and Hf sandwich complexes and activated by a large excess of MAO (Table 1). The main target of the studies, namely, the synthesis of Group 4 oil base stocks, required the use of specific types of product characteristic such as the kinematic viscosity at a given temperature, KVt (KV100 are given in Table 1), and viscosity index, VI, as an alternative to the degree of polymerization, DPn, or oligomer distribution.
The degree of oligomerization, DPn, depends on the structure of the metallocene pre-catalyst, AlMAO/Zr ratio, and reaction conditions. Unsubstituted zirconocene dichloride 1 and monosubstituted and disubstituted zirconocenes catalyzed the formation of the mixtures of lower oligomers. The presence of bulky alkyl or aryl substituents in the cyclopentadienyl rings resulted in decreasing activities of metallocenes and an increased content of higher oligomers; increasing the number of alkyl substituents entailed the same effect. The early results in the study of the oligomerization of α-olefins in the presence of zirconocenes 1 and 8 at AlMAO/Zr ~ 200 [47] were complemented substantially by Nifant’ev et al. [91], who established that under these conditions, the products of side reactions (2-alkenes and alkanes) typically exceeded 10 wt %. Therefore, bis-cyclopentadienyl complexes at high AlMAO/Zr ratios have poor prospects for the oligomerization of α-olefins.
The derivatives of substituted indenes and fluorenes demonstrated more promising catalytic properties. High yields of the oligomer fractions were obtained for metallocenes 53, 56 [98], and 61 [93]. For these complexes, the degree of oligomerization, DPn, can be affected by the hydrogen pressure and reaction temperature with no reduction in the yield of the oligomer fraction.
In order to conclude this section on metallocene-catalyzed oligomerization at high AlMAO/Zr ratios, it is important to note the publication of Jiang et al. [101], which was a thorough study of the microstructure of 1-butene/1-dodecene copolymers, obtained in the presence of (η5-C5Me4H)2ZrCl2, activated by 100–500 eq. of MAO. Detailed investigations of the kinetics and mechanisms of the formation of α-olefin oligomers in the presence of (η5-C5H4-n-Bu)2ZrCl2 [102] and (η5-C5H5)2ZrCl2 [103] after activation by 102–103 eq. of MAO have also been of particular interest.

3.3. Zirconocene-Catalyzed Oligomerization of α-Olefins at Low AlMAO/Zr Ratios

A systematic study of the zirconocene-catalyzed oligomerization of α-olefins at low AlMAO/Zr ratios was started in recent years. With the use of the method of the two-stage activation of LZrCl2 (with TIBA and then MAO, see Section 3.1), Nifant’ev et al. studied the catalytic performance of a wide range of zirconocenes [80,90,91,92]. The results of these studies are presented in Table 2.
During the research, the side reactions of the isomerization and reduction of the starting α-olefins were studied. In was established that in some cases, the content of 2-alkenes in the reaction products can reach values of 20% and higher (for example, for zirconocene 36 [90]). The formation of 2-alkenes is a greatly underestimated problem of the metallocene-catalyzed oligomerization of α-olefins; the isomerization of the starting monomers to inert internal olefins seriously diminishes the yields of oligomers, thus generally devaluing the method of metallocene-catalyzed oligomerization in the production of polyolefin oils and lubricants.
The feasibility of the ligand design is a substantial advantage of the zirconocene catalysis; the inherently high stability of the bis(η5-cyclopentadienyl)Zr fragment allows for a fruitful search of the catalyst without the drawbacks of the unnecessary wasting of the starting α-olefins.
Figure 2 illustrates this idea; activation by 10 eq. of modified methylalumoxane MMAO-12, bis-cyclopentadienyl complex 8 was clearly inferior to that by ansa-zirconocene 35 in terms of catalytic activity, but both zirconocenes 8 and 35 were less active and selective than zirconocene 59 [91]. Using 59, Nifant’ev et al. separated oligomers of 1-hexene, 1-octene, and 1-decene for DPn = 2–5 and proved the homogeneity of their structure [91]; similar results were reported later by Mi et al., who used the less active zirconium complexes 1, 2, 10, and 50 [104]. The complex 59 is a representative of metallocenes containing heterocycle-fused η5-cyclopentadienyl fragments, “heterocenes”. In the early 2000s, such complexes were extensively studied by the chemists of the Basell Polyolefins and Exxon Mobil companies in close cooperation with M.V. Lomonosov Moscow University in the polymerization of ethylene and propylene [105,106,107,108]. To date, heterocenes are considered as the most promising single-site oligomerization catalysts (see Section 4.2 and Section 5).

3.4. Zirconocene-Catalyzed Oligomerization of α-Olefins, Activated by Perfluoroaryl Borates

To avoid the use of a large excess of organoaluminium in the activation of metallocenes, MAO can be replaced with perfluoroaryl borates. This method, proposed by Marks et al. [109,110,111], has been successfully used in the oligomerization of α-olefins (Table 3).
The activation by perfluoroalkyl borates, apparently, resulted in the formation of more electrophilic separate ion pairs, which caused the possibility of side processes unusual for zirconocene/MAO catalysts. The 1H NMR analysis of the end-groups of 1-decene oligomers, obtained in the presence of zirconocenes 32–34, clearly demonstrated the product β-hydride’s elimination from the secondary Zr–alkyl complexes [112]. The formation of such complexes does not affect the carbon skeleton of the oligomers; however, it inevitably results in the slowing down of the oligomerization. A substantially more important process—namely, the β-elimination of the n-hexyl fragment (Scheme 5, reaction pathway C)—was detected in the oligomerization of 1-octene catalyzed by bis(indenyl) hafnium complex 54 [73]. The products of this side reaction represent allyl-terminated oligooctenes that are able to react with the formation of long-chain branched polymers.
Experiments on the oligomerization of 1-decene in the presence of the 47-Me/[PhNHMe2][B(C6F5)4] catalytic system, performed by the chemists of Total company [125], deserve special notice. The content of the C30 fraction in the reaction products reached a value of 70%, comparing favorably with those in BF3-catalyzed oligomerization.
In addition to MAO and perfluoroaryl borates, fluorinated aluminosilicate, in combination with TIBA, was successfully used in the zirconocene-catalyzed oligomerization of α-olefins [97] (Table 4).

3.5. Post-Metallocene Catalysts in the Oligomerization of α-Olefins

Post-metallocene catalysts that have been intensively and fruitfully studied in the polymerization and oligomerization of ethylene and propylene [126,127,128,129,130,131,132,133,134] were of limited use in the oligomerization of higher α-olefins. The Group 8 metal complexes 70 [135] and 71 [136] (Scheme 6) were inferior to zirconocenes in terms of catalytic activity and, therefore, are of no interest for practical applications. The Group 4 post-metallocenes have greater potential in selective oligomerization. The carbene zirconium complex 72 with bulky phenolate fragments (Scheme 7) in the presence of [Ph3C][B(C6F5)4] demonstrated moderate activity in the non-selective oligomerization of 1-hexene; however, activation by [PhNHMe2][B(C6F5)4] resulted in the formation of a trimerization product with ~77% yield [137]. At the same time, the benzimidazole analog 73 catalyzed non-selective oligomerization regardless of the type of activator [138]. Zirconium complexes with [OSSO]-type ligands 74, 75 [139], and 76 [140] (Scheme 6) in the presence of dried modified methylaluminoxane (dMMAO) catalyzed the formation of lower 1-hexene oligomers with excellent vinylidene selectivity. Apparently, the mechanism of the oligomerization catalyzed by 72–76 is similar to the mechanism of zirconocene-catalyzed oligomerization.
The metallacyclic mechanism of the coordination oligomerization of α-olefins (Scheme 7a) [130,141] is highly attractive regarding the selectivity of the formation of the trimer fraction. This mechanism is considered proven for chromium (III) complexes 77–82 of tridentate cyclic ligands (Scheme 7b) [142,143,144,145]. In the presence of 100 eq. of MAO, the complexes 77 and 78 catalyzed the trimerization of 1-hexene with high selectivity; dimers and tetramers were found in less than 1%, and TONs ~103 were detected at room temperature [142]. The structures and ratios of the major isomers in the C18 fraction are presented in Scheme 7c. One year later [143], Wasserscheid et al. studied the trimerization of 1-decene and 1-dodecene, catalyzed by a series of the complexes 79–82 with different substituents at N atoms; the complex 80 with 2-ethylhexyl substituents demonstrated the best catalytic performance in terms of trimerization selectivity and productivity. The impact of the steric bulk of the alkyl substituent R’ on trimerization selectivity was studied in 2016 by Cohon and Köhn [144] for complexes 83–86 (Scheme 7b). The ratios of the products of trimerization of 1-hexene are presented in Table 5.
The metallacyclic mechanism was also proposed for the Ti (IV) complex 87 [146]. In the presence of B(C6F5)3, this complex demonstrated more than 95% selectivity in the trimerization of 1-pentene, 1-hexene, and 1-decene with TONs ~350 (C5, C6) and 100 (C10). Among the trimers produced, ca. 85% were one regioisomer (Scheme 7d). The major olefin product is proposed to form by a tail-to-tail coupling, followed by 1,2-insertion and selective β-hydride elimination.
The theoretical aspects of three possible Cosse–Arlman, Green–Rooney, and metallacyclic mechanisms of α-olefin oligomerization were studied theoretically by Copéret et al. [147]; the findings of this original article warrant further experimental studies.
Note that the Group 8 metal complexes demonstrated high efficiency in the oligomerization of ethylene [148,149,150] and norbornene [149,150,151]. The promising results in the selective oligomerization of propylene [152] and oligomerization/polymerization of 1-butene [153,154] and higher α-olefins [153,155,156,157,158] allow the consideration of such complexes as prospective post-metallocene oligomerization catalysts if the problem of moderate productivity could be solved.

4. The Use of Methylenealkanes

As shown above (see Section 2.1), methylenealkanes can be easily obtained by the zirconocene-catalyzed dimerization of α-olefins. The yields of linear α-olefin dimers typically exceed values of 90% in the event that an efficient pre-catalyst (i.e., 6, Scheme 2b) is used [40]. In addition, methylenealkanes are unavoidable by-products of α-olefin oligomerization (see Section 3). The problem of the utilization of α-olefin dimers is of great relevance and importance [33,41,159].
Methylenealkanes are close structural analogs of isobutylene. The presence of the reactive C=C bond and a substantial difference in the environments of these unsaturated carbon atoms allows the consideration of methylenealkanes as prospective starting compounds for the regioselective synthesis of amphiphilic organic molecules and polymers. A number of possible directions for the synthetic use of methylenealkanes were demonstrated by us with the example of 5-methyleneundecane [41] (Figure 3). Below, we will refer to some of the notable examples of the use of methylenealkanes in the synthesis of organic compounds and polymers.

4.1. Free Radical Addition to Methylenealkanes

The ease of free radical addition of MeC(O)SH using the method developed by Klotz et al. [160] was demonstrated on the example of 5-methyleneundecane (Figure 3) [41]. The closely related free-radical hydrophosphinylation of methylenealkanes was studied by Nifant’ev et al. in order to obtain hydrolytically stable extractants of rare-earth metals [161] (Scheme 8). Branched alkylphosphinic acids, obtained by the hydrophosphinylation of methylenealkanes, also demonstrated promising anti-wear properties [162].

4.2. Free Radical Polymerization of Methylenealkanes

The ability of methylenealkanes to form copolymers with polar vinyl monomers was demonstrated by Yamago et al. with the example of the organotellurium-mediated living radical polymerization (TERP) of 6-methyleneundecane with acrylates; the tendency to form alternating copolymers was demonstrated [163]. Later, Nifant’ev et al. studied the copolymerization of a series of α-olefin dimers with maleic anhydride [164]. In copolymerization experiments, performed in hydrocarbon media at 80–100 °C, azobisisobutyronitrile (AIBN)- or benzoyl peroxide (BPO)-initiated reactions resulted in the formation of copolymers with 1:1 comonomer ratios (Scheme 9), which would suggest an alternating nature of the reaction products. The post-modification of the copolymers obtained by the reactions with higher linear amines and alcohols (Scheme 9) resulted in copolymers with promising pour point depressant characteristics (Figure 4).
The DFT modeling of copolymerization of olefins with maleic anhydride (MA) [165] confirmed the preference of the alternating reaction pathway for methylenealkanes. The possible Alder-ene side reaction (Figure 5a) was also studied; the results of calculations demonstrated that this thermally induced process cannot complete with alternating polymerization under the reaction conditions due to the relatively high level of the free energy of the corresponding transition state (Figure 5b). At elevated temperatures (180–200 °C), this reaction proceeded within 4–6 h with good yields [165,166]; the Alder-ene adducts were used as a starting compounds in the synthesis of bis-succinimide friction modifiers for transmission fluids [166].

4.3. Epoxydation and Related Reactions

The reaction of methylenealkanes with H2O2/HCOOH resulted in the formation of the corresponding 1,2-diols with good yields (Scheme 10a) [167]. The acid-catalyzed rearrangement of the diols to the corresponding aldehydes, followed by the reaction with 1,2-diol, yielded branched acetals (Scheme 10a) [167]. Using toluene as a solvent, the reaction was stopped at the stage of the oxirane [168,169]; the acid-catalyzed rearrangement of the latter in the presence of H5Mo12O41P yielded the corresponding aldehyde (Scheme 10b) [168]. The first reaction sequence was the subject of the study of Harvey et al. [170] that represents a perfect example of neglect of the patent sources.

4.4. Methylenealkanes as Alkylating Reagents

In contrast with the acid-catalyzed oligomerization of linear α-olefins, accompanied by rearrangements with the formation of a large number of isomeric products, methylenealkanes in the presence of acids form products with the same carbon skeleton (Scheme 11). Kissin and Schwab achieved 90% conversions of 5-methyleneundecane after 5 h of the reaction at 60 °C with 87% “dimer of dimer” selectivity using silica-supported EtAlCl2 [47]. The C40 fraction obtained by the dimerization of 9-methylenenonadecane (dimer of 1-decene) had promising viscosity characteristics (KV100 of 6.4 cSt and VI of 147) [47]. The product of the hydrogenolysis of this compound represents a promising low-viscosity PAO base [171]. Nifant’ev et al. proposed a more efficient catalytic system (1 mol % of tert-BuCl and EtAlCl2) that allowed the achievement of 98% conversions of 1-hexene, 1-octene, and 1-decene dimers after 2 h of the reaction at –30 °C [91]. Methylenealkanes were also used in the electrophilic alkylation of diphenylamine, catalyzed by acid-treated clays or ionic liquids [172].

4.5. Catalytic Transformations of Methylenealkanes

The hydroformylation of 9-methylenenonadecane in the presence of 0.01 mol % of (Ph3P)3Rh(CO)H resulted in the formation of the corresponding aldehyde (Scheme 12a) with a 76% yield [173]. A phosphine-modified cobalt catalyst was less efficient (66% yield) [174]. The best results, a 92% yield with 99% selectivity, were obtained using a (acac)Rh(CO)2/PPh3 catalyst [175]. The closely related methoxycarbonylation of methylenealkanes (Scheme 12b) was accompanied by the isomerization of the starting hydrocarbons; the rational design of the Pd/diphosphine catalyst had made it possible to reach average yields of the branched methyl esters [176]. The esters obtained were used in the synthesis of Group 5 oil base stocks with promising viscosity characteristics [177].
Catalytic hydrosilylation was another potentially significant process that allowed the obtaining of highly branched disiloxane with promising viscosity characteristics [178] (Scheme 12c). The same products can be clearly obtained by the hydrolysis of the branched chlorosilanes easily accessible via the hydrosilylation by Me2SiHCl, catalyzed by a Karstedt catalyst [41] (see Figure 3).

5. Oils and Lubricants Based on Coordination Oligomers of α-Olefins

As was demonstrated previously, the viscosity properties such as VI and pour point (PP) of poly-α-olefin (PAO) oil base stocks depend strongly on the architecture of the constituent hydrocarbons [16,17,179,180]. Linear hydrocarbons, petroleum waxes, (Figure 6, A), which are present in large amounts in Group I and II oils, have high PPs. Consequently, these oils have limitations for their use since they cannot provide secure low-temperature engine start and transmission performance. Group III oil base hydrocarbons, which contain compounds with short branches (Figure 6, B) and cycloalkanes (Figure 6, C), also have relatively high PPs and low-temperature viscosity values. Long-chain branched hydrocarbons (Figure 6, D) are characterized by low PPs and high Vis and therefore represent the most prospective group of hydrocarbons for use as high-grade bases of engine oils and transmission fluids.
As mentioned in the Introduction section, cationic oligomerization is accompanied by a huge number of rearrangements, including peculiar reactions proposed by Shubkin [14] and studied later by Gee et al. [15] (Scheme 13). The products of metallocene-catalyzed oligomerization are vinylidene-type α-olefin oligomers with uniform molecular structures (Scheme 1a). A gas chromatogram of the C20 fraction of the products of the cationic oligomerization of 1-decene (Figure 7a) [15] confirms the complexity of the process with the formation of large number of reaction products; the difference between this grim picture and the gas chromatogram of the products of zirconocene-catalyzed oligomerization (Figure 7b) [103] clearly establishes the prospects of “metallocene” oligomers in terms of the structural homogeneity.
The transformation of the α-olefin oligomers to PAO base stocks necessitates catalytic hydrogenation. Electrophilic oligomerization led to the partial formation of tetra-substituted olefins (Scheme 13); the presence of >C=C< fragments significantly hampers the complete hydrogenolysis of double bonds. The ease of the hydrogenation is an additional benefit of the coordination α-olefin oligomers. The viscosity characteristics of the α-olefin oligomers obtained using electrophilic and metallocene catalysts and hygrogenated oligomers (PAO basestocks) are given in Table 6 and illustrated by Figure 8 [91]. These data clearly demonstrate that 1-hexene oligomers have little or no value for use as PAO base stocks due to low viscosity indices and high pour point values. The oligomers of 1-octene prepared by the zirconocene-catalyzed reaction have medium viscosity and outperform the 1-octene oligomers obtained in the presence of BF3–ROH according to viscosity indices, while possessing the same low-temperature kinematic viscosity. The oligomers of 1-decene synthesized by the zirconocene-catalyzed process significantly outperform the electrophilic oligomers obtained in the presence of BF3–ROH and can be considered as base stocks for modern PAOs.
The above pertains to oligomers obtained by the zirconocene-catalyzed process (Scheme 1a); however, as mentioned in Section 3.5, coordination oligomerization can proceed by a metallacyclic mechanism with the formation of products with different molecular structures (Scheme 8). The comparison of the viscosity characteristics of 1-decene trimers obtained by the zirconocene-catalyzed reaction and a metallacyclic process (Cr catalysts 79, 80, 82) suggests that metallocene catalysis is preferable for the production of PAO oil base stocks.

6. Conclusions

Thus, it can be concluded that the zirconocene-catalyzed oligomerization of higher α-olefins represents a flexible and resource-efficient method for the synthesis of methylenealkanes (vinylidene dimers of α-olefins, >90% yields with >98% selectivities) and oligomers with a given DPn. A broader view of the importance of the molecular structure and molecular design that emerged over recent years resulted in the development of advanced “metallocene” technologies for poly-α-olefin oils and lubricants by leading petrochemical companies such as Exxon, Idemitsu, and Mobil. The further progress in this field is related to the creation of the novel metallocene catalysts in order to achieve enhanced thermal stability, catalytic productivity, and selectivity in the synthesis of the desired oligomer fractions. Our recent research on 1-octene oligomerization and polymerization [80] further strongly suggests the high potential of “heterocenes” as a new generation of single-site catalysts of α-olefin oligomerization. We have obtained early results that are extremely promising.
The problem of the utilization of methylenealkanes, which are imminent side products of metallocene-catalyzed oligomerization, is still relevant. The fundamental difference between methylenealkanes and isobutylene consists of the ability of methylenealkanes to isomerize with the formation of more stable branched olefins with >C=CH– fragments. The research and development of the catalysts and processes without such isomerization is an actual affront to researchers’ professionalism.

Author Contributions

Conceptualization, P.I.; methodology, I.N. and P.I.; writing–original draft preparation, P.I.; writing–review and editing, I.N. and P.I.; visualization, P.I.; supervision, I.N.; project administration, I.N.; funding acquisition, I.N. All authors have read and agreed to the published version of the manuscript.

Funding

This work was carried out within the State Program of TIPS RAS.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Qiao, J.; Guo, M.; Wang, L.; Liu, D.; Zhang, X.; Yu, L.; Song, W.; Liu, Y. Recent advances in polyolefin technology. Polym. Chem. 2011, 2, 1611–1623. [Google Scholar] [CrossRef]
  2. Shamiri, A.; Chakrabarti, M.H.; Jahan, S.; Hussain, M.A.; Kaminsky, W.; Aravind, P.V.; Yehye, W.A. The Influence of Ziegler-Natta and Metallocene Catalysts on Polyolefin Structure, Properties, and Processing Ability. Materials 2014, 7, 5069–5108. [Google Scholar] [CrossRef] [PubMed]
  3. Collins, R.A.; Russell, A.F.; Mountford, P. Group 4 metal complexes for homogeneous olefin polymerisation: A short tutorial review. Appl. Petrochem. Res. 2015, 5, 153–171. [Google Scholar] [CrossRef] [Green Version]
  4. Busico, V. Metal-catalysed olefin polymerisation into the new millennium: A perspective outlook. Dalton Trans. 2009, 41, 8794–8802. [Google Scholar] [CrossRef]
  5. Sauter, D.W.; Taoufik, M.; Boisson, C. Polyolefins, a Success Story. Polymers 2017, 9, 185. [Google Scholar] [CrossRef] [Green Version]
  6. Benda, R.; Bullen, J.; Plomer, A. Synthetics basics: Polyalphaolefins—Base fluids for high-performance lubricants. J. Synth. Lubric. 1996, 13, 41–57. [Google Scholar] [CrossRef]
  7. Nicholas, C.P. Applications of light olefin oligomerization to the production of fuels and chemicals. Appl. Catal. A Gen. 2017, 543, 82–97. [Google Scholar] [CrossRef]
  8. Ivchenko, P.V.; Nifant’ev, I.E.; Tavtorkin, A.V. Polyolefin Drag Reducing Agents (Review). Petrol. Chem. 2016, 56, 775–787. [Google Scholar] [CrossRef]
  9. Nifant’ev, I.E.; Shlyakhtin, A.V.; Tavtorkin, A.N.; Korchagina, S.A.; Chinova, M.S.; Vinogradov, A.A.; Vinogradov, A.A.; Roznyatovsky, V.A.; Khaidapova, D.D.; Ivchenko, P.V. The synthesis of ultra-high molecular weight poly(1-hexene)s by low-temperature Ziegler-Natta precipitation polymerization in fluorous reaction media. Polymer 2018, 139, 98–106. [Google Scholar] [CrossRef]
  10. Grumel, V.; Brull, R.; Pasch, H.; Raubenheimer, H.G.; Sanderson, R.; Wahner, U.M. Poly(pent-1-ene) synthesized with the syndiospecific catalyst i-Pr(Cp)(9-Flu)ZrCl2/MAO. Macromol. Mater. Eng. 2002, 287, 559–564. [Google Scholar] [CrossRef]
  11. Scupinska, J. Oligomerization of a-Olefins to Higher Oligomers. Chem. Rev. 1991, 91, 613–648. [Google Scholar] [CrossRef]
  12. Ray, S.; Rao, P.V.C.; Choudary, N.V. Poly-α-olefin-based synthetic lubricants: A short review on various synthetic routes. Lubric. Sci. 2012, 24, 23–44. [Google Scholar] [CrossRef]
  13. Busca, G. Acid Catalysts in Industrial Hydrocarbon Chemistry. Chem. Rev. 2007, 107, 5366–5410. [Google Scholar] [CrossRef] [PubMed]
  14. Shubkin, R.L.; Baylerian, M.S.; Maler, A.R. Olefin Oligomer Synthetic Lubricants: Structure and Mechanism of Formation. Ind. Eng. Chem. Prod. Res. Dev. 1980, 19, 15–19. [Google Scholar] [CrossRef]
  15. Gee, J.C.; Small, B.L.; Hope, K.D. Behavior of protonated cyclopropyl intermediates during polyalphaolefin synthesis: Mechanism and predicted product distribution. J. Phys. Org. Chem. 2012, 25, 1409–1417. [Google Scholar] [CrossRef]
  16. Brennan, J.A. Wide-temperature range synthetic hydrocarbon fluids. Ind. Eng. Chem. Prod. Res. Dev. 1980, 19, 2–6. [Google Scholar] [CrossRef]
  17. Onopchenko, A.; Cupples, B.L.; Kresge, A.N. Boron fluoride-catalyzed oligomerization of alkenes: Structures, mechanisms, and properties. Ind. Eng. Chem. Prod. Res. Dev. 1983, 22, 182–191. [Google Scholar] [CrossRef]
  18. Sun, H.; Shen, B.; Wu, D.; Guo, X.; Li, D. Supported Al–Ti bimetallic catalysts for 1-decene oligomerization: Activity, stability and deactivation mechanism. J. Catal. 2016, 339, 84–92. [Google Scholar] [CrossRef]
  19. Hogg, J.M.; Coleman, F.; Ferrer-Ugalde, A.; Atkins, M.P.; Swadźba-Kwaśny, M. Liquid coordination complexes: A new class of Lewis acids as safer alternatives to BF3 in synthesis of polyalphaolefins. Green Chem. 2015, 17, 1831–1841. [Google Scholar] [CrossRef]
  20. Antunes, B.M.; Rodrigues, A.E.; Lin, Z.; Portugal, I.; Silva, C.M. Alkenes oligomerization with resin catalysts. Fuel Proc. Technol. 2015, 138, 86–99. [Google Scholar] [CrossRef]
  21. Wang, W.; Jiang, S.; Shen, Y.; Xia, S.; Xu, J. Synthesis of high viscosity index base stock and study on the lubricating properties. Ind. Lubricat. Tribol. 2016, 68, 52–56. [Google Scholar] [CrossRef]
  22. Díaz-Rey, M.R.; Paris, C.; Martínez-Franco, R.; Moliner, M.; Martínez, C.; Corma, A. Efficient Oligomerization of Pentene into Liquid Fuels on Nanocrystalline Beta Zeolites. ACS Catal. 2017, 7, 6170–6178. [Google Scholar] [CrossRef]
  23. Nicholas, C.P.; Laipert, L.; Prabhakar, S. Oligomerization of Light Olefins to Gasoline: An Advanced NMR Characterization of Liquid Products. Ind. Eng. Chem. Res. 2016, 55, 9140–9146. [Google Scholar] [CrossRef]
  24. Echaroj, S.; Santikunaporn, M.; Chavadej, S. Transformation of Bioderived 1-Decanol to Diesel-like Fuel and Biobased Oil via Dehydration and Oligomerization Reactions. Energy Fuels 2017, 31, 9465–9476. [Google Scholar] [CrossRef]
  25. Silva, M.S.A.F.; Fernandes, A.; Neves, P.; Antunes, M.M.; Rocha, S.M.; Ribeiro, M.F.; Silva, C.M.; Valente, A.A. Mesostructured Catalysts Based on the BEA Topology for Olefin Oligomerisation. ChemCatChem 2018, 10, 2741–2754. [Google Scholar] [CrossRef]
  26. Kwon, M.-H.; Chae, H.-J.; Park, M.B. Oligomerization of 1-hexene over designed SBA-15 acid catalysts. J. Ind. Eng. Chem. 2018, 65, 397–405. [Google Scholar] [CrossRef]
  27. Fehér, C.; Tomasek, S.; Hancsók, J.; Skoda-Földes, R. Oligomerization of light olefins in the presence of a supported Brønsted acidic ionic liquid catalyst. Appl. Catal. B Environ. 2018, 239, 52–60. [Google Scholar] [CrossRef]
  28. Liu, P.; Redekop, E.; Gao, X.; Liu, W.-C.; Olsbye, U.; Somorjai, G.A. Oligomerization of Light Olefins Catalyzed by Brønsted-Acidic Metal–Organic Framework-808. J. Am. Chem. Soc. 2019, 141, 11557–11564. [Google Scholar] [CrossRef]
  29. Silva, A.F.; Fernandes, A.; Antunes, M.M.; Ribeiro, M.F.; Silva, C.M.; Valente, A.A. Olefin oligomerisation over nanocrystalline MFI-based micro/mesoporous zeotypes synthesised via bottom-up approaches. Renew. Energy 2019, 138, 820–832. [Google Scholar] [CrossRef]
  30. Zhang, L.; Ke, M.; Song, Z.; Liu, Y.; Shan, W.; Wang, Q.; Xia, C.; Li, C.; He, C. Improvement of the Catalytic Efficiency of Butene Oligomerization Using Alkali Metal Hydroxide-Modified Hierarchical ZSM-5 Catalysts. Catalysts 2018, 8, 298. [Google Scholar] [CrossRef] [Green Version]
  31. Moon, S.; Chae, H.-J.; Park, M.B. Oligomerization of light olefins over ZSM-5 and beta zeolite catalysts by modifying textural properties. Appl. Catal. A Gen. 2018, 553, 15–23. [Google Scholar] [CrossRef]
  32. Lee, D.; Kim, H.; Park, Y.-K.; Jeon, J.-K. Oligomerization of Butene Mixture over NiO/Mesoporous Aluminosilicate Catalyst. Catalysts 2018, 8, 456. [Google Scholar] [CrossRef] [Green Version]
  33. Janiak, C.; Blank, F. Metallocene Catalysts for Olefin Oligomerization. Macromol. Symp. 2006, 236, 14–22. [Google Scholar] [CrossRef]
  34. Janiak, C. Metallocene and related catalysts for olefin, alkyne and silane dimerization and oligomerization. Coord. Chem. Rev. 2006, 250, 66–94. [Google Scholar] [CrossRef]
  35. Belov, G.P. Selective Dimerization, Oligomerization, Homopolymerization and Copolymerization of Olefins with Complex Organometallic Catalysts. Russ. J. Appl. Chem. 2008, 81, 1655–1666. [Google Scholar] [CrossRef]
  36. Slaugh, L.H.; Schoenthal, G.W. Vinylidene Olefin Process. U.S. Patent 4658078, 14 April 1987. [Google Scholar]
  37. Christoffers, J.; Bergman, R.G. Catalytic Dimerization Reactions of α-Olefins and α,ω-Dienes with Cp2ZrCl2/Poly(methylalumoxane): Formation of Dimers, Carbocycles, and Oligomers. J. Am. Chem. Soc. 1996, 118, 4715–4716. [Google Scholar] [CrossRef]
  38. Christoffers, J.; Bergman, R.G. Zirconocene-alumoxane (1:1)—A catalyst for the selective dimerization of α-olefins. Inorg. Chim. Acta 1998, 270, 20–27. [Google Scholar] [CrossRef]
  39. Thiele, S.; Erker, G. Adjusting the Features of Active Metallocene Ziegler Systems for Their Potential Use as Carbon-Carbon Coupling Catalysts in Organic Synthesis. Chem. Ber. 1997, 130, 201–207. [Google Scholar] [CrossRef]
  40. Nifant’ev, I.E.; Vinogradov, A.A.; Vinogradov, A.A.; Ivchenko, P.V. Zirconocene-catalyzed dimerization of 1-hexene: Two-stage activation and structure–catalytic performance relationship. Catal. Commun. 2016, 79, 6–10. [Google Scholar] [CrossRef]
  41. Nifant’ev, I.; Ivchenko, P.; Tavtorkin, A.; Vinogradov, A.; Vinogradov, A. Non-traditional Ziegler-Natta catalysis in α-olefin transformations: Reaction mechanisms and product design. Pure Appl. Chem. 2017, 89, 1017–1032. [Google Scholar] [CrossRef]
  42. Nifant’ev, I.E.; Vinogradov, A.A.; Vinogradov, A.A.; Churakov, A.V.; Ivchenko, P.V. Synthesis of zirconium(III) complex by reduction of O[SiMe2(η-C5H4)]ZrCl2 and its selectivity in catalytic dimerization of hex-1-ene. Mendeleev Commun. 2018, 28, 467–469. [Google Scholar] [CrossRef]
  43. Nifant’ev, I.E.; Vinogradov, A.A.; Vinogradov, A.A.; Ivchenko, P.V. The Method of the Syntheiss of Vinylidene Olefins. RU Patent 2652118, 25 April 2018. [Google Scholar]
  44. Janiak, C.; Lange, K.C.H.; Marquardt, P. α-Olefin oligomers with narrow molar mass distributions from zirconocene/methylaluminoxane catalysts—An examination of the structure-reactivity relationship. Macromol. Rapid Commun. 1995, 16, 643–650. [Google Scholar] [CrossRef]
  45. Janiak, C.; Lange, K.C.H.; Marquardt, P.; Krüger, R.-P.; Hanselmann, R. Analyses of Propene and 1-Hexene Oligomers from Zirconocene/MAO Catalysts—Mechanistic Implications by NMR, SEC, and MALDI-TOF MS. Macromol. Chem. Phys. 2002, 203, 129–138. [Google Scholar] [CrossRef]
  46. Janiak, C.; Lange, K.C.H.; Marquardt, P. Alkyl-substituted cyclopentadienyl- and phospholyl-zirconium/MAO catalysts for propene and 1-hexene oligomerization. J. Mol. Catal. A Chem. 2002, 180, 43–58. [Google Scholar] [CrossRef]
  47. Kissin, Y.V.; Schwab, F.C. Post-Oligomerization of alpha-Olefin Oligomers: A Route to Single-Component and Multicomponent Synthetic Lubricating Oils. J. Appl. Polym. Sci. 2009, 111, 273–280. [Google Scholar] [CrossRef]
  48. Boccia, A.C.; Costabile, C.; Pragliola, S.; Longo, P. Selective Dimerization of γ-Branched α-Olefins in the Presence of C2 Group-4 Metallocene-Based Catalysts. Macromol. Chem. Phys. 2004, 205, 1320–1326. [Google Scholar] [CrossRef]
  49. Bagheri, V.; Eisenberg, D.C.; Ratliff, K.S.; Benda, R.; Lanier, C.V. Oligomer oils and their manufacture. U.S. Patent 6548724, 15 April 2003. [Google Scholar]
  50. Song, W.; Heilman, W.J. Synthesis of Poly-Alpha Olefin and Use Thereof. U.S. Patent Application 2003055184, 20 March 2003. [Google Scholar]
  51. Fujikawa, S.; Yokota, K.; Okano, M.; Tsuji, M. Method for Producing α-Olefin Oligomers and Lubricating Oil Compositions. U.S. Patent Application 2011207977, 25 August 2011. [Google Scholar]
  52. Martin, R.W.; Deckman, D.E.; Kelly, K.J.; Emett, C.J.; Hagemeister, M.P.; Harrington, B.A.; Lin, C.-Y.; Matsunaga, P.T.; Ruff, C.J.; Stavens, K.B. Low Viscosity Engine Oil Compositions. U.S. Patent 9234150, 12 January 2016. [Google Scholar]
  53. Emett, C.J.; Hagemeister, M.P.; Harrington, B.A.; Lin, C.Y.; Matsunaga, P.T.; Ruff, C.J.; Stavens, K.B. Process to Produce Improved Poly Alpha Olefin Composition. U.S. Patent 9365788, 14 June 2016. [Google Scholar]
  54. van der Heijden, H.; Hessen, B.; Orpen, A.G. A Zwitterionic Zirconocene Alkyl Complex as a Single-Component α-Olefin Dimerization Catalyst. J. Am. Chem. Soc. 1998, 120, 1112–1113. [Google Scholar] [CrossRef] [Green Version]
  55. Takeuchi, K.; Fujikawa, S. Base Oil for Oil Drilling Fluid and Oil Drilling Fluid Composition. U.S. Patent Application 2011251445, 13 October 2011. [Google Scholar]
  56. Fujikawa, S.; Okamoto, T.; Yokota, K. Process for Producing Unsaturated Hydrocarbon Compound. U.S. Patent 8119850, 21 February 2012. [Google Scholar]
  57. Marks, T.J.; Yang, X. Homogeneous Alpha-Olefin Dimerization Catalysts. U.S. Patent 5500398, 19 March 1996. [Google Scholar]
  58. Baldwin, S.M.; Bercaw, J.E.; Brintzinger, H.H. Alkylaluminum-Complexed Zirconocene Hydrides: Identification of Hydride-Bridged Species by NMR Spectroscopy. J. Am. Chem. Soc. 2008, 130, 17423–17433. [Google Scholar] [CrossRef] [Green Version]
  59. Parfenova, L.V.; Kovyazin, P.V.; Tyumkina, T.V.; Islamov, D.N.; Lyapina, A.R.; Karchevsky, S.G.; Ivchenko, P.V. Reactions of bimetallic Zr, Al-hydride complexes with methylaluminoxane: NMR and DFT study. J. Organomet. Chem. 2017, 851, 30–39. [Google Scholar] [CrossRef]
  60. Pankratyev, E.Y.; Tyumkina, T.V.; Parfenova, L.V.; Khalilov, L.M.; Khursan, S.L.; Dzhemilev, U.M. DFT Study on Mechanism of Olefin Hydroalumination by XAlBui2 in the Presence of Cp2ZrCl2 Catalyst. I. Simulation of Intermediate Formation in Reaction of HAlBui2 with Cp2ZrCl2. Organometallics 2009, 28, 968–977. [Google Scholar] [CrossRef]
  61. Pankratyev, E.Y.; Tyumkina, T.V.; Parfenova, L.V.; Khalilov, L.M.; Khursan, S.L.; Dzhemilev, U.M. DFT and Ab Initio Study on Mechanism of Olefin Hydroalumination by XAlBui2 in the Presence of Cp2ZrCl2 Catalyst. II. Olefin Interaction with Catalytically Active Centers. Organometallics 2011, 30, 6078–6089. [Google Scholar] [CrossRef]
  62. Nifant’ev, I.; Vinogradov, A.; Vinogradov, A.; Karchevsky, S.; Ivchenko, P. Zirconocene-Catalyzed Dimerization of α-Olefins: DFT Modeling of the Zr-Al Binuclear Reaction Mechanism. Molecules 2019, 24, 3565. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  63. Hanton, M.J.; Daubney, L.; Lebl, T.; Polas, S.; Smith, D.M.; Willemse, A. Selective dimerisation of α-olefins using tungsten-based initiators. Dalton Trans. 2010, 7025–7037. [Google Scholar] [CrossRef]
  64. Gunasekara, T.; Preston, A.Z.; Zeng, M.; Abu-Omar, M.M. Highly Regioselective α-Olefin Dimerization Using Zirconium and Hafnium Amine Bis(phenolate) Complexes. Organometallics 2017, 36, 2934–2939. [Google Scholar] [CrossRef]
  65. Leitch, D.C.; Lam, Y.C.; Labinger, J.A.; Bercaw, J.E. Upgrading Light Hydrocarbons via Tandem Catalysis: A Dual Homogeneous Ta/Ir System for Alkane/Alkene Coupling. J. Am. Chem. Soc. 2013, 135, 10302–10305. [Google Scholar] [CrossRef] [Green Version]
  66. Leitch, D.C.; Labinger, J.A.; Bercaw, J.E. Scope and Mechanism of Homogeneous Tantalum/Iridium Tandem Catalytic Alkane/Alkene Upgrading using Sacrificial Hydrogen Acceptors. Organometallics 2014, 33, 3353–3365. [Google Scholar] [CrossRef] [Green Version]
  67. Broene, R.D.; Brookhart, M.; Lamanna, W.M.; Volpe, A.F. Cobalt-Catalyzed Dimerization of α-Olefins to Give Linear α-Olefin Products. J. Am. Chem. Soc. 2005, 127, 17194–17195. [Google Scholar] [CrossRef]
  68. Kretschmer, W.P.; Troyanov, S.I.; Meetsma, A.; Hessen, B.; Teuben, J.H. Regioselective Homo- and Codimerization of α-Olefins Catalyzed by Bis(2,4,7-trimethylindenyl)yttrium Hydride. Organometallics 1998, 17, 284–286. [Google Scholar] [CrossRef]
  69. Piers, W.E.; Shapiro, P.J.; Bunel, E.E.; Bercaw, J.E. Coping with extreme Lewis acidity: Strategies for the synthesis of stable, mononuclear organometallic derivatives of scandium. Synlett 1990, 74–84. [Google Scholar] [CrossRef]
  70. Huang, Q.; Chen, L.; Ma, L.; Fu, Z.; Yang, W. Synthesis and characterization of oligomer from 1-decene catalyzed by supported Ziegler–Natta catalysts. Eur. Polym. J. 2005, 41, 2909–2915. [Google Scholar] [CrossRef]
  71. Huang, Q.; Chen, L.; Sheng, Y.; Ma, L.; Fu, Z.; Yang, W. Synthesis and characterization of oligomer from 1-decene catalyzed by AlCl3/TiCl4/SiO2/Et2AlCl. J. Appl. Polym. Sci. 2006, 101, 584–590. [Google Scholar] [CrossRef]
  72. Kawahara, N.; Saito, J.; Matsuo, S.; Kaneko, H.; Matsugi, T.; Toda, Y.; Kashiwa, N. Study on unsaturated structures of polyhexene, poly(4-methylpentene) and poly(3-methylpentene) prepared with metallocene catalysts. Polymer 2007, 48, 425–428. [Google Scholar] [CrossRef]
  73. Brant, P.; Jiang, P.; Lovell, J.; Crowther, D. Termination events in sterically hindered metallocene-catalyzed olefin oligomerizations: Vinyl chain ends in oligooctenes. Organometallics 2016, 35, 2836–2839. [Google Scholar] [CrossRef]
  74. Shao, H.; Wang, R.; Li, H.; Guo, X.; Jiang, T. Synthesis of low-molecular-weight poly-α-olefins using silicon-bridged zirconocene catalyst for lubricant basestock. Arab. J. Chem. 2020, 13, 2715–2721. [Google Scholar] [CrossRef]
  75. Kim, I.; Zhou, J.-M.; Chung, H. Higher α-olefin polymerizations catalyzed by rac-Me2Si(1-C5H2-2-CH3-4-tBu)2Zr(NMe2)2/Al(iBu)3/[Ph3C][B(C6F5)4]. J. Polym. Sci. Part A Polym. Chem. 2000, 38, 1687–1697. [Google Scholar] [CrossRef]
  76. Zhao, X.; Odian, G.; Rossi, A. Kinetics, polymer molecular weights, and microstructure in zirconocene-catalyzed 1-hexene polymerization. J. Polym. Sci. Part A Polym. Chem. 2000, 38, 3802–3811. [Google Scholar] [CrossRef]
  77. Babu, G.N.; Newmark, R.A.; Chien, J.C.W. Microstructure of Poly(1-hexene) Produced by ansa-Zirconocenium Catalysis. Macromolecules 1994, 27, 3383–3388. [Google Scholar] [CrossRef]
  78. Grumel, V.; Brüll, R.; Pasch, H.; Raubenheimer, H.G.; Sanderson, R.; Wahner, U.M. Homopolymerization of Higher 1-Olefins with Metallocene/MAO Catalysts. Macromol. Mater. Eng. 2001, 286, 480–487. [Google Scholar] [CrossRef]
  79. Babushkin, D.E.; Panchenko, V.N.; Brintzinger, H.H. Zirconium Allyl Complexes as Participants in Zirconocene-Catalyzed alpha-Olefin Polymerizations. Angew. Chem. Int. Ed. 2014, 53, 9645–9649. [Google Scholar] [CrossRef]
  80. Nifant’ev, I.E.; Vinogradov, A.A.; Vinogradov, A.A.; Churakov, A.V.; Bagrov, V.V.; Kashulin, I.A.; Roznyatovsky, V.A.; Grishin, Y.K.; Ivchenko, P.V. The catalytic behavior of heterocenes activated by TIBA and MMAO under a low Al/Zr ratios in 1-octene polymerization. Appl. Catal. A: General 2019, 571, 12–24. [Google Scholar] [CrossRef]
  81. Bryliakov, K.P.; Semikolenova, N.V.; Yudaev, D.V.; Zakharov, V.A.; Brintzinger, H.H.; Ystenes, M.; Rytter, E.; Talsi, E.P. 1H-, 13C-NMR and ethylene polymerization studies of zirconocene/MAO catalysts: Effect of the ligand structure on the formation of active intermediates and polymerization kinetics. J. Organomet. Chem. 2003, 683, 92–102. [Google Scholar] [CrossRef] [Green Version]
  82. Tritto, I.; Donetti, R.; Sacchi, M.C.; Locatelli, P.; Zannoni, G. Dimethylzirconocene−Methylaluminoxane Catalyst for Olefin Polymerization:  NMR Study of Reaction Equilibria. Macromolecules 1997, 30, 1247–1252. [Google Scholar] [CrossRef]
  83. Babushkin, D.E.; Semikolenova, N.V.; Zakharov, V.A.; Talsi, E.P. Mechanism of dimethylzirconocene activation with methylaluminoxane: NMR monitoring of intermediates at high Al/Zr ratios. Macromol. Chem. Phys. 2000, 201, 558–567. [Google Scholar] [CrossRef]
  84. Ehm, C.; Cipullo, R.; Budzelaar, P.H.M.; Busico, V. Role of TMA in polymerization. Dalton Trans. 2016, 45, 6847–6855. [Google Scholar] [CrossRef] [PubMed]
  85. Trefz, T.K.; Henderson, M.A.; Linnolahti, M.; Collins, S.; McIndoe, J.S. Mass Spectrometric Characterization of Methylaluminoxane-Activated Metallocene Complexes. Chem. Eur. J. 2015, 21, 2980–2991. [Google Scholar] [CrossRef] [PubMed]
  86. Talarico, G.; Budzelaar, P.H.M. Variability of Chain Transfer to Monomer Step in Olefin Polymerization. Organometallics 2008, 27, 4098–4107. [Google Scholar] [CrossRef]
  87. Lieber, S.; Brintzinger, H.-H. Propene Polymerization with Catalyst Mixtures Containing Different ansa-Zirconocenes: Chain Transfer to Alkylaluminum Cocatalysts and Formation of Stereoblock Polymers. Macromolecules 2000, 33, 9192–9199. [Google Scholar] [CrossRef]
  88. Babushkin, D.E.; Brintzinger, H.H. Reactive intermediates formed during olefin polymerization by methylalumoxane-activated ansa-zirconocene catalysts: Identification of a chain-carrying intermediate by NMR methods. J. Am. Chem. Soc. 2010, 132, 452–453. [Google Scholar] [CrossRef] [Green Version]
  89. Adamu, S.; Atiqullah, M.; Malaibari, Z.O.; Al-Harthi, M.A.; Emwas, A.-H.M.; Ul-Hamid, A. Metallocene-catalyzed ethylene−α-olefin isomeric copolymerization: A perspective from hydrodynamic boundary layer mass transfer and design of MAO anion. J. Taiwan Ins. Chem. Eng. 2016, 60, 92–105. [Google Scholar] [CrossRef] [Green Version]
  90. Nifant’ev, I.E.; Vinogradov, A.A.; Vinogradov, A.A.; Bezzubov, S.I.; Ivchenko, P.V. Catalytic oligomerization of α-olefins in the presence of two-stage activated zirconocene catalyst based on 6,6-dimethylfulvene ‘dimer’. Mendeleev Commun. 2017, 27, 35–37. [Google Scholar] [CrossRef]
  91. Nifant’ev, I.E.; Vinogradov, A.A.; Vinogradov, A.A.; Sedov, I.V.; Dorokhov, V.G.; Lyadov, A.S.; Ivchenko, P.V. Structurally uniform 1-hexene, 1-octene, and 1-decene oligomers: Zirconocene/MAO-catalyzed preparation, characterization, and prospects of their use as low-viscosity low-temperature oil base stocks. Appl. Catal. A Gen. 2018, 549, 40–50. [Google Scholar] [CrossRef]
  92. Ivchenko, P.V.; Nifant’ev, I.E.; Vinogradov, A.A.; Krut’ko, D.P.; Shandryuk, G.A. Crosslinked α-olefin-diene copolymers prepared using a metallocene catalyst deposited on the surface of SiO2-modified Fe3O4: Ferromagnetic oil sponges. Polym. Sci. Ser. B 2017, 59, 83–90. [Google Scholar] [CrossRef]
  93. DiMaio, A.J.; Baranski, J.R.; Budworth, J.G.; Gillis, D.J. Process for Producing Liquid Polyalphaolefin Polymer, Metallocene Catalyst therefor, the Resulting Polymer and Lubricant Containing Same. U.S. Patent 6858767, 22 February 2005. [Google Scholar]
  94. Londaitsbehere, A.; Cuenca, T.; Mosquera, M.E.G.; Cano, J.; Milione, S.; Grassi, A. 1,3-Double Siloxo-Bridged Zirconium Metallocene for Propene and 1-Hexene Regioselective Oligomerization. Organometallics 2012, 31, 2108–2111. [Google Scholar] [CrossRef]
  95. Welle, A.; Wassenaar, J.; Slawinski, M. Use of a Metallocene Catalyst to Produce a Polyalpha-Olefin. U.S. Patent 9688792, 27 June 2017. [Google Scholar]
  96. Wu, M.M.-S.; Baugh, L.S.; Canich, J.A.; Chee, C.S.; Hagemeister, M.P.; Jackson, A.; Jiang, P.; Lee, G.H.; Lo, F.Y.-K.; Rucker, S.P.; et al. Polyalpha-Olefin Compositions and Processes to Produce the Same. U.S. Patent Application 2009005279, 01 January 2009. [Google Scholar]
  97. Small, B.L.; Hope, K.D.; Masino, A.P.; McDaniel, M.P.; Buck, R.M.; Beaulieu, W.B.; Yang, Q.; Baralt, E.J.; Netemeyer, E.J.; Kreischer, B. Oligomerization of Alpha Olefins Using Metallocene-SSA Catalyst Systems and Use of the Resultant Polyalphaolefins to Prepare Lubricant Blends. U.S. Patent 8536391, 17 September 2013. [Google Scholar]
  98. Di Maio, A.J. Process for the Oligmerization of Alpha-Olefins Having Low Unsaturation. U.S. Patent 7129306, 31 October 2006. [Google Scholar]
  99. Minami, H.; Egawa, T. Process for Producing a Polymer of an Alpha-Olefin and Lubricant. U.S. Patent Application 2002143113, 03 October 2002. [Google Scholar]
  100. Iimure, Y.; Hirano, H.; Tohi, Y.; Upakawa, N. Synthetic Lubricating Oil and Lubricating Oil Composition. U.S. Patent 7795194, 14 September 2010. [Google Scholar]
  101. Shao, H.; Li, H.; Lin, J.; Jiang, T.; Guo, X.; Li, J. Metallocene-catalyzed oligomerizations of 1-butene and α-olefins: Toward synthetic lubricants. Eur. Polym. J. 2014, 59, 208–217. [Google Scholar] [CrossRef]
  102. Kissin, Y.V. Detailed Kinetics of 1-Hexene Oligomerization Reaction with (n-Bu-Cp)2ZrCl2–MAO Catalyst. Macromol. Chem. Phys. 2009, 210, 1241–1246. [Google Scholar] [CrossRef]
  103. Kissin, Y.V. Oligomerization reactions of 1-hexene with metallocene catalysts: Detailed data on reaction chemistry and kinetics. Mol. Catal. 2019, 463, 87–93. [Google Scholar] [CrossRef]
  104. Dong, S.Q.; Mi, P.K.; Xu, S.; Zhang, J.; Zhao, R.D. Preparation and Characterization of Single-Component Poly-α-olefin Oil Base Stocks. Energy Fuels 2019, 33, 9796–9804. [Google Scholar] [CrossRef]
  105. De Rosa, C.; Auriemma, F.; Di Capua, A.; Resconi, L.; Guidotti, S.; Camurati, I.; Nifant’ev, I.E.; Laishevtsev, I.P. Structure-Property Correlations in Polypropylene from Metallocene Catalysts: Stereodefective, Regioregular Isotactic Polypropylene. J. Am. Chem. Soc. 2004, 126, 17040–17049. [Google Scholar] [CrossRef]
  106. Nifant’ev, I.E.; Laishevtsev, I.P.; Ivchenko, P.V.; Kashulin, I.A.; Guidotti, S.; Piemontesi, F.; Camurati, I.; Resconi, L.; Klusener, P.A.A.; Rijsemus, J.J.H.; et al. C1-Symmetric Heterocyclic Zirconocenes as Catalysts for Propylene Polymerization, 1. ansa-Zirconocenes with Linked Dithienocyclopentadienyl-Substituted Cyclopentadienyl Ligands. Macromol. Chem. Phys. 2004, 205, 2275–2291. [Google Scholar] [CrossRef]
  107. Resconi, L.; Guidotti, S.; Camurati, I.; Frabetti, R.; Focante, F.; Nifant’ev, I.E.; Laishevtsev, I.P. C1-Symmetric Heterocyclic Zirconocenes as Catalysts for Propylene Polymerization, 2. ansa-Zirconocenes with Linked Dithienocyclopentadienyl-Substituted Indenyl Ligands. Macromol. Chem. Phys. 2005, 206, 1405–1438. [Google Scholar] [CrossRef]
  108. Ryabov, A.N.; Gribkov, D.V.; Izmer, V.V.; Voskoboynikov, A.Z. Zirconium Complexes with Cyclopentadienyl Ligands Involving Fused a Thiophene Fragment. Organometallics 2002, 21, 2842–2855. [Google Scholar] [CrossRef]
  109. Yang, X.; Stern, C.L.; Marks, T.J.; Cationic Metallocene Polymerization Catalysts. Synthesis and Properities of the Cationic Metallocene Polymerization Catalysts. Synthesis and Properities of the First Base-Free Zirconocene Hydride. Angew. Chem. Int. Ed. 1992, 31, 1375–1377. [Google Scholar] [CrossRef]
  110. Chen, E.Y.-X.; Marks, T.J. Cocatalysts for Metal-Catalyzed Olefin Polymerization: Activators, Activation Processes, and Structure-Activity Relationships. Chem. Rev. 2000, 100, 1391–1434. [Google Scholar] [CrossRef] [PubMed]
  111. Chen, M.-C.; Roberts, J.A.S.; Seyam, A.M.; Li, L.; Zuccaccia, C.; Stahl, N.G.; Marks, T.J. Diversity in Weakly Coordinating Anions. Mono- and Polynuclear Halo(perfluoroaryl)metalates as Cocatalysts for Stereospecific Olefin Polymerization:  Synthesis, Structure, and Reactivity. Organometallics 2006, 25, 2833–2850. [Google Scholar] [CrossRef]
  112. Park, J.H.; Jang, Y.E.; Jeon, J.Y.; Go, M.J.; Lee, J.; Kim, S.K.; Lee, S.-I.; Lee, B.Y. Preparation of ansa-metallocenes for production of poly(α-olefin) lubricants. Dalton Trans. 2014, 43, 10132–10138. [Google Scholar] [CrossRef]
  113. Wu, M.M.; Coker, C.L.; Walzer, J.F.; Jiang, P. Process to Produce Low Viscosity Poly-Alfa-Olefins. U.S. Patent 8207390, 26 June 2012. [Google Scholar]
  114. Wu, M.M.; Coker, C.L.; Walzer, J.F.; Jiang, P.; Rucker, S.P. Process to Produce High Viscosity Fluids. U.S. Patent 7989670, 02 August 2011. [Google Scholar]
  115. Wu, M.M.; Pafford, B.J.; Stavens, K.B. Polyalphaolefins by Oligomerization and Isomerization. U.S. Patent Application 2014323665, 30 October 2014. [Google Scholar]
  116. Hagemeister, M.P.; Jiang, P.; Wu, M.M.; Yang, N. Production of Shear-Stable High Viscosity PAO. U.S. Patent 9365663, 14 June 2016. [Google Scholar]
  117. Wu, M.M.; Hagemeister, M.P.; Yang, N. Process to Produce Polyalphaolefins. U.S. Patent 8513478, 20 August 2013. [Google Scholar]
  118. Jiang, H.; Yu, K. Catalytic polymerization of 1-decene using a silicon-bridged metallocene system. Petrol. Sci. Technol. 2017, 35, 1451–1456. [Google Scholar] [CrossRef]
  119. Katayama, K.; Noda, H.; Shimizu, H.; Okano, M. Alpha-Olefin (co)Polymer, Hydrogenated α-Olefin (co)Polymer and Lubricating Oil Composition Containing Them. U.S. Patent Application 2012302481, 29 November 2012. [Google Scholar]
  120. Shimizu, H.; Katayama, K.; Noda, H.; Okano, M. 1-Octene, 1-Decene, 1-Dodecene Ternary Copolymer and Lubricants Therewith. U.S. Patent Application 2014256997, 11 September 2014. [Google Scholar]
  121. Shimizu, H.; Katayama, K.; Noda, H.; Okano, M. 1-Octene/1-Decene Copolymer and Libricating-Oil Composition Containing Same. U.S. Patent Application 2014309151, 16 October 2014. [Google Scholar]
  122. Patil, A.O.; Bodige, S.; Luo, S.; Chu, J.W.; Stavens, K.; Harrrington, B.A. Ultra High Viscosity Synthetic Base Stocks and Process for Preparing Same. U.S. Patent Application 2014213834, 31 July 2014. [Google Scholar]
  123. Patil, A.O.; Bodige, S. Synthetic Libricant Basestocks and Methods of Preparation Thereof. U.S. Patent 9422497, 23 August 2016. [Google Scholar]
  124. Wu, M.M.; Rucker, S.P.; Canich, A.M. Process for Producing Novel Synthetic Basestocks. U.S. Patent 9701595, 11 July 2017. [Google Scholar]
  125. Courtiade, M.; Sanson, J.; Welle, A.; Slawinski, M.; Wassenaar, J. Method for Preparing Low-Viscosity Lubricating Polyolefins. U.S. Patent Application 2017226441, 10 August 2017. [Google Scholar]
  126. Gibson, V.C.; Spitzmesser, S.K. Advances in Non-Metallocene Olefin Polymerization Catalysis. Chem. Rev. 2003, 103, 283–315. [Google Scholar] [CrossRef]
  127. Gibson, V.C.; Redshaw, C.; Solan, G.A. Bis(imino)pyridines: Surprisingly Reactive Ligands and a Gateway to New Families of Catalysts. Chem. Rev. 2007, 107, 1745–1776. [Google Scholar] [CrossRef]
  128. Budagumpi, S.; Kim, K.-H.; Kim, I. Catalytic and coordination facets of single-site non-metallocene organometallic catalysts with N-heterocyclic scaffolds employed in olefin polymerization. Coord. Chem. Rev. 2011, 255, 2785–2809. [Google Scholar] [CrossRef]
  129. Sydora, O.L.; Jones, T.C.; Small, B.L.; Nett, A.J.; Fischer, A.A.; Carney, M.J. Selective Ethylene Tri-/Tetramerization Catalysts. ACS Catal. 2012, 2, 2452–2455. [Google Scholar] [CrossRef]
  130. Agapie, T. Selective ethylene oligomerization: Recent advances in chromium catalysis and mechanistic investigations. Coord. Chem. Rev. 2011, 255, 861–880. [Google Scholar] [CrossRef]
  131. van Leeuwen, P.W.N.M.; Clément, N.D.; Tschan, M.J.-L. New processes for the selective production of 1-octene. Coord. Chem. Rev. 2011, 255, 1499–1517. [Google Scholar] [CrossRef]
  132. Small, B.L. Discovery and Development of Pyridine-bis(imine) and Related Catalysts for Olefin Polymerization and Oligomerization. Acc. Chem. Res. 2015, 48, 2599–2611. [Google Scholar] [CrossRef] [PubMed]
  133. Baier, M.C.; Zuideveld, M.A.; Mecking, S. Post-Metallocenes in the Industrial Production of Polyolefins. Angew. Chem. Int. Ed. 2014, 53, 9722–9744. [Google Scholar] [CrossRef]
  134. Alferov, K.A.; Belov, G.P.; Meng, Y. Chromium catalysts for selective ethylene oligomerization to 1-hexene and 1-octene: Recent results. Appl. Catal. A Gen. 2017, 542, 71–124. [Google Scholar] [CrossRef]
  135. Raucoules, R.; de Bruin, T.; Raybaud, P.; Adamo, C. Theoretical Unraveling of Selective 1-Butene Oligomerization Catalyzed by Iron−Bis(arylimino)pyridine. Organometallics 2009, 28, 5358–5367. [Google Scholar] [CrossRef]
  136. Majoumo-Mbe, F.; Lönnecke, P.; Volkis, V.; Sharma, M.; Eisen, M.S.; Hey-Hawkins, E. Oligomerization of α-olefins by the dimeric nickel bisamido complex [Ni{1-N(PMes2)-2-N(μ-PMes2)C6H4-κ3N,N′,P,-κ1P′}]2 activated by methylalumoxane (MAO). J. Organomet. Chem. 2008, 693, 2603–2609. [Google Scholar] [CrossRef]
  137. Dagorne, S.; Bellemin-Laponnaz, S.; Romain, C. Neutral and Cationic N-Heterocyclic Carbene Zirconium and Hafnium Benzyl Complexes: Highly Regioselective Oligomerization of 1-Hexene with a Preference for Trimer Formation. Organometallics 2013, 32, 2736–2743. [Google Scholar] [CrossRef]
  138. Despagnet-Ayoub, E.; Takase, M.K.; Henling, L.M.; Labinger, J.A.; Bercaw, J.E. Mechanistic Insights on the Controlled Switch from Oligomerization to Polymerization of 1-Hexene Catalyzed by an NHC-Zirconium Complex. Organometallics 2015, 34, 4707–4716. [Google Scholar] [CrossRef] [Green Version]
  139. Nakata, N.; Nakamura, K.; Ishii, A. Highly efficient and 1,2-regioselective method for the oligomerization of 1-hexene promoted by zirconium precatalysts with [OSSO]-type bis(phenolate) ligands. Organometallics 2018, 37, 2640–2644. [Google Scholar] [CrossRef]
  140. Nakata, N.; Nakamura, K.; Nagaoka, S.; Ishii, A. Carbazolyl-Substituted [OSSO]-Type Zirconium(IV) Complex as a Precatalyst for the Oligomerization and Polymerization of α-Olefins. Catalysts 2019, 9, 528. [Google Scholar] [CrossRef] [Green Version]
  141. Manyik, R.M.; Walker, W.E.; Wilson, T.P. A soluble chromium-based catalyst for ethylene trimerization and polymerization. J. Catal. 1977, 47, 197–209. [Google Scholar] [CrossRef]
  142. Köhn, R.D.; Haufe, M.; Kociok- Köhn, G.; Grimm, S.; Wasserscheid, P.; Keim, W. Selective Trimerization of α-Olefins with Triazacyclohexane Complexes of Chromium as Catalysts. Angew. Chem. Int. Ed. 2000, 39, 4337–4339. [Google Scholar] [CrossRef]
  143. Wasserscheid, P.; Grimm, S.; Köhn, R.D.; Haufe, M. Synthesis of Synthetic Lubricants by Trimerization of 1-Decene and 1-Dodecene with Homogeneous Chromium Catalysts. Adv. Synth. Catal. 2001, 343, 814–818. [Google Scholar] [CrossRef]
  144. Coxon, A.G.N.; Köhn, R.D. Efficient 1-Hexene Trimerization with Triazacyclohexane Chromium Catalysts and Detailed Product Analysis by 13C NMR. ACS Catal. 2016, 6, 3008–3016. [Google Scholar] [CrossRef] [Green Version]
  145. Luo, S.; Patil, A.O. Processes for Preparing Low Viscosity Lubricating Oil Base Stocks. U.S. Patent 8889931, 18 November 2014. [Google Scholar]
  146. Sattler, A.; Labinger, J.A.; Bercaw, J.E. Highly Selective Olefin Trimerization Catalysis by a Borane-Activated Titanium Trimethyl Complex. Organometallics 2013, 32, 6899–6902. [Google Scholar] [CrossRef] [Green Version]
  147. Gordon, C.P.; Shirase, S.; Yamamoto, K.; Andersen, R.A.; Eisenstein, O.; Copéret, C. NMR chemical shift analysis decodes olefin oligo- and polymerization activity of d0 group 4 metal complexes. Proc. Natl. Acad. Sci. USA 2018, 115, E5867–E5876. [Google Scholar] [CrossRef] [Green Version]
  148. 148 Speiser, F.; Braunstein, P.; Saussine, L. Catalytic Ethylene Dimerization and Oligomerization: Recent Developments with Nickel Complexes Containing P,N-Chelating Ligands. Acc. Chem. Res. 2005, 38, 784–793. [Google Scholar] [CrossRef]
  149. 149 Yao, Z.-J.; Deng, W. Half-sandwich late transition metal complexes based on functionalized carborane ligands. Coord. Chem. Rev. 2016, 309, 21–35. [Google Scholar] [CrossRef]
  150. 150 Yao, Z.-J.; Li, P.; Li, K.; Deng, W. Synthesis, structure and catalytic polymerization activity of half-sandwich cyclometallated iridium complexes. Appl. Organomet. Chem. 2018, 32, e4239. [Google Scholar] [CrossRef]
  151. 151 Antonov, A.A.; Semikolenova, N.V.; Zakharov, V.A.; Zhang, W.; Wang, Y.; Sun, W.-H.; Talsi, E.P.; Bryliakov, K.P. Vinyl Polymerization of Norbornene on Nickel Complexes with Bis(imino)pyridine Ligands Containing Electron-Withdrawing Groups. Organometallics 2012, 31, 1143–1149. [Google Scholar] [CrossRef]
  152. 152 Mlinar, A.N.; Keitz, B.K.; Gygi, D.; Bloch, E.D.; Long, J.R.; Bell, A.T. Selective Propene Oligomerization with Nickel(II)-Based Metal−Organic Frameworks. ACS Catal. 2014, 4, 717–721. [Google Scholar] [CrossRef]
  153. 153 Behr, A.; Bayrak, Z.; Peitz, S.; Stochniol, G.; Maschmeyer, D. Oligomerization of 1-butene with a homogeneous catalyst system based on allylic nickel complexes. RSC Adv. 2015, 5, 41372–41376. [Google Scholar] [CrossRef]
  154. 154 Forget, S.; Olivier-Bourbigou, H.; Delcroix, D. Homogeneous and Heterogeneous Nickel-Catalyzed Olefin Oligomerization: Experimental Investigation for a Common Mechanistic Proposition and Catalyst Optimization. ChemCatChem 2017, 9, 2408–2417. [Google Scholar] [CrossRef]
  155. 155 Guo, L.; Dai, S.; Sui, X.; Chen, C. Palladium and Nickel Catalyzed Chain Walking Olefin Polymerization and Copolymerization. ACS Catal. 2016, 6, 428–441. [Google Scholar] [CrossRef] [Green Version]
  156. 156 Hu, H.; Gao, H.; Chen, D.; Li, G.; Tan, Y.; Liang, G.; Zhu, F.; Wu, Q. Ligand-Directed Regioselectivity in Amine–Imine Nickel-Catalyzed 1-Hexene Polymerization. ACS Catal. 2015, 5, 122–128. [Google Scholar] [CrossRef]
  157. 157 O’Connor, K.S.; Lamb, J.R.; Vaidya, T.; Keresztes, I.; Klimovica, K.; LaPointe, A.M.; Daugulis, O.; Coates, G.W. Understanding the Insertion Pathways and Chain Walking Mechanisms of α-Diimine Nickel Catalysts for α-Olefin Polymerization: A 13C NMR Spectroscopic Investigation. Macromolecules 2017, 50, 7010–7027. [Google Scholar] [CrossRef]
  158. 158 Ojwach, S.O.; Darkwa, J. Perspective and future prospects of tandem olefin oligomerization and Friedel–Crafts alkylation reactions catalyzed by iron, cobalt, nickel and palladium complexes. Catal. Sci. Technol. 2019, 9, 2078–2096. [Google Scholar] [CrossRef]
  159. Aruleswaran, N.R.; Sharko, P.T.; Crump, J.G. Vinylidene Dimer Derivatives. U.S. Patent Application 2015284350, 08 October 2015. [Google Scholar]
  160. Kerbal, A. Synthesis and Glutathione S-Transferase Structure−Affinity Relationships of Nonpeptide and Peptidase-Stable Glutathione Analogues. J. Med. Chem. 1998, 41, 2278–2288. [Google Scholar] [CrossRef]
  161. Nifant’ev, I.E.; Minyaev, M.E.; Tavtorkin, A.N.; Vinogradov, A.A.; Ivchenko, P.V. Branched alkylphosphinic and disubstituted phosphinic and phosphonic acids: Effective synthesis based on α-olefin dimers and applications in lanthanide extraction and separation. RSC Adv. 2017, 7, 24122–24128. [Google Scholar] [CrossRef] [Green Version]
  162. Nifant’ev, I.E.; Lyadov, A.S.; Tavtorkin, A.N.; Vinogradov, A.A.; Kochubeev, A.A.; Ivchenko, P.V. Branched alkylphosphinic acids demonstrate explicit anti-wear effect. Mendeleev Commun. 2019, 29, 558–560. [Google Scholar] [CrossRef]
  163. Mishima, E.; Tamura, T.; Yamago, S. Controlled Copolymerization of Acrylate and 6-Methyleneundecane by Organotellurium-Mediated Living Radical Polymerization (TERP). Macromolecules 2012, 45, 2989–2994. [Google Scholar] [CrossRef]
  164. Nifant’ev, I.E.; Vinogradov, A.A.; Bondarenko, G.N.; Korchagina, S.A.; Shlyakhtin, A.V.; Roznyatovsky, V.A.; Ivchenko, P.V. Copolymers of Maleic Anhydride and Methylene Alkanes: Synthesis, Modification, and Pour Point Depressant Properties. Polym. Sci. Ser. B 2018, 60, 469–480. [Google Scholar] [CrossRef]
  165. Nifant’ev, I.; Vinogradov, A.; Vinogradov, A.; Ivchenko, P. DFT Modeling of the Alternating Radical Copolymerization and Alder-Ene Reaction between Maleic Anhydride and Olefins. Polymers 2020, 12, 744. [Google Scholar] [CrossRef] [Green Version]
  166. Shanker, S.K.; Shiga, M.; Fuchi, M.; Nakagawa, T. Lubricating Oil Composition and Method for Operating Automatic Transmission. U.S. Patent Application 2013029890, 31 January 2013. [Google Scholar]
  167. Sato, H.; Okamoto, T. Dioxolane Derivative and Method for Producing Same. EP Patent 1792900, 06 June 2007. [Google Scholar]
  168. Sato, H.; Kashiwamura, T.; Ikeda, Y. Process for Producing Aldehyde with 2-Postiion Branched Long-Chain Alkyl. EP Patent 1908746, 09 April 2008. [Google Scholar]
  169. Sato, H.; Shishikura, A. Alkyl Acetal Compound, Process for Producing the Same, and Lubricatiog Oil Composition. U.S. Patent Application 2008234152, 25 September 2008. [Google Scholar]
  170. Harvey, B.G.; Meylemansa, H.A.; Quintana, R.L. Synthesis of renewable plasticizer alcohols by formal anti-Markovnikov hydration of terminal branched chain alkenes via a borane-free oxidation/reduction sequence. Green Chem. 2012, 14, 2450–2456. [Google Scholar] [CrossRef]
  171. Sato, H.; Kamimura, H. Process for Producing Saturated Aliphatic Hydrocarbon Compound, and Lubricant Composition. U.S. Patent 8373011, 12 February 2013. [Google Scholar]
  172. Patil, A.O. Diphenylamine Functionalization of Poly-Alpha-Olefins. U.S. Patent 7847030, 07 December 2009. [Google Scholar]
  173. Sato, H.; Kashiwamura, T.; Okamoto, T.; Yokota, K. Carbonyl Compound Containing Long-Chain Branched Alkyl Group. U.S. Patent 7402610, 22 July 2008. [Google Scholar]
  174. De Kraker, A.R. Olefin Oligomer Composition. U.S. Patent 8383869, 26 February 2013. [Google Scholar]
  175. Patil, A.; Lewis, K.G.; Bodige, S.; Zushma, S. Ester Compounds, Lubricating Oil Composition Containing Same and Process for Making Same. U.S. Patent Application 2019062663, 28 February 2019. [Google Scholar]
  176. Nafant’ev, I.E.; Sevostyanova, N.T.; Batashev, S.A.; Vinogradov, A.A.; Vinogradov, A.A.; Churakov, A.V.; Ivchenko, P.V. Synthesis of methyl β-alkylcarboxylates by Pd/diphosphine-catalyzed methoxycarbonylation of methylenealkanes RCH2CH2C(R)=CH2. Appl. Catal. A Gen. 2019, 581, 123–132. [Google Scholar] [CrossRef]
  177. Nifant’ev, I.; Bagrov, V.; Vinogradov, A.; Vinogradov, A.; Ilyin, S.; Sevostyanova, N.; Batashev, S.; Ivchenko, P. Methylenealkane-based Low-Viscosity Ester Oils: Synthesis and Outlook. Lubricants 2020, 8, 50. [Google Scholar] [CrossRef]
  178. Patil, A.O.; Bodige, S. Low Viscosity, Low Volatility Lubricating Oil Basestocks. U.S. Patent 9822326, 21 November 2017. [Google Scholar]
  179. Denis, J. The relationships between structure and rheological properties of hydrocarbons and oxygenated compounds used as base stocks. J. Synth. Lubr. 1984, 1, 201–238. [Google Scholar] [CrossRef]
  180. Lahtela, M.; Pakkanen, T.A.; Nissfolk, F. Molecular Modeling of Poly-a-olefin Synthetic Oils. J. Phys. Chem. 1995, 99, 10267–10271. [Google Scholar] [CrossRef]
Polymers 12 01082 sch001 550
Scheme 1. Coordination oligomerization (a) and polymerization (b) of α-olefins.
Scheme 1. Coordination oligomerization (a) and polymerization (b) of α-olefins.
Polymers 12 01082 sch001
Polymers 12 01082 sch002 550
Scheme 2. Early works on the zirconocene-catalyzed dimerization of α-olefins [37,38,39] (a); high efficiency of the pre-catalyst 6 [40,41] (b); cationic Zr–Al catalytic species proposed to explain the reactivity of zirconocene under low MAO/Zr ratios [40,41] (c).
Scheme 2. Early works on the zirconocene-catalyzed dimerization of α-olefins [37,38,39] (a); high efficiency of the pre-catalyst 6 [40,41] (b); cationic Zr–Al catalytic species proposed to explain the reactivity of zirconocene under low MAO/Zr ratios [40,41] (c).
Polymers 12 01082 sch002
Polymers 12 01082 sch003 550
Scheme 3. Metallocene pre-catalysts studied in the coordination oligomerization of α-olefins.
Scheme 3. Metallocene pre-catalysts studied in the coordination oligomerization of α-olefins.
Polymers 12 01082 sch003
Polymers 12 01082 g001 550
Figure 1. Cooperative effect in Zr–Al transition states of the β-hydride elimination stage in the framework of the Zr–Al binuclear mechanism [62]. Copyright (2019) MDPI.
Figure 1. Cooperative effect in Zr–Al transition states of the β-hydride elimination stage in the framework of the Zr–Al binuclear mechanism [62]. Copyright (2019) MDPI.
Polymers 12 01082 g001
Polymers 12 01082 sch004 550
Scheme 4. Other metal complexes that are active in the selective oligomerization of α-olefins (a); formation of vinylidene olefins in the presence of W and Ta complexes (b).
Scheme 4. Other metal complexes that are active in the selective oligomerization of α-olefins (a); formation of vinylidene olefins in the presence of W and Ta complexes (b).
Polymers 12 01082 sch004
Polymers 12 01082 sch005 550
Scheme 5. Traditional mechanisms of chain release in α-olefin polymerization with a formation of characteristic chain-end groups (routes A–E) and saturated polyolefin species (route H) [72,73,80].
Scheme 5. Traditional mechanisms of chain release in α-olefin polymerization with a formation of characteristic chain-end groups (routes A–E) and saturated polyolefin species (route H) [72,73,80].
Polymers 12 01082 sch005
Polymers 12 01082 g002 550
Figure 2. Fragments of 1H NMR spectra of the reaction mixtures of 1-decene oligomerization (2 h, 100 °C), catalyzed by zirconocenes 8, 35, and 59, activated by 10 eq. of MMAO-12. Reprinted with permission from [91]. Copyright (2018) Elsevier B.V.
Figure 2. Fragments of 1H NMR spectra of the reaction mixtures of 1-decene oligomerization (2 h, 100 °C), catalyzed by zirconocenes 8, 35, and 59, activated by 10 eq. of MMAO-12. Reprinted with permission from [91]. Copyright (2018) Elsevier B.V.
Polymers 12 01082 g002
Polymers 12 01082 sch006 550
Scheme 6. Post-metallocene pre-catalysts studied in the non-selective coordination oligomerization of α-olefins.
Scheme 6. Post-metallocene pre-catalysts studied in the non-selective coordination oligomerization of α-olefins.
Polymers 12 01082 sch006
Polymers 12 01082 sch007 550
Scheme 7. (a) Metallacyclic mechanism of the coordination trimerization of α-olefins; (b) Precatalysts of trimerization; (c) Product distribution for the trimerization of 1-hexene, catalyzed by 77/MAO [142]; (d) The main product of the trimerization of α-olefins, catalyzed by 87 [146].
Scheme 7. (a) Metallacyclic mechanism of the coordination trimerization of α-olefins; (b) Precatalysts of trimerization; (c) Product distribution for the trimerization of 1-hexene, catalyzed by 77/MAO [142]; (d) The main product of the trimerization of α-olefins, catalyzed by 87 [146].
Polymers 12 01082 sch007
Polymers 12 01082 g003 550
Figure 3. 5-methyleneundecane derivatives and their prospective applications. Reprinted with permission from [41]. Copyright (2017) De Gruyter.
Figure 3. 5-methyleneundecane derivatives and their prospective applications. Reprinted with permission from [41]. Copyright (2017) De Gruyter.
Polymers 12 01082 g003
Polymers 12 01082 sch008 550
Scheme 8. Synthesis of alkylphosphinic and disubstituted phosphonic acids [161].
Scheme 8. Synthesis of alkylphosphinic and disubstituted phosphonic acids [161].
Polymers 12 01082 sch008
Polymers 12 01082 sch009 550
Scheme 9. Synthesis and modification of alternating copolymers of methylenealkanes and maleic anhydride [164].
Scheme 9. Synthesis and modification of alternating copolymers of methylenealkanes and maleic anhydride [164].
Polymers 12 01082 sch009
Polymers 12 01082 g004 550
Figure 4. Morphology of paraffin crystals in the absence (A) and in the presence (B) of the pour point depressant, the octadecanol-modified copolymer of maleic anhydride and 9-methylenenonadecane [164].
Figure 4. Morphology of paraffin crystals in the absence (A) and in the presence (B) of the pour point depressant, the octadecanol-modified copolymer of maleic anhydride and 9-methylenenonadecane [164].
Polymers 12 01082 g004
Polymers 12 01082 g005 550
Figure 5. (a) The Alder-ene reaction between maleic anhydride (MA) and methylenealkanes; (b) Optimized geometry of the transition state of the Alder-ene reaction between MA and 3-methyleneheptane [165].
Figure 5. (a) The Alder-ene reaction between maleic anhydride (MA) and methylenealkanes; (b) Optimized geometry of the transition state of the Alder-ene reaction between MA and 3-methyleneheptane [165].
Polymers 12 01082 g005
Polymers 12 01082 sch010 550
Scheme 10. Epoxidation of methylenealkanes with a formation of (a) 1,2-diols or (b) oxiranes; and related reactions.
Scheme 10. Epoxidation of methylenealkanes with a formation of (a) 1,2-diols or (b) oxiranes; and related reactions.
Polymers 12 01082 sch010
Polymers 12 01082 sch011 550
Scheme 11. Electrophilic dimerization of α-olefin dimers, methylenealkanes [47,91,171].
Scheme 11. Electrophilic dimerization of α-olefin dimers, methylenealkanes [47,91,171].
Polymers 12 01082 sch011
Polymers 12 01082 sch012 550
Scheme 12. Catalytic transformations of methylenealkanes: (a) Hydrofirmylation [173,175]; (b) Methoxycarbonylation [176]; (c) Hydrosilylation [178].
Scheme 12. Catalytic transformations of methylenealkanes: (a) Hydrofirmylation [173,175]; (b) Methoxycarbonylation [176]; (c) Hydrosilylation [178].
Polymers 12 01082 sch012
Polymers 12 01082 g006 550
Figure 6. Main structural types of hydrocarbons—components of oils. Reprinted with permission from [91]. Copyright (2018) Elsevier B.V.
Figure 6. Main structural types of hydrocarbons—components of oils. Reprinted with permission from [91]. Copyright (2018) Elsevier B.V.
Polymers 12 01082 g006
Polymers 12 01082 sch013 550
Scheme 13. Rearrangements in the cationic oligomerization of α-olefins [14,15].
Scheme 13. Rearrangements in the cationic oligomerization of α-olefins [14,15].
Polymers 12 01082 sch013
Polymers 12 01082 g007 550
Figure 7. (a) Gas chromatogram showing peaks for C20 olefin isomers during acid-catalyzed 1-decene oligomerization. Reprinted with permission from [15]. Copyright (2012) Wiley-VCH Verlag GmbH & Co; (b) Gas chromatorgams (C12–C30 range, left) and dimer range (right) of 1-hexene oligomers produced with the 8/MAO catalyst at 70 °C. Reprinted with permission from [103]. Copyright (2019) Elsevier B. V.
Figure 7. (a) Gas chromatogram showing peaks for C20 olefin isomers during acid-catalyzed 1-decene oligomerization. Reprinted with permission from [15]. Copyright (2012) Wiley-VCH Verlag GmbH & Co; (b) Gas chromatorgams (C12–C30 range, left) and dimer range (right) of 1-hexene oligomers produced with the 8/MAO catalyst at 70 °C. Reprinted with permission from [103]. Copyright (2019) Elsevier B. V.
Polymers 12 01082 g007
Polymers 12 01082 g008 550
Figure 8. Viscosity characteristics of 1-decene (green), 1-octene (red), and 1-hexene (blue) oligomers obtained by coordination polymerization [91] and in the presence of BF3–ROH [16]. D3*: decene trimer obtained using [EBTHI]ZrCl2–TIBA–perfluoroborate [52]. The range of technical requirements for promising poly-α-olefin oils (PAOs) was limited to the segment corresponding to VI = 100 for KV100 = 2 and VI = 120 for KV100 = 6. Reprinted with permission from [91]. Copyright (2018) Elsevier B. V.
Figure 8. Viscosity characteristics of 1-decene (green), 1-octene (red), and 1-hexene (blue) oligomers obtained by coordination polymerization [91] and in the presence of BF3–ROH [16]. D3*: decene trimer obtained using [EBTHI]ZrCl2–TIBA–perfluoroborate [52]. The range of technical requirements for promising poly-α-olefin oils (PAOs) was limited to the segment corresponding to VI = 100 for KV100 = 2 and VI = 120 for KV100 = 6. Reprinted with permission from [91]. Copyright (2018) Elsevier B. V.
Polymers 12 01082 g008
Table
Table 1. Metallocene-catalyzed oligomerization of α-olefins at high Al/Zr ratios
Table 1. Metallocene-catalyzed oligomerization of α-olefins at high Al/Zr ratios
Cat.Mon.[Mon]/[Zr][Al]/
[Zr]		T, °CH2, barTOF, h−1DPnKV100 1VI2Additional RemarksRef.
or Oligomer Distribution for DPn 2,3,4,5
1C61.3 × 105400050–5.9 × 1044.9–––[45,46]
C62 × 10320060––% olig. 45 (2):20 (3–5), res. 21 3[91]
C82 × 10320060––% olig. 45 (2):25 (3–5), res. 15[91]
C101.0 × 105100040–1.1 × 104–41196–[93]
C101.0 × 105100080–3.2 × 104–2.5181–[93]
C103.0 × 104305012.9 × 104% olig. 42:11:17:5, res. 35[51]
C105.0 × 10430070–9.2 × 103–1716724% of dimer[49]
C105.0 × 104300110–3.7 × 103–5.915255% of dimer[49]
C141.6 × 10353040–1.1 × 103% olig. 42:25:16:8, res. 6[50]
C141.6 × 10353060–>2 × 103% olig. 60:23:8:4, res. 5[50]
3C101.0 × 105100040–1.1 × 104–2460344–[93]
7C61.3 × 105400050–9.4 × 1045.7–––[45,46]
8C61.3 × 105400050–2.0 × 1043.9–– [45,46]
C62 × 10320060–-% olig. 15 (2):30 (3–5), res. 41[91]
C850020060–-% olig. 31 (2):41 (3–5), res. 16[91]
C101.0 × 105100090–6.3 × 104–2.3163 [93]
C103.0 × 104305012.7 × 104% olig. 47:26:11:4, res. 12[51]
C103.0 × 104100501>3 × 104% olig. 44:27:11:5, res. 13[51]
C103.0 × 1043005012.8 × 104% olig. 54:28:9:3, res. 6[51]
C103.0 × 1046005012.9 × 104% olig. 27:28:16:9, res. 20[51]
C105.0 × 104300110–6.0 × 103–6.715649% of dimer[49]
C105.0 × 104300110–6.0 × 103–6.715649% of dimer[49]
9C102.7 × 10334050–>3 × 103% olig. 43:24:11:5, res. 17[50]
C103.0 × 104305011.6 × 104% olig. 28:12:8:6, res. 46[51]
C105.0 × 104300110–6.0 × 103–5.715250% of dimer[49]
13C61.3 × 105400050–3.2 × 10414-- [45,46]
14C105.0 × 104300110–6.1 × 103–8.215940% of dimer[49]
19C103 × 104305011.5 × 104% olig. 25:24:10:6, res. 25[51]
20C105.0 × 10430070–1.1 × 104–611906% of dimer[49]
C105.0 × 104300110–9.8 × 103–1716215% of dimer[49]
23C103.0 × 104305018 × 103% olig. 13:5:4:3, res. 75[51]
24C61.3 × 105400050–7.5 × 10414–– [45,46]
25C61.3 × 105400050–3.9 × 10445–– [45,46]
26C61.3 × 105400050–6.5 × 10483–– [45,46]
C105.0 × 10430070–1.2 × 104-154–1% of dimer[49]
28, X = ClC61.3 × 105400050–3.4 × 10419–– [45,46]
C105.0 × 10430070–2.3 × 103–1152245% of dimer[49]
37C61.0 × 10350025–630~349% of dimer[94]
38C101.5 × 105100080–8.3 × 10426101– [95]
C101.5 × 10510008058.2 × 1041428– [95]
C101.5 × 105100080151.3 × 1051232– [95]
41C101.0 × 105250100–1.1 × 10472–– [96]
42C81.7 × 10510002540 63831– [97]
44C101.5 × 105100080–7.4 × 10427143– [95]
C101.5 × 10510008051.2 × 1051771– [95]
C101.5 × 105100080151.9 × 1051986– [95]
47C101.0 × 105100040–1.0 × 105–702296 [93]
48C102.6 × 105600806.9611–11211 [98]
51C101.3 × 1055008013.88.3 × 104–112208 [98]
52C101.0 × 105100040–5.0 × 104–2460344 [93]
C102.6 × 10520010013.88.9 × 10421116214 [98]
53C102.6 × 1052501006.92.6 × 1051994213 [98]
C102.6 × 10525090–5.6 × 1041331227– [98]
C102.6 × 105250901.71.0 × 10557453– [98]
C102.6 × 105250903.42.6 × 10540333– [98]
C102.6 × 105250906.92.6 × 1051994– [98]
C102.6 × 1052509013.82.1 × 1051239179 [98]
56C104.2 × 1052608013.81.4 × 1052125183 [98]
57C82.5 × 105100065–1.4 × 10523139192 [99]
C82.5 × 10510006582.2 × 1051843168 [99]
60C82.0 × 105100025–1.3 × 105831119– [97]
61C101.0 × 105100040–1.0 × 105–2460344 [93]
C103.0 × 105100070–2.4 × 10564635282 [93]
C103.0 × 1051000150–1.6 × 105–58195 [93]
C103.0 × 10550070–2.3 × 105–1134307 [93]
C103.0 × 10525070–1.7 × 105–1308314 [93]
C103.0 × 1051000700.51.5 × 105–1074308 [93]
C103.0 × 10510007012.1 × 105–863296 [93]
C103.0 × 10510007022.0 × 105–722288 [93]
C103.0 × 105100070132.4 × 105–512271 [93]
C63.0 × 105100090–1.8 × 105–2862251 [93]
C83.0 × 105100090–2.0 × 105–888276 [93]
C103.0 × 105100090–1.6 × 105–515272 [93]
C123.0 × 105100090–1.3 × 105–402264 [93]
62C107.0 × 10515006381.6 × 1051537177 [100]
1 Kinematic viscosity at 100 °C. 2 Viscosity index. 3 In % by weight, DPn in the brackets, res.—residue, higher oligomers.
Table
Table 2. Zirconocene-catalyzed oligomerization of α-olefins at low Al/Zr ratios
Table 2. Zirconocene-catalyzed oligomerization of α-olefins at low Al/Zr ratios
Cat.Mon.[Mon]/[Zr]AlTIBA/ZrAlMAO
/Zr		T, °CH2, barConv. (h)DPnAdditional RemarksRef.
or Oligomer Distribution
1C62 × 103201060–97 (4)% olig. 85 (2):12 (3–5), res. 1 1[91]
8C62 × 103201060–85 (4)% olig. 35 (2):36 (3–5), res. 20[91]
C62 × 103201060199 (4)% olig. 50 (2):31 (3–5), res. 11[91]
C82 × 103201060–83 (4)% olig. 40 (2):40 (3–5), res. 11[91]
C102 × 103201060–72 (4)% olig. 38 (2):35 (3–5), res. 17[91]
C102 × 1032010100–69 (4)% olig. 40 (2):36 (3–5), res. 10[91]
10C62 × 103201060–16 (4)% olig. 40 (2):30 (3–5), res. 19[91]
18C62 × 103201060–92 (4)% olig. 35 (2):31 (3–5), res. 31[91]
22C62 × 103201060–72 (4)% olig. 8 (2):34 (3–5), res. 55[91]
26C64 × 103804060–90 (4)38 [92]
30C62 × 103201060–89 (4)44 [91]
31C64 × 103804060–75 (4)190 [92]
35C62 × 103201060–98 (4)% olig. 41 (2):28 (3–5), res. 24[91]
C82 ×·103201060–98 (4)% olig. 36 (2):32 (3–5), res. 29[91]
C102 × 103201060–98 (4)% olig. 40 (2):33 (3–5), res. 35[91]
C102 × 1032010100–98 (4)% olig. 41 (2):34 (3–5), res. 19[91]
36C62·× 103201060–98 (4)% olig. 40 (2):30 (3–5), res. 11[90]
41C62 × 103201060–95 (4)% olig. 22 (2):32 (3–5), res. 39[91]
42C62 × 103201060–94 (4)% olig. 20 (2):31 (3–5), res. 40[91]
45C62·× 103201060–88 (4)25 [91]
C64 × 103804060–76 (4)25 [92]
46C62 × 103201060–94 (4)108 [91]
47C62 × 103201060–92 (4)37 [91]
C64 × 103804060–94 (4)35 [92]
50C64 × 103804060–95 (4)108 [92]
55C64 × 103804060–95 (4)68 [92]
59C62 × 103201060–100 (4)% olig. 9 (2):17 (3–5), res. 72[91]
C62 × 1032010601100 (4)% olig. 13 (2):24 (3–5), res. 57[91]
C82 × 103201060–100 (4)% olig. 23 (2):30 (3–5), res. 45[91]
C82 × 103201080–100 (4)% olig. 28 (2):26 (3–5), res. 44[91]
C82 × 1032010100–100 (4)% olig. 37 (2):34 (3–5), res. 27[91]
C82 × 1032010120–100 (4)% olig. 44 (2):32 (3–5), res. 21[91]
C82 × 10320101001100 (4)% olig. 47 (2):34 (3–5), res. 8[91]
C82 × 10320101201100 (4)% olig. 51 (2):40 (3–5), res. 10[91]
C102 × 1032010100–93 (4)% olig. 44 (2):45 (3–5), res. 7[91]
C102 × 1032010100199 (4)% olig. 45 (2):41 (3–5), res. 6[91]
C102 × 1032010120199 (4)% olig. 51 (2):33 (3–5), res. 10[91]
1 The ratios of dimer and lower oligomer fractions, and residue.
Table
Table 3. Zirconocene-catalyzed oligomerization of α-olefins, with activation by perfluoroaryl borates.
Table 3. Zirconocene-catalyzed oligomerization of α-olefins, with activation by perfluoroaryl borates.
Cat.Mon.[Mon]
/[Zr]		Al/ZrT, °CH2, barTOF, h−1DPnKV100VIAlR3, Additional RemarksRef.
or Oligomer Distribution for DPn 2,3,4,5+
11, X = MeC105.2 × 10550100–1.0·× 10327103–Al(n-Oct)3, NB 1[113]
C105.2·× 1055010033.6·× 1052311.3–Al(n-Oct)3, NB[113]
16, X = MeC105.2·× 10550100–5.2·× 10410.64.5–Al(n-Oct)3, NB[113]
C105.2·× 10550120–3.1·× 1048.83.4–Al(n-Oct)3, NB[113]
C105.2·× 105501003.77.8·× 1049.53.7–Al(n-Oct)3, NB[113]
C105.2·× 1055012038.0·× 1048.33.1–Al(n-Oct)3, NB[113]
17, X = MeC105.2·× 10550100–8.4·× 1031810.2–Al(n-Oct)3, NB[113]
C105.2·× 10550120–1.2·× 104114.9–Al(n-Oct)3, NB[113]
C105.2·× 1055012035.9·× 10410.64.5–Al(n-Oct)3, NB[113]
8C105.2·× 10550100–6.3 × 1049.34.0–Al(n-Oct)3, NB[113]
C105.2·× 10550120–3.9 × 1047.93.1–Al(n-Oct)3, NB[113]
C105.2·× 1055010037.4·× 1049.03.8–Al(n-Oct)3, NB[113]
C105.2·× 1055012038.8·× 1047.93.1–Al(n-Oct)3, NB[113]
20C105.2·× 1055010038.7·× 1047.93.0–Al(n-Oct)3, NB[113]
C105.2·× 1055012038.8·× 1047.52.8–Al(n-Oct)3, NB[113]
21, X = MeC108.5·× 104450–1.3·× 104-96199Al(n-Oct)3, NB[114]
C108.5·× 10446011.6·× 104-44180Al(n-Oct)3, NB[114]
C108.5·× 10447011.8·× 104-20179Al(n-Oct)3, NB[114]
C108.5·× 10448012.0·× 104-11.0163Al(n-Oct)3, NB[114]
C108.5·× 104410011.7·× 104-8.0161Al(n-Oct)3, NB[114]
C108.5·× 104412012.1·× 104-5.0151Al(n-Oct)3, NB[114]
C105.2·× 1055080–2.2·× 104135.9–Al(n-Oct)3, NB[113]
C105.2·× 10550100–3.3 ×·104104.1148Al(n-Oct)3, NB[113]
C105.2·× 10550120–3.3·× 1048.53.3–Al(n-Oct)3, NB[113]
C105.2·× 1055010031.2·× 1058.63.3–Al(n-Oct)3, NB[113]
26C101.2·× 105100110–––3.9144TIBA, NB[115]
27, X = MeC105.2·× 10550100–7.2·× 103104.1–Al(n-Oct)3, NB[113]
C105.2·× 10550120–1.8·× 1048.33.1–Al(n-Oct)3, NB[113]
C105.2·× 1055010031.1·× 1059.33.6–Al(n-Oct)3, NB[113]
C105.2·× 1055012033.1·× 1048.03.0–Al(n-Oct)3, NB[113]
28, X = MeC105.2·× 1055010032.0·× 1047.62.8–Al(n-Oct)3, NB[113]
C105.2·× 1055012031.4·× 1047.93.2–Al(n-Oct)3, NB[113]
32C102.6·× 105200120–4.7·× 1049.6/7.0/4.0/2.6 + 64TIBA, CB 2[112]
33C82.6·× 105200120–1.9·× 10513.1/14.1/11.8/33.4TIBA, CB[112]
C102.6·× 105200120–1.5·× 10513.3/14.3/11.3/34.7TIBA, CB[112]
34C102.6·× 105200120–9.1·× 10417.0/18.4/13.9/24.6TIBA, CB[112]
38C101.5·× 105200120+1.2·× 1056.65.5164TIBA, NB[95]
C101.5·× 105200140+1.2·× 1054.42.6140TIBA, NB[95]
39, X = MeC102.0·× 10520120–~2·× 105~3C30 3.4
C40 9.3		128 158Al(n-Oct)3, NB[52,53]
C108.9·× 1040.0160–7.3·× 10432169225Al(n-Oct)3, NB[116]
C108.9·× 1040.0180–8.4·× 1041426.5169Al(n-Oct)3, NB[116]
C108.9·× 1040.01100–8.8·× 1049.311.2150Al(n-Oct)3, NB[116]
40C103.6·× 105>10070–3.1·× 105-18.5164TIBA, CB[117]
C103.6·× 105>100100–2.0·× 105-8.9153TIBA, NB[117]
C103.6·× 105>100100–2.5·× 105-14.6158TIBA, CB[117]
48C103.5·× 105>10050–1.5·× 1052263715379TIBA, NB[117]
C103.5·× 105>10084–2.9·× 10580724291TIBA, NB[117]
C103.5·× 105>100100–2.3·× 10564363250TIBA, NB[117]
50C102–4·× 10520-20060–1001–101.0·× 105–253–586247–281TIBA, NB[118]
58C8/C121.0·× 105101000.5~1·× 10515–3539–140175–212TIBA, NB[119]
C8/C10/C121.0·× 105101000.5~1·× 10515–3040–120179–205TIBA, NB[120]
C8/C101.0·× 105101000.5~1·× 10519–3245–109175–204TIBA, NB[121]
61C104.4·× 105108023.6·× 105-834304TIBA, NB[122]
C104.4·× 1051010522.4·× 10576622289TIBA, NB[123,124]
C104.4·× 1051011023.2·× 10571558280TIBA, NB[122]
C104.4·× 1051012022.4·× 10563434270TIBA, NB[122]
C104.4·× 1051013022.4·× 10557377266TIBA, NB[122]
1 NB: [PhNMe2H][B(C6F5)4]. 2 CB: [CPh3][B(C6F5)4].
Table
Table 4. Oligomerization of 1-octene, catalyzed by zirconium complexes, activated by triisobutylalumnium (TIBA) and fluorinated aluminosilicate [97].
Table 4. Oligomerization of 1-octene, catalyzed by zirconium complexes, activated by triisobutylalumnium (TIBA) and fluorinated aluminosilicate [97].
Cat.[Mon]/[Zr]T, °CTOF, h–1KV100VI
11.1 × 105903.1 × 1038.9211
85.6 × 1051054.1 × 10445175
93.1 × 1051103.4 × 10462186
151.5 × 106701.3 × 105130222
295.5 × 105902.5 × 1048.3157
424.3 × 1051203.1 × 104159214
434.4 × 1051203.6 × 104132200
451.1 × 105909.0 × 10323169
474.2 × 1051154.3 × 104136210
491.0 × 1051005.2 × 10310.3194
Table
Table 5. The regioisomers produced in the trimerization of 1-hexene with a range of catalysts [144].
Table 5. The regioisomers produced in the trimerization of 1-hexene with a range of catalysts [144].
Polymers 12 01082 i001
Cat.Regioisomer Abundance (%)
ABCDEFGHIKLM
8339.922.411.816.53.62.00.90.40.21.20.40.7
8438.519.215..515.63.71.90.80.60.21.50.41.4
8546.915.33.019.78.33.11.50.30.20.70.30.7
8636.928.81.619.89.12.20.70.1<0.10.4<0.10.3
Table
Table 6. Viscosity characteristics of α-olefin oligomers.1
Table 6. Viscosity characteristics of α-olefin oligomers.1
No. of C AtomsOligomerKV−40,
sSt		KV40,
sSt		KV100,
sSt		VIPP, °CRef.
12H2H9.001.28––−73[91]
16O2–2.6–– [91]
16O2H53.12.82––−43[91]
18H3 3.12 [91]
18H3h167.23.57––−94[91]
18H3h (BF3 catalyst)1653.81.4–<−55[16]
20D2 4.551.714 [91]
20D2h 5.30–14−7[91]
24H4 7.552.1062 [91]
24H4h13358.932.2846−79[91]
24H4h (BF3 catalyst)17809.82.694 [16]
24H22h303012.42.7227−71[91]
24O3 6.52.06114 [91]
24O3h552.17.562.2092−86[91]
24O3H (BF3 catalyst)5808.02.392<−55[16]
30H5 17.553.676 [91]
30H5h679819.23.876−67[91]
30H5h (BF3 catalyst)785018.13.896 [16]
30D3 14.613.65140 [91]
30D3h (catalyst 79) 12.23.2126 [143]
30D3h (catalyst 80) 13.03.3131 [143]
30D3h (catalyst 82) 12.13.2137 [143]
30D3h189715.053.70137−75[91]
30D3h [EBTHI]Zr - borate 13.53.39128 [52]
30D3h (BF3 catalyst)207015.63.7122<−55[16]
32O4 13.943.44125 [91]
32O4h313518.44.0115−74[91]
32O4h (BF3 catalyst)475020.04.1106<−55[16]
32O22 28.15.4130 [91]
32O22h637429.45.4119−68[91]
40O5 32.96.05132 [91]
40O5h1165136.26.4129−68[91]
40O5h (BF3 catalyst)1022530.95.6124 [16]
40D4 31.36.03142 [91]
40D4h863134.56.52145−66[91]
30D4h (BF3 catalyst)747529.05.7141 [16]
40D22 29.435.90150 [91]
40D22h1561542.07.25136−52[91]
1 Abbreviations used: H—1-hexene, O—1-octene, D—1-decene oligomers; 2–5—DPn value; 22—dimer of dimer; h—hydrogenated.

Share and Cite

MDPI and ACS Style

Nifant’ev, I.; Ivchenko, P. Fair Look at Coordination Oligomerization of Higher α-Olefins. Polymers 2020, 12, 1082. https://0-doi-org.brum.beds.ac.uk/10.3390/polym12051082

AMA Style

Nifant’ev I, Ivchenko P. Fair Look at Coordination Oligomerization of Higher α-Olefins. Polymers. 2020; 12(5):1082. https://0-doi-org.brum.beds.ac.uk/10.3390/polym12051082

Chicago/Turabian Style

Nifant’ev, Ilya, and Pavel Ivchenko. 2020. "Fair Look at Coordination Oligomerization of Higher α-Olefins" Polymers 12, no. 5: 1082. https://0-doi-org.brum.beds.ac.uk/10.3390/polym12051082

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop