Next Article in Journal
Activation Energy Determination in Case of Independent Complex Kinetic Processes
Next Article in Special Issue
Effect of Initial Salt Composition on Physicochemical and Structural Characteristics of Zero-Valent Iron Nanopowders Obtained by Borohydride Reduction
Previous Article in Journal
Experimental Investigation of Grout Nonlinear Flow Behavior through Rough Fractures
Previous Article in Special Issue
Effect of Heating Oxidation on the Surface/Interface Properties and Floatability of Anthracite Coal
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Processes
Volume 7
Issue 10
10.3390/pr7100737
processes-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Communication

Reusing Cow Manure for the Production of Activated Carbon Using Potassium Hydroxide (KOH) Activation Process and Its Liquid-Phase Adsorption Performance

by
Wen-Tien Tsai
1,*,
Po-Cheng Huang
2 and
Yu-Quan Lin
2
1
Graduate Institute of Bioresources, National Pingtung University of Science and Technology, Pingtung 912, Taiwan
2
Department of Environmental Science and Engineering, National Pingtung University of Science and Technology, Pingtung 912, Taiwan
*
Author to whom correspondence should be addressed.
Processes 2019, 7(10), 737; https://0-doi-org.brum.beds.ac.uk/10.3390/pr7100737
Submission received: 18 September 2019 / Revised: 8 October 2019 / Accepted: 8 October 2019 / Published: 14 October 2019
(This article belongs to the Special Issue Application of Advanced Oxidation Processes)
Browse Figures
Versions Notes

Abstract

:
In this work, cow manure (CM) was reused as a potential precursor in the production of activated carbon (AC) using a potassium hydroxide activation process at different temperatures (i.e., 500, 600 and 700 °C). The optimal activated carbon from cow manure (CM-AC) with high specific surface area (ca. 950 m2/g) was further investigated for its adsorption performance in the removal of a model compound (i.e., methylene blue) from aqueous solution with various initial concentrations and adsorbent dosages at 25 °C. It was found that the resulting AC could be an effective adsorbent for removal of cationic dye from aqueous solution in comparison with a commercial coal-based AC. Based on the observations of the energy dispersive X-ray spectroscopy and Fourier transform infrared spectroscopy (FTIR), the CM-AC adsorbent has a stronger interaction with the cationic compound due to its more oxygen-containing complex on the surface. Furthermore, the adsorption kinetic parameters fitted using the pseudo-second order model with high correlations were in accordance with their pore properties.

1. Introduction

Water pollution caused by organic pollutants (e.g., dye, pesticide) is a serious issue because it can degrade water quality and render it toxic to public health and the environment. In general, there are two advanced treatment processes for removal of contaminants from the water bodies [1]. One belongs to destructive processes such as ozone oxidation and the Fenton method [2]. Other processes are recuperative. Among the recuperative process, adsorption may be the most used method due to its features of easy operation, high efficiency and simple design [3]. Therefore, carbon adsorption by granular activated carbon (GAC) or powdered activated carbon (PAC) has been considered as one of the best available technologies in the water and wastewater treatment processes for removal of organic pollutants [4,5]. However, the adsorption process is not a low-cost method because commercial activated carbon (AC) products have higher prices and the regeneration or disposal when they are exhausted will generate additional issues. In recent years, the use of low-cost precursors in the preparation of AC for the removal of various types of pollutants from water and wastewater has been reviewed [6,7,8,9,10,11]. Obviously, utilizing organic wastes or residues as AC precursors poses several advantages such as climate change mitigation (reduction of greenhouse gas emissions), biomass energy production (reusing exhausted AC as auxiliary fuel), and waste management (improvement of environmental quality).
Cattle manure or dung is a renewable resource because it mainly comes from the undigested residue of cellulose-based feeds being excreted by livestock animal species such as cow (dairy cattle) and bull. Generally, cattle manure was converted into fertilizer or soil amendment by composting because composted manure contains many dissolved organic matter (DOM) fractions [12]. Without proper treatment or management, it can cause some environmental problems, including air quality deterioration (e.g., odor), public hazards (e.g., infectious pathogen and asphyxia poisoning), greenhouse gas emissions (e.g., carbon dioxide and methane), and water pollution (e.g., eutrophication) [13]. Due to its high carbon content, this biomass resource can be thermally converted into various forms of energy sources (i.e., heat or electricity) [13,14,15,16,17,18,19,20] and biochar used as an adsorbent [21,22,23,24,25,26], but this approach may encounter some drawbacks, including low energy yield and air pollutants (e.g., sulfur oxides, nitrogen oxides, carbon monoxide and particulate matters) being emitted [27]. In order to upgrade its additional value of reuse, the production of AC from cow manure and its adsorption applications have been reported in recent years [28,29,30,31,32,33,34,35,36].
AC may be the frequently used carbon material in different state-of-the-art applications due to its physical and electrochemical properties, including high surface area, wide pore distribution and large specific capacitance [10,37]. In general, there are two methods for producing AC: physical and chemical activation processes [38]. Physical activation involves carbonization and activation in a single step or two separate steps at higher temperature under the atmosphere of gasification gas (i.e., steam or carbon dioxide). The resulting AC possesses poor pore properties as compared to AC prepared from chemical activation. By contrast, AC production using chemical activation is performed in a single step at a lower temperature using precursor impregnated with chemical reagents (i.e., potassium hydroxide, phosphoric acid, or zinc chloride). However, some impurities like potassium (K), zinc (Zn) or phosphorus (P), depending on the chemical reagents used, can be found in AC products, thus raising the production costs due to the additional processes for removing these residual activation reagents. As reviewed above, little research has performed the reuse of cow manure or cattle manure as a feedstock for producing AC. In the reports by Machida’s group [28,29,30,31,32,33,34,35,36], they first studied the production of AC from cattle manure compost (CMC) using chemical activation with zinc chloride (ZnCl2). Furthermore, the CMC-derived activated carbon was tested to evaluate the liquid-phase adsorption performances of various adsorption targets, including phenol, methylene blue, water vapor, metal ions (i.e., Cu, Pb), and 2-methylisoborneol. In another recent study by Li et al. [36], AC was also produced from cow manure using chemical activators like potassium carbonate (K2CO3) and ZnCl2, showing that the values of specific surface area range from 114 to 893 m2/g. The authors also treated the wastewater from a cow farm with the resulting ACs.
Although many studies have reported the utilization of cow manure as a precursor for producing ACs [28,29,30,31,32,33,34,35,36], they were mostly produced using chemical activation with ZnCl2 and potassium carbonate (K2CO3). On the other hand, the adsorption performances of the resulting AC products were not compared with commercial AC. Thus, the main purposes of this paper were to produce highly porous AC from cow manure using a potassium hydroxide (KOH) activation process at different temperatures. Subsequently, the resulting AC with the optimal pore properties was performed to evaluate its effectiveness in the removal of cationic dye (i.e., methylene blue) from the aqueous solution. Finally, the adsorption performances for the removal of methylene blue from aqueous solution were compared between the CM-based AC and commercial coal-based AC.

2. Materials and Methods

2.1. Materials

The precursor for producing AC was obtained from the Livestock Research Institute (Tainan, Taiwan). The cow (Holstein) manure (CM) sample was dried using a hot air circulating oven for about one week. The methods for characterizing its main thermochemical properties were similar to the previous studies [26,39], showing that the dried CM is composed mainly of volatile matter (about 80 wt%) with 42 wt% carbon. The potassium hydroxide (KOH; Merck Co., Darmstadt, Germany) was used to impregnate CM to produce AC using chemical activation. As methylene blue was commonly selected as a probe compound for determining the adsorption capacity of AC quickly [37], this cationic dye, which was purchased from Merck Co., was used as an organic pollutant target in the work. In order to compare the adsorption performance of the resulting AC with commercial AC, a product (Filtrasorb-300; Calgon Carbon Co., Moon Township, PA, USA) for liquid-phase applications was used to remove methylene blue (MB) at the same adsorption conditions.

2.2. Impregnation and Activation Experiments

The preparation of AC from CM was carried out using the KOH activation process referred to in a previous study [40]. In the present study, the CM impregnated with KOH (KOH-CM) was described as follows: 10 g of CM was mixed with 5 g of KOH in 150 cm3 of de-ionized water and stirred using a magnetic bar at about 75 °C for 30 min, and then decanted into the supernatant prior to being dried at about 105 °C for 24–48 h. Subsequently, the KOH-CM (about 3 g) was activated by passing nitrogen gas (500 cm3/min) at a heating rate of about 10 °C/min up to the specified temperature (i.e., 500, 600, and 700 °C, respectively). Similarly to the procedures in the impregnation with KOH, the AC product was poured into 3 N HCl solution, then heated at about 75 °C for 30 min and finally rinsed with deionized water (150 cm3) three times to remove the residual KOH and inherent ash minerals effectively. Prior to the determination of pore properties, the resulting AC products (denoted as CM-AC-500, CM-AC-600 and CM-AC-700) were dried at about 105 °C for 24 h.

2.3. Characterization of Resulting and Commercial ACs

The pore properties of the resulting AC (CM-AC) products and the commercial AC (Filtrasorb-300) were determined by its N2 adsorption-desorption isotherms at the temperature of liquid nitrogen (i.e., −196 °C) on the Micromeritics ASAP 2020 accelerated surface area and porosimetry system. Based on the analytical methods applied, the types of pore characterization included specific surface area, pore volume and pore size. For example, the specific surface area of the resulting AC can be obtained using the Brunauer–Emmett–Teller (BET) method in the relative pressure (P/P0) range of 0.05–0.30. The total pore volume is indicative of the liquid nitrogen amount adsorbed at P/P0 of about 0.99 [41]. According to the values of the BET surface area and total pore volume, the mean pore diameter or width can be further estimated by assuming the cylindrical geometry [42].
In order to elucidate the elemental compositions of AC on the surface, energy dispersive X-ray spectroscopy (Swift ED3000, Oxford Instruments, Abingdon, UK) was conducted to observe their contents of carbon, oxygen and other elements. The data could be associated with the interaction between the AC adsorbent and target adsorbate in the liquid-phase adsorption system. Using the potassium bromide (KBr) pellet technique, the Fourier infrared spectrometer (FT/IR-4600, JASCO Co., Tokyo, Japan) was further used to measure the functional groups on the surface of the resulting AC (CM-AC) and the commercial AC (Filtrasorb-300) in the range 4000–400 cm−1.

2.4. Adsorption Performance Experiments

Following the adsorption experiments referred to in a previous study [43], the batch adsorption kinetics of the CM-AC-700 were carried out in a 3-L mixing tank with four baffles. In the work, the data on the adsorption uptake of methylene blue (MB) by the MC-AC-700 from aqueous solution (2 liters) were obtained at the fixed solution temperature of 25 °C and agitation speed of 200 rpm under the determining adsorption process parameters, including initial MB concentrations (i.e., C0 = 5, 10, 15 and 20 mg/L) and AC dosages (i.e., 0.1, 0.3 and 0.5 g, based on the solution volumes of 2 L, which were abbreviated by 0.1, 0.3 and 0.5 g/2 L). During the adsorption experiments, an aliquot solution (about 10 cm3) was taken out at specified intervals (i.e., 5, 10, 20, 30, 40, 50 and 60 min). After filtrating with mixed cellulose esters membrane filter with a size of 25 mm, the analysis of dye concentration (i.e., Ct) in the remaining filtrate solution was immediately measured with a UV/Visible spectrophotometer (U-2900, Hitachi Co., Tokyo, Japan) at the maximum absorption wavelength (i.e., 661 nm). It should be noted that about half of the solution sample after the filtration was first discarded to dye the filter completely. The adsorbed amount of MB (qt, mg/g) was obtained by the AC mass, solution volume (i.e., 2 L), and the difference between C0 and Ct. On the other hand, this work also compared the adsorption performance of a commercial AC (i.e., Filtrasorb-300) with the CM-AC-700. The adsorption conditions were fixed at an initial MB concentration of 10 mg/L, AC dosage of 0.3 g/2 L, agitation speed of 200 rpm, and temperature of 25 °C.

3. Results and Discussion

3.1. Pore Properties of Resulting and Commercial ACs

Table 1 listed the pore properties of the resulting ACs (CM-AC) and commercial AC (Filtrasorb 300), including surface area, pore volume and average pore diameter. Obviously, an increase in the activation temperature created the higher pore properties due to the development of more micropores. In addition, CM-AC-700 possessed favorable pore properties by comparison with Filtrasorb-300. For instance, the BET surface area of CM-AC-700 (i.e., 946 m2/g) is slightly higher than that of Filtrasorb-300 (i.e., 660 m2/g). Based on the data of surface area, regardless of the calculation methods, the ratio of that of Filtrasorb-300 to that of CM-AC-700 is close to 0.70. Using the data of total pore volume, the ratio of that of Filtrasorb-300 to that of CM-AC-700 was 0.68, close to 0.70. This result gave an indication of the pore size difference between CM-AC-700 and Filtrasorb-300. As mentioned above, we confidently inferred that the contribution to total pore volume of Filtrasorb-300 should be mostly from micropores. These results were in accordance with their average pore diameters (3.04 vs. 2.32 nm, listed in Table 1). As shown in Table 1, the BET surface area values of the resulting AC products (CM-AC-600 and CM-AC-700) are higher than that (445 m2/g) of biomass-based AC prepared from plant (Jatropha curcas L.) root with similar KOH activation conditions [44]. For large adsorbate molecules having similar dimensions to MB, CM-AC-700 could be preferable to remove them from the aqueous system due to the steric sizes of adsorbate molecules [45].
To describe pore structures of the AC studied, the adsorption-desorption isotherms of nitrogen (N2) at liquid nitrogen temperature (i.e., −196 °C) is the commonly used method [41]. Figure 1 showed the N2 adsorption-desorption isotherms of CM-AC-700 and Filtrasorb-300. Obviously, these ACs belonged to type I isotherms due to their microporous feature (i.e., pore width < 2 nm) [46]. Because of its high potential for adsorption, the micropore filling occurs significantly at P/P0 of < 0.05 [46]. On the other hand, the hysteresis loops occurred at the isotherms from the adsorption to desorption route, especially for CM-AC-700. It is well known that the loop is associated with mesoporous solids, where capillary condensation occurs at higher relative pressures. As listed in Table 1, these isotherms (Figure 1) also confirmed that CM-AC-700 has larger pore properties with wider pore size in comparison with Filtrasorb-300. Furthermore, the hysteresis loop pattern can be correlated with corresponding pore shapes. According to the classification of adsorption hysteresis loops recommended by the International Union of Pure and Applied Chemistry (IUPAC), the isotherms in Figure 1 belong to the type H4 loops [41], which are given by many ACs and some other microporous adsorbents with slit-shaped pores.

3.2. Adsorption Performances of AC

Figure 2 and Figure 3 show the adsorption performances of CM-AC-700 for MB removal at the specific adsorption conditions under various initial MB concentrations and AC dosages, respectively. Obviously, the fast decrease in residual MB concentrations (Ct/C0) occurred at a limited time. It implies that strong interactions between the cationic dye and the resulting AC exist. In this work, the pseudo-second order model was used to fit the adsorption system [47]. In order to fit the adsorption kinetic data, its linear form can be expressed as:
t/qt = 1/(k × qe2) + (1/qe) × t,
where qt is the adsorbed amount of MB at time t (mg/g), qe is the adsorbed amount of MB fitted at equilibrium (mg/g), k is the rate constant (g/(mg·min)), and t is the time (min). Furthermore, the time required for the adsorbent (i.e., CM-AC) to take up half as much adsorbate (i.e., MB) as occurs at equilibrium (i.e., t = t1/2 as qt = qe/2) can be obtained by the following equation.
t1/2 = 1/(k × qe)
The fitted values of kinetic parameters for the adsorption system were listed in Table 2 and Table 3. Obviously, the kinetics of MB adsorption into CM-AC followed this model with high correlation coefficients (>0.99). As listed in Table 2, the fitted adsorption capacity (i.e., qe) decreased as the initial MB concentration (i.e., C0) increased. The decrease of qe with increasing adsorbent dosage implies the exhaustion of adsorption onto excessive adsorbent due to the limited MB molecules. On the other hand, the rate constant values significantly increased at higher adsorbent dosage because of the increase in more adsorption sites provided. This result agrees with previous studies with relation to the adsorption of dyes onto activated carbon and clay [45,48,49]. On the other hand, the fitted adsorption capacity (seen in Table 3) indicated an increasing trend as the initial MB concentration (i.e., C0) increased. This result can be expected because more adsorbate molecules were adsorbed at the equilibrium condition onto the adsorbent without exhausting its adsorption.
Figure 4 shows the adsorption kinetic profiles of CM-AC-700 in comparison with that of the commercial AC at the same conditions, that is, initial MB concentration of 10 mg/L, CM-AC-700 dosage of 0.3 g/2 L, agitation speed of 200 rpm, and temperature of 25 °C. As listed in Table 4, CM-AC-700 exhibited a better adsorption performance for the removal of MB from the aqueous solution as compared to the commercial AC (Filtrasorb-300). This difference between the fitted values of adsorption capacities (i.e., qe) can be associated with the interactions between the adsorbate and the adsorbent, including the pore properties of the adsorbent for physical adsorption and the electrostatic attraction interaction between the cationic dye and the negatively charged surface [44]. The observations using energy dispersive X-ray spectroscopy (Figure 5) showed a higher content of oxygen on the CM-AC-700 surface in comparison with the adsorbent Filtrasorb-300, thus enhancing its polar nature (i.e., hydrophilicity, acidity) due to more oxygen complexes or groups on the surface [50]. These surface oxygen complexes and oxygen-containing functional groups (e.g., carboxylic, carbonyl, phenolic groups) could arise from its lignocellulosic constituents and ashes (consisting mainly of silica, alumina, alkaline and alkaline earth metals) in the starting materials (i.e., CM). The carbon contents of the resulting carbon materials were further analyzed using an elemental analyzer and showed a range from 60 to 65 wt%, while that of the commercial activated carbon (Filtrasorb-300) demonstrated a range up to about 90 wt%. These results were consistent with the energy dispersive X-ray spectroscopy analyses (Figure 5). Therefore, the interaction between the cationic dye (MB molecule) and the adsorbent CM-AC-700 via stronger van der Waals forces or other binding forms also plays a vital role in the liquid-phase adsorption. On the other hand, Figure 6 depicted the Fourier transform infrared spectroscopy (FTIR) spectra of CM-AC700 and Filtrasorb-300. The peaks of CM-AC-700 at about 3440, 2400, 1630, 1380, 1180 and 620 cm−1 could be mostly associated with functional groups containing oxygen (i.e., O–H, C=O, C–O) [51], which were more significant than those of Filtrasorb-300. For example, there is a broad absorption peak at 3440 cm−1 in the CM-AC-700, which is assigned to the stretching vibration of O–H. In addition, a sharp peak at about 3440 cm−1 may correspond to the bending band of O–H. The interaction between the cationic dye and the adsorbent CM-AC-700 via stronger van der Waals forces or other binding forms also plays a vital role in the adsorption process.

4. Conclusions

The thermochemical conversion of cattle manure can be positively related to climate change mitigation (reduction of greenhouse gas emissions) and waste and wastewater management (improvement of environmental quality). In this work, based on the experimental results of the chemical, pore and adsorption properties for the resulting and commercial ACs, cattle (cow) manure could be an excellent precursor for producing AC at different temperatures (i.e., 500, 600 and 700 °C) using a KOH activation process. The conclusions can be itemized as follows:
-
The nitrogen adsorption-desorption isotherms of the resulting ACs showed that an increase in the activation temperature created the higher pore properties due to the development of more micropores.
-
The optimal AC product (i.e., CM-AC-700) showed its microporous feature with the pore properties of a BET surface area of 946 m2/g and total pore volume of about 0.72 cm3/g, which are close to those of common commercial ACs.
-
The resulting AC could be an effective low-cost adsorbent for the removal of cationic dye (i.e., methylene blue, MB) from aqueous solution based on the fittings of the pseudo-second order model.
-
The resulting AC exhibited a better adsorption performance for the removal of MB from the aqueous solution as compared to the commercial AC.
-
The cow manure-derived adsorbent has a stronger interaction due to its larger pore properties and more oxygen-containing complex on the surface based on the observations of energy dispersive X-ray spectroscopy and Fourier transform infrared spectroscopy (FTIR).

Author Contributions

Conceptualization, W.-T.T.; methodology, P.-C.H.; validation, P.-C.H.; data curation, Y.-Q.L.; formal analysis, Y.-Q.L; writing—original draft preparation, W.-T.T.; writing—review and editing, W.-T.T.

Funding

This research received no external funding.

Acknowledgments

The authors express sincere appreciation to the Instrument Center of National Pingtung University of Science and Technology for assistance with the energy dispersive X-ray spectroscopy (EDS) observation.

Conflicts of Interest

The authors declare no conflicts of interest.

References

  1. Teodosiu, C.; Gilca, A.F.; Barjoveanu, G.; Fiore, S. Emerging pollutants removal through advanced drinking water treatment: A review on processes and environmental performances assessment. J. Clean. Prod. 2018, 197, 1210–1221. [Google Scholar] [CrossRef]
  2. Hodaifa, G.; Callardo, P.A.R.; Garcia, C.A.; Kowalska, M.; Seyedsalehi, M. Chemical oxidation methods for treatment of real industrial olive oil mill wastewater. J. Taiwan Inst. Chem. Eng. 2019, 97, 247–254. [Google Scholar] [CrossRef]
  3. Garcia, J.R.; Sedran, U.; Zaini, M.A.A.; Zakaria, Z.A. Preparation, characterization, and dye removal study of activated carbon prepared from palm kernel shell. Environ. Sci. Pollut. Res. 2018, 25, 5076–5085. [Google Scholar] [CrossRef] [PubMed]
  4. Jeirani, Z.; Niu, C.H.; Soltan, J. Adsorption of emerging pollutants on activated carbon. Rev. Chem. Eng. 2017, 33, 491–522. [Google Scholar] [CrossRef]
  5. Al-Ghouti, M.A.; Al-Kaabi, M.A.; Ashfag, M.Y.; Da’na, D.A. Produced water characteristics, treatment and reuse: A review. J. Water Process Eng. 2019, 28, 222–239. [Google Scholar] [CrossRef]
  6. Loannidou, O.; Zabaniotou, A. Agricultural residues as precursors for activated carbon production—A review. Renew. Sustain. Energy Rev. 2007, 11, 1966–2005. [Google Scholar] [CrossRef]
  7. Demirbas, A. Agricultural based activated carbons for the removal of dyes from aqueous solutions: A review. J. Hazard. Mater. 2009, 167, 1–9. [Google Scholar] [CrossRef]
  8. Alslaibi, T.M.; Abustan, I.; Ahmad, M.A.; Foul, A.A. A review: Production of activated carbon from agricultural byproducts via conventional and microwave heating. J. Chem. Technol. Biotechnol. 2013, 88, 1183–1190. [Google Scholar] [CrossRef]
  9. Abioye, A.M.; Ani, F.N. Recent development in the production of activated carbon electrodes from agricultural waste biomass for supercapacitors: A review. Renew. Sustain. Energy Rev. 2015, 52, 1282–1293. [Google Scholar] [CrossRef]
  10. Yahya, M.A.; Al-Qodah, Z.; Ngah, C.W.Z. Agricultural bio-waste materials as potential sustainable precursors used for activated carbon production: A review. Renew. Sustain. Energy Rev. 2015, 46, 218–235. [Google Scholar] [CrossRef]
  11. Gonzalez-Garcia, P. Activated carbon from lignocellulosics precursors: A review of the synthesis methods, characterization techniques and applications. Renew. Sustain. Energy Rev. 2018, 82, 1393–1414. [Google Scholar] [CrossRef]
  12. Lu, Y.; Shan, G.; Huang, J.; Li, Q. Insights into characteristics of dissolved organic matter fractions in co-composted dairy manure and Chinese herbal residues. Waste Biomass Valor. 2018, 9, 777–782. [Google Scholar] [CrossRef]
  13. Cantrell, K.B.; Ducey, T.; Ro, K.S.; Hunt, P.G. Livestock waste-to-bioenergy generation opportunities. Bioresour. Technol. 2008, 99, 7941–7953. [Google Scholar] [CrossRef] [PubMed]
  14. Dagnall, S.; Hill, J.; Pegg, D. Resource mapping and analysis of farm livestock manures—assessing the opportunities for biomass-to-energy schemes. Bioresour. Technol. 2000, 71, 225–234. [Google Scholar] [CrossRef]
  15. Raven, R.P.J.M. Implementation of manure digestion and co-combustion in the Dutch electricity regime: A multi-level analysis of market implementation in the Netherlands. Energy Policy 2004, 32, 29–39. [Google Scholar] [CrossRef]
  16. Carlin, N.; Annamalai, K.; Sweeten, J.; Mukhtar, S. Thermo-chemical conversion analysis on dairy manure-based biomass through direct combustion. Int. J. Green Energy 2007, 4, 133–159. [Google Scholar] [CrossRef]
  17. Cantrell, K.B.; Hunt, P.G.; Uchimiya, M.; Novak, J.M.; Ro, K.S. Impact of pyrolysis temperature and manure source on physicochemical characteristics of biochar. Bioresour. Technol. 2012, 107, 419–428. [Google Scholar] [CrossRef]
  18. Fernandez-Lopez, M.; Puig-Gamero, M.; Lopez-Gonzalez, D.; Avalos-Ramirez, A.; Valverde, J.; Sanchez-Silva, L. Life cycle assessment of swine and dairy manure: Pyrolysis and combustion processes. Bioresour. Technol. 2015, 182, 184–192. [Google Scholar] [CrossRef]
  19. Kim, J.K.; Kim, H.S.; Park, S.U.; Lee, H.D.; Kim, S.C. Combustion possibility of cattle manure as a blended fuel of pulverized coal fired power plant using TGA and 100 kg/h test furnace. J. Chem. Eng. Jpn. 2015, 48, 307–319. [Google Scholar] [CrossRef]
  20. Yi, B.J.; Yuan, Q.X.; Cao, H.L.; Niu, W.J.; Wang, M.; Zhu, Y.; Yan, S.P. Effect of alkali and alkaline earth metal species on the combustion characteristics of cattle manures. RSC Adv. 2018, 8, 11705–11713. [Google Scholar] [CrossRef] [Green Version]
  21. Xu, X.Y.; Cao, X.D.; Zhao, L.; Wang, H.L.; Yu, H.R.; Gao, B. Removal of Cu, Zn, and Cd from aqueous solutions by the dairy manure-derived biochar. Environ. Sci. Pollut. Res. 2013, 20, 358–368. [Google Scholar] [CrossRef] [PubMed]
  22. Cao, H.L.; Xin, Y.; Yuan, Q.X. Prediction of biochar yield from cattle manure pyrolysis via least squares support vector machine intelligent approach. Bioresour. Technol. 2016, 202, 158–164. [Google Scholar] [CrossRef] [PubMed]
  23. Ma, F.F.; Zhao, B.W.; Diao, J.R.; Qiao, H.T.; Zhong, J.K. Sorption of cadmium by biochar produced from pyrolysis of cattle manure in aqueous solution. Fresen. Environ. Bull. 2016, 25, 5226–5236. [Google Scholar]
  24. Zhu, Y.; Yi, B.J.; Yuan, Q.X.; Wang, M.; Yan, S.P. Removal of methylene blue from aqueous solution by cattle manure-derived low temperature biochar. RSC Adv. 2018, 8, 19917–19929. [Google Scholar] [CrossRef] [Green Version]
  25. Chen, Z.L.; Zhang, J.Q.; Huang, L.; Yuan, Z.H.; Li, Z.J.; Liu, M.C. Removal of Cd and Pb with biochar made from dairy manure at low temperature. J. Integr. Agric. 2019, 18, 201–210. [Google Scholar] [CrossRef] [Green Version]
  26. Tsai, T.W.; Hsu, C.H.; Lin, Y.Q. Highly porous and nutrients-rich biochar derived from dairy cattle manure and its potential for removal of cationic compound from water. Agriculture 2019, 9, 114. [Google Scholar] [CrossRef]
  27. Klass, D.J. Biomass for Renewable Energy, Fuels, and Chemicals; Academic Press: San Diego, CA, USA, 1998. [Google Scholar]
  28. Qian, Q.R.; Machida, M.; Tatsumoto, H. Preparation of activated carbons from cattle-manure compost by zinc chloride activation. Bioresour. Technol. 2007, 98, 353–360. [Google Scholar] [CrossRef]
  29. Qian, Q.R.; Machida, M.; Aikawa, M.; Tatsumoto, H. Effect of ZnCl2 impregnation ratio on pore structure of activated carbons prepared from cattle manure compost: Application of N2 adsorption-desorption isotherms. J. Mater. Cycles Waste Manag. 2008, 10, 53–61. [Google Scholar] [CrossRef]
  30. Qian, Q.R.; Machida, M.; Tatsumoto, H. Textural and surface chemical characteristics of activated carbons prepared from cattle manure compost. Waste Manag. 2008, 28, 1064–1071. [Google Scholar] [CrossRef]
  31. Qian, Q.R.; Sunohara, S.; Kato, Y.; Zaini, M.A.A.; Machida, M.; Tatsumoto, H. Water vapor adsorption onto activated carbons prepared from cattle manure compost. Appl. Surf. Sci. 2008, 254, 4868–4874. [Google Scholar] [CrossRef]
  32. Qian, Q.R.; Chen, Q.H.; Machida, M.; Tatsumoto, H.; Mochidzuki, K.; Sakoda, A. Removal of organic contaminants from aqueous solution by cattle manure compost (CMC) derived activated carbons. Appl. Surf. Sci. 2009, 255, 6107–6114. [Google Scholar] [CrossRef]
  33. Zaini, M.A.A.; Amano, Y.; Machida, M. Removal of lead (II) binding properties of heat-treated cattle-manure-compost-activated carbons. Desalin. Water Treat. 2014, 52, 6420–6429. [Google Scholar] [CrossRef]
  34. Zaini, M.A.A.; Okayama, R.; Machida, M. Adsorption of aqueous metal ions on cattle-manure-compost based activated carbons. J. Hazard. Mater. 2009, 170, 1119–1124. [Google Scholar] [CrossRef] [PubMed]
  35. Watanabe, T.; Zaini, M.A.A.; Amano, Y.; Machida, M. Removal of 2-methylisoborneol from aqueous solution by cattle manure compost (CMC) derived activated carbons. J. Water Supply Res. Technol.-AQUA 2014, 63, 239–247. [Google Scholar] [CrossRef]
  36. Li, H.C.; Yang, S.S.; Sun, H.Z.; Liu, X.H. Production of activated carbon from cow manure for wastewater treatment. BioResources 2018, 13, 3135–3143. [Google Scholar] [CrossRef]
  37. Marsh, H.; Rodriguez-Reinoso, F. Activated Carbon; Elsevier: Amsterdam, The Netherlands, 2006. [Google Scholar]
  38. Ge, C.; Lian, D.; Cui, S.; Gao, J.; Lu, J. Highly selective CO2 capture on waste polyurethane foam-based activated carbon. Processes 2019, 7, 592. [Google Scholar] [CrossRef]
  39. Liu, S.C.; Tsai, W.T. Thermochemical characteristics of dairy manure and its derived biochars from a fixed-bed pyrolysis. Int. J. Green Energy 2016, 13, 963–968. [Google Scholar] [CrossRef]
  40. Tsai, T.W.; Chang, C.Y.; Wang, S.Y.; Chang, C.F.; Chien, S.F.; Sun, H.F. Preparation of activated carbons from corn cob catalyzed by potassium salts and subsequent gasification with CO2. Bioresour. Technol. 2001, 78, 203–208. [Google Scholar] [CrossRef]
  41. Lowell, S.; Shields, J.E.; Thomas, M.A.; Thommes, M. Characterization of Porous Solids and Powders: Surface Area, Pore Size and Density; Springer: Dordrecht, The Netherlands, 2006. [Google Scholar]
  42. Smith, J.M. Chemical Engineering Kinetics, 3rd ed.; McGraw-Hill: New York, NY, USA, 1981. [Google Scholar]
  43. Tsai, W.T.; Hsu, H.C.; Su, T.Y.; Lin, K.Y.; Lin, C.M.; Dai, T.H. The adsorption of cationic dye from aqueous solution onto acid-activated andesite. J. Hazard. Mater. 2007, 147, 1056–1062. [Google Scholar] [CrossRef]
  44. Alvarez-Mateos, P.; Garcia-Martin, T.F.; Guerrero-Vacas, F.J.; Maranjo-Calderon, C.; Barrios-Sanchez, C.C.; Perez-Camino, M.C. Valorization of a high-acidity residual oil generated in the waste cooking oils recycling industries. Grasas Aceites 2019, 70, 335. [Google Scholar] [CrossRef] [Green Version]
  45. Tamai, H.; Yoshida, T.; Sasaki, M.; Yasuda, H. Dye adsorption on mesoporous activated carbon fiber obtained from pitch containing yttrium complex. Carbon 1999, 37, 983–989. [Google Scholar] [CrossRef]
  46. Gregg, S.J.; Sing, K.S.W. Adsorption, Surface Area, and Porosity; Academic Press: London, UK, 1982. [Google Scholar]
  47. Ho, Y.S.; Chiang, C.C.; Hsu, Y.C. Sorption kinetics for dye removal from aqueous solution using activated clay. Sep. Sci. Technol. 2001, 36, 2473–2488. [Google Scholar] [CrossRef]
  48. Demirbas, E.; Kobya, M.; Sulak, M.T. Adsorption kinetics of a basic dye from aqueous solutions onto apricot stone activated carbon. Bioresour. Technol. 2008, 99, 5368–5373. [Google Scholar] [CrossRef] [PubMed]
  49. Ghaedi, M.; Golestani Nasab, A.; Khodadoust, S.; Rajabi, M.; Azizian, S. Application of activated carbon as adsorbents for efficient removal of methylene blue: Kinetics and equilibrium study. J. Ind. Eng. Chem. 2014, 20, 2317–2324. [Google Scholar] [CrossRef]
  50. Suzuki, M. Adsorption Engineering; Elsevier: Amsterdam, The Netherlands, 1990. [Google Scholar]
  51. Islam, M.S.; Ang, B.C.; Gharehkhani, S.; Afifi, A.B.M. Adsorption capability of activated carbon synthesized from coconut shell. Carbon Lett. 2016, 20, 1–9. [Google Scholar] [CrossRef] [Green Version]
Processes 07 00737 g001 550
Figure 1. N2 adsorption-desorption isotherms of cow manure-derived activated carbon (CM-AC) and commercial activated carbon (i.e., Filtrasorb-300).
Figure 1. N2 adsorption-desorption isotherms of cow manure-derived activated carbon (CM-AC) and commercial activated carbon (i.e., Filtrasorb-300).
Processes 07 00737 g001
Processes 07 00737 g002 550
Figure 2. Effect of adsorbent CM-AC-700 dosage on methylene blue (MB) adsorption (initial MB concentrations = 10 mg/L, agitation speed = 200 rpm, and temperature = 25 °C); symbols: measurement data, full lines: calculated from the fitted values (Table 2).
Figure 2. Effect of adsorbent CM-AC-700 dosage on methylene blue (MB) adsorption (initial MB concentrations = 10 mg/L, agitation speed = 200 rpm, and temperature = 25 °C); symbols: measurement data, full lines: calculated from the fitted values (Table 2).
Processes 07 00737 g002
Processes 07 00737 g003 550
Figure 3. Effect of initial MB concentration on MB adsorption; adsorption conditions: adsorbent CM-AC-700 dosage = 0.3 g/2 L, adsorption temperature = 25 °C, and agitation speed = 200 rpm; symbols: measurement data, full lines: calculated from the fitted values (Table 3).
Figure 3. Effect of initial MB concentration on MB adsorption; adsorption conditions: adsorbent CM-AC-700 dosage = 0.3 g/2 L, adsorption temperature = 25 °C, and agitation speed = 200 rpm; symbols: measurement data, full lines: calculated from the fitted values (Table 3).
Processes 07 00737 g003
Processes 07 00737 g004 550
Figure 4. Effect of different ACs on MB adsorption; adsorption conditions: initial MB concentration = 10 mg/L, adsorbent dosage = 0.2 g/2 L, adsorption temperature = 25 °C, and agitation speed = 200 rpm; symbols: experimental data, full lines: calculated from Equation (1) and Table 4.
Figure 4. Effect of different ACs on MB adsorption; adsorption conditions: initial MB concentration = 10 mg/L, adsorbent dosage = 0.2 g/2 L, adsorption temperature = 25 °C, and agitation speed = 200 rpm; symbols: experimental data, full lines: calculated from Equation (1) and Table 4.
Processes 07 00737 g004
Processes 07 00737 g005a 550Processes 07 00737 g005b 550
Figure 5. Energy dispersive X-ray spectroscopy spectra of (a) CM-AC-700 and (b) Filtrasorb-300.
Figure 5. Energy dispersive X-ray spectroscopy spectra of (a) CM-AC-700 and (b) Filtrasorb-300.
Processes 07 00737 g005aProcesses 07 00737 g005b
Processes 07 00737 g006 550
Figure 6. Fourier transform infrared spectroscopy (FTIR) spectra of CM-AC-700 and Filtrasorb-300.
Figure 6. Fourier transform infrared spectroscopy (FTIR) spectra of CM-AC-700 and Filtrasorb-300.
Processes 07 00737 g006
Table
Table 1. Pore properties of resulting activated carbons (ACs), cow manure-derived activated carbon (CM-AC) and commercial AC (Filtrasorb-300).
Table 1. Pore properties of resulting activated carbons (ACs), cow manure-derived activated carbon (CM-AC) and commercial AC (Filtrasorb-300).
PropertyCM-AC-500 CM-AC-600 CM-AC-700 Filtrasorb-300
Single point surface area (m2/g) a385.0634.0912.6643.0
BET surface area (m2/g) b383.3627.9946.3660.0
Langmuir surface area (m2/g) 576.0935.91297.6934.6
Micropore surface area (m2/g) c212.8425.5673.8499.4
External surface area (m2/g) d170.5202.4272.5160.6
Total pore volume (cm3/g) e0.3710.5600.7190.382
Micropore volume (cm3/g) c0.1130.2230.3300.250
Pore diameter (Å) f38.735.730.423.2
a Obtained at relative pressure (P/P0) of about 0.30. b Calculated in the range 0.05 < relative pressure (P/P0) < 0.30. c Micropore area by t-plot method. d Obtained by subtracting micropore surface area from Brunauer–Emmett–Teller (BET) surface area. e Total pore volume obtained at relative pressure (P/P0) of about 0.99. f Obtained from the values of total pore volume and BET surface area.
Table
Table 2. Kinetic parameters for methylene blue (MB) adsorption onto adsorbent CM-AC-700 at various adsorbent dosages based on pseudo-second order model a.
Table 2. Kinetic parameters for methylene blue (MB) adsorption onto adsorbent CM-AC-700 at various adsorbent dosages based on pseudo-second order model a.
Adsorbent Dosage (g/2 L)k (g/mg·min)qe (mg/g)Correlation Coefficientt1/2 (min)
0.10.0005142.860.98714.0
0.30.001676.340.9998.2
0.50.008442.740.9992.8
a Adsorption conditions: initial MB concentration = 10 mg/L, agitation speed = 200 rpm, and temperature = 25 °C.
Table
Table 3. Kinetic parameters for methylene blue (MB) adsorption onto adsorbent CM-AC-700 at initial MB concentrations based on pseudo-second order model a.
Table 3. Kinetic parameters for methylene blue (MB) adsorption onto adsorbent CM-AC-700 at initial MB concentrations based on pseudo-second order model a.
Initial MB Concentration (mg/L)k (g/mg·min)qe (mg/g)Correlation Coefficientt1/2 (min)
50.002840.320.9938.9
100.001676.340.9998.2
150.0008113.640.99911.0
200.0004151.520.99616.5
a Adsorption conditions: adsorbent MC-AC dosage = 0.3 g/2 L, agitation speed = 200 rpm, and temperature = 25 °C.
Table
Table 4. Kinetic parameters for methylene blue (MB) adsorption onto resulting AC (CM-AC-700) and commercial AC (Filtrasorb-300) based on pseudo-second order model a.
Table 4. Kinetic parameters for methylene blue (MB) adsorption onto resulting AC (CM-AC-700) and commercial AC (Filtrasorb-300) based on pseudo-second order model a.
Adsorbentk (g/mg·min)qe (mg/g)Correlation Coefficientt1/2 (min)
CM-AC-7000.001676.340.9998.2
Filtrasorb-3000.003820.880.94412.6
a Adsorption conditions: initial MB concentration = 10 mg/L, adsorbent dosage = 0.3 g/2 L, agitation speed = 200 rpm, and temperature = 25 °C.

Share and Cite

MDPI and ACS Style

Tsai, W.-T.; Huang, P.-C.; Lin, Y.-Q. Reusing Cow Manure for the Production of Activated Carbon Using Potassium Hydroxide (KOH) Activation Process and Its Liquid-Phase Adsorption Performance. Processes 2019, 7, 737. https://0-doi-org.brum.beds.ac.uk/10.3390/pr7100737

AMA Style

Tsai W-T, Huang P-C, Lin Y-Q. Reusing Cow Manure for the Production of Activated Carbon Using Potassium Hydroxide (KOH) Activation Process and Its Liquid-Phase Adsorption Performance. Processes. 2019; 7(10):737. https://0-doi-org.brum.beds.ac.uk/10.3390/pr7100737

Chicago/Turabian Style

Tsai, Wen-Tien, Po-Cheng Huang, and Yu-Quan Lin. 2019. "Reusing Cow Manure for the Production of Activated Carbon Using Potassium Hydroxide (KOH) Activation Process and Its Liquid-Phase Adsorption Performance" Processes 7, no. 10: 737. https://0-doi-org.brum.beds.ac.uk/10.3390/pr7100737

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop