Free Volume Effect via Various Chemical Structured Monomers on Adhesion Property and Relative Permittivity in Acrylic Pressure Sensitive Adhesives
Next Article in Special Issue
Effect of Iron Oxide Nanoparticles on the Physical Properties of Medium Density Fiberboard
Previous Article in Journal
Biomimetic Polyurethane 3D Scaffolds Based on Polytetrahydrofuran Glycol and Polyethylene Glycol for Soft Tissue Engineering
Previous Article in Special Issue
Effect of Lignin Content on Properties of Flexible Transparent Poplar Veneer Fabricated by Impregnation with Epoxy Resin
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 12
Issue 11
10.3390/polym12112632
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Larch Bark as a Formaldehyde Scavenger in Thermal Insulation Panels

by
Marius Cătălin Barbu
1,2,
Yasmin Lohninger
1,
Simon Hofmann
1,
Günther Kain
1,3,
Alexander Petutschnigg
1 and
Eugenia Mariana Tudor
1,2,*
1
Forest Products Technology and Timber Construction Department, Salzburg University of Applied Sciences, Markt 136a, 5431 Kuchl, Austria
2
Faculty of Furniture Design and Wood Engineering, Transilvania University of Brasov, B-dul. Eroilor nr. 29, 500036 Brasov, Romania
3
Higher Technical College Hallstatt, Lahnstraße 69, 4830 Hallstatt, Austria
*
Author to whom correspondence should be addressed.
Polymers 2020, 12(11), 2632; https://0-doi-org.brum.beds.ac.uk/10.3390/polym12112632
Submission received: 9 October 2020 / Revised: 3 November 2020 / Accepted: 5 November 2020 / Published: 10 November 2020
(This article belongs to the Special Issue Advances in Wood Composites III)
Browse Figures
Versions Notes

Abstract

:
The aim of this study is to investigate the formaldehyde content and emissions of bark-based insulation panels bonded with three types of adhesives: urea formaldehyde, melamine urea-formaldehyde, and tannin-based adhesives. These panels were produced at two levels of density—300 and 500 kg/m3—and a thickness of 20 mm, and the influence of the adhesive amount and type on the formaldehyde emissions and content was measured. Other mechanical and physical properties such as modulus of rupture, modulus of elasticity, internal bond, and dimensional stability were also scrutinized. With one exception, all the panels belonged to the super E0 classification for free formaldehyde content (perforator value ≤1.5 mg/100 g oven dry mass of panels). The measurements using the desiccator method for formaldehyde emissions assigned all the testing specimens in the F **** category for low-emission panels according to the Japanese International Standards.

1. Introduction

A feasible building culture includes environmentally friendly alternatives for heat insulation materials. Natural insulation, produced from renewable resources, gained increased popularity in the last few decades. The challenge of developing eco-friendly building materials leads to products that are designed for well-being and health [1]. During this time, insulating materials developed to such a high range that they met most all of customers’ expectations. However, only one insulating material cannot fulfill all requirements, and the ecological aspects are not always reflected in the most expensive products [2]. Some properties such as low diffusion resistance, moisture resistance, good impact sound insulation, high compressive strength, exclude each other [3]. Regarding the market for heat insulation materials, the main products are still polystyrene or mineral wool, which are nowadays competing with high-performance new and recyclable products [4,5]. The manufacturing of nature-based heat insulation materials involves less fossil fuel energy [6] and less energy-intensive processes [7]. The recycling of building waste (thermal insulation materials, synthetic or mineral) is problematic. Their degradation is very slow and might generate toxic substances [5]. Insulating materials are manufactured for different applications and with particular properties, according to the final use [3]. Of these properties, the most important one is thermal conductivity, complemented by other properties such as compressive strength and fire behavior, all of them in a direct relationship with the end use [8]. The hazards correlated with the manufacturing of thermal insulation panels have increased due to chemical substances being included in the fabrication process [9]. Moreover, the contaminant emission standards for building materials have been significantly extended [1]. Therefore, the impact of exposure to unhealthy materials on humans during and after the preparation process must be assessed. The tendency of modern work and lifestyle shows that people spend about 90% of their daily life in indoor areas [10]. Air pollution, especially indoors, is responsible for the high rate of lung cancer [1]. Formaldehyde is a well-known air pollutant and the first carcinogen in humans [11]. Reducing formaldehyde levels in indoor and outdoor applications is an important topic nowadays [12]. One natural by-product of the wood industry—namely, tree bark—can be successfully used for the reduction in formaldehyde emissions in wood-based composites—e.g., spruce bark (Picea abies) [13]. Jahanshaei et al. [14] developed an eco-friendly tannin-phenol formaldehyde resin to decrease the formaldehyde level of wood composites [15] using a bark alkaline extractive from lodgepole pine (Pinus contorta) to produce bio-based melamine formaldehyde resins. Benuang bark (Octomeles sumatrana/BN) and duabanga bark (Duabanga moluccana/DB) can act as filler in phenol-formaldehyde [16] adhesives. Red cedar bark (Thuja plicata) was analyzed in compounds with isocyanates (pMDI) resins [17,18]; the authors analyzed the influence of beech bark (Fagus sylvatica) in adhesive mixtures used in plywood (Ply) and [19] carried out research on the effects of using birch bark (Betula pendula) particles with various dimensions as a filler for urea-formaldehyde resin in Ply, similar to the study of [20], who analyzed the role of walnut, chestnut, fir, and spruce bark flours instead of wheat flour in Ply production. The radical scavenging activity of the outer and inner bark of alder (Alnus glutinosa L.), oak (Quercus robur L.), and pine (Pinus sylvestris L.) was studied by [12,21]; the authors studied the capacity of larch bark (Larix decidua Mill.) for formaldehyde removal in wood adhesives. Larch bark could be used as thermal insulating material for buildings, with an average 20% lower thermal conductivity than wood [22]. Larch inner bark is on average 35% lighter than larch wood (300 kg/m3) and is therefore well suited to be used for thermal insulation purposes [23]. The aim of this study is to analyze the role of larch bark as a formaldehyde scavenger in thermal insulation boards when bonded with a tannin-based adhesive, urea-formaldehyde (UF), and melamine urea-formaldehyde (MUF).

2. Materials and Methods

The larch bark was sourced from Graggaber Sawmill (Unternberg, Austria). The bark was dried in a vacuum kiln dryer (Brunner–Hildebrand High VAC-S, HV-S1, Hannover, Germany) from a 50% to 6% moisture content. The drying temperature was 60 °C at a pressure of 200–250 mbar. The bark was subsequently crushed in a 4-spindle shredder (RS40) at the Untha Co. (Kuchl, Austria), and repeatedly screened using a sieve shaker Retsch AS 200 (Haan, Deutschland) to obtain 6–10 mm particles.
The bark-based insulation panels (50 × 50 cm), with two levels of density—300 and 500 kg/m3—and a thickness of 20 mm, were prepared with 8%, 12%, and 16% adhesives as follows: UF (Dynea Prefere 10F102, Krems, Austria) with 1% ammonium sulphate hardener; MUF type Prefere 4561 (Dynea, Krems, Austria) with 1% hardener type Prefere 5011 (Dynea, Krems, Austria) and a tannin-based adhesive (Table 1). The latter was prepared with an extract powder from Colatan GT5 Quebracho tannin (Schinopsis Lorentzii and Schinopsis balansae) from Christian Markmann Co. (Hamburg, Germany), reinforced with 5% resorcinol, hexa-methylenetetramine (hexamine) from Merck Schuchardt, Hohenbrunn, Germany (C 99%) and 32% sodium hydroxide solution from Carl Roth (Karlsruhe, Germany). Amounts of 50% tannin extract powder and 50% water were stirred with 700 and 1500 rpm in a mechanical mixer. Then, 10% of hexamine was added to adjust the pH value of the mixed solution to 9 using a sodium hydroxide solution. The blending of bark particles with the adhesives was conducted in a ploughshare mixer ENT type WHB-75 for 10 min. The panels were pressed at 180 °C for 8 min using a laboratory press, Höfer HLOP 280 (Taiskirchen, Austria), with the following adjustment tensile of 0.97 at a measurement range of 4000–20,000 N. The panels were pressed with a press factor of 24 s/mm (significantly higher compared to industry). The maximal pressure was 30 bar and the minimal was 10 bar. The press cycle included a pre-heating stage at 19 mm for 30 s, then the boards were pressed for 7.5 min.
The formaldehyde testing methods can be divided into three categories, according to [24]: total amount testing method—e.g., perforation; static emission testing method—e.g., desiccator; and dynamic emission testing method—e.g., chamber. For this study, the perforator method, mostly used in industry, and the desiccator method [25] were chosen. This study follows the previous research of [12,22,26,27].
The testing of formaldehyde content was carried out according to [28]. Small specimens (25 × 25 mm, 110 g each batch) were extracted by means of boiling toluene and then transferred into distilled or demineralized water. The formaldehyde emission was sampled through perforation in water and analyzed photometrically with the acetylacetone method. The perforator value depends on the moisture content of the specimens [29], which was determined according to [30]. The perforator values were corrected to boards conditioned to a moisture content of 6.5%. This method demands a running time of 3 h and is used mostly for production control in the wood-based panels industry [29].
One of the testing methods used to determine the formaldehyde emission from insulating boards was made according to [31]. Prior to this test, the 150 ± 1 × 50 ± 1 mm specimens were conditioned for one week to a constant mass in a climate chamber at 20 ± 2 °C and a relative air humidity of 65 ± 5%. Eight samples from each board were cut carefully and the edges were sealed with paraffin. Then, the test pieces were placed for 24 h at 20 °C in a desiccator filled with 300 mL of deionized water underneath the samples. The quantity of formaldehyde released was determined from the concentration of formaldehyde absorbed in deionized water based on the Hantzsch reaction between formaldehyde and ammonium ions and acetylacetone with an output of diacetyldihydrolutidine. The concentration of formaldehyde in the solution was determined photometrically [31]. The mechanical properties were determined by employing a universal testing machine, Zwick Roell 250 (Ulm, Germany), for the measurement of the modulus of rupture and the modulus of elasticity according to [32], the internal bond according to [33], and the thickness swelling and water absorption according to [34].
The values of thermal conductivity were not reported in this study, because they were described in the research of [27].

3. Results and Discussion

3.1. Free Formaldehyde Content and Formaldehyde Emission

With only one exception (sample bonded with 12% UF and 500 kg/m3), the mean values of free formaldehyde content corrected to 6.5% moisture content of the larch bark insulating boards glued with UF and tannin, determined by a perforator test, are included in the super E0 category, being lower than 1.5 mg/100 g oven dry (o.d.) (Figure 1). There is no significant difference between the free formaldehyde content of specimens bonded with UF or MUF for both density ranges of 300 and 500 kg/m3. In the case of tannin-based adhesive, the values did not reach more than 0.5 mg/100 g oven dry mass of panels.
At a density of 300 kg/m3, the highest amount of free formaldehyde was detected for the sample bonded with 12% UF (1.07 mg/100 g o.d.) and the lowest value for the sample bonded with 12% tannin-based adhesive (0.34 mg/100 g o.d.). This trend is due to the fact that formaldehyde reacts with tannins and produces polymerization through methylene bridges to reactive positions of the flavonoid molecules [35].
It is interesting how an amount of 12% UF and MUF adhesive results in higher levels of free formaldehyde content compared to a percentage of 16%. In the latter case, the measured values are all between 0.5 and 1.5 mg/100 g o.d. Urea acts indeed as a formaldehyde scavenger mingled with the polyphenols in the larch bark, the tannins. The reason for larch bark being able to retain formaldehyde and diminishing its emission [36] is due to its condensed tannin content of 56 ± 6 mg/kg of dry European larch bark (Larix decidua Mill.) [37]. The values of free formaldehyde content lower than 0.5 mg/100 g for the tannin-bonded panels are justified by the reaction of the hardener hexamine, which does not decompose to formaldehyde and ammonia due to the mixing with chemical species with very reactive nucleophilic sites, such as condensed flavonoid tannins. The results of this reaction are the building of aminomethylene bridges before any chance to yield formaldehyde [38]
The formaldehyde emission measured for the samples of larch bark-based insulation boards are all below 0.1 mg/L (Figure 2). That means that all the boards can be included in the F **** classification. From the four levels of formaldehyde limits defined by the Japanese International Standards (JIS), F **** is the most rigorous one, with an average value of less than 0.3 mg/L. It is also known as zero formaldehyde emission (≤0.3 mg/L) and is similar to the formaldehyde emission from natural wood (0.1–0.3 mg/L), determined through the desiccator method [25].
The same tendency observed for the free formaldehyde at 12% UF at 500 kg/m3 (Figure 2) was detected also for the formaldehyde emission of the same sample (three times bigger compared with the sample with 16% UF). For the other samples, the difference in glue percentage from 12% to 16% is interesting to observe because the increased adhesive amount does not significantly influence the level of formaldehyde emission (from 0 to 0.03 mg/L).

3.2. Mechanical and Physical Properties of Larch Bark Insulating Panels

Aside from the capacity of tannins to act as a formaldehyde scavenger, their effect on the mechanical and physical properties was determined in this study. The values for the modulus of rupture (MOR); modulus of elasticity (MOE); internal bond (IB); the dimensional stability—thickness swelling (TS) and water absorption (WA) after 24 h immersion in water at 20 °C—are presented in Table 2.

3.3. Moduli of Rupture and Elasticity

The dependence of MOR on density is clearly reflected in Figure 3. For the panels with 300 kg/m3, the MOR did not reach more than 0.4 N/mm2. The lowest values of MOR were measured for the samples bonded with tannin-based adhesive for all percentages of glue amounts. There is no significant influence on MOR considering the use of UF or MUF.
MOR increases at 500 kg/m3, being almost nine times higher than that of the panels with a density of 300 kg/m3. In this case, at 8% glue the values of MOR in the case of bonding with UF or MUF are quite similar. For 12% UF, the MOR of the panels is 3.27 N/mm2 and 30%, 40% higher compared with the 12% MUF and 12% tannin-based adhesive. An increase in the adhesive amount above 12% does not improve the MOR, with all the measured values being under 3 N/mm2.
The trend described for MOR is similar in the case of the measured values for MOE at both densities, with the exception of the tannin-based samples with a density of 300 kg/m3, which are 0 N/mm2 for all glue percentages (Figure 4). Twelve percent UF and MUF does not definitely influence the MOE. At 16% adhesive, the MOE is almost equal for UF and MUF. With increased density (500 kg/m3), the values of MOE increase too, from a minimum of 200 N/mm2 (8% tannin-based adhesive) to 560 N/mm2 (12% UF).

3.4. Internal Bond

The values of IB (Figure 5) are comparable for UF, MUF, and tannin for a glue amount of 8% and a density of 300 kg/m3 (up to 0.08 N/mm2). At 12% glue, UF and MUF perform analogously (0.09 N/mm2), and for the tannin-bonded panels an IB of 0.14 N/mm2 was recorded (the same value at 16% glue). There is a slight increase for 16% UF (0.17 N/mm2) compared to 0.15 and 0.14 N/mm2 for MUF and tannin adhesive, respectively. For the 500 kg/m³ density, at two levels of glue amount, 8% and 16%, the influence of adhesive is not significant. Only at 12% resin is there a significant difference between the values for MUF, tannin (0.32 N/mm2), and UF (0.38 N/mm2), which is at the same level (0.35 N/mm2) as the P2 particleboard (used for furniture components, partitions, flooring base, packaging, and sandwich panels) according to [39].

3.5. Thickness Swelling and Water Absorption after 24 h

The resin type significantly influences the TS and WA [27,40] reported about the increase in TS and WA when using tannin-based adhesives. For both density ranges, all the tannin-bonded samples recorded the highest values for thickness swelling (Figure 6) after 24 h of water immersion (18.5%, 11%, and 12%) for 8%, 12%, and 16% glue amounts (300 kg/m3) and 26%, 16%, and 13% at a density of 500 kg/m3. The testing specimens bonded with UF had the lowest thickness swelling—under 10% for a density of 300 kg/m3 and under 14.6% for 500 kg/m3.
More than 80% WA was measured for the tannin-glued samples for the three different glue amounts (Figure 7). With UF and MUF, the WA decreases under 100% at a density of 300 kg/m3, with a minimum of 68% for the MUF-bonded samples. When the density increases with 200 kg/m3, the water absorption of the tannin-bonded specimens is from 60% (16% glue) to 90% (8% glue), from 35% (12% glue) to 87% (8% glue) in the case of UF, and from 36% (12% glue) to 64% (8% glue). A lower adhesive amount has a direct influence on the dimensional stability of the insulation panels. The TS and WA improve at glue percentages of 12% and 16%, respectively.

4. Conclusions

The high amounts of tannins in the larch bark (about 30%) [37,41] determine a decrease in formaldehyde emissions due to the ability of larch bark to retain formaldehyde and diminish its emission due to its condensed tannin content [36]. Jahanshaei et al. [14] stated that the condensed polyflavonoid tannins (polyphenols) of the bark can withstand reactions with formaldehyde in both acid and alkaline media. With the exception of the panels bonded with 12% UF at a density of 500 kg/m3 with a measured perforator value (free formaldehyde content) of 1.85 mg/100 g o.d., which belongs to the E0 category (≤3.5 mg/100 g o.d.), the rest of the insulation boards are included in the super E0 category (≤1.5 mg/100 g o.d.).
Regarding the formaldehyde emission measured with desiccator method, all the investigated values were lower than 0.1 mg/L, which is three times lower than the limit for the F **** JIS classification for formaldehyde emissions. It results that the bark-based insulation panels present an increased eco-efficiency compared to wood, which has a level of 0.1–0.3 mg/L formaldehyde emission.
MOR is not one of the strengths of these panels. It was a maximum of 3 N/mm2 measured for the panel bonded with UF, while other values did not reach more than 2 N/mm2 when the other adhesives, MUF and tannin, were involved. Nevertheless, light bark particleboard will be probably used for non-structural applications where the MOR obtained is sufficient.
The MOE was zero for the tannin samples at a 300 kg/m3 density and reached 560 N/mm2 for the panels with 12% UF and 500 kg/m3. Both MOR and MOE are at a down level for all typed of bark-based insulation panels. The maximal value measured for the IB was 0.44 N/mm2, which is in accordance with the results of [27].
The dimensional stability was improved by the use of UF and MUF adhesives.
The use of bark for insulation panels ensured decreased levels of free formaldehyde content and formaldehyde emissions at a level which is not reachable when using only wood particles glued with the same adhesive types and amounts. The recyclability of these insulation panels compared with similar products, principally mineral-based, recommend this alternative and sustainable raw material tree bark for eco-friendly applications, especially for indoor purposes.
The specific impact on the reduction in free formaldehyde and formaldehyde content of the larch bark recommend this raw material for further research in green construction solutions.

Author Contributions

Conceptualization, M.C.B., Y.L. and S.H.; methodology, G.K., M.C.B. and A.P., validation, E.M.T., A.P.; formal analysis, E.M.T.; investigation, Y.L., S.H.; resources, S.H. and Y.L.; writing—original draft preparation E.M.T.; writing—review and editing, E.M.T., M.C.B., G.K.; visualization, G.K., A.P. and M.C.B.; supervision, E.M.T. and G.K. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Acknowledgments

We would like to address our thanks to Ing. Thomas Wimmer, FH Salzburg, Christian Fuchsberger, Kaindl Co, Wels, Austria, for the support with formaldehyde measurements. Our thanks go also to Untha Co., Kuchl, Austria, for the particle-size reduction, Dynea Co, Krems, Austria, for providing the UF and MUF adhesives for this project.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Wi, J.H.; Park, Y.U.; Kim, S. Evaluation of environmental impact on the formaldehyde emission and flame-retardant performance of thermal insulation materials. J. Hazard. Mater. 2020, 402, 123463. [Google Scholar] [CrossRef] [PubMed]
  2. Asdrubali, F.; D’Alessandro, F.; Schiavoni, S. A review of unconventional sustainable building insulation materials. Sustain. Mater. Technol. 2015, 4, 1–17. [Google Scholar] [CrossRef]
  3. Rudolphi, A.; Pfundstein, M. Insulating Materials: Principles, Materials, Applications; Walter De Gruyter: Basel, Switzerland, 2012; Available online: http://0-search-ebscohost-com.brum.beds.ac.uk/login.aspx?direct=true&scope=site&db=nlebk&db=nlabk&AN=642009 (accessed on 1 September 2020).
  4. Kalnæs, S.E.; Jelle, B.P. Vacuum insulation panel products: A state-of-the-art review and future research pathways. Appl. Energy. 2014, 116, 355–375. [Google Scholar] [CrossRef] [Green Version]
  5. Tsalagkas, D.; Börcsök, Z.; Pásztory, Z. Thermal, physical and mechanical properties of surface overlaid bark-based insulation panels. Eur. J. Wood Prod. 2019, 77, 721–730. [Google Scholar] [CrossRef] [Green Version]
  6. Hanson, J.L.; Kopp, K.B.; Yesiller, N.; Cooledge, C.M.; Klee, E. (Eds.) The Use of Recycled Materials as Thermal Insulation in Underground Construction; Humboldt State Univ.: Arcata, CA, USA, 2016. [Google Scholar]
  7. Bozsaky, D. Nature-Based Thermal Insulation Materials from Renewable Resources—A State-Of-The-Art Review. Slovak J. Civ. Eng. 2019, 27, 52–59. [Google Scholar] [CrossRef] [Green Version]
  8. Abdou, A.A.; Budaiwi, I.M. Comparison of Thermal Conductivity Measurements of Building Insulation Materials under Various Operating Temperatures. J. Build. Phys. 2005, 29, 171–184. [Google Scholar] [CrossRef]
  9. Naldzhiev, D.; Mumovic, D.; Strlic, M. Polyurethane insulation and household products—A systematic review of their impact on indoor environmental quality. Build. Environ. 2020, 169, 106559. [Google Scholar] [CrossRef]
  10. Klepeis, N.E.; Nelson, W.C.; Ott, W.R.; Robinson, J.P.; Tsang, A.M.; Switzer, P.; Behar, J.V.; Hern, S.C.; Engelmann, W.H. The National Human Activity Pattern Survey (NHAPS): A resource for assessing exposure to environmental pollutants. J. Expo. Anal. Environ. Epidemiol. 2001, 11, 231–252. [Google Scholar] [CrossRef] [Green Version]
  11. WHO. WHO Guidelines for Indoor Air Quality: Selected Pollutants; World Health Organization: Geneva, Switzerland, 2010. Available online: https://apps.who.int/iris/handle/10665/260127 (accessed on 1 September 2020).
  12. Tudor, E.M.; Barbu, M.C.; Petutschnigg, A.; Réh, R.; Krišťák, Ľ. Analysis of Larch-Bark Capacity for Formaldehyde Removal in Wood Adhesives. Int. J. Environ. Res. Public Health 2020, 17, 764. [Google Scholar] [CrossRef] [Green Version]
  13. Medved, S.; Gajsek, U.; Tudor, E.M.; Barbu, M.C.; Antonovic, A. Efficiency of bark for reduction of formaldehyde emission from particleboards. Wood Res. 2019, 2019, 307–316. [Google Scholar]
  14. Jahanshaei, S.; Tabarsa, T.; Asghari, J. Eco-friendly tannin-phenol formaldehyde resin for producing wood composites. Pigment Resin Technol. 2012, 41, 296–301. [Google Scholar] [CrossRef]
  15. Chai, Y.; Zhao, Y.; Yan, N. Synthesis and Characterization of Biobased Melamine Formaldehyde Resins from Bark Extractives. Ind. Eng. Chem. Res. 2014, 53, 11228–11238. [Google Scholar] [CrossRef]
  16. Marbun, S.D.; Wahyudi, I.; Suryana, J.; Nawawi, D.S. Bonding strength of benuang and duabanga glulams using their barks as phenol formaldehyde-filler. Appl. Adhes. Sci. 2020, 8. [Google Scholar] [CrossRef]
  17. Chen, H.; Yan, N. Application of Western red cedar (Thuja plicata) tree bark as a functional filler in pMDI wood adhesives. Ind. Crop. Prod. 2018, 113, 1–9. [Google Scholar] [CrossRef]
  18. Réh, R.; Igaz, R.; Krišťák, Ľ.; Ružiak, I.; Gajtanska, M.; Božíková, M.; Kučerka, M. Functionality of Beech Bark in Adhesive Mixtures Used in Plywood and Its Effect on the Stability Associated with Material Systems. Materials 2019, 12, 1298. [Google Scholar] [CrossRef] [Green Version]
  19. Mirski, R.; Kawalerczyk, J.; Dziurka, D.; Wieruszewski, M.; Trocinski, A. Effects of using bark particles with various dimensions as a filler for urea-formaldehyde resin in plywood. BioResources 2020, 2020, 1692–1701. [Google Scholar]
  20. Aydin, I.; Demirkir, C.; Colak, S.; Colakoglu, G. Utilization of bark flours as additive in plywood manufacturing. Eur. J. Wood Prod. 2017, 75, 63–69. [Google Scholar] [CrossRef]
  21. Skrypnik, L.; Grigorev, N.; Michailov, D.; Antipina, M.; Danilova, M.; Pungin, A. Comparative study on radical scavenging activity and phenolic compounds content in water bark extracts of alder (Alnus glutinosa (L.) Gaertn.), oak (Quercus robur L.) and pine (Pinus sylvestris L.). Eur. J. Wood Prod. 2019, 77, 879–890. [Google Scholar] [CrossRef]
  22. Kain, G.; Güttler, V.; Barbu, M.-C.; Petutschnigg, A.; Richter, K.; Tondi, G. Density related properties of bark insulation boards bonded with tannin hexamine resin. Eur. J. Wood Prod. 2014, 72, 417–424. [Google Scholar] [CrossRef]
  23. Petutschnigg, A.; Barbu, M.C.; Tudor, E.M.; Berger, G.; Tondi, G.; Kain, G. Neue Baumaterialien für nachhaltige Konstruktionen. Österreichische Ing. Archit. Z. 2017, 2017, 159–163. [Google Scholar]
  24. Zhu, H.; Lu, Z.; Li, X.; Zhang, J.; Yuan, M. Analysis on test methods for determining formaldehyde emission from wood-based products. China Wood Ind. 2009, 2009, 37–40. [Google Scholar]
  25. Zhang, J.; Song, F.; Tao, J.; Zhang, Z.; Shi, S.Q. Research Progress on Formaldehyde Emission of Wood-Based Panel. Int. J. Polym. Sci. 2018, 2018, 1–8. [Google Scholar] [CrossRef]
  26. Kain, G.; Stratev, D.; Tudor, E.M.; Lienbacher, B.; Weigl, M.; Barbu, M.C.; Petutschnigg, A. Qualitative investigation on VOC-emissions from spruce (Picea abies) and larch (Larix decidua) loose bark and bark panels. Eur. J. Wood Prod. 2020, 78, 403–412. [Google Scholar] [CrossRef] [Green Version]
  27. Kain, G.; Tudor, E.M.; Barbu, M.C. Bark Thermal Insulation Panels: An Explorative Study on the Effects of Bark Species. Polymers 2020, 12, 2140. [Google Scholar] [CrossRef]
  28. Wood-Based Panels—Determination of Formaldehyde Release—Part 5: Extraction Method (Called the Perforator Method); EN ISO 12460-5:2016; ISO: Geneva, Switzerland, 2016.
  29. Salthammer, T.; Mentese, S.; Marutzky, R. Formaldehyde in the indoor environment. Chem. Rev. 2010, 110, 2536–2572. [Google Scholar] [CrossRef]
  30. Wood-Based Panels—Sampling and Cutting of Test Pieces; ISO-16999:2003; European Committee for Standardization: Brussels, Belgium, 2003.
  31. Determination of the Emission of Formaldehyde from Building Boards—Desiccator Method; JIS A 1460:2015; European Committee for Standardization: Brussels, Belgium, 2015.
  32. Wood-Based Panels. Determination of Modulus of Elasticity in Bending and of Bending Strength; EN 310:1993; European Committee for Standardization: Brussels, Belgium, 1993.
  33. Particleboards and Fibreboards. Determination of Tensile Strength Perpendicular to the Plane of the Board; EN 319:1993; European Committee for Standardization: Brussels, Belgium, 1993.
  34. Particleboards and Fibreboards. Determination of Swelling in Thickness after Immersion in Water; EN 317:1993; European Committee for Standardization: Brussels, Belgium, 1993.
  35. Pizzi, A. Hot-setting tannin–urea–formaldehyde exterior wood adhesives. Adhes. Age 1977, 1977, 17–29. [Google Scholar]
  36. Cameron, F.A.; Pizzi, A. Tannin-induced formaldehyde release depression in urea-formaldehyde particleboard. In Formaldehyde Release from Wood Products; Chapter 15; Meyer, B., Kottes-Andrews, B.A., Reinardt, R.M., Eds.; American Chemical Society Symposium Series; ACS Publications: Washington, DC, USA, 1985; p. 205. [Google Scholar]
  37. Bianchi, S. Extraction and Characterization of Bark Tannins from Domestic Softwood Species. Ph.D. Thesis, Faculty of Mathematics, Informatics and Natural Sciences, Department of Biology, University of Hamburg, Hamburg, Germany, 2016. [Google Scholar]
  38. Pizzi, A. Types, processing and properties of bioadhesives for wood and fibers. In Advances in Biorefineries; Waldron, K., Ed.; Woodhead Publishing: Cambridge, UK, 2014. [Google Scholar]
  39. Wood-Based Panels for Use in Construction—Characteristics, Evaluation of Conformity and Marking; EN 13986:2015; European Committee for Standardization: Brussels, Belgium, 2015.
  40. Tudor, E.M.; Barbu, M.C.; Petutschnigg, A.; Réh, R. Added-value for wood bark as a coating layer for flooring tiles. J. Clean. Prod. 2018, 170, 1354–1360. [Google Scholar] [CrossRef]
  41. Sachsse, H.A. Eigenschaften und Verwertung des Lärchenholzes. Allg. Forstz. 1979, 1979, 118–122. [Google Scholar]
Polymers 12 02632 g001 550
Figure 1. Free formaldehyde content (mg/100 g o.d.) for both the measured and (moisture-)corrected values for larch-bark insulating boards (300 and 500 kg/m3).
Figure 1. Free formaldehyde content (mg/100 g o.d.) for both the measured and (moisture-)corrected values for larch-bark insulating boards (300 and 500 kg/m3).
Polymers 12 02632 g001
Polymers 12 02632 g002 550
Figure 2. Formaldehyde emission (mg/L) of the larch bark-based insulation boards 300 and 500 kg/m3 bonded with UF, MUF, and tannin-based adhesives.
Figure 2. Formaldehyde emission (mg/L) of the larch bark-based insulation boards 300 and 500 kg/m3 bonded with UF, MUF, and tannin-based adhesives.
Polymers 12 02632 g002
Polymers 12 02632 g003 550
Figure 3. Modulus of rupture at three levels of glue amount for 300 kg/m3 (left) and 500 kg/m3 (right).
Figure 3. Modulus of rupture at three levels of glue amount for 300 kg/m3 (left) and 500 kg/m3 (right).
Polymers 12 02632 g003
Polymers 12 02632 g004 550
Figure 4. Modulus of elasticity at three levels of glue amount for 300 kg/m3 (left) and 500 kg/m3 (right).
Figure 4. Modulus of elasticity at three levels of glue amount for 300 kg/m3 (left) and 500 kg/m3 (right).
Polymers 12 02632 g004
Polymers 12 02632 g005 550
Figure 5. Internal bond at three levels of glue amount for 300 kg/m3 (left) and 500 kg/m3 (right).
Figure 5. Internal bond at three levels of glue amount for 300 kg/m3 (left) and 500 kg/m3 (right).
Polymers 12 02632 g005
Polymers 12 02632 g006 550
Figure 6. Thickness swelling after 24 h at three levels of glue amount for 300 kg/m3 (left) and 500 kg/m3 (right).
Figure 6. Thickness swelling after 24 h at three levels of glue amount for 300 kg/m3 (left) and 500 kg/m3 (right).
Polymers 12 02632 g006
Polymers 12 02632 g007 550
Figure 7. Water absorption after 24 h at three levels of glue amount for 300 kg/m3 (left) and 500 kg/m3 (right).
Figure 7. Water absorption after 24 h at three levels of glue amount for 300 kg/m3 (left) and 500 kg/m3 (right).
Polymers 12 02632 g007
Table
Table 1. Experimental design with the factors density and resin content (based on the oven-dried weight of bark particles).
Table 1. Experimental design with the factors density and resin content (based on the oven-dried weight of bark particles).
BoardDensityGlueGlueMoisture
(kg/m3)TypeAmount (%)Content (%)
UF1500UF88.7
UF2500UF1210.1
UF3500UF168.7
UF4300UF88.4
UF5300UF129.6
UF6300UF168.2
MUF1500MUF84.2
MUF2500MUF124.4
MUF3500MUF164.8
MUF4300MUF89.2
MUF5300MUF127.7
MUF6500MUF88.4
T1500Tannin125.8
T2500Tannin167.3
T3300Tannin89.9
T4300Tannin127.6
T5300Tannin168.4a
T6300Tannin165.9
Table
Table 2. Mechanical and physical properties of the larch-bark insulation panels (standard deviation in parentheses).
Table 2. Mechanical and physical properties of the larch-bark insulation panels (standard deviation in parentheses).
SampleMOR (N/mm2)MOE (N/mm2)IB (N/mm2)TS 24 h (%)WA 24 h (%)
300UF80.29 (0.03)35.02 (3.62)0.07 (0.01)8.5 (0.81)93.71 (2.02)
300UF120.33 0.04)57.15 (12.98)0.09 (0.02)6.54 (1.9)81.75 (1.2)
300UF160.38 (0.02)50.22 (5.35)0.17 (0.04)5.21 (1.98)70.86 (0.56)
500UF81.39 (0.17)283.18 (29.95)0.19 (0.02)14.64 (0.93)78.08 (1.68)
500UF123.27 (0.53)556.78 (26.36)0.38 (0.04)8.42 (1.35)34.79 (3.31)
500UF162.01 (0.09)403.05 (73.24)0.44 (0.03)7.18 (1.1)43.8 (7.29)
300MUF80.19 (0.07)34.36 (2.15)0.08 (0.02)10.41 (1.71)87.09 (4.35)
300MUF120.37 (0.02)63.16 (6.83)0.09 (0)8.72 (1.9)75.23 (3.43)
300MUF160.38 (0.06)52 (5.92)0.15 (0.02)9.38 (3.04)67.55 (3.92)
500MUF81.55 (0.01)278.16 (7.03)0.21 (0)13.36 (2.81)64.21 (3.96)
500MUF122.33 (0.09)414.41 (13.68)0.32 (0.03)8.86 (1.24)47.48 (5.99)
500MUF162.92 (0.61)511.28 (53.99)0.45 (0.06)7.51 (0.61)36.14 (4.89)
300T80.05 (0.01)0 (0)0.07 (0.01)18.47 (2.34)105.3 (1.08)
300T120.07 (0)0 (0)0.14 (0.01)10.79 (1.59)93.71 (2.23)
300T160.05 (0)0 (0)0.14 (0.01)11.85 (1.75)91.81 (0.91)
500T80.94 (0.07)187.72 (16.32)0.18 (0.01)25.89 (1.74)91.53 (2.16)
500T121.87 (0.09)363.59 (11.05)0.32 (0.03)15.59 (1.42)73.41 (6.16)
500T162.24 (0.39)432.26 (41.71)0.43 (0.01)13.06 (1.34)57.86 (8.84)
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Barbu, M.C.; Lohninger, Y.; Hofmann, S.; Kain, G.; Petutschnigg, A.; Tudor, E.M. Larch Bark as a Formaldehyde Scavenger in Thermal Insulation Panels. Polymers 2020, 12, 2632. https://0-doi-org.brum.beds.ac.uk/10.3390/polym12112632

AMA Style

Barbu MC, Lohninger Y, Hofmann S, Kain G, Petutschnigg A, Tudor EM. Larch Bark as a Formaldehyde Scavenger in Thermal Insulation Panels. Polymers. 2020; 12(11):2632. https://0-doi-org.brum.beds.ac.uk/10.3390/polym12112632

Chicago/Turabian Style

Barbu, Marius Cătălin, Yasmin Lohninger, Simon Hofmann, Günther Kain, Alexander Petutschnigg, and Eugenia Mariana Tudor. 2020. "Larch Bark as a Formaldehyde Scavenger in Thermal Insulation Panels" Polymers 12, no. 11: 2632. https://0-doi-org.brum.beds.ac.uk/10.3390/polym12112632

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.